For 7475 Al alloy,there were micrographs showing filaments or whiskers formation during the separation stage of superplastic elongation.This indicates the presence of liquid phase which accommodates grain boundary sli...For 7475 Al alloy,there were micrographs showing filaments or whiskers formation during the separation stage of superplastic elongation.This indicates the presence of liquid phase which accommodates grain boundary sliding to reach superplasticity.On the other hand,there is no such phenomenon reported regarding Mg alloy in literatures.Scanning electron microscopic(SEM)fractography exceptionally exhibits a mark of grain boundary sliding and its accommodating mechanism of inter-granular liquid phase.Under the testing conditions of 350℃ and 1×10- 4s -1,the initially fine-grained structure(3.7μm)yields 642%superplastic elongation and exhibits fluffy appearance on the fractured surface.For other specimens showing less superplasticity,their fractured surfaces exhibit partial fluffy appearance.展开更多
It is important to inhibit the precipitation of η phases in precipitation strengthened Fe-Ni based alloys,as they will deteriorate not only the mechanical property but also the hydrogen resistance.The present investi...It is important to inhibit the precipitation of η phases in precipitation strengthened Fe-Ni based alloys,as they will deteriorate not only the mechanical property but also the hydrogen resistance.The present investigation shows that grain boundary engineering(GBE) can retard the formation and growth of ηphase in J75 alloy.After GBE treatment with 5% cold rolling followed by annealing at 1000℃ for 1 h,the fraction of special boundaries(SBs) increases from 38.4% in conventional alloy to 77.2% and the fraction of special triple junctions increases from 10% to 74%.During 800℃ aging treatment,quite amount of cellular η phases adjacent to random grain boundary(RGB) will be found in conventional alloy,and only a few small η phases have been observed in GBE treatment alloy subjected to the same aging treatment for long time.The reason for GBE in inhibiting precipitation of η phase can be attributed to not only introducing high fraction of SBs but also breaking the connectivity of RGB networks.As nucleation and growth of η phases on SBs are difficult due to their lower Ti concentration and diffusion rate,and the disruption of RGB networks reduces supply of Ti atoms to the η phases significantly,which impedes their growth at RGB.展开更多
文摘For 7475 Al alloy,there were micrographs showing filaments or whiskers formation during the separation stage of superplastic elongation.This indicates the presence of liquid phase which accommodates grain boundary sliding to reach superplasticity.On the other hand,there is no such phenomenon reported regarding Mg alloy in literatures.Scanning electron microscopic(SEM)fractography exceptionally exhibits a mark of grain boundary sliding and its accommodating mechanism of inter-granular liquid phase.Under the testing conditions of 350℃ and 1×10- 4s -1,the initially fine-grained structure(3.7μm)yields 642%superplastic elongation and exhibits fluffy appearance on the fractured surface.For other specimens showing less superplasticity,their fractured surfaces exhibit partial fluffy appearance.
基金supported by the National Natural Science Foundation of China and China Academy of Engineering Physics[No.U1730140]National Key Research and Development Program of China[Grant No.2019YFB1505201]。
文摘It is important to inhibit the precipitation of η phases in precipitation strengthened Fe-Ni based alloys,as they will deteriorate not only the mechanical property but also the hydrogen resistance.The present investigation shows that grain boundary engineering(GBE) can retard the formation and growth of ηphase in J75 alloy.After GBE treatment with 5% cold rolling followed by annealing at 1000℃ for 1 h,the fraction of special boundaries(SBs) increases from 38.4% in conventional alloy to 77.2% and the fraction of special triple junctions increases from 10% to 74%.During 800℃ aging treatment,quite amount of cellular η phases adjacent to random grain boundary(RGB) will be found in conventional alloy,and only a few small η phases have been observed in GBE treatment alloy subjected to the same aging treatment for long time.The reason for GBE in inhibiting precipitation of η phase can be attributed to not only introducing high fraction of SBs but also breaking the connectivity of RGB networks.As nucleation and growth of η phases on SBs are difficult due to their lower Ti concentration and diffusion rate,and the disruption of RGB networks reduces supply of Ti atoms to the η phases significantly,which impedes their growth at RGB.