Experimental Study on Influence of Dimples on Lubrication Performance of Glass Fiber-epoxy Resin Composite under Natural Seawater Lubrication

Bionic non-smooth surface is widely applied in metal and ceramics materials. In order to introduce this technology to high pressure seawater pump, the influence of bionic non-smooth surface on the engineering plastics used in pump should be investigated. The comparative tests are carried out with a ring-on-disc configuration under 800, 1000, 1200 and 1400 r/min in order to research the influence of the bionic non-smooth surface on glass fiber-epoxy resin composite（GF/EPR） under natural seawater lubrication. The disc surfaces are textured with five kinds of pits, which are semi-spherical, conical, cone-cylinder combined, cylindrical pits and through holes, respectively. A smooth surface is tested as reference. The results show that the lubrication performance of dimpled GF/EPR sample is much better than that of the smooth sample under all rotational speeds. The semi-spherical pits surface has more obvious friction reduction than the others, which shows that the least reduction is approximately 43.29% of smooth surface under 1200 r/rain. However, the wear level is only marginally influenced by dimples. The surface morphology investigations disclose severe modifications caused by abrasive wear primarily. The results are helpful to vary friction properties of GF/EPR by non-smooth surface, or provide references to the design of non-smooth surfaces under certain condition.

Influence of Non-smooth Surface on Tribological Properties of Glass Fiber-epoxy Resin Composite Sliding against Stainless Steel under Natural Seawater Lubrication

With the development of bionics, the bionic non-smooth surfaces are introduced to the field of tribology. Although non-smooth surface has been studied widely, the studies of non-smooth surface under the natural seawater lubrication are still very fewer, especially experimental research. The influences of smooth and non-smooth surface on the frictional properties of the glass fiber-epoxy resin composite（GF/EPR） coupled with stainless steel 316 L are investigated under natural seawater lubrication in this paper. The tested non-smooth surfaces include the surfaces with semi-spherical pits, the conical pits, the cone-cylinder combined pits, the cylindrical pits and through holes. The friction and wear tests are performed using a ring-on-disc test rig under 60 N load and 1000 r/min rotational speed. The tests results show that GF/EPR with bionic non-smooth surface has quite lower friction coefficient and better wear resistance than GF/EPR with smooth surface without pits. The average friction coefficient of GF/EPR with semi-spherical pits is 0.088, which shows the largest reduction is approximately 63.18% of GF/EPR with smooth surface. In addition, the wear debris on the worn surfaces of GF/EPR are observed by a confocal scanning laser microscope. It is shown that the primary wear mechanism is the abrasive wear. The research results provide some design parameters for non-smooth surface, and the experiment results can serve as a beneficial supplement to non-smooth surface study.

Mechanical properties of short carbon/glass fiber reinforced high mechanical performance epoxy resins

To research the relationship between epoxy and fiber inherent property and mechanical properties of composite,we prepared a series of composites using three kinds of high mechanical performance epoxy resins as matrices and reinforced by the same volume fraction(5%)of short carbon and glass fiber.Their mechanical properties were investigated from the perspective of chemical structure and volume shrinkage ratio of epoxy.We analyzed their tensile strength and modulus based on the mixing rule and Halpin-Tsai eq...

Determination of Water Diffusion Coefficients and Dynamics in Adhesive/Carbon Fiber Reinforced Epoxy Resin Composite Joints

To determinate the water diffusion coefficients and dynamics in adhesive/carben fiber reinforced epoxy resin composite joints, energy dispersive X-ray spectroscopy analysis（EDX） is used to establish the content change of oxy- gen in the adhesive in adhesive/carbon fther reinforced epoxy resin composite joints. As water is made up of oxygen and hydrogen, the water diffusion coefficients and dynamics in adhesive/carben fiber reinforced epoxy resin composite joints can be obtained from the change in the content of oxygen in the adhesive during humidity aging, via EDX analy-sis. The authors have calculated the water diffusion coefficients and dynamics in the adhesive/carbon fiber reinforced epoxy resin composite joints with the aid of beth energy dispersive X-ray spectroscopy and elemental analysis. The de- termined results with EDX analysis are almost the same as those determined with elemental analysis and the results al- so show that the durability of the adhesive/carbon fther reinforced epoxy resin composite joints subjected to silane cou- pling agent treatment is better than those subjected to sand paper burnishing treatment and chemical oxidation treat- ment.

Research on properties of hollow glass microspheres/epoxy resin composites applied in deep rock in-situ temperature-preserved coring

Deep petroleum resources are in a high-temperature environment.However,the traditional deep rock coring method has no temperature preserved measures and ignores the effect of temperature on rock porosity and permeability,which will lead to the distortion of the petroleum resources reserves assessment.Therefore,the hollow glass microspheres/epoxy resin(HGM/EP)composites were innovatively proposed as temperature preserved materials for in-situ temperature-preserved coring(ITP-Coring),and the physical,mechanical,and temperature preserved properties were evaluated.The results indicated that:As the HGM content increased,the density and mechanical properties of the composites gradually decreased,while the water absorption was deficient without hydrostatic pressure.For composites with 50 vol%HGM,when the hydrostatic pressure reached 60 MPa,the water absorption was above 30.19%,and the physical and mechanical properties of composites were weakened.When the hydrostatic pressure was lower than 40 MPa,the mechanical properties and thermal conductivity of composites were almost unchanged.Therefore,the composites with 50 vol%HGM can be used for ITPCoring operations in deep environments with the highest hydrostatic pressure of 40 MPa.Finally,to further understand the temperature preserved performance of composites in practical applications,the temperature preserved properties were measured.An unsteady-state heat transfer model was established based on the test results,then the theoretical change of the core temperature during the coring process was obtained.The above tests results can provide a research basis for deep rock in-situ temperature preserved corer and support accurate assessment of deep petroleum reserves.

Kinetic Study of Resin-Curing on Carbon Fiber/Epoxy Resin Composites by Microwave Irradiation

Microwave processing has great potential for improving composite manufacturing such as reduction of curing time, energy requirements and operational costs. In this paper, the effects of microwave irradiation for resin-curing of carbon fiber/epoxy resin composite that was composed of discontinuous carbon fibers of 130 μm or 3 mm were investigated. The mechanical properties of carbon fiber/epoxy resin composite cured by microwave irradiation for 20 min at 120°C were similar to ones of the sample prepared by conventional oven for 180 min at 120°C. Microwavecured carbon fiber/epoxy resin composite had higher glass transition temperature than the one prepared by conventional oven. The relation between curing time and flexural modulus indicated that the curing velocity of microwave-irradiated carbon fiber/epoxy resin composite was 9 times faster than the one prepared by conventional oven. Furthermore, activation energies for resincuring reaction on microwave and conventional-cured carbon fiber/epoxy resin composite were estimated. The resin-curing reaction in carbon fiber/epoxy resin composite was promoted by microwave irradiation.

Mechanical Properties of Glass Fiber/Unsaturated Polyester Resin Composite Water Collector

The water collector is operated in the humid and hot environment of the cooling tower all the year round.It also needs to carry part of the weight of water and silt.Therefore,it is particularly critical to optimize the material of the water collector and improve its mechanical properties.Polyester,a general term of polymer obtained from polyols and polyacids,is a kind of engineering plastics with excellent properties and wide applications.Glass fiber is a reinforced plastic reinforcement material,and the biggest characteristic of it is the high tensile strength and good heat resistance.In this paper,glass fiber reinforced polyester resin composite material is prepared,its tensile properties and bending properties are tested,and the performance of the imported material JK2020B is compared and analyzed.The results show that the elastic modulus along the fiber direction is relatively high,but the interlayer force in the direction of thickness and width is very small.This review provides a guidance for production process.

Interlaminar Fracture Toughness of Epoxy Glass Fiber Fly Ash Laminate Composite

Epoxy glass fiber laminate composite (PMCs) are finding ever increasing applications in aerospace and automobile industries due to its high strength to weight ratio and resistance to aqueous environment. Additions of particulate reinforcements in the polymer matrix are reported to improve the Interlaminar Shear Strength and Interlaminar Fracture Toughness of the composites. In the present investigation, epoxy glass fiber laminate composites were processed using hand layup and vacuum bagging technique. The particulate reinforcement precipitator fly ash (25 - 45 μm) was added in the epoxy matrix by mechanical mixing up to 10 wt%. The effects of fly ash reinforcement on the mechanical properties and Interlaminar Fracture Toughness were studied before and after exposure to aqueous fog in a salt fog chamber at 45°C. In unexposed condition Mode I interlaminar fracture toughness of epoxy glass fiber laminate composite improved by the addition of fly ash reinforcement 10% (By weight) by 49.43% and when it was subjected to aqueous fog for 10 days the interlaminar fracture toughness improved 58.42%. Exposure to aqueous fog for 10 days causes plasticization of resin matrix and weakening of fiber/matrix interface results in improvement in interlaminar fracture toughness. The fracture surfaces were analyzed using scanning electron microscopy.

Studies on Mechanical Properties of Jute/E-Glass Fiber Reinforced Epoxy Hybrid Composites

Hybrid materials of any class are essential for current demands. This paper deals with the hybrid effect of composites made of jute/E-Glass fibers which are fabricated by hand layup method using LY556 Epoxy resin and HY951 hardener. The properties of this hybrid composite are determined by testing like tensile, flexural, impact, and inter laminar shear strength which are evaluated experimentally according to ASTM standards. The result of the test shows that hybrid composite of jute/ E-glass fiber has far better properties than that of jute fiber composite. However, it is found that the hybrid composite has better strength as compared to jute fiber composite fabricated separately with glass fiber.

Effect of E-44 Epoxy Resin and Pyrolysis Temperature on the Adhesion Strength of SiBCN Ceramic

An adhesive of the SiBCN ceramic was synthesized through the polymer derived ceramics(PDC)route.Meanwhile with higher adhesion strength and simpler process condition,the polyborosilazane(PSNB)was modified by E-44 epoxy resin.The E-44 epoxy resin was used to promote the oxidation process of SiBCN,in other words,to produce more amount of SiO2-B2O3 glasses.The phase composition,elemental analysis,chemical bonds and microstructure were investigated by using X-ray diffraction(XRD),X-ray photoelectron spectroscopy(XPS),and scanning electron microscope(SEM)measurements.The E-44 modified adhesives were cured at 120℃in air for 2 h,and were pyrolyzed at 1200,1400,and 1500℃for 2 h in air,respectively.The highest adhesion strength of the modified adhesive was up to 5.33,12.23,and 12.50 MPa after being heat treated at 1200,1400,and 1500℃,respectively.Finally,we proposed an adhesion model and revealed the adhesion mechanism of SiBCN ceramic.

Effect of Silane Coupling Agent on the Flexural Property of Glass Fiber Reinforced Composite Film

Transparent glass fiber reinforced composites films ware fabricated by UV light induced chemical crosslinking of composite materials consisting of glass fiber and UV curable resin in film state. In order to apply film to flexible device, excellent flexural property is required, then the delamination should not occurred between glass fiber and UV curable resin when film is bent. To minimize delamination and improve the interfacial adhesion at interface between glass fiber and UV curable resin, the γ-aminopropyl triethoxy silane and γ-glycid oxypropyl trimethoxy silane were applied for the surface treatment of glass fibers. Silanization of glass fiber surface was checked by scanning electron microscopy and the degree of delamination of composite film was confirmed through the bending test, ASTEM290-96a, used by haze meter.

On-line Monitoring of Epoxy Resin Exposed to Acid Solution

In this study, a new on-line health monitoring technology for the determination of the penetration of environment solution into epoxy resin was pursued. A corrosion sensor including plastic optical fiber and pH indicator was fabricated. The color-change layer of this sensor appeared after immersion in sulfuric acid solution, which could be examined by using optical fiber and spectrophotometer. The results showed that the penetration of sulfuric acid was detected by adding bromophenol blue （BPB） in the corrosion sensor. This system could be applied to on-line health monitoring of chemical equipment structures.

Phosphorylated Salicylic Acid as Flame Retardant in Epoxy Resins and Composites

A novel,versatile flame retardant substructure based on phosphorylated salicylic acid(SCP)is described and used in the synthesis of new flame retardants for HexFlow
RTM6,a high-performance epoxy resin used in resin transfer molding processes as composite matrix.The starting material salicylic acid can be obtained from natural sources.SCP as reactive phosphorus chloride is converted with a novolak,a novolak containing 9,10-dihydro-9-oxa-10-phospha-phenanthrene-10-oxide(DOPO)substituents or DOPO-hydroquinone to flame retardants with sufficient thermal stability and high char yield.Additionally,these flame retardants are soluble in the resin as well as react into the epoxy network.The determined thermal stability and glass transition temperatures of flame retarded neat resin samples as well as the interlaminar shear strength of corresponding carbon fiber reinforced composite materials showed the applicability of these flame retardants.Neat resin samples and composites were tested for their flammability by UL94 and/or flame-retardant performance by cone calorimetry.All tested flame retardants decrease the peak of heat release rate by up to 54%for neat resin samples.A combination of DOPO and SCP in one flame retardant shows synergistic effects in char formation and the mode of action adapts to neat resin or fiber-reinforced samples,so there is efficient flame retardancy in both cases.Therefore,a tailoring of SCP based flame retardants is possible.Additionally,these flame retardants efficiently reduce fiber degradation during combustion of carbon fiber-reinforced epoxy resins as observed by scanning electron microscopy and energy dispersive X-ray spectroscopy.

Preparation and Mechanical Properties of UV⁃Assisted Filament Winding Glass Fiber Reinforced Polymer⁃Matrix Composite

This paper studied the preparation and mechanical properties of glass fiber reinforced polymer-matrix composite rings prepared by filament winding assisted by ultraviolet(UV)curing.A ray-tracing method was used to calculate the penetration ability of UV light in the resin casting,and then a typical composite ring with dual⁃curing characteristics was prepared by UV-assisted curing.The effects of winding speed and thermal initiator concentration on the distribution of fiber fraction and mechanical properties were studied.Microscopic morphology was used for the observation of the differences in fiber volume fraction.Mechanical properties tests and scanning electron micrographs were performed to investigate the failure and damage mechanisms of the composite ring samples.The ray tracing results indicate that the UV light can pass through a single yarn thickness and the energy transmitted is sufficient to cure the back side quickly.The experimental results show that the mechanical properties of the composite ring prepared in this paper are comparable to those of the heat-cured samples,which is sufficient to meet the requirements of the flywheel.

Studies on interacting Blends of Acrylated Epoxy resin based Poly(Ester-Amide)s and Vinyl EsterResin

Epoxy resin based Unsaturated poly(ester-amide) resins (UPEAs) can be prepared by many methods but here these were prepared by reported method [1]. These UPEAs were then treated with acrylotl chloride to afford acrylated UPEAs resin (i.e. AUPEAs). Interacting blends of equal proportional AUPEAs and vinyl ester epoxy (VE) resin were prepared. APEAs and AUPEAs were characterized by elemental analysis, molecular weight determined by vapour pressure osmometer and by IR spectral study and by thermogravimetry. The curing of interacting blends was monitored on differential scanning calorimeter (DSC). Based on DSC data in situ glass reinforced composites of the resultant blends have been prepared and characterized for mechanical, electrical and chemical properties. Unreinforced blends were characterized by thermogravimetry (TGA).

Mechanical Properties of Submicron Glass Fiber Reinforced Vinyl Ester Composite

Vinyl ester (VE) resin inherently has intrinsic brittleness due to its high cross-link density. To improve mechanical performance, micro/nano fillers are widely used to modify this matrix. In present study, glass fiber in submicron scale at low contents was added into VE to prepare submicron composite (sMC). The impact resistance of un-notched sMC degraded with the increase of sGF content while that of notched-sMC remained the unchanged. Flexural properties of sMCs also were the same with that of neat resin. The results of Dynamic mechanical analysis (DMA) test showed the slight increase of storage modulus and the decrease of tan delta value in the case of sMC compared to those of un-filled matrix. However, the Mode I fracture toughness of sMC improved up to 26% and 61% corresponding to 0.3 and 0.6 wt% glass fiber used. The compact tension sample test suggests that there is the delay of crack propagation under tensile cyclic load in resin reinforced by submicron glass fiber. The number of failure cycle enlarged proportionally with the increment of sGF content in matrix.

Fabrication and Characterization of Glass Fiber with SiC Reinforced Polymer Composites

Glass Fiber Reinforced Polymeric (GFRP) Composites are most commonly used as bumpers for vehicles, electrical equipment panels, and medical devices enclosures. These materials are also widely used for structural applications in aerospace, automotive, and in providing alternatives to traditional metallic materials. The paper fabricated epoxy and polyester resin composites by using silicon carbide in various proportions along with GFRP. The hand lay-up technique was used to fabricate the laminates. To determine the properties of fabricated composites, the tensile, impact, and flexural tests were conducted. This method of fabrication was very simple and cost-effective. Their mechanical properties like yield strength, yield strain, Young’s modulus, flexural modulus, and impact energy were investigated. The mechanical properties of the GFRP composites were also compared with the fiber volume fraction. The fiber volume fraction plays a major role in the mechanical properties of GFRP composites. Young’s modulus and tensile strength of fabricated composites were modelled and compared with measured values. The results show that composites with epoxy resin demonstrate higher strength and modulus compared to composites with polyester resin.

Influence of Glass Fiber wt% and Silanization on Mechanical Flexural Strength of Reinforced Acrylics

The aim is to evaluate the flexural strength of acrylic resin bars depending on the addiction of glass fibers with or without previous 3-methacryloxypropyl-trimethoxysilane (silane) application. Short fibers (3 mm) were treated and added to an acrylic resin powder, being further mixed with acrylic liquid to create bars (25 × 2 × 2 mm) of 11 experimental groups (N = 10), according to the interaction of experimental factors: weight % of glass fibers: (0.5;1;3;4;6 and 7) and silane application (with silane (S) or without silane (N)). Flexural strength and scanning microscopy evaluation were performed (SEM). Data (MPa) were submitted to ANOVA and Tukey (α = 5%). A significant difference between groups was observed (p = 0.001): S7%(128.85 ± 35.76)a, S6% (119.31 ± 11.97)ab, S4% (116.98 ± 25.23)ab, N4% (107.85 ± 24.88)abc, S1% (96.29 ± 20.65)bc, S0.5% (89.29 ± 7.33)cd, S3% (89.0 ± 11.27)cd, N3% (86.79 ± 17.63)cd, N1% (85.43 ± 16.44)cd, Control (73.29 ± 25.0)de, N0.5% (59.58 ± 19.46)e. For N groups, it was not possible to include more than 4%wt fibers. SEM showed better fiber-resin interaction for S groups, and fractures around fibers on N groups. Previous silane application enables the addiction of greater quantity of glass fibers and better interaction with the acrylic resin resulting in higher flexural strength. Without silane, fibers seem to act as initial crack points due to poor interaction.