Degradation induced by the negative bias temperature instability(NBTI)can be attributed to three mutually uncoupled physical mechanisms,i.e.,the generation of interface traps(ΔV_(IT)),hole trapping in pre-existing ga...Degradation induced by the negative bias temperature instability(NBTI)can be attributed to three mutually uncoupled physical mechanisms,i.e.,the generation of interface traps(ΔV_(IT)),hole trapping in pre-existing gate oxide defects(ΔV_(HT)),and the generation of gate oxide defects(ΔV_(OT)).In this work,the characteristic of NBTI for p-type MOSFET fabricated by using a 28-nm high-k metal gate(HKMG)process is thoroughly studied.The experimental results show that the degradation is enhanced at a larger stress bias and higher temperature.The effects of the three underlying subcomponents are evaluated by using the comprehensive models.It is found that the generation of interface traps dominates the NBTI degradation during long-time NBTI stress.Moreover,the NBTI parameters of the power-law time exponent and temperature activation energy as well as the gate oxide field acceleration are extracted.The dependence of operating lifetime on stress bias and temperature is also discussed.It is observed that NBTI lifetime significantly decreases as the stress increases.Furthermore,the decrease of charges related to interface traps and hole detrapping in pre-existing gate oxide defects are used to explain the recovery mechanism after stress.展开更多
The conduction mechanism of stress induced leakage current （SILC） through 2nm gate oxide is studied over a gate voltage range between 1.7V and stress voltage under constant voltage stress （CVS）. The simulation res...The conduction mechanism of stress induced leakage current （SILC） through 2nm gate oxide is studied over a gate voltage range between 1.7V and stress voltage under constant voltage stress （CVS）. The simulation results show that the SILC is formed by trap-assisted tunnelling （TAT） process which is dominated by oxide traps induced by high field stresses. Their energy levels obtained by this work are approximately 1.9eV from the oxide conduction band, and the traps are believed to be the oxygen-related donor-like defects induced by high field stresses. The dependence of the trap density on stress time and oxide electric field is also investigated.展开更多
文摘Degradation induced by the negative bias temperature instability(NBTI)can be attributed to three mutually uncoupled physical mechanisms,i.e.,the generation of interface traps(ΔV_(IT)),hole trapping in pre-existing gate oxide defects(ΔV_(HT)),and the generation of gate oxide defects(ΔV_(OT)).In this work,the characteristic of NBTI for p-type MOSFET fabricated by using a 28-nm high-k metal gate(HKMG)process is thoroughly studied.The experimental results show that the degradation is enhanced at a larger stress bias and higher temperature.The effects of the three underlying subcomponents are evaluated by using the comprehensive models.It is found that the generation of interface traps dominates the NBTI degradation during long-time NBTI stress.Moreover,the NBTI parameters of the power-law time exponent and temperature activation energy as well as the gate oxide field acceleration are extracted.The dependence of operating lifetime on stress bias and temperature is also discussed.It is observed that NBTI lifetime significantly decreases as the stress increases.Furthermore,the decrease of charges related to interface traps and hole detrapping in pre-existing gate oxide defects are used to explain the recovery mechanism after stress.
文摘The conduction mechanism of stress induced leakage current （SILC） through 2nm gate oxide is studied over a gate voltage range between 1.7V and stress voltage under constant voltage stress （CVS）. The simulation results show that the SILC is formed by trap-assisted tunnelling （TAT） process which is dominated by oxide traps induced by high field stresses. Their energy levels obtained by this work are approximately 1.9eV from the oxide conduction band, and the traps are believed to be the oxygen-related donor-like defects induced by high field stresses. The dependence of the trap density on stress time and oxide electric field is also investigated.