Comparative Study on Processing Property Between CWW CO_2 Gas Shielded Welding and SAW

Cable welding wire（CWW）CO2gas shielded welding is an innovative process arc welding with high efficiency,high quality and low consumption,in which cable wire is used as consumable electrode.CWW CO2gas shielded welding and submerged arc welding（SAW）are used for contrast studies on processing property of high strength steel A36used in ship structure.The results show that the shapes of weld seam,using CWW CO2gas shielded welding and SAW,are good and no weld defect such as air hole,flaw,slag inclusion,incomplete fusion,lack of penetration and so on are found in the weld seam.Because the rotating of arc during CWW CO2gas shielded welding process has a strong stirring effect on molten pool,the grain in the heat affected zone（HAZ）of the joints,using CWW CO2 gas shielded welding,is small.Tensile failure positions of joints by CWW CO2gas shielded welding and SAW are all in the base metal,but tensile strength of CWW CO2gas shielded welding joint is higher than that of SAW joint by an average of 2.3%.The average impact energy of HAZ,using CWW CO2gas shielded welding and SAW,is almost equal,but the average impact energy of the weld seam using CWW CO2gas shielded welding is increased by 6%,and the average impact energy of the fusion line is increased by 7%.The 180°bending tests for the joints of CWW CO2 gas shielded welding and SAW are all qualified,and the joints hardness is all less than HV 355,but hardness of CWW CO2gas shielded welding wire welding joint near the fusion line is obviously lower.It can be concluded that the properties of CWW CO2gas shielded welding are better than those of the SAW joint,and CWW CO2gas shielded welding is suitable for welding high strength steel A36used in ship structure.

Effect of Tempering Temperature on Strength and Toughness of Novel Carbide-Free Bainite/Martensite Duplex Phase Steel

The microstructure in the weld metals for HQ130+QJ63 high strength steels, which are welded by Ar CO 2 gas shielded metal arc welding, was analyzed by means of microscope and scan electron microscope (SEM). The relative content of different microstructure was evaluated with XQF 2000 micro image analyzer. The effect of acicular ferrite content on the impact toughness was also studied. The test results indicated that the main microstructure in the weld metals of HQ130+QJ63 high strength steels is acicular ferrite and a few pro eutectic ferrite on the boundary of original austenite grain. Near the fusion zone there are columnar grains whose direction coefficient (X) is 3 22, but the microstructure in the center of the weld metal is isometric grain, whose direction coefficient X=1 In order to avoid welding crack and improve welding technology the weld heat input should be strictly controlled in 10-16 kJ/cm. Thus, the main microstructure in the weld metals is fine acicular ferrite and the content of pro eutectic ferrite is limited. The impact toughness in the weld metals of HQ130+QJ63 steels can be ensured and can meet the requirements for application in engineering and machinery.

Numerical simulation of DE- GMAW of magnesium alloy cylinder

Double-electrode gas shielded arc welding （ DE - GMAW） was used to weld the magnesium alloy cylinder with the diameter of 200 mm and the thickness of 6 mm. In order to study the residual stress distribution of AZ31B magnesiunl alloy welding point, numerical sinmlation of welding temperature field, stress field and residual stress were carried out by MSC. mare software. The results show that the residual stress in the weld and the heat affected zone is large, and with the increase of the distance away from the weld center, the residual stress decreases. In most areas, the longitudinal residual stress is greater than the transverse residual stress （except for the inside and outside surfaces of the weld） , all of which provides theoretical support for the study of magnesiunl alloy welding residual stress.

Analysis Microstructure of Weld Metal for HQ130+QJ63 High Strength Steel

The microstructure in the weld metals for HQ130 + QJ63 high strength steels,which are welded by Ar-CO_2 gas shielded metal arc welding,was analyzed by means of microscope and scan electron microscope(SEM).The relative content of different microstructure was evaluated with XQF-2000 micro-image analyzer.The effect of acicular ferrite content on the impact toughness was also studied.The test results indicated that the main microstructure in the weld metals of HQ130 + QJ63 high strength steels is acicular ferrite and a few pro-eutectic ferrite on the boundary of original austenite grain.Near the fusion zone there are columnar grains whose direction coefficient(X) is 3.22,but the microstructure in the center of the weld metal is isometric grain,whose direction coefficient X = 1.In order to avoid welding crack and improve welding technology the weld heat input should be strictly controlled in 10-16 kJ/cm.Thus,the main microstructure in the weld metals is fine acicular ferrite and the content of pro-eutectic ferrite is limited.The impact toughness in the weld metals of HQ130+ QJ63 steels can be ensured and can meet the requirements for application in engineering and machinery.