化学法制备Al_2O_3包覆TiH_2颗粒发泡剂

利用非均匀成核法 ,以 pH缓冲溶液作沉淀剂 ,研究了Al2 O3 包覆TiH2 粉末的包裹技术。结果表明 ,Al3 + 浓度对包覆层显微结构有影响 ,当Al3 + 浓度为 0 .0 5mol/L ,pH值为 4.5时 ,可以获得好的氧化铝前驱体包覆TiH2 颗粒 ,经 35 0℃煅烧可得到均匀、致密的Al2 O3 /TiH2 包覆颗粒。当包覆层厚大于 1.42 μm时 ,Al2 O3 /TiH2 包覆颗粒释放氢气过程被显著地延迟 ,这种延迟效应对泡沫铝制备具有重要的实用价值。采用Al2 O3 /TiH2包覆粉体作为发泡剂 ,成功制备出多孔泡沫铝材料。

Al_2O_3/TiH_2包覆粉体的制备及其释氢性能的研究

The technique to prepare TiH\-2 coated with layers of Al\-2O\-3 particles by heterogeneous nucleation method with HAc\|NaAc buffer solution as precipitation reagent was studied. The results show that the microscopic structure of Al\-2O\-3 coating layers depends on the pH value and Al\+\{3+\} concentration range in the solution. The homogeneous and compact coating layers with Al\-2O\-3\|coated TiH\-2 particles can be obtained at 0.05 mol/L and pH=4.5, after heating at 350 ℃. The hydrogen releasing of Al\-2O\-3/TiH\-2 particle is notably delayed with the increase of the temperature, and the delay effect can be used in the production of Al foams.

SiO_2/Al_2O_3复合包覆TiH_2颗粒的制备及释氢性能的研究

采用非均匀成核法,通过控制滴加反应物的速度、pH值等,实现SiO2和Al2O3在TiH2颗粒表面形核,制备包覆有SiO2和Al2O3的复合型TiH2发泡剂.观察了包覆层形貌,进行了释氢试验.实验结果表明:SiO2/Al2O3包覆层平滑、分布均匀,形成内松外紧的结构,使得释氢时间达到120s.

TiH_2表面包覆SiO_2的结构和机理分析及释氢性能的研究

采用非均相形核法,以HCl为酸化剂在TiH_2颗粒发泡剂表面合成了SiO_2包覆层,并进行释氢试验。采用扫描电子显微镜(SEM)和能谱(EDS)对包覆层结构进行了分析,探讨了包覆层延缓释放氢气的机理。结果表明,pH值对发泡剂表面的成膜过程影响较大,当溶液pH值为9.5时SiO_2在TiH_2颗粒表面形成致密的包覆层;制得的发泡剂有效延迟释氢时间可达120s。