This paper studied the preparation and mechanical properties of glass fiber reinforced polymer-matrix composite rings prepared by filament winding assisted by ultraviolet(UV)curing.A ray-tracing method was used to cal...This paper studied the preparation and mechanical properties of glass fiber reinforced polymer-matrix composite rings prepared by filament winding assisted by ultraviolet(UV)curing.A ray-tracing method was used to calculate the penetration ability of UV light in the resin casting,and then a typical composite ring with dual⁃curing characteristics was prepared by UV-assisted curing.The effects of winding speed and thermal initiator concentration on the distribution of fiber fraction and mechanical properties were studied.Microscopic morphology was used for the observation of the differences in fiber volume fraction.Mechanical properties tests and scanning electron micrographs were performed to investigate the failure and damage mechanisms of the composite ring samples.The ray tracing results indicate that the UV light can pass through a single yarn thickness and the energy transmitted is sufficient to cure the back side quickly.The experimental results show that the mechanical properties of the composite ring prepared in this paper are comparable to those of the heat-cured samples,which is sufficient to meet the requirements of the flywheel.展开更多
The aim is to evaluate the flexural strength of acrylic resin bars depending on the addiction of glass fibers with or without previous 3-methacryloxypropyl-trimethoxysilane (silane) application. Short fibers (3 mm) we...The aim is to evaluate the flexural strength of acrylic resin bars depending on the addiction of glass fibers with or without previous 3-methacryloxypropyl-trimethoxysilane (silane) application. Short fibers (3 mm) were treated and added to an acrylic resin powder, being further mixed with acrylic liquid to create bars (25 × 2 × 2 mm) of 11 experimental groups (N = 10), according to the interaction of experimental factors: weight % of glass fibers: (0.5;1;3;4;6 and 7) and silane application (with silane (S) or without silane (N)). Flexural strength and scanning microscopy evaluation were performed (SEM). Data (MPa) were submitted to ANOVA and Tukey (α = 5%). A significant difference between groups was observed (p = 0.001): S7%(128.85 ± 35.76)a, S6% (119.31 ± 11.97)ab, S4% (116.98 ± 25.23)ab, N4% (107.85 ± 24.88)abc, S1% (96.29 ± 20.65)bc, S0.5% (89.29 ± 7.33)cd, S3% (89.0 ± 11.27)cd, N3% (86.79 ± 17.63)cd, N1% (85.43 ± 16.44)cd, Control (73.29 ± 25.0)de, N0.5% (59.58 ± 19.46)e. For N groups, it was not possible to include more than 4%wt fibers. SEM showed better fiber-resin interaction for S groups, and fractures around fibers on N groups. Previous silane application enables the addiction of greater quantity of glass fibers and better interaction with the acrylic resin resulting in higher flexural strength. Without silane, fibers seem to act as initial crack points due to poor interaction.展开更多
Ultra-violet(UV)curing is an efficient method for composite molding.Firstly,thermophysical properties of UV cured glass-fiber reinforced plastics are conducted.Material properties are studied for various kinds of post...Ultra-violet(UV)curing is an efficient method for composite molding.Firstly,thermophysical properties of UV cured glass-fiber reinforced plastics are conducted.Material properties are studied for various kinds of postcuring modes.Then the UV curing method is suggested in manufacturing V-crimp folded core for sandwich panels.Two kinds of processing schemes for V-crimp folded core manufacturing using UV curing are presented.Finally,the effect of post-curing on the mechanical properties of folded core sandwiches is experimentally studied,and optimum modes of post-curing are determined.The experimental results show that the ultimate compressive strength of the folded sandwiches is increased by 60% after post-curing with the optimum post-curing mode.展开更多
Effects of ultrasonic vibrations on mechanical properties of fiber reinforced plastics were investigated during molding resin impregnation process in vacuum assisted resin transfer molding.?The vacuum bag including th...Effects of ultrasonic vibrations on mechanical properties of fiber reinforced plastics were investigated during molding resin impregnation process in vacuum assisted resin transfer molding.?The vacuum bag including the preformed each?non-crimp fabrics (carbon and glass fibers)?was placed in a water bath of an ultrasonic wave generator during resin impregnation. The mechanical properties of the laminates were evaluated?through the mechanical strength tests and scanning electron microscope?(SEM) observation. The results revealed that ultrasonic waves improved transverse tensile, flexural, interlaminar shear, and compressive strengths of the carbon fiber (CF) laminates and interlaminar shear and compressive strengths of the glass fiber (GF) laminates. It was found from SEM observation that the fracture modes of the CF and GF laminates processed using ultrasonic waves were resin fracture. Accordingly, the adhesion of the fiber/resin interface was improved by oscillating ultrasonic vibration during resin impregnation, leading to an increase of the interface strength.展开更多
基金supported by the National Key Laboratory of Science and Technology on Helicopter Transmission(Nanjing University of Aeronautics and Astronautics)(No.HTL-A-20K01)the Pretension and Relaxation Mechanism of Thermoplastic Prepreg Tape Winding with Tension Used to Hi-Speed Permanent Magnet Machine Sleeve(No.51903249)the Priority Academic Program Development of Jiangsu Higher Education Institutions and the Fundamental Research Funds for the Central Universities。
文摘This paper studied the preparation and mechanical properties of glass fiber reinforced polymer-matrix composite rings prepared by filament winding assisted by ultraviolet(UV)curing.A ray-tracing method was used to calculate the penetration ability of UV light in the resin casting,and then a typical composite ring with dual⁃curing characteristics was prepared by UV-assisted curing.The effects of winding speed and thermal initiator concentration on the distribution of fiber fraction and mechanical properties were studied.Microscopic morphology was used for the observation of the differences in fiber volume fraction.Mechanical properties tests and scanning electron micrographs were performed to investigate the failure and damage mechanisms of the composite ring samples.The ray tracing results indicate that the UV light can pass through a single yarn thickness and the energy transmitted is sufficient to cure the back side quickly.The experimental results show that the mechanical properties of the composite ring prepared in this paper are comparable to those of the heat-cured samples,which is sufficient to meet the requirements of the flywheel.
基金The authors thank NAP/MEPA-Esalq-USP for support,assistance and availability of the laboratory and microscopy equipment which enabled the development of this research.
文摘The aim is to evaluate the flexural strength of acrylic resin bars depending on the addiction of glass fibers with or without previous 3-methacryloxypropyl-trimethoxysilane (silane) application. Short fibers (3 mm) were treated and added to an acrylic resin powder, being further mixed with acrylic liquid to create bars (25 × 2 × 2 mm) of 11 experimental groups (N = 10), according to the interaction of experimental factors: weight % of glass fibers: (0.5;1;3;4;6 and 7) and silane application (with silane (S) or without silane (N)). Flexural strength and scanning microscopy evaluation were performed (SEM). Data (MPa) were submitted to ANOVA and Tukey (α = 5%). A significant difference between groups was observed (p = 0.001): S7%(128.85 ± 35.76)a, S6% (119.31 ± 11.97)ab, S4% (116.98 ± 25.23)ab, N4% (107.85 ± 24.88)abc, S1% (96.29 ± 20.65)bc, S0.5% (89.29 ± 7.33)cd, S3% (89.0 ± 11.27)cd, N3% (86.79 ± 17.63)cd, N1% (85.43 ± 16.44)cd, Control (73.29 ± 25.0)de, N0.5% (59.58 ± 19.46)e. For N groups, it was not possible to include more than 4%wt fibers. SEM showed better fiber-resin interaction for S groups, and fractures around fibers on N groups. Previous silane application enables the addiction of greater quantity of glass fibers and better interaction with the acrylic resin resulting in higher flexural strength. Without silane, fibers seem to act as initial crack points due to poor interaction.
基金supported by the Ministry of Education and Science of Russian Federation (No.RFMEFI57414X0078)
文摘Ultra-violet(UV)curing is an efficient method for composite molding.Firstly,thermophysical properties of UV cured glass-fiber reinforced plastics are conducted.Material properties are studied for various kinds of postcuring modes.Then the UV curing method is suggested in manufacturing V-crimp folded core for sandwich panels.Two kinds of processing schemes for V-crimp folded core manufacturing using UV curing are presented.Finally,the effect of post-curing on the mechanical properties of folded core sandwiches is experimentally studied,and optimum modes of post-curing are determined.The experimental results show that the ultimate compressive strength of the folded sandwiches is increased by 60% after post-curing with the optimum post-curing mode.
文摘Effects of ultrasonic vibrations on mechanical properties of fiber reinforced plastics were investigated during molding resin impregnation process in vacuum assisted resin transfer molding.?The vacuum bag including the preformed each?non-crimp fabrics (carbon and glass fibers)?was placed in a water bath of an ultrasonic wave generator during resin impregnation. The mechanical properties of the laminates were evaluated?through the mechanical strength tests and scanning electron microscope?(SEM) observation. The results revealed that ultrasonic waves improved transverse tensile, flexural, interlaminar shear, and compressive strengths of the carbon fiber (CF) laminates and interlaminar shear and compressive strengths of the glass fiber (GF) laminates. It was found from SEM observation that the fracture modes of the CF and GF laminates processed using ultrasonic waves were resin fracture. Accordingly, the adhesion of the fiber/resin interface was improved by oscillating ultrasonic vibration during resin impregnation, leading to an increase of the interface strength.