Four kinds of galvanized steel sheets having different surface roughness values were used to prepare the steel sheets with a self-lubricated coating. The effects of surface roughness on the surface lubrication perform...Four kinds of galvanized steel sheets having different surface roughness values were used to prepare the steel sheets with a self-lubricated coating. The effects of surface roughness on the surface lubrication performance of the steel sheets were examined using a friction coefficient tester. Results revealed large dynamic friction coefficients for the galvanized steel sheets, which increased remarkably with surface roughness. Once the self-lubricated coating was applied, significant drops in the dynamic friction coefficients were measured. After the first stage of the friction test,the coefficients were almost unchanged, which reflected a weak dependence on the surface roughness of the self-lubricated steel sheets. However, the dynamic friction coefficients gradually increased as the test progressed, where these increase clearly correlated with the surface roughness of the self-lubricated steel sheets.展开更多
In recent years,the concern about environmental protection is increasing on a world scale.Major manufacturers of home appliances and OA equipment have introduced so-called 'green procurement schemes' for reduc...In recent years,the concern about environmental protection is increasing on a world scale.Major manufacturers of home appliances and OA equipment have introduced so-called 'green procurement schemes' for reducing environmentally harmful substances in manufacturing process and end products. Under such background,a new type of chromate-free organic composite coated electro-galvanized steel sheet with high conductivity was developed by Baosteel,which meets the EU RoHS Directive(Restriction of the Hazardous Substances) and other related laws and regulations on environmental safety.It also provides excellent surface electrical conductivity,corrosion resistance,fingerprint resistance,solvent resistance,coating adhesion, heat resistance,formability and other special properties to meet the demand of manufacture's process of OA machine. Compared with previously developed anti-fingerprinting coated electro-galvanized steel sheet,this newly developed product has a good balance between high corrosion resistance(time to 5%white rust in salt spray test is 120 h for flat panel and 72 h for worked potion) and conductivity(surface electro-resistivity in accordance with LOREAST is less than 0.1 milliohm ) due to the special design of coating's structure.Besides,It also provides the properties of grounding and shielding against electromagnetic waves.The evaluation of surface performances of new product showed that it is comparable or even better than the similar products. Currently,the newly developed product has been commercialized. In this paper,the major properties are discussed,such as corrosion resistance,surface electrical conductivity, fingerprint resistance,solvent resistance,coating adhesion(ink/melamine alkyd paint),heat resistance and formability.Furthermore,the application is also briefly described.展开更多
In recent years, the waterborne free intermediate coating process has been widely used in the automotive industry. Because the baking times and coating thickness are decreased, the surface covering capability of the p...In recent years, the waterborne free intermediate coating process has been widely used in the automotive industry. Because the baking times and coating thickness are decreased, the surface covering capability of the painting process is reduced, which directly affects the appearance quality（ long-and short-wave values） of the body paint. Thus, there are correspondingly higher requirements for the white body surface profile prior to painting. The surface profile of the white body is mainly affected by the plate material, the surface profile, and the deformation process. So,the change rule for the surface profile during deformation of the steel plate is a key factor in coating appearance optimization. In this paper, we first analyze the typical deformation of the outer cover of a car body. Then ,we examine the change tendency of the surface profile of steel plates with respect to different deformation rates, specifically for a steel plate comprising a hot-dip galvanized bake-hardened steel sheet. Based on our analysis of the influence of the deformation on the coating appearance,we selected 3% ,5% ,and 8% deformation rates in this research. We found the roughness （Ra） value in the typical deformation range （3% -8% ） of the car body to exhibit a decreasing trend at first and then an increasing trend. The Ra value of the 8% deformation is not more than the original plate test value. When the Pc value of the original plate is in the lower range （ about 60）, it exhibits a slight increasing trend in the deformation process （3 % -8 % ）. And when the Pc value of the original plate is in the higher range （ about 120 ）, it exhibits no increasing trend in the deformation process （ 3% -8% ）. In contrast,the waviness （WCA） value in the car body＇s typical deformation range （3%-8%） shows a significant growth trend.展开更多
对不同色差的热镀锌钢板用不同方法进行了微观检测分析,探究产生表面色差的原因。利用扫描电子显微镜（Scanning Electron Microscope,SEM）检测发现,表面出现色差的热镀锌钢板的镀层表面存在大量的孔洞,其直径约为1~4μm。通过X射线光...对不同色差的热镀锌钢板用不同方法进行了微观检测分析,探究产生表面色差的原因。利用扫描电子显微镜（Scanning Electron Microscope,SEM）检测发现,表面出现色差的热镀锌钢板的镀层表面存在大量的孔洞,其直径约为1~4μm。通过X射线光电子能谱（X-Ray Photoelectron Spectroscopy,XPS）分析,检测到这些孔洞区C元素和O元素的含量较高,说明含有夹杂物。通过镀层的X射线衍射（X-Ray Diffraction,XRD）分析及三维表面形貌检测发现,与表面色泽均匀的热镀锌钢板相比,表面出现色差的热镀锌钢板的结晶度较高,并且晶粒大小不均匀,镀层表面的纹理不规则。从光学角度来讲,这些因素都导致了热镀锌钢板表面出现色泽差异。展开更多
文摘Four kinds of galvanized steel sheets having different surface roughness values were used to prepare the steel sheets with a self-lubricated coating. The effects of surface roughness on the surface lubrication performance of the steel sheets were examined using a friction coefficient tester. Results revealed large dynamic friction coefficients for the galvanized steel sheets, which increased remarkably with surface roughness. Once the self-lubricated coating was applied, significant drops in the dynamic friction coefficients were measured. After the first stage of the friction test,the coefficients were almost unchanged, which reflected a weak dependence on the surface roughness of the self-lubricated steel sheets. However, the dynamic friction coefficients gradually increased as the test progressed, where these increase clearly correlated with the surface roughness of the self-lubricated steel sheets.
文摘In recent years,the concern about environmental protection is increasing on a world scale.Major manufacturers of home appliances and OA equipment have introduced so-called 'green procurement schemes' for reducing environmentally harmful substances in manufacturing process and end products. Under such background,a new type of chromate-free organic composite coated electro-galvanized steel sheet with high conductivity was developed by Baosteel,which meets the EU RoHS Directive(Restriction of the Hazardous Substances) and other related laws and regulations on environmental safety.It also provides excellent surface electrical conductivity,corrosion resistance,fingerprint resistance,solvent resistance,coating adhesion, heat resistance,formability and other special properties to meet the demand of manufacture's process of OA machine. Compared with previously developed anti-fingerprinting coated electro-galvanized steel sheet,this newly developed product has a good balance between high corrosion resistance(time to 5%white rust in salt spray test is 120 h for flat panel and 72 h for worked potion) and conductivity(surface electro-resistivity in accordance with LOREAST is less than 0.1 milliohm ) due to the special design of coating's structure.Besides,It also provides the properties of grounding and shielding against electromagnetic waves.The evaluation of surface performances of new product showed that it is comparable or even better than the similar products. Currently,the newly developed product has been commercialized. In this paper,the major properties are discussed,such as corrosion resistance,surface electrical conductivity, fingerprint resistance,solvent resistance,coating adhesion(ink/melamine alkyd paint),heat resistance and formability.Furthermore,the application is also briefly described.
文摘In recent years, the waterborne free intermediate coating process has been widely used in the automotive industry. Because the baking times and coating thickness are decreased, the surface covering capability of the painting process is reduced, which directly affects the appearance quality（ long-and short-wave values） of the body paint. Thus, there are correspondingly higher requirements for the white body surface profile prior to painting. The surface profile of the white body is mainly affected by the plate material, the surface profile, and the deformation process. So,the change rule for the surface profile during deformation of the steel plate is a key factor in coating appearance optimization. In this paper, we first analyze the typical deformation of the outer cover of a car body. Then ,we examine the change tendency of the surface profile of steel plates with respect to different deformation rates, specifically for a steel plate comprising a hot-dip galvanized bake-hardened steel sheet. Based on our analysis of the influence of the deformation on the coating appearance,we selected 3% ,5% ,and 8% deformation rates in this research. We found the roughness （Ra） value in the typical deformation range （3% -8% ） of the car body to exhibit a decreasing trend at first and then an increasing trend. The Ra value of the 8% deformation is not more than the original plate test value. When the Pc value of the original plate is in the lower range （ about 60）, it exhibits a slight increasing trend in the deformation process （3 % -8 % ）. And when the Pc value of the original plate is in the higher range （ about 120 ）, it exhibits no increasing trend in the deformation process （ 3% -8% ）. In contrast,the waviness （WCA） value in the car body＇s typical deformation range （3%-8%） shows a significant growth trend.