Magnesia Bricks for Glass Furnace(MgO Content≥95%)

1 Scope This standard specifies the classification, technical requirements, test methods, inspection rules, marking, packing, transportation, and storage of magnesia bricks for glass furnace.

Sintered AZS Bricks for Glass Melting Furnace

1 Scope This standard specifies the brand, technical requirements, test methods, inspection rules, marking, packing, transportation, storage, and quality certificate of sintered AZS bricks for glass melting furnace. This standard is applicable to sintered AZS bricks for glass melting furnace.

Fireclay Refractory Bricks for Glass Melting Furnace

This standard is applicable to fireclay refractory bricks with unit weight ≥ 50 kg for glass melting furnaces.

Silica Refractory Bricks for Glass Melting Furnace

1 Scope This standard specifies the classification, technical requirements, test method, inspection rules, marking, packing, transportation, storage and quality certification of silica refractory bricks for glass melting furRaces.

Low Porosity Fireclay Bricks for Glass Melting Furnace

This standard specifies the classification, technical requirements, test methods, inspection rules, marking, packing, transportation, storage and quality certificate of low porosity fireclay bricks for glass melting furnace.

High Quality Silica Bricks for Glass Melting Furnace

This standard specifies the classification, technical requirements, test method, inspection rules, marking, packing, transportation, storage and quality certification of high quality silica bricks for glass melting furnace.

超高大曲面玻璃砖幕墙施工技术

北京市某工程采用超高大曲面玻璃砖幕墙进行装饰,为解决传统施工工艺存在的问题,对超高大曲面玻璃砖幕墙施工关键技术进行研究,提出玻璃砖内吊挂法。采用玻璃砖内吊挂法施工时,可将传统玻璃砖幕墙施工时的受力体系进行转换,通过不锈钢通丝吊杆承受单元体玻璃砖全部重力荷载,利用转接件将各单元体进行连接,采用玻璃胶填充玻璃砖层间缝隙,以保证幕墙具有良好的整体性、稳定性、安全性和观感。

平板玻璃大型熔窑碹顶结构受力仿真分析

利用仿真分析方法对大型玻璃熔窑碹顶结构进行模拟,探究碹顶结构的受力稳定性,并对不同尺寸的碹顶在冷态和热态工作环境下的变形和应力进行分析。结果表明,不同跨度的总变形量随跨度的增加最大变形量数值逐渐增大,而且中部变形量大的区域向两侧逐渐增加;碹顶最大应力值位置主要集中在碹顶中部碹厚的2/3和碹角位置,碹角位置应力集中情况严重,要合理选择碹角耐火材料;大跨度熔窑碹顶会因碹顶角部耐火材料性能和拉条拉力不足等情况出现风险,在合理的结构设计下对施工、硅砖质量以及熔化的燃烧制度等提出更高要求。

木丝水泥填充墙-RC框架抗震性能试验研究

为研究木丝水泥填充墙-钢筋混凝土(RC)框架的抗震性能和破坏机理,共制作五个试件进行低周反复试验,其中一个试件为普通砖填充墙-RC框架对比试件,两个试件为开窗洞的木丝水泥填充墙-RC框架,另外两个试件为添加玻璃纤维网格布的木丝水泥填充墙-RC框架,并分析试件的滞回曲线、骨架曲线、延性系数、耗能情况与刚度退化等指标。试验结果表明,木丝水泥填充墙-RC框架的抗震性能良好,刚度退化速度远小于普通砖填充墙-RC框架,耗能能力在试件开裂后超过普通砖填充墙-RC框架;在木丝水泥填充墙-RC框架上开窗洞后会削弱其承载力,但破坏时裂缝只是沿四个窗角分别向四个填充墙角扩展,最终形成“X”形裂缝,而木丝水泥填充墙-RC框架与混凝土之间的粘结面未被破坏,在木丝水泥填充墙-RC框架表面加入玻璃纤维网格布后可以减少墙面裂纹的产生,且提高了极限承载力和延性系数,并抑制了刚度的快速下降。

异型耐火材料砖的三维建模与加工制造

由于异型耐火材料砖材质及形状的因素影响,传统的加工不能满足要求。根据耐火材料砖设计图纸,在厂家定制耐火材料砖毛坯,同时设计专用工装夹具、三维软件Pro/E编程软件和数控机床带直角铣头三者相互配合,可满足正常的加工程序。

蓄热室玻璃窑炉砌筑细节与要点

窑炉使用寿命的长短不仅与窑炉设计、耐材选择、日常维护和玻璃配方有关,而且与砌筑质量息息相关。砌筑质量差,会加速堵塞窑炉蓄热室,容易造成窑炉大碹窜火、掉砖以及熔化池漏料等问题,严重的会影响窑炉的使用寿命。从蓄热式窑炉基础的校正与定位、窑炉钢立柱安装、炉条碹砌筑、蓄热室墙体砌筑、筒型砖码放、池底保温层砌筑等环节入手,探讨窑炉砌筑中的一些要点与注意事项。

A Discussion on Stability of Mg-AI-spinet Crown of Glass Melters

In order to understand the failure mechanism of magnesia-alumina spinel crown of glass melters,a discussion on the stability of Mg-Al-spinel crown of glass melters was given in this paper.The discussion focused on the weight balance in the crown arch made of spinel or silica bricks,the creep of spinel crown bricks at high temperatures,the thermal stress distribution in crown bricks as well as at brick joints,and the displacement behavior of crown arch during heat-up of glass melter.It is believed that the tangential stress in spinel crown is much higher than that in silica crown due to the large differenee in their densities,and that the thermal stresses in the crown brick result in opening of a part of the brickto-brick joints at the cold side of the crown,and increase of the tangential stress needed for balancing the weight of the crown.Both defect migration in lattice or along grain boundary and viscous flow in glass phase at grain boundary contribute to the creep of crown bricks at high temperatures.The creep of the matrix of spinel brick is more significant than that of coarse grains because impurities,such as silica and calcia,are concentrated in it.For keeping the crown stable during heat-up period it is important to adjust properly the horizontal positions of each skew brick as temperature increasing based on correctly evaluating the thermal expansion according to the thermal expansion coefficient of the crown brick.

再生混合骨料混凝土的配合比设计与力学性能研究

基于建筑废弃物不断增多和固体废弃物资源化利用的需求,制备了不同再生砖骨料替代率和水玻璃浸泡处理的再生混合骨料混凝土试件。研究了再生砖骨料替代率和水玻璃浸泡处理对试件抗压强度和劈裂抗拉强度的影响。结果表明,在相同龄期下,试件的抗压强度/劈裂抗拉强度会随着再生砖骨料替代率增加而呈现逐渐减小;浸泡水玻璃试件的抗压强度/劈裂抗拉强度都会高于未浸泡水玻璃的试件,即进行浸泡水玻璃处理有助于提升再生混合骨料混凝土试件的抗压强度和劈裂抗拉强度。经过水玻璃浸泡的试件在再生砖替代率为40%时,仍然能够满足C30混凝土的抗压强度要求;再生砖替代率为20%的经过水玻璃浸泡试件的劈裂抗拉强度仍然要高于未经过水玻璃浸泡的纯再生混凝土试件(A0)。通过三次多项式拟合得到了抗压强度/劈裂抗拉强度与再生砖替代率之间的关系表达式,拟合曲线相关系数的可靠性都较高,可以初步采用关系表达式对再生混合骨料试件的抗压强度/劈裂抗拉强度进行预测。

玻璃砖在被动式绿色建筑墙体结构节能改造中的应用

针对传统建筑墙体的隔热性能不足,能源消耗较高的问题,分析玻璃砖在被动式绿色建筑墙体结构节能改造中的应用。通过BIM技术中的Revit软件和Ecotect能耗分析软件建立建筑墙体结构模型,模拟分析能耗。通过改造建筑墙体参数降低建筑能耗至最小值,建立目标函数,引入一种灰狼寻优算法对其求解,得到建筑墙体结构节能改造方案。算例分析结果表明,玻璃砖年总能耗分别为预制木质外墙挂板方案的66%、保温板方案的63%、泡沫混凝土复合墙板方案的56%。玻璃砖的应用对于被动式绿色建筑墙体结构节能改造具有良好的效果。

超高薄型小尺寸吊挂体系实心玻璃砖幕墙施工技术

以北泡轻钢地块一期夹芯板车间改造(北京国际设计周永久会址)项目为例,通过深化设计、调整采光井位置实心玻璃砖幕墙的砌筑形式和施工工艺,提升玻璃砖幕墙砌筑效率及平整度、垂直度效果。通过系列措施的实施,在保证玻璃砖幕墙整体设计观感效果美观以及施工实践的基础上,通过系统分析和科学总结,实现了采用薄型小尺寸实心玻璃砖砌筑超高玻璃砖幕墙整体结构稳定的目的,可为今后类似超高玻璃砖幕墙施工提供参考。

电熔刚玉砖在浮法玻璃熔窑中的应用

电熔刚玉砖因其在抗玻璃侵蚀、抗发泡、抗结石等方面优异的性能,在浮法玻璃熔窑有着重要的应用。论文主要介绍了电熔刚玉砖的种类与理化性能,以及在浮法玻璃熔窑的工程项目中实际的应用。

基于FTIR的变电站建筑玻璃砖粘接剩余强度测试研究

为了提升变电站建筑玻璃砖粘接的可靠性,研究基于FTIR分析的变电站建筑玻璃砖粘接剩余强度预测方法。选取改性硅烷聚氨酯粘接材料ISR70-08作为变电站建筑玻璃砖粘接材料,利用VERTEX70型的显微红外光谱仪采集变电站建筑玻璃砖中的粘接材料的FTIR光谱,利用WDW-E型电子万能试验机测试变电站建筑玻璃砖的粘接剩余强度。试验结果表明,采用该方法依据所采集的变电站建筑玻璃砖粘接材料的FTIR光谱,预测变电站建筑玻璃砖粘接剩余强度,剩余强度预测结果与实际剩余强度相差极小。

浅谈高锂玻璃对熔铸锆刚玉砖的侵蚀

通过静态侵蚀和动态侵蚀实验研究高锂玻璃对熔铸锆刚玉砖的侵蚀程度,测试了实际生产中高锂玻璃液对窑炉中的熔铸锆刚玉砖侵蚀后的表面成分,分析了高锂玻璃对熔铸锆刚玉砖侵蚀严重的原因。研究结果表明,原料中的锂元素对熔铸锆刚玉砖的侵蚀严重,这是由于锂离子半径小且化合价低,扩散系数大,更容易与熔铸锆刚玉砖中的酸性氧化物SiO_(2)和两性氧化物A1_(2)O_(3)反应,进而造成侵蚀。

基板玻璃窑炉电熔高锆砖关键性能研究

通过对不同型号电熔高锆砖热膨胀率、体积电阻率、抗侵蚀及发泡等关键性能进行对比研究,选出性能最优的电熔高锆砖材料为产线窑炉的高效稳定运行提供技术支撑。结果表明:几种型号的电熔高锆砖热膨胀曲线基本一致,抗侵蚀性能及体积电阻率略有差异,基于实验结果对比分析,探索出性能最佳的电熔高锆砖材料。