The alteration of the strength, hardness and impact ductility of 5CrNiMo steel using three different additions of RE La element is studied in this paper. The mechanical properties of 5CrNiMo steel with RE La additions...The alteration of the strength, hardness and impact ductility of 5CrNiMo steel using three different additions of RE La element is studied in this paper. The mechanical properties of 5CrNiMo steel with RE La additions are be compared with that of the 5CrNiMo steel on the same heat-treatment condition without RE La element addition. The results show that the strength, hardness and impact ductility of 5CrNiMo steel will be improved obviously when the content of RE La element is proper, and as the content of RE La element is 0.033%(mass fraction), the 5CrNiMo steel has the best mechanical properties.展开更多
The fatigue behavior of cemented carbide die under service load in the multistage cold forging of steel was investigated. It was found that the fatigue cracks do not initiate at the stress concentration position and t...The fatigue behavior of cemented carbide die under service load in the multistage cold forging of steel was investigated. It was found that the fatigue cracks do not initiate at the stress concentration position and the crack initiation position can be classified to three types. The crack initiation position can be predicted by FEM only when the plastic deformation of the die is considered.展开更多
文摘The alteration of the strength, hardness and impact ductility of 5CrNiMo steel using three different additions of RE La element is studied in this paper. The mechanical properties of 5CrNiMo steel with RE La additions are be compared with that of the 5CrNiMo steel on the same heat-treatment condition without RE La element addition. The results show that the strength, hardness and impact ductility of 5CrNiMo steel will be improved obviously when the content of RE La element is proper, and as the content of RE La element is 0.033%(mass fraction), the 5CrNiMo steel has the best mechanical properties.
文摘The fatigue behavior of cemented carbide die under service load in the multistage cold forging of steel was investigated. It was found that the fatigue cracks do not initiate at the stress concentration position and the crack initiation position can be classified to three types. The crack initiation position can be predicted by FEM only when the plastic deformation of the die is considered.