A new composite two component grout comprised of modified urea-formaldehyde resin and cement was formulated to take account of the advantages and disadvantages of both the cement grout and the chem- ical grout. The ne...A new composite two component grout comprised of modified urea-formaldehyde resin and cement was formulated to take account of the advantages and disadvantages of both the cement grout and the chem- ical grout. The new grout is designed for water blocking by reinforcing as well as seepage control by bore grouting. The A component consists of a modified urea-formaldehyde resin A component, some cement, and some water. The B component is an alkaline coagulant. An orthogonal test of four factors at three lev- els showed that gel time increased with increased water content and with urea-formaldehyde resin con- tent. Gel time decreased at increased levels of alkaline coagulant. The A component of this new composite grout is stable over time. A mixed cross-over test showed that as the volume ratio of A to B increases the gel time falls at first but then increases. The solid strength decreases with increasing levels of the B com- ponent. The solid strength increases over time and becomes stable by the 28th day after mixing. The vis- cosity increases with increasing levels of resin A component. The increase is exponential and may be fit to： μ = 8.162e0.0286x.展开更多
The selective water plugging agent was prepared by heating the blends of the polyacry-lamide inverse latex, modified urea formaldehyde resin, crosslinking agent and catalysts.The results show that using different type...The selective water plugging agent was prepared by heating the blends of the polyacry-lamide inverse latex, modified urea formaldehyde resin, crosslinking agent and catalysts.The results show that using different types of polymers and additives or changing in theirproportion of the blends, the gelling viscosity, starting point of gelling and other propertiesof the IPN can be controlled.展开更多
基金the Graduate Developing Innovation Project of Jiangsu Province of China (No. CXZZ11-0306)the Major State Basic Research and Development Program of China (No.2007CB209400)
文摘A new composite two component grout comprised of modified urea-formaldehyde resin and cement was formulated to take account of the advantages and disadvantages of both the cement grout and the chem- ical grout. The new grout is designed for water blocking by reinforcing as well as seepage control by bore grouting. The A component consists of a modified urea-formaldehyde resin A component, some cement, and some water. The B component is an alkaline coagulant. An orthogonal test of four factors at three lev- els showed that gel time increased with increased water content and with urea-formaldehyde resin con- tent. Gel time decreased at increased levels of alkaline coagulant. The A component of this new composite grout is stable over time. A mixed cross-over test showed that as the volume ratio of A to B increases the gel time falls at first but then increases. The solid strength decreases with increasing levels of the B com- ponent. The solid strength increases over time and becomes stable by the 28th day after mixing. The vis- cosity increases with increasing levels of resin A component. The increase is exponential and may be fit to： μ = 8.162e0.0286x.
文摘The selective water plugging agent was prepared by heating the blends of the polyacry-lamide inverse latex, modified urea formaldehyde resin, crosslinking agent and catalysts.The results show that using different types of polymers and additives or changing in theirproportion of the blends, the gelling viscosity, starting point of gelling and other propertiesof the IPN can be controlled.