Light-weight magnesium -aluminate spinel materi- als were prepared by foaming-gel process with polyalumi- nium chloride （PAC） as gel. Effect of solid loading in initial slurry on microstructure, porosity, pore size ...Light-weight magnesium -aluminate spinel materi- als were prepared by foaming-gel process with polyalumi- nium chloride （PAC） as gel. Effect of solid loading in initial slurry on microstructure, porosity, pore size distri- bution, thermal conductivity and mechanical properties was investigated. The results show that the bulk density of the light-weight magnesium -aluminate spinel mate- rials is in the range of O. 7 1.2 g cm-3 ; pore size distribution curves show single-peak characteristics and the mean pore size is in the range of 30. 83 - 61.37 μm ; with the increase of solid loading, the linear shrinkage of the green body during firing and the permanent change in dimensions on heating at l 600 ℃ for 3 h de- crease, but the bulk density increases, the mechanical properties increase obviously; the maximum compressive strength and bending strength reach 35. 25 MPa and 9. 92 MPa, respectively, while the bulk density is 1. 16 g · cm ; and the thermal conductivity at 1 000 ℃ tea- ches 0. 371 W · m-1 . K-1 while the bulk density is O. 7 -3 g · cm展开更多
基金supported by the National Basic Research Program of China(973 Program,No.2010CB735810)
文摘Light-weight magnesium -aluminate spinel materi- als were prepared by foaming-gel process with polyalumi- nium chloride （PAC） as gel. Effect of solid loading in initial slurry on microstructure, porosity, pore size distri- bution, thermal conductivity and mechanical properties was investigated. The results show that the bulk density of the light-weight magnesium -aluminate spinel mate- rials is in the range of O. 7 1.2 g cm-3 ; pore size distribution curves show single-peak characteristics and the mean pore size is in the range of 30. 83 - 61.37 μm ; with the increase of solid loading, the linear shrinkage of the green body during firing and the permanent change in dimensions on heating at l 600 ℃ for 3 h de- crease, but the bulk density increases, the mechanical properties increase obviously; the maximum compressive strength and bending strength reach 35. 25 MPa and 9. 92 MPa, respectively, while the bulk density is 1. 16 g · cm ; and the thermal conductivity at 1 000 ℃ tea- ches 0. 371 W · m-1 . K-1 while the bulk density is O. 7 -3 g · cm