As the galvanized steels used for electrical and office appliances has achieved a complete chrome-free production worldwide,surface treatment technologies have entered a new phase of development.Grenter effort will be...As the galvanized steels used for electrical and office appliances has achieved a complete chrome-free production worldwide,surface treatment technologies have entered a new phase of development.Grenter effort will be made in exploring new frontier for future surface treatment technologies.A greater contribution will be made for environmental protection,energy-saving and resource-saving,to prevent globalwarming.展开更多
A group of projection welding experiments and joints tension-shear tests are carried out for cold-rolled steel sheets, galvanized steel sheets (GSS) without treatment, GSS with phosphating and GSS with surface greasin...A group of projection welding experiments and joints tension-shear tests are carried out for cold-rolled steel sheets, galvanized steel sheets (GSS) without treatment, GSS with phosphating and GSS with surface greasing, respectively. The experimental results are regressively analyzed on the computers, then the projection welded joint tension-shear strength curve and the perfect welding currents range of each material are obtained. The results show that surface treatments of galvanized steels have effects on their spot weldabilities. Among the four kinds of materials, GSS with surface greasing have the worst spot weldability, for they need higher welding current and have a narrow welding current range.展开更多
The present work aimed at using rare earth lanthanum salt and trimethoxy(viny)silance as chromate substitutes for galvanized steel passivation, in contrast to zinc coating samples treated with chromate.The corrosion...The present work aimed at using rare earth lanthanum salt and trimethoxy(viny)silance as chromate substitutes for galvanized steel passivation, in contrast to zinc coating samples treated with chromate.The corrosion resistance was assessed by electrochemical impedance spectroscopy(EIS) and neutral salt spray tests(NSS).Scanning electron microscopy(SEM) was used to characterize the sample surfaces.The organic coating adhesion on the panel was also investigated via varnishes-cross cut tests.The results indicated that rare earth and silane two-step treatment gave more effective anticorrosion performance than Cr, which also provided good paint adhesion.The coating formation mechanism was also discussed.展开更多
A complex film on hot-dip galvanized steel sheet(HDG) was prepared by immersing the sheet in 0.1wt.% Ce(NO3)3 solution and 5vol.% silane solution in turn.The corrosion protection of the complex film was evaluated ...A complex film on hot-dip galvanized steel sheet(HDG) was prepared by immersing the sheet in 0.1wt.% Ce(NO3)3 solution and 5vol.% silane solution in turn.The corrosion protection of the complex film was evaluated by potentiodynamic linear polarization(LPR), electrochemical impendence spectra(EIS) and natural salt spray(NSS) tests and compared with that of single cerium film and silane film.The results showed that, the presence of these films on the zinc coating hindered corrosion reaction by reducing the rate of both anodic and cathodic reaction in the corrosion process, and the corrosion protection of the complex film was much better than that of single cerium film or silane film and closed to that of chromate film, because the polarization resistance Rp and electrochemical impendence were increased markedly.Microstructure and chemical composition of these pretreated films were also investigated by scanning electron microscopy(SEM) and AES.展开更多
A novel cerium-tannic acid passivation treatment was performed on galvanized steel. The corrosion resistance of cerium-tannic passivated samples was tested by dropping test with 0.5 wt.% CuSO4 aqueous solution. The ma...A novel cerium-tannic acid passivation treatment was performed on galvanized steel. The corrosion resistance of cerium-tannic passivated samples was tested by dropping test with 0.5 wt.% CuSO4 aqueous solution. The mass loss per unit area of passivated samples was measured after the corrosion in 0.5 mol/L NaCl + 0.005 mol/L H2SO4 at room temperature for 96 h. The electrochemical behaviors of cerium, tannic acid, and cerium-tannic acid passivated samples on galvanized steel in 0.5 mol/L NaCl solution were investigated by polarization curves and electrochemical impendence spectra. The corrosion equivalent circuit was established according to the impedance characteristics. The results show that cerium-tannic acid treated samples exhibit better corrosion resistance than the sole cerium or tannic acid treated samples under the same condition. The mechanism of synergistic effect for cerium-tannic acid passivation on galvanized steel was discussed.展开更多
The corrosion behavior and mechanism of hot-dip galvanized steel and interstitial-free (IF) substrate with alkaline mud adhesion were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), ...The corrosion behavior and mechanism of hot-dip galvanized steel and interstitial-free (IF) substrate with alkaline mud adhesion were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), electrochemical impedance spectroscopy (EIS), and linear polarization. The results show that non-uniform corrosion occurs on the galvanized steel and IF substrate during 250 h with the mud adhesion. The corrosion products on the galvanized steel are very loose and porous, which are mainly ZnO, Zn5(OH)8C12·H2O and Zn(OH)2, and Fe-Zn alloy layer with a lower corrosion rate is exposed on the galvanized steel surface; however, the corrosion products on IF substrate are considerably harder and denser, whose compositions of rust are mainly FeOOH and Fe3O4, and several pits appear on their surface. The results of continuous EIS and linear polarization measurements exhibit a corrosion mechanism, that is, under activation control, the charge transfer resistances present different tendencies between the galvanized steel and IF substrate; in addition, the evolution of linear polarization resistances is similar to that of charge transfer resistances. The higher contents of dissolved oxygen and Cl^- ions in the mud play an important role in accelerating the corrosion.展开更多
Powdering/exfoliating of coatings and scratching galvanized steels and high strength steels (HSS), are the main forms of surface damage in the forming of which result in increased die maintenance cost and scrap rate...Powdering/exfoliating of coatings and scratching galvanized steels and high strength steels (HSS), are the main forms of surface damage in the forming of which result in increased die maintenance cost and scrap rate. In this study, a special rectangular box was developed to investigate the behavior and characteristics of surface damage in sheet metal forming (SMF) processes. U-channel forming tests were conducted to study the effect of tool hardness on surface damage in the forming of high strength steels and galvanized steels (hot-dip galvanized and galvannealed steels). Experimental results indicate that sheet deformation mode influences the severity of surface damage in SMF and surface damage occurs easily at the regions where sheet specimen deforms under the action of compressive stress. Die corner is the position where surface damage initiates. For HSS sheet, surface damage is of major interest due to high forming pressure. The HSS and hot-dip galvanized steels show improved ability of damage-resistance with increased hardness of the forming tool. However, for galvannealed steel it is not the forming tool with the highest hardness value that performs best.展开更多
To improve the corrosion resistance of phosphate coatings, the phosphated hot-dip galvanized (HDG) steel was post-sealed with cerium nitrate solution. The morphology, composition, corrosion resistance of the coatings ...To improve the corrosion resistance of phosphate coatings, the phosphated hot-dip galvanized (HDG) steel was post-sealed with cerium nitrate solution. The morphology, composition, corrosion resistance of the coatings was investigated by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and neutral salt spray (NSS) tests. The results show that after post-sealing the phosphated HDG samples with cerium nitrate solution, the pores among the zinc phosphate crystals are sealed by the compounds containing phosphorus, oxygen and cerium; the zinc phosphate crystals are covered by the flocculent cerium compounds; and the continuous composite coatings are formed on HDG steel. The corrosion resistance of the composite coatings, which increases with the increase in phosphating time and cerium nitrate post-sealing time, is far higher than that of the single phosphate coatings. The composite coatings with the optimal corrosion resistance are obtained for phosphating 300 s and post-sealing 300 s; and the corrosion resistance is more outstanding than that of the chromate coatings.展开更多
Resistance spot brazing was used to perform the lap test of pure aluminum 1060 and SGCC hot-dip galvanized steel plate,the joint interface structure was studied,and the mechanical properties of the joint were tested.T...Resistance spot brazing was used to perform the lap test of pure aluminum 1060 and SGCC hot-dip galvanized steel plate,the joint interface structure was studied,and the mechanical properties of the joint were tested.The results show that the aluminum-silicon(Al-Si)alloy solder used in the test has good wetting,and an intermetallic compound with a double-layer structure and uneven thickness is produced at the welded joint interface after welding.The thickness is<10μm.The welding current is at 7.8 kA,the tensile shear load of the joint reaches a peak value of about 4.72 kN.Under the same process parameters,the tensile shear load of the resistance spot brazed joint is significantly higher than that of the spot welded joint.The joint fracture mostly occurs on the aluminum plate side,and mainly at the heat-affected zone and not at the welding point.It indicates that the quality of the spot brazed joint is good,but due to the local"unbrazed"defect on the aluminum side interface of the weld,tensile stress will occur at the weld interface and the stress effect on the intermetallic compound.It is easy to produce cracks.展开更多
The process properties and interface behavior of CO_2 laser brazing with automatic wire feed for galvanized steel sheets were investigated, in which the brazing filler metal was CuSi3 and no flux was used. As to the a...The process properties and interface behavior of CO_2 laser brazing with automatic wire feed for galvanized steel sheets were investigated, in which the brazing filler metal was CuSi3 and no flux was used. As to the appearance quality of the brazing seams, the roles of the processing parameters, such as brazing speed, wire feeding rate, inclination and feeding direction of the wire, laser power, spot diameter and heating position, were assessed. The further investigation indicates that the behavior of the active elements Si, Mn and Zn are significantly influenced by energy input. At the interface, the microstructure of the base metal was composed of columnar crystals and the acicular α solid solution was found on the filler metal side.展开更多
Four kinds of galvanized steel sheets having different surface roughness values were used to prepare the steel sheets with a self-lubricated coating. The effects of surface roughness on the surface lubrication perform...Four kinds of galvanized steel sheets having different surface roughness values were used to prepare the steel sheets with a self-lubricated coating. The effects of surface roughness on the surface lubrication performance of the steel sheets were examined using a friction coefficient tester. Results revealed large dynamic friction coefficients for the galvanized steel sheets, which increased remarkably with surface roughness. Once the self-lubricated coating was applied, significant drops in the dynamic friction coefficients were measured. After the first stage of the friction test,the coefficients were almost unchanged, which reflected a weak dependence on the surface roughness of the self-lubricated steel sheets. However, the dynamic friction coefficients gradually increased as the test progressed, where these increase clearly correlated with the surface roughness of the self-lubricated steel sheets.展开更多
The microstructure and elements distribution of the deep cryogenic treatmentelectrodes and non-cryogenic treatment electrodes for spot welding hot dip galvanized steel areobserved by a scanning electrical microscope. ...The microstructure and elements distribution of the deep cryogenic treatmentelectrodes and non-cryogenic treatment electrodes for spot welding hot dip galvanized steel areobserved by a scanning electrical microscope. The grain sizes, the resistivity and the hardness ofthe electrodes before and after deep cryogenic treatment are measured by X-ray diffraction, the DCdouble arms bridge and the Brinell hardness testing unit respectively. The spot welding processperformance of hot dip galvanized steel plate is tested and the relationship between microstructureand physical properties of deep cryogenic treatment electrodes is analyzed. The experimental resultsshow that deep cryogenic treatment makes Cr, Zr in deep cryogenic treatment electrodes emanatedispersedly and makes the grain of deep cryogenic treatment electrodes smaller than non-cryogenictreatment ones so that the electrical conductivity and the thermal conductivity of deep cryogenictreatment electrodes are improved very much, which make spot welding process performance of the hotdip galvanized steel be improved.展开更多
The details of a research study of galvanized steel tube under web crippling were presented. A total of 48 galvanized steel square hollow sections with different boundary conditions, loading conditions, bearing length...The details of a research study of galvanized steel tube under web crippling were presented. A total of 48 galvanized steel square hollow sections with different boundary conditions, loading conditions, bearing lengths and web slenderness were tested. The experimental scheme, failure modes, load-displacement curves and strain intensity distribution curves were also presented. The investigation was focused on the effects of loading condition, bearing length and slenderness on web crippling ultimate capacity, initial compressive stiffness and ductility of galvanized steel tube. The results show that web crippling ultimate capacity increases linearly with the increase of the bearing length under EOF and IOF loading condition. In the end-flange and ITF loading conditions, strain intensity of the centerline of web reaches the peak and decreases progressively from central web to flanges. Finite element models were developed to numerically simulate the tests in terms of failure modes and ultimate capacity. Web crippling strength of galvanized steel tube increases linearly with the increase of the ratio of the bearing length to web thickness and decrease of web slenderness. The effect of ratio of galvanized layer thickness to web thickness on web crippling strength is small. Based on the results of the parametric study, a number of calculation formulas proposed in this work can be successfully employed as a design rule for predicting web crippling ultimate capacity of galvanized steel tube under four loading and boundary conditions.展开更多
In recent years, the waterborne free intermediate coating process has been widely used in the automotive industry. Because the baking times and coating thickness are decreased, the surface covering capability of the p...In recent years, the waterborne free intermediate coating process has been widely used in the automotive industry. Because the baking times and coating thickness are decreased, the surface covering capability of the painting process is reduced, which directly affects the appearance quality( long-and short-wave values) of the body paint. Thus, there are correspondingly higher requirements for the white body surface profile prior to painting. The surface profile of the white body is mainly affected by the plate material, the surface profile, and the deformation process. So,the change rule for the surface profile during deformation of the steel plate is a key factor in coating appearance optimization. In this paper, we first analyze the typical deformation of the outer cover of a car body. Then ,we examine the change tendency of the surface profile of steel plates with respect to different deformation rates, specifically for a steel plate comprising a hot-dip galvanized bake-hardened steel sheet. Based on our analysis of the influence of the deformation on the coating appearance,we selected 3% ,5% ,and 8% deformation rates in this research. We found the roughness (Ra) value in the typical deformation range (3% -8% ) of the car body to exhibit a decreasing trend at first and then an increasing trend. The Ra value of the 8% deformation is not more than the original plate test value. When the Pc value of the original plate is in the lower range ( about 60), it exhibits a slight increasing trend in the deformation process (3 % -8 % ). And when the Pc value of the original plate is in the higher range ( about 120 ), it exhibits no increasing trend in the deformation process ( 3% -8% ). In contrast,the waviness (WCA) value in the car body's typical deformation range (3%-8%) shows a significant growth trend.展开更多
The main objective of this work was to evaluate the presence of lead and cadmium in galvanized steel tubes by hot-dip used exclusively for drinking water supply.In this research,samples of galvanized tubes were remove...The main objective of this work was to evaluate the presence of lead and cadmium in galvanized steel tubes by hot-dip used exclusively for drinking water supply.In this research,samples of galvanized tubes were removed from walls of residential buildings with 30 years of use.In the process of hot galvanizing,the manufacturing standards allow or for low cost conveniences,and the use of primary zinc ingot with 1.6%metallic impurities,such as lead and cadmium,is allowed,enabling the incorporation of these metals into the zinc coating deposited on the carbon steel.The associated corrosion of these tubes can release these toxic metals,contaminating the drinking water used by residents.The samples taken from the tubes were evaluated by a square-wave anodic stripping voltammetry technique,and the results for lead and cadmium suggested randomly distributed levels,indicating that the contents of these contaminants depend mainly on the quality of the added primary zinc and the operational conditions of the immersion bath.The metallographic evaluations performed on the samples of the galvanized tubes showed irregularities in thickness and even a lack of the zinc layer deposited on the carbon steel surface.These facts suggest that galvanized tubes should not be used for drinking water.展开更多
An inorganic lubrication treatment for a galvanized steel sheet was developed to improve the press formability of automotive body panels. The properties and application of Baosteel's inorganic-lubricant-coated galvan...An inorganic lubrication treatment for a galvanized steel sheet was developed to improve the press formability of automotive body panels. The properties and application of Baosteel's inorganic-lubricant-coated galvanized steel sheet are demonstrated. Compared with galvanized steel sheets without the inorganic lubricant coating,the Baosteel inorganic-lubricant-coated galvanized steel sheet has a lower friction coefficient and excellent lubricating ability,more homogeneous tribological and stamping behaviors,lower sensitivity to stamping parameters,excellent spot weldability,good adhesivity,and perfect phosphate compatibility and paintability. These results verify that the Baosteel inorganic-lubricant-coated galvanized steel sheet has excellent press formability and a huge market application potential.展开更多
Hot-dip galvanized steel is one of the most used materials in equipment and metallic structures of the Brazilian electric sector. Although carbon steel is the main substrate in the galvanizing hot-dip process, recentl...Hot-dip galvanized steel is one of the most used materials in equipment and metallic structures of the Brazilian electric sector. Although carbon steel is the main substrate in the galvanizing hot-dip process, recently, weathering steel has been used as an alternative material to be galvanized. In the transmission line segment of the Brazilian electric sector, for instance, compact towers made of galvanized weathering steel have been installed to conduct energy through urban sites. It is well known that weathering steel, depending on wet and dry cycles and on the pollutants present in the atmosphere, develops a protective patina made of its corrosion products. The patina is dense and strongly adhered to the substrate, blocking the active surface and, thus, reducing the corrosion rate of the base metal. However, when the weathering steel is galvanized, the substrate surface has a layer of zinc and zinc-iron intermetallic alloys. When the sacrificial layer is consumed by atmospheric corrosion, critical questions remain to be answered regarding the underlying substrate. Will the patina of weathering steel be formed? In what condition? Does the hot-dip galvanizing process modify the weathering steel microstructure? The present work carried out an experimental research to shed light on the anticorrosive behavior of hot-dip galvanized weathering steel, after the zinc layer is corroded. This was done by a controlled pickling process, where the zinc layer was removed simulating its consumption during real corrosion processes. The results, obtained through electrochemical techniques and different accelerated corrosion tests, showed that galvanizing weathering steel is a promising technology to enhance the lifetime of structures used in the Brazilian electric sector.展开更多
Currently, Living Wall Systems (LWSs) are assuming great importance in the built environment, due to environmental and aesthetic advantages, as well as the use of urban residual space and underutilized surfaces of bui...Currently, Living Wall Systems (LWSs) are assuming great importance in the built environment, due to environmental and aesthetic advantages, as well as the use of urban residual space and underutilized surfaces of buildings. However, the maintenance and the durability of the materials used have been a challenge for architects and professionals in the field. The aim of this paper is to evaluate the anti-corrosion performance of a steel framing profile, galvanized carbon steel (55% Al-Zn), a sustainable material with easy assembly, to apply LWS in the hot and humid tropical climate of Niterói (Rio de Janeiro, Brazil). In order to create the conditions of the tests, “X” cut were made in Al-Zn coating, sanding, and application of epoxy and glass fiber-reinforced polyester. After the experiments that lasted four months, the 55% Al-Zn coating was analyzed using Scanning Electron Microscope (SEM) and energy dispersive X-ray spectroscopy (EDS). The results of the tests were promising for the use of this galvanized steel for application as a support for green vertical facades. 55% Al-Zn coatings are recommended for marine atmospheres due to their good anti-corrosion performance.展开更多
This study aims to enhance the adhesion strength and anti-corrosion performance of the cold galvanizing coating(CGC)applied on the hot-dip galvanized steel(HDG).Polydopamine(PDA)is deposited on the HDG surface with di...This study aims to enhance the adhesion strength and anti-corrosion performance of the cold galvanizing coating(CGC)applied on the hot-dip galvanized steel(HDG).Polydopamine(PDA)is deposited on the HDG surface with different time ranges and as an interlayer between CGC and HDG through covalent immobilization.The surface morphology and the covalent interaction between PDA/HDG are exhibited by scanning electron microscope(SEM),atomic force microscopy(AFM)and X-ray photoelectron spectroscopy(XPS).The pull-off adhesion tests before and after neutral slat spry tests show an enhanced dry adhesion strength and less adhesion loss of the hybrid CGC/PDA coated HDG compared with the direct CGC coated HDG.In addition,open circuit potential(OCP)reveals that the corrosion protection performance of the hybrid CGC/PDA coated HDG increases by 200%(up to 201 d)and the corrosion density icorrattaining about 4.45×10^(-7)A/cm^(2).Electrochemical impedance spectroscopy(EIS)measurements and X-ray diffraction(XRD)analysis confirm that the precipitate of the stable chelation formed by PDA and Zn^(2+)between CGC and HDG substrate can also improve the corrosion protection performance.Such a strategy of strengthening adhesion and forming the chelate compound at the HDG surface promises a new route to corrosion protection of CGC on HDG.展开更多
Modified lanthanum salt conversion coatings prepared by rare earth salt route based on lanthanum nitrate solution were proposed as alternatives to the process involving toxic hexavalent chromate.The structure and comp...Modified lanthanum salt conversion coatings prepared by rare earth salt route based on lanthanum nitrate solution were proposed as alternatives to the process involving toxic hexavalent chromate.The structure and composition of the coating were determined with X-ray energy dispersive spectrometer and X-ray photoelectron spectroscopy.The surface morphologies of the treated samples were observed with scanning electron microscopy.The natural salt spray and electrochemical impendence spectra tests were carried ...展开更多
文摘As the galvanized steels used for electrical and office appliances has achieved a complete chrome-free production worldwide,surface treatment technologies have entered a new phase of development.Grenter effort will be made in exploring new frontier for future surface treatment technologies.A greater contribution will be made for environmental protection,energy-saving and resource-saving,to prevent globalwarming.
文摘A group of projection welding experiments and joints tension-shear tests are carried out for cold-rolled steel sheets, galvanized steel sheets (GSS) without treatment, GSS with phosphating and GSS with surface greasing, respectively. The experimental results are regressively analyzed on the computers, then the projection welded joint tension-shear strength curve and the perfect welding currents range of each material are obtained. The results show that surface treatments of galvanized steels have effects on their spot weldabilities. Among the four kinds of materials, GSS with surface greasing have the worst spot weldability, for they need higher welding current and have a narrow welding current range.
文摘The present work aimed at using rare earth lanthanum salt and trimethoxy(viny)silance as chromate substitutes for galvanized steel passivation, in contrast to zinc coating samples treated with chromate.The corrosion resistance was assessed by electrochemical impedance spectroscopy(EIS) and neutral salt spray tests(NSS).Scanning electron microscopy(SEM) was used to characterize the sample surfaces.The organic coating adhesion on the panel was also investigated via varnishes-cross cut tests.The results indicated that rare earth and silane two-step treatment gave more effective anticorrosion performance than Cr, which also provided good paint adhesion.The coating formation mechanism was also discussed.
基金supported by the United Nations Common Fund for Commodities (CFC/LZSG/12)
文摘A complex film on hot-dip galvanized steel sheet(HDG) was prepared by immersing the sheet in 0.1wt.% Ce(NO3)3 solution and 5vol.% silane solution in turn.The corrosion protection of the complex film was evaluated by potentiodynamic linear polarization(LPR), electrochemical impendence spectra(EIS) and natural salt spray(NSS) tests and compared with that of single cerium film and silane film.The results showed that, the presence of these films on the zinc coating hindered corrosion reaction by reducing the rate of both anodic and cathodic reaction in the corrosion process, and the corrosion protection of the complex film was much better than that of single cerium film or silane film and closed to that of chromate film, because the polarization resistance Rp and electrochemical impendence were increased markedly.Microstructure and chemical composition of these pretreated films were also investigated by scanning electron microscopy(SEM) and AES.
基金supported by the Science and Technology Foundation of the Department of Education of Jiangxi Province,China (No. GJJ08205)
文摘A novel cerium-tannic acid passivation treatment was performed on galvanized steel. The corrosion resistance of cerium-tannic passivated samples was tested by dropping test with 0.5 wt.% CuSO4 aqueous solution. The mass loss per unit area of passivated samples was measured after the corrosion in 0.5 mol/L NaCl + 0.005 mol/L H2SO4 at room temperature for 96 h. The electrochemical behaviors of cerium, tannic acid, and cerium-tannic acid passivated samples on galvanized steel in 0.5 mol/L NaCl solution were investigated by polarization curves and electrochemical impendence spectra. The corrosion equivalent circuit was established according to the impedance characteristics. The results show that cerium-tannic acid treated samples exhibit better corrosion resistance than the sole cerium or tannic acid treated samples under the same condition. The mechanism of synergistic effect for cerium-tannic acid passivation on galvanized steel was discussed.
基金supported by the National Natural Science Foundation of China(No.50571022)the National Science & Technology Infrastructure Development Program of China(No.2005DKA10400)
文摘The corrosion behavior and mechanism of hot-dip galvanized steel and interstitial-free (IF) substrate with alkaline mud adhesion were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), electrochemical impedance spectroscopy (EIS), and linear polarization. The results show that non-uniform corrosion occurs on the galvanized steel and IF substrate during 250 h with the mud adhesion. The corrosion products on the galvanized steel are very loose and porous, which are mainly ZnO, Zn5(OH)8C12·H2O and Zn(OH)2, and Fe-Zn alloy layer with a lower corrosion rate is exposed on the galvanized steel surface; however, the corrosion products on IF substrate are considerably harder and denser, whose compositions of rust are mainly FeOOH and Fe3O4, and several pits appear on their surface. The results of continuous EIS and linear polarization measurements exhibit a corrosion mechanism, that is, under activation control, the charge transfer resistances present different tendencies between the galvanized steel and IF substrate; in addition, the evolution of linear polarization resistances is similar to that of charge transfer resistances. The higher contents of dissolved oxygen and Cl^- ions in the mud play an important role in accelerating the corrosion.
基金supported by the National Natural Science Foundation of China under grant No. 50605043
文摘Powdering/exfoliating of coatings and scratching galvanized steels and high strength steels (HSS), are the main forms of surface damage in the forming of which result in increased die maintenance cost and scrap rate. In this study, a special rectangular box was developed to investigate the behavior and characteristics of surface damage in sheet metal forming (SMF) processes. U-channel forming tests were conducted to study the effect of tool hardness on surface damage in the forming of high strength steels and galvanized steels (hot-dip galvanized and galvannealed steels). Experimental results indicate that sheet deformation mode influences the severity of surface damage in SMF and surface damage occurs easily at the regions where sheet specimen deforms under the action of compressive stress. Die corner is the position where surface damage initiates. For HSS sheet, surface damage is of major interest due to high forming pressure. The HSS and hot-dip galvanized steels show improved ability of damage-resistance with increased hardness of the forming tool. However, for galvannealed steel it is not the forming tool with the highest hardness value that performs best.
文摘To improve the corrosion resistance of phosphate coatings, the phosphated hot-dip galvanized (HDG) steel was post-sealed with cerium nitrate solution. The morphology, composition, corrosion resistance of the coatings was investigated by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and neutral salt spray (NSS) tests. The results show that after post-sealing the phosphated HDG samples with cerium nitrate solution, the pores among the zinc phosphate crystals are sealed by the compounds containing phosphorus, oxygen and cerium; the zinc phosphate crystals are covered by the flocculent cerium compounds; and the continuous composite coatings are formed on HDG steel. The corrosion resistance of the composite coatings, which increases with the increase in phosphating time and cerium nitrate post-sealing time, is far higher than that of the single phosphate coatings. The composite coatings with the optimal corrosion resistance are obtained for phosphating 300 s and post-sealing 300 s; and the corrosion resistance is more outstanding than that of the chromate coatings.
文摘Resistance spot brazing was used to perform the lap test of pure aluminum 1060 and SGCC hot-dip galvanized steel plate,the joint interface structure was studied,and the mechanical properties of the joint were tested.The results show that the aluminum-silicon(Al-Si)alloy solder used in the test has good wetting,and an intermetallic compound with a double-layer structure and uneven thickness is produced at the welded joint interface after welding.The thickness is<10μm.The welding current is at 7.8 kA,the tensile shear load of the joint reaches a peak value of about 4.72 kN.Under the same process parameters,the tensile shear load of the resistance spot brazed joint is significantly higher than that of the spot welded joint.The joint fracture mostly occurs on the aluminum plate side,and mainly at the heat-affected zone and not at the welding point.It indicates that the quality of the spot brazed joint is good,but due to the local"unbrazed"defect on the aluminum side interface of the weld,tensile stress will occur at the weld interface and the stress effect on the intermetallic compound.It is easy to produce cracks.
文摘The process properties and interface behavior of CO_2 laser brazing with automatic wire feed for galvanized steel sheets were investigated, in which the brazing filler metal was CuSi3 and no flux was used. As to the appearance quality of the brazing seams, the roles of the processing parameters, such as brazing speed, wire feeding rate, inclination and feeding direction of the wire, laser power, spot diameter and heating position, were assessed. The further investigation indicates that the behavior of the active elements Si, Mn and Zn are significantly influenced by energy input. At the interface, the microstructure of the base metal was composed of columnar crystals and the acicular α solid solution was found on the filler metal side.
文摘Four kinds of galvanized steel sheets having different surface roughness values were used to prepare the steel sheets with a self-lubricated coating. The effects of surface roughness on the surface lubrication performance of the steel sheets were examined using a friction coefficient tester. Results revealed large dynamic friction coefficients for the galvanized steel sheets, which increased remarkably with surface roughness. Once the self-lubricated coating was applied, significant drops in the dynamic friction coefficients were measured. After the first stage of the friction test,the coefficients were almost unchanged, which reflected a weak dependence on the surface roughness of the self-lubricated steel sheets. However, the dynamic friction coefficients gradually increased as the test progressed, where these increase clearly correlated with the surface roughness of the self-lubricated steel sheets.
基金This projecti is supported by National Natural Science Foundation of China (No.50175080).
文摘The microstructure and elements distribution of the deep cryogenic treatmentelectrodes and non-cryogenic treatment electrodes for spot welding hot dip galvanized steel areobserved by a scanning electrical microscope. The grain sizes, the resistivity and the hardness ofthe electrodes before and after deep cryogenic treatment are measured by X-ray diffraction, the DCdouble arms bridge and the Brinell hardness testing unit respectively. The spot welding processperformance of hot dip galvanized steel plate is tested and the relationship between microstructureand physical properties of deep cryogenic treatment electrodes is analyzed. The experimental resultsshow that deep cryogenic treatment makes Cr, Zr in deep cryogenic treatment electrodes emanatedispersedly and makes the grain of deep cryogenic treatment electrodes smaller than non-cryogenictreatment ones so that the electrical conductivity and the thermal conductivity of deep cryogenictreatment electrodes are improved very much, which make spot welding process performance of the hotdip galvanized steel be improved.
基金Projects(51278209,51378077,51478047)supported by the National Natural Science Foundation of ChinaProject(ZQN-PY110)supported by Promotion Program for Young and Middle-aged Teacher in Science and Technology Research of Huaqiao University,China+1 种基金Project(2014FJ-NCET-ZR03)supported by Program for New Century Excellent Talents in Fujian Province University,ChinaProject(JA13005)supported by Incubation Program for Excellent Young Science and Technology Talents in Fujian Province Universities,China
文摘The details of a research study of galvanized steel tube under web crippling were presented. A total of 48 galvanized steel square hollow sections with different boundary conditions, loading conditions, bearing lengths and web slenderness were tested. The experimental scheme, failure modes, load-displacement curves and strain intensity distribution curves were also presented. The investigation was focused on the effects of loading condition, bearing length and slenderness on web crippling ultimate capacity, initial compressive stiffness and ductility of galvanized steel tube. The results show that web crippling ultimate capacity increases linearly with the increase of the bearing length under EOF and IOF loading condition. In the end-flange and ITF loading conditions, strain intensity of the centerline of web reaches the peak and decreases progressively from central web to flanges. Finite element models were developed to numerically simulate the tests in terms of failure modes and ultimate capacity. Web crippling strength of galvanized steel tube increases linearly with the increase of the ratio of the bearing length to web thickness and decrease of web slenderness. The effect of ratio of galvanized layer thickness to web thickness on web crippling strength is small. Based on the results of the parametric study, a number of calculation formulas proposed in this work can be successfully employed as a design rule for predicting web crippling ultimate capacity of galvanized steel tube under four loading and boundary conditions.
文摘In recent years, the waterborne free intermediate coating process has been widely used in the automotive industry. Because the baking times and coating thickness are decreased, the surface covering capability of the painting process is reduced, which directly affects the appearance quality( long-and short-wave values) of the body paint. Thus, there are correspondingly higher requirements for the white body surface profile prior to painting. The surface profile of the white body is mainly affected by the plate material, the surface profile, and the deformation process. So,the change rule for the surface profile during deformation of the steel plate is a key factor in coating appearance optimization. In this paper, we first analyze the typical deformation of the outer cover of a car body. Then ,we examine the change tendency of the surface profile of steel plates with respect to different deformation rates, specifically for a steel plate comprising a hot-dip galvanized bake-hardened steel sheet. Based on our analysis of the influence of the deformation on the coating appearance,we selected 3% ,5% ,and 8% deformation rates in this research. We found the roughness (Ra) value in the typical deformation range (3% -8% ) of the car body to exhibit a decreasing trend at first and then an increasing trend. The Ra value of the 8% deformation is not more than the original plate test value. When the Pc value of the original plate is in the lower range ( about 60), it exhibits a slight increasing trend in the deformation process (3 % -8 % ). And when the Pc value of the original plate is in the higher range ( about 120 ), it exhibits no increasing trend in the deformation process ( 3% -8% ). In contrast,the waviness (WCA) value in the car body's typical deformation range (3%-8%) shows a significant growth trend.
文摘The main objective of this work was to evaluate the presence of lead and cadmium in galvanized steel tubes by hot-dip used exclusively for drinking water supply.In this research,samples of galvanized tubes were removed from walls of residential buildings with 30 years of use.In the process of hot galvanizing,the manufacturing standards allow or for low cost conveniences,and the use of primary zinc ingot with 1.6%metallic impurities,such as lead and cadmium,is allowed,enabling the incorporation of these metals into the zinc coating deposited on the carbon steel.The associated corrosion of these tubes can release these toxic metals,contaminating the drinking water used by residents.The samples taken from the tubes were evaluated by a square-wave anodic stripping voltammetry technique,and the results for lead and cadmium suggested randomly distributed levels,indicating that the contents of these contaminants depend mainly on the quality of the added primary zinc and the operational conditions of the immersion bath.The metallographic evaluations performed on the samples of the galvanized tubes showed irregularities in thickness and even a lack of the zinc layer deposited on the carbon steel surface.These facts suggest that galvanized tubes should not be used for drinking water.
文摘An inorganic lubrication treatment for a galvanized steel sheet was developed to improve the press formability of automotive body panels. The properties and application of Baosteel's inorganic-lubricant-coated galvanized steel sheet are demonstrated. Compared with galvanized steel sheets without the inorganic lubricant coating,the Baosteel inorganic-lubricant-coated galvanized steel sheet has a lower friction coefficient and excellent lubricating ability,more homogeneous tribological and stamping behaviors,lower sensitivity to stamping parameters,excellent spot weldability,good adhesivity,and perfect phosphate compatibility and paintability. These results verify that the Baosteel inorganic-lubricant-coated galvanized steel sheet has excellent press formability and a huge market application potential.
文摘Hot-dip galvanized steel is one of the most used materials in equipment and metallic structures of the Brazilian electric sector. Although carbon steel is the main substrate in the galvanizing hot-dip process, recently, weathering steel has been used as an alternative material to be galvanized. In the transmission line segment of the Brazilian electric sector, for instance, compact towers made of galvanized weathering steel have been installed to conduct energy through urban sites. It is well known that weathering steel, depending on wet and dry cycles and on the pollutants present in the atmosphere, develops a protective patina made of its corrosion products. The patina is dense and strongly adhered to the substrate, blocking the active surface and, thus, reducing the corrosion rate of the base metal. However, when the weathering steel is galvanized, the substrate surface has a layer of zinc and zinc-iron intermetallic alloys. When the sacrificial layer is consumed by atmospheric corrosion, critical questions remain to be answered regarding the underlying substrate. Will the patina of weathering steel be formed? In what condition? Does the hot-dip galvanizing process modify the weathering steel microstructure? The present work carried out an experimental research to shed light on the anticorrosive behavior of hot-dip galvanized weathering steel, after the zinc layer is corroded. This was done by a controlled pickling process, where the zinc layer was removed simulating its consumption during real corrosion processes. The results, obtained through electrochemical techniques and different accelerated corrosion tests, showed that galvanizing weathering steel is a promising technology to enhance the lifetime of structures used in the Brazilian electric sector.
文摘Currently, Living Wall Systems (LWSs) are assuming great importance in the built environment, due to environmental and aesthetic advantages, as well as the use of urban residual space and underutilized surfaces of buildings. However, the maintenance and the durability of the materials used have been a challenge for architects and professionals in the field. The aim of this paper is to evaluate the anti-corrosion performance of a steel framing profile, galvanized carbon steel (55% Al-Zn), a sustainable material with easy assembly, to apply LWS in the hot and humid tropical climate of Niterói (Rio de Janeiro, Brazil). In order to create the conditions of the tests, “X” cut were made in Al-Zn coating, sanding, and application of epoxy and glass fiber-reinforced polyester. After the experiments that lasted four months, the 55% Al-Zn coating was analyzed using Scanning Electron Microscope (SEM) and energy dispersive X-ray spectroscopy (EDS). The results of the tests were promising for the use of this galvanized steel for application as a support for green vertical facades. 55% Al-Zn coatings are recommended for marine atmospheres due to their good anti-corrosion performance.
基金supported by the Ling Chuang Research Project of China National Nuclear Corporation(Grant No.E041F212Z1)。
文摘This study aims to enhance the adhesion strength and anti-corrosion performance of the cold galvanizing coating(CGC)applied on the hot-dip galvanized steel(HDG).Polydopamine(PDA)is deposited on the HDG surface with different time ranges and as an interlayer between CGC and HDG through covalent immobilization.The surface morphology and the covalent interaction between PDA/HDG are exhibited by scanning electron microscope(SEM),atomic force microscopy(AFM)and X-ray photoelectron spectroscopy(XPS).The pull-off adhesion tests before and after neutral slat spry tests show an enhanced dry adhesion strength and less adhesion loss of the hybrid CGC/PDA coated HDG compared with the direct CGC coated HDG.In addition,open circuit potential(OCP)reveals that the corrosion protection performance of the hybrid CGC/PDA coated HDG increases by 200%(up to 201 d)and the corrosion density icorrattaining about 4.45×10^(-7)A/cm^(2).Electrochemical impedance spectroscopy(EIS)measurements and X-ray diffraction(XRD)analysis confirm that the precipitate of the stable chelation formed by PDA and Zn^(2+)between CGC and HDG substrate can also improve the corrosion protection performance.Such a strategy of strengthening adhesion and forming the chelate compound at the HDG surface promises a new route to corrosion protection of CGC on HDG.
基金supported by the International Zinc Association,Belgium (IZA/CA/056)
文摘Modified lanthanum salt conversion coatings prepared by rare earth salt route based on lanthanum nitrate solution were proposed as alternatives to the process involving toxic hexavalent chromate.The structure and composition of the coating were determined with X-ray energy dispersive spectrometer and X-ray photoelectron spectroscopy.The surface morphologies of the treated samples were observed with scanning electron microscopy.The natural salt spray and electrochemical impendence spectra tests were carried ...