In order to discuss the mechanisms of permanent fixation of wood compression set , compressed wood of Chinese fir (Cunninghamia lanceolata) was irradiated by gamma rays from 60 Co. The irradiation doses wer...In order to discuss the mechanisms of permanent fixation of wood compression set , compressed wood of Chinese fir (Cunninghamia lanceolata) was irradiated by gamma rays from 60 Co. The irradiation doses were 0 (for match specim ens), 10 3, 5×10 3, 10 4, 5×10 4, 10 5, 5×10 5, 10 6, 5×10 6 Gy, res pectively. Then the weight loss, the equilibrium moisture content (EMC), the rec overy of wood compression set after adsorption (RSA) and the recovery after imme rsion in water (RSW), as well as the creep behaviour under a dry specimen condit ion and under an adsorption and subsequent desorption condition were measured an d discussed. This research proves that the doses of gamma irradiation have great effect on weight loss, EMC, RSA, RSW of irradiated compressed wood of Chinese f ir. The weight loss and the EMC increase, the RSA and the RSW fall drastically w hen the irradiation doses exceed 10 6 Gy. Both the instantaneous compliance and the creep compliance of the irradiated specimens under the two measurement cond itions show the general trend of increase with the increase of gamma irradiation doses. It can be deduced that decomposition or decrystallization reactions happ en in the wood cell wall at high gamma irradiation doses, especially at doses of around 5×10 6 Gy. In addition, this research proves that decomposition of mai n components of cell wall of compressed wood will lead to fixation of compressio n set of wood to a certain degree.展开更多
文摘In order to discuss the mechanisms of permanent fixation of wood compression set , compressed wood of Chinese fir (Cunninghamia lanceolata) was irradiated by gamma rays from 60 Co. The irradiation doses were 0 (for match specim ens), 10 3, 5×10 3, 10 4, 5×10 4, 10 5, 5×10 5, 10 6, 5×10 6 Gy, res pectively. Then the weight loss, the equilibrium moisture content (EMC), the rec overy of wood compression set after adsorption (RSA) and the recovery after imme rsion in water (RSW), as well as the creep behaviour under a dry specimen condit ion and under an adsorption and subsequent desorption condition were measured an d discussed. This research proves that the doses of gamma irradiation have great effect on weight loss, EMC, RSA, RSW of irradiated compressed wood of Chinese f ir. The weight loss and the EMC increase, the RSA and the RSW fall drastically w hen the irradiation doses exceed 10 6 Gy. Both the instantaneous compliance and the creep compliance of the irradiated specimens under the two measurement cond itions show the general trend of increase with the increase of gamma irradiation doses. It can be deduced that decomposition or decrystallization reactions happ en in the wood cell wall at high gamma irradiation doses, especially at doses of around 5×10 6 Gy. In addition, this research proves that decomposition of mai n components of cell wall of compressed wood will lead to fixation of compressio n set of wood to a certain degree.