A high strength self-compacting pervious concrete(SCPC) with top-bottom interconnected pores was prepared in this paper. The frost-resisting durability of such SCPC in different deicing salt concentrations(0%, 3%, 5%,...A high strength self-compacting pervious concrete(SCPC) with top-bottom interconnected pores was prepared in this paper. The frost-resisting durability of such SCPC in different deicing salt concentrations(0%, 3%, 5%, 10%, and 20%) was investigated. The mass-loss rate, relative dynamic modulus of elasticity, compressive strength, flexural strength and hydraulic conductivity of SCPC after 300 freeze-thaw cycles were measured to evaluate the frost-resisting durability. In addition, the microstructures of SCPC near the top-bottom interconnected pores after 300 freeze-thaw cycles were observed by SEM. The results show that the high strength SCPC possesses much better frost-resisting durability than traditional pervious concrete(TPC) after 300 freeze-thaw cycles, which can be used in heavy loading roads. The most serious freeze-thaw damage emerges in the SCPC immersed in the 3% of Na Cl solution, while there is no obvious damage in 20% of Na Cl solution. Furthermore, it can be deduced that the high strength SCPC can be used for 100 years in a cold environment.展开更多
The purpose of this study is to comparatively evaluate the wear resistance of concretes under abrasion rates. Five concrete mix proportions of a fixed water-cement ratio of 0.45 were considered in the study, but the c...The purpose of this study is to comparatively evaluate the wear resistance of concretes under abrasion rates. Five concrete mix proportions of a fixed water-cement ratio of 0.45 were considered in the study, but the constituent materials, age of concrete and exposure contact conditions were varied. The coarse aggregate type employed in the study was crushed granite. The compressive strength and abrasion resistance of concretes were tested between at ages 7 to 70 days and 100 - 500 revolutions of abrasion wheels respectively. The study revealed that the compressive strength and abrasion resistance had the optimal performance when the coarse aggregate content was 45% and the worst performance when the fine aggregate content was 28.7% of the total weight of concrete constituents. There was a remarkable loss of concrete particles to wear between 200 revs and 300 revs of abrasion wheel contact. Concrete grade in excess of 60 N/mm2 is required to resist abrasion beyond 200 revolutions of abrasion wheel contact on concrete specimens. Concretes investigated also showed weak resistance to deep abrasion at and above 300 revolutions of abrasion wheel contact.展开更多
基金Funded by the National Natural Science Foundation of China(No.51878081).
文摘A high strength self-compacting pervious concrete(SCPC) with top-bottom interconnected pores was prepared in this paper. The frost-resisting durability of such SCPC in different deicing salt concentrations(0%, 3%, 5%, 10%, and 20%) was investigated. The mass-loss rate, relative dynamic modulus of elasticity, compressive strength, flexural strength and hydraulic conductivity of SCPC after 300 freeze-thaw cycles were measured to evaluate the frost-resisting durability. In addition, the microstructures of SCPC near the top-bottom interconnected pores after 300 freeze-thaw cycles were observed by SEM. The results show that the high strength SCPC possesses much better frost-resisting durability than traditional pervious concrete(TPC) after 300 freeze-thaw cycles, which can be used in heavy loading roads. The most serious freeze-thaw damage emerges in the SCPC immersed in the 3% of Na Cl solution, while there is no obvious damage in 20% of Na Cl solution. Furthermore, it can be deduced that the high strength SCPC can be used for 100 years in a cold environment.
文摘The purpose of this study is to comparatively evaluate the wear resistance of concretes under abrasion rates. Five concrete mix proportions of a fixed water-cement ratio of 0.45 were considered in the study, but the constituent materials, age of concrete and exposure contact conditions were varied. The coarse aggregate type employed in the study was crushed granite. The compressive strength and abrasion resistance of concretes were tested between at ages 7 to 70 days and 100 - 500 revolutions of abrasion wheels respectively. The study revealed that the compressive strength and abrasion resistance had the optimal performance when the coarse aggregate content was 45% and the worst performance when the fine aggregate content was 28.7% of the total weight of concrete constituents. There was a remarkable loss of concrete particles to wear between 200 revs and 300 revs of abrasion wheel contact. Concrete grade in excess of 60 N/mm2 is required to resist abrasion beyond 200 revolutions of abrasion wheel contact on concrete specimens. Concretes investigated also showed weak resistance to deep abrasion at and above 300 revolutions of abrasion wheel contact.