In this study,the tribological behaviors of graphene as a lubricant additive for steel/copper and steel/steel friction pairs were compared.For the steel/copper friction pair,the graphene sheets remarkably decreased th...In this study,the tribological behaviors of graphene as a lubricant additive for steel/copper and steel/steel friction pairs were compared.For the steel/copper friction pair,the graphene sheets remarkably decreased the coefficient of friction and wear scar depth under low loads,but these slightly increased under high loads.The steel/steel friction pair showed excellent tribological properties even under high loads.Severe plastic deformation on the copper surface reduced the stability of the graphene tribofilm because of a rough copper transfer film on the steel during the running-in period.The results provide a better understanding of the mechanism of graphene as a lubricant additive.展开更多
The corrosion and tribocorrosion behaviors of AISI 304 austenitic stainless steel and Cr26Mo1 ultrapure high chromium ferrite stainless steel in 3.5 wt.%NaCl and 0.5 mol/L H2SO4 solutions were investigated.Microelectr...The corrosion and tribocorrosion behaviors of AISI 304 austenitic stainless steel and Cr26Mo1 ultrapure high chromium ferrite stainless steel in 3.5 wt.%NaCl and 0.5 mol/L H2SO4 solutions were investigated.Microelectrode electrochemical measurement technology was applied to identify electrochemistry behaviors during tribocorrosion tests in situ.The surface morphologies and compositions of the wear tracks were analyzed by scanning electron microscopy and Raman spectrum.The results showed that compositions of stainless steels,corrosive mediums and applied loads have great influence on tribocorrosion behaviors of stainless steels.Firstly,the corrosion resistance in static state of stainless steels primarily dominates its tribocorrosion behavior;meanwhile,better mechanical properties are in favor of tribocorrosion resistance.Secondly,the corrosion rate is promoted significantly in 3.5%NaCl solution by friction,while the tendency is inconspicuous in 0.5 mol/L H2SO4 solution.Last but not least,passive films on stainless steels can be wiped off by small friction force.With the increase in applied load,the effect of friction converts to forming friction oxide film from removing passivation film,so that a critical load exists below which the friction force can promote the corrosion process extremely.展开更多
基金This work was supported by National Natural Science Foundation of China(Nos.51527901 and 51335005)the National Key Basic Research Program of China(973 Program,No.2014CB046404)Tribology Science Fund of State Key Laboratory of Tribology(No.SKLTKF18A02).
文摘In this study,the tribological behaviors of graphene as a lubricant additive for steel/copper and steel/steel friction pairs were compared.For the steel/copper friction pair,the graphene sheets remarkably decreased the coefficient of friction and wear scar depth under low loads,but these slightly increased under high loads.The steel/steel friction pair showed excellent tribological properties even under high loads.Severe plastic deformation on the copper surface reduced the stability of the graphene tribofilm because of a rough copper transfer film on the steel during the running-in period.The results provide a better understanding of the mechanism of graphene as a lubricant additive.
基金supported by PetroChina Key Core Technology Project(21ZG10)the Strategic Priority Research Program of the Chinese Academy of Sciences(Grant No.XDC04040400).
文摘The corrosion and tribocorrosion behaviors of AISI 304 austenitic stainless steel and Cr26Mo1 ultrapure high chromium ferrite stainless steel in 3.5 wt.%NaCl and 0.5 mol/L H2SO4 solutions were investigated.Microelectrode electrochemical measurement technology was applied to identify electrochemistry behaviors during tribocorrosion tests in situ.The surface morphologies and compositions of the wear tracks were analyzed by scanning electron microscopy and Raman spectrum.The results showed that compositions of stainless steels,corrosive mediums and applied loads have great influence on tribocorrosion behaviors of stainless steels.Firstly,the corrosion resistance in static state of stainless steels primarily dominates its tribocorrosion behavior;meanwhile,better mechanical properties are in favor of tribocorrosion resistance.Secondly,the corrosion rate is promoted significantly in 3.5%NaCl solution by friction,while the tendency is inconspicuous in 0.5 mol/L H2SO4 solution.Last but not least,passive films on stainless steels can be wiped off by small friction force.With the increase in applied load,the effect of friction converts to forming friction oxide film from removing passivation film,so that a critical load exists below which the friction force can promote the corrosion process extremely.