(Ti, Al)N gradient nano-coating was deposited on the surface of 1Cr11Ni2W2MoV stainless steel by the MTP-8-800 arc ion plating equipment. And the oxidation performance at high temperature for 500h was tested under t...(Ti, Al)N gradient nano-coating was deposited on the surface of 1Cr11Ni2W2MoV stainless steel by the MTP-8-800 arc ion plating equipment. And the oxidation performance at high temperature for 500h was tested under the condition of the surrounding air temperature 700℃. The test results show that, because of the structural features of the （Ti, Al）N coating, the coating becomes the compact and continuous Al2O3 film, which can protect the basis material effectively in the process of the high temperature oxidizing. The oxidation kinetics of the coating accord with parabolic law.展开更多
Fe-based composite coatings were fabricated on 5 CrNiMo die steel by laser beam melting a precursor mixture of ferrotitanium,ferrochromium,ferromolybdenum,B4 C and Y2 O3 powders.Micro structure and properties of the c...Fe-based composite coatings were fabricated on 5 CrNiMo die steel by laser beam melting a precursor mixture of ferrotitanium,ferrochromium,ferromolybdenum,B4 C and Y2 O3 powders.Micro structure and properties of the coatings were studied by X-ray diffraction(XRD),scanning electron microscopy(SEM),energy-dispersive spectrometer(EDS),resistance furnace and high-temperature tribometer.The results show that(Ti,Mo)C particles with flower-like and(Ti,Mo)B2 with block-like shapes are in situ formed during laser cladding.Volume faction of multiple ceramic particles increases with the increasing of Y2 O3.The cumulative oxidation mass of the coating with 2 wt% Y2 O3 is decreased by one-third than that of the coating without Y2 O3.The oxidation layer of the coating with Y2 O3 is getting smooth.Meanwhile,high temperature wear volume loss of the coating with 2 wt% Y2 O3 is about 40% that of the coating without Y2 O3.The coating with 2 wt% Y2 O3 shows a smoother wear scar and few flat grooves are observed after high temperature wear test.展开更多
文摘(Ti, Al)N gradient nano-coating was deposited on the surface of 1Cr11Ni2W2MoV stainless steel by the MTP-8-800 arc ion plating equipment. And the oxidation performance at high temperature for 500h was tested under the condition of the surrounding air temperature 700℃. The test results show that, because of the structural features of the （Ti, Al）N coating, the coating becomes the compact and continuous Al2O3 film, which can protect the basis material effectively in the process of the high temperature oxidizing. The oxidation kinetics of the coating accord with parabolic law.
基金the Natural Science Foundation of Shandong Province(ZR2017MEE021),China。
文摘Fe-based composite coatings were fabricated on 5 CrNiMo die steel by laser beam melting a precursor mixture of ferrotitanium,ferrochromium,ferromolybdenum,B4 C and Y2 O3 powders.Micro structure and properties of the coatings were studied by X-ray diffraction(XRD),scanning electron microscopy(SEM),energy-dispersive spectrometer(EDS),resistance furnace and high-temperature tribometer.The results show that(Ti,Mo)C particles with flower-like and(Ti,Mo)B2 with block-like shapes are in situ formed during laser cladding.Volume faction of multiple ceramic particles increases with the increasing of Y2 O3.The cumulative oxidation mass of the coating with 2 wt% Y2 O3 is decreased by one-third than that of the coating without Y2 O3.The oxidation layer of the coating with Y2 O3 is getting smooth.Meanwhile,high temperature wear volume loss of the coating with 2 wt% Y2 O3 is about 40% that of the coating without Y2 O3.The coating with 2 wt% Y2 O3 shows a smoother wear scar and few flat grooves are observed after high temperature wear test.