The Al/fly ash composites are fabricated by liquid reactive sintering P/M process with fly ash particles as intensifying phases. The reactivity and newly formed phases during liquid sintering process have been analyze...The Al/fly ash composites are fabricated by liquid reactive sintering P/M process with fly ash particles as intensifying phases. The reactivity and newly formed phases during liquid sintering process have been analyzed by combing Thermochemicdl data base calculation and XRD characterization. The results show that some of constituents in fly ash have reacted with liquid aluminum so that the elemental Si, Fe, Ti as well as some amount of intermetallic compounds occur. The properties of aluminum/fly ash composites have been improved. With the fraction of fly ash increase, the composite density decreases; the hardness and the modulus of the composite increases, and the composite wear resistance are significantly increased. The fly ash reinforced composites represent a sort of low cost product with possible widespread applications in the automotive, small engine, and electromechanical machinery sectors.展开更多
To reveal the influence of mechanical activation on the performance of fly ash, the microanalysis（the energy spectroscopy, XRD and SEM）, the distribution size of particle of fly ash and cement paste intensity of var...To reveal the influence of mechanical activation on the performance of fly ash, the microanalysis（the energy spectroscopy, XRD and SEM）, the distribution size of particle of fly ash and cement paste intensity of various age for different grinding time were studied. The relationships of the activity and the composition of fly ash, microstructure and the distribution of particle size by mechanical activation of fly ash were obtained. The internal glass beads with activity were released by grinding fly ash for a certain time. The particle specific surface area was improved and the hydration reaction of the interface and the surface active center was increased by grinding. The granularity distributing of fly-ash trended towards optimization. The polar molecules or ions were easier to intrude into the internal cavity of the vitreous body. The active silica and alumina of fly ash were rapidly depolymerized. Each performance index of fly ash was increased before grinding for 20 min. Cement paste intensity of various age increased along with the grinding time, and the early strength increase range was big, but the later period intensity increase range hastened slightly. The internal part of vitreous of fly ash was destroyed if the fly ash continued to be ground and the activity of fly ash was reduced. It is suggested that Guozhuang＇s fly ash should be ground for 20 min.展开更多
文摘The Al/fly ash composites are fabricated by liquid reactive sintering P/M process with fly ash particles as intensifying phases. The reactivity and newly formed phases during liquid sintering process have been analyzed by combing Thermochemicdl data base calculation and XRD characterization. The results show that some of constituents in fly ash have reacted with liquid aluminum so that the elemental Si, Fe, Ti as well as some amount of intermetallic compounds occur. The properties of aluminum/fly ash composites have been improved. With the fraction of fly ash increase, the composite density decreases; the hardness and the modulus of the composite increases, and the composite wear resistance are significantly increased. The fly ash reinforced composites represent a sort of low cost product with possible widespread applications in the automotive, small engine, and electromechanical machinery sectors.
基金Funded by the National Natural Science Foundation of China(No.51574055)
文摘To reveal the influence of mechanical activation on the performance of fly ash, the microanalysis（the energy spectroscopy, XRD and SEM）, the distribution size of particle of fly ash and cement paste intensity of various age for different grinding time were studied. The relationships of the activity and the composition of fly ash, microstructure and the distribution of particle size by mechanical activation of fly ash were obtained. The internal glass beads with activity were released by grinding fly ash for a certain time. The particle specific surface area was improved and the hydration reaction of the interface and the surface active center was increased by grinding. The granularity distributing of fly-ash trended towards optimization. The polar molecules or ions were easier to intrude into the internal cavity of the vitreous body. The active silica and alumina of fly ash were rapidly depolymerized. Each performance index of fly ash was increased before grinding for 20 min. Cement paste intensity of various age increased along with the grinding time, and the early strength increase range was big, but the later period intensity increase range hastened slightly. The internal part of vitreous of fly ash was destroyed if the fly ash continued to be ground and the activity of fly ash was reduced. It is suggested that Guozhuang＇s fly ash should be ground for 20 min.