Municipal solid waste incineration products of bottom ash(BA),fly ash(FA),and pickling sludge(PS),causing severe environ-mental pollution,were transformed into glass ceramic foams with the aid of CaCO3 as a pore-foami...Municipal solid waste incineration products of bottom ash(BA),fly ash(FA),and pickling sludge(PS),causing severe environ-mental pollution,were transformed into glass ceramic foams with the aid of CaCO3 as a pore-foaming agent during sintering.The effect of the BA/FA mass ratio on the phase composition,pore morphology,pore size distribution,physical properties,and glass structure was investigated,with results showing that with the increase in the BA/FA ratio,the content of the glass phase,Si-O-Si,and Q3Si units decrease gradually.The glass transmission temperature of the mixture was also reduced.When combined,the glass viscosity decreases,causing bubble coalescence and uneven pore distribution.Glass ceramic foams with uniform spherical pores are fabricated.When the content of BA,FA,and PS are 35wt%,45wt%,and 20wt%,respectively,contributing to high performance glass ceramic foams with a bulk density of 1.76 g/cm3,porosity of 56.01%,and compressive strength exceeding 16.23 MPa.This versatile and low-cost approach provides new insight into synergistically recycling solid wastes.展开更多
基金the National key R&D projects(Nos.2019YFC1907101,2019YFC1907103,2017YFB0702304)the Key R&D project in Ningxia Hui Autonomous Region(No.2020BCE01001)+5 种基金the National Natural Science Foundation of China(No.51672024)the Xijiang Innovation and Entrepreneurship Team(No.2017A0109004)the Program of China Scholarships Coun-cil(No.201806465040)the Fundamental Research Funds for the Central Universities(Nos.FRF-IC-19-007,FRF-IC-19-017Z,FRF-MP-19-002,FRF-TP-19-003B1,FRF-GF-19-032B,and 06500141)the State Key Laboratory for Ad-vanced Metals and Materials(No.2019Z-05)the Integ-ration of Green Key Process Systems MIIT.
文摘Municipal solid waste incineration products of bottom ash(BA),fly ash(FA),and pickling sludge(PS),causing severe environ-mental pollution,were transformed into glass ceramic foams with the aid of CaCO3 as a pore-foaming agent during sintering.The effect of the BA/FA mass ratio on the phase composition,pore morphology,pore size distribution,physical properties,and glass structure was investigated,with results showing that with the increase in the BA/FA ratio,the content of the glass phase,Si-O-Si,and Q3Si units decrease gradually.The glass transmission temperature of the mixture was also reduced.When combined,the glass viscosity decreases,causing bubble coalescence and uneven pore distribution.Glass ceramic foams with uniform spherical pores are fabricated.When the content of BA,FA,and PS are 35wt%,45wt%,and 20wt%,respectively,contributing to high performance glass ceramic foams with a bulk density of 1.76 g/cm3,porosity of 56.01%,and compressive strength exceeding 16.23 MPa.This versatile and low-cost approach provides new insight into synergistically recycling solid wastes.