The preparing method,rolling technology and mechanical properties of low chromium semi-steel grinding ball by cross rolling were studied.The results show that when the low chromium semi-steel bar is forged from55mm to...The preparing method,rolling technology and mechanical properties of low chromium semi-steel grinding ball by cross rolling were studied.The results show that when the low chromium semi-steel bar is forged from55mm to50mm,cross-rolled into grinding ball at 1 000-1 050℃,air cooled and tempered at 550℃for 2h,the best mechanical properties,especially the abrasive resistance under the action of hard abrasive,can be obtained.展开更多
The low-energy, multi-impact fracture resistance and the abrasiveness of the cross-rolled low alloy white cast iron grinding balls were studied after heat treatments at residual rolling temperature. Moreover, the mean...The low-energy, multi-impact fracture resistance and the abrasiveness of the cross-rolled low alloy white cast iron grinding balls were studied after heat treatments at residual rolling temperature. Moreover, the means by which they are damaged and characters of the wear surface were analyzed. The results show that high resistance to impact fracture and high abrasiveness can be achieved after appropriate heat treatment at residual rolling temperature. This kind of heat treatment technology has several advantages under low impact and hard abrasive. These results are very useful for determining the optimized heat treatment technology at residual rolling temperatures.展开更多
The low-energy multi-impact fracture resistance of the cross rolled low chromium cast semi-steel containing RE grinding balls was studied. Moreover, its damage mode was analyzed by means of metallographic examination,...The low-energy multi-impact fracture resistance of the cross rolled low chromium cast semi-steel containing RE grinding balls was studied. Moreover, its damage mode was analyzed by means of metallographic examination, scanning electron microscopic examination and drop ball test. The results show that it can obtain extractive impact fracture resistance after proper heat treatment. More advantages were obtained for the ball worked in the condition of low-imp ductility act. The main reasons are the function of RE and the change in morphology of eutectic carbide network.展开更多
基金Item Sponsored by Guiding Program of Science and Technology Research of Hebei of China(94122123)
文摘The preparing method,rolling technology and mechanical properties of low chromium semi-steel grinding ball by cross rolling were studied.The results show that when the low chromium semi-steel bar is forged from55mm to50mm,cross-rolled into grinding ball at 1 000-1 050℃,air cooled and tempered at 550℃for 2h,the best mechanical properties,especially the abrasive resistance under the action of hard abrasive,can be obtained.
基金Item Sponsored by Guiding Program of Science and Technology Research of Jilin Province of China (20000513)
文摘The low-energy, multi-impact fracture resistance and the abrasiveness of the cross-rolled low alloy white cast iron grinding balls were studied after heat treatments at residual rolling temperature. Moreover, the means by which they are damaged and characters of the wear surface were analyzed. The results show that high resistance to impact fracture and high abrasiveness can be achieved after appropriate heat treatment at residual rolling temperature. This kind of heat treatment technology has several advantages under low impact and hard abrasive. These results are very useful for determining the optimized heat treatment technology at residual rolling temperatures.
文摘The low-energy multi-impact fracture resistance of the cross rolled low chromium cast semi-steel containing RE grinding balls was studied. Moreover, its damage mode was analyzed by means of metallographic examination, scanning electron microscopic examination and drop ball test. The results show that it can obtain extractive impact fracture resistance after proper heat treatment. More advantages were obtained for the ball worked in the condition of low-imp ductility act. The main reasons are the function of RE and the change in morphology of eutectic carbide network.