The mechanical properties of metal components are determined by the solidification behaviour and microstructure. A quantitative phase field model is used to investigate the microstructure evolution of fusedcoating add...The mechanical properties of metal components are determined by the solidification behaviour and microstructure. A quantitative phase field model is used to investigate the microstructure evolution of fusedcoating additive manufacturing, by which to improve the quality of deposition. During the fused-coating process, the molten metal in a crucible flows out of a nozzle and then reaches the substrate. The solidification happens at the moment when the molten metal comes into contact with substrate moving in three-dimensional space. The macroscopic heat transfer model of fused-coating is established to get the temperature field considered as the initial temperature boundary conditions in the phase field model. The numerical and experimental results show that the morphology of grains varies with different solidification environments. Columnar grains are observed during the early period at the bottom of fused-coating layer and the equiaxed grains appear subsequently ahead of the columnar grains. Columnar dendrites phase field simulations about the grains morphology and solute distribution are conducted considering the solidification environments. The simulation results are in good agreement with experimental results.展开更多
基金supported by the National Key R&D Program(2016YFB1100400)the Ministry of Education,China(6141A02022109)
文摘The mechanical properties of metal components are determined by the solidification behaviour and microstructure. A quantitative phase field model is used to investigate the microstructure evolution of fusedcoating additive manufacturing, by which to improve the quality of deposition. During the fused-coating process, the molten metal in a crucible flows out of a nozzle and then reaches the substrate. The solidification happens at the moment when the molten metal comes into contact with substrate moving in three-dimensional space. The macroscopic heat transfer model of fused-coating is established to get the temperature field considered as the initial temperature boundary conditions in the phase field model. The numerical and experimental results show that the morphology of grains varies with different solidification environments. Columnar grains are observed during the early period at the bottom of fused-coating layer and the equiaxed grains appear subsequently ahead of the columnar grains. Columnar dendrites phase field simulations about the grains morphology and solute distribution are conducted considering the solidification environments. The simulation results are in good agreement with experimental results.