Theoretical consideration was conducted on a relation between pore diameter and interfacialarea between pores and fibers when pores uniforinly distribute in C/C composites. It was shownthat bonding at the fiber/matrix...Theoretical consideration was conducted on a relation between pore diameter and interfacialarea between pores and fibers when pores uniforinly distribute in C/C composites. It was shownthat bonding at the fiber/matrix interface apparently decreased with decreasing a pore diameter,and consequently a new idea of microspace modification concept was proposed for controllingfracture behavior of C/C composites. Four types of C/C composites with various pore structureswere fabricated by hot-pressing, and their fracture behavior was investigated by three pointbending tests. The fracture behavior of the C/C composites was changed from brittle one topseudo ductile one with decreasing the pore diameter. This result supported the validity of themicrospace modification concept proposed in this paper.展开更多
文摘Theoretical consideration was conducted on a relation between pore diameter and interfacialarea between pores and fibers when pores uniforinly distribute in C/C composites. It was shownthat bonding at the fiber/matrix interface apparently decreased with decreasing a pore diameter,and consequently a new idea of microspace modification concept was proposed for controllingfracture behavior of C/C composites. Four types of C/C composites with various pore structureswere fabricated by hot-pressing, and their fracture behavior was investigated by three pointbending tests. The fracture behavior of the C/C composites was changed from brittle one topseudo ductile one with decreasing the pore diameter. This result supported the validity of themicrospace modification concept proposed in this paper.