The RAFM（reduced activation ferritic/martensitic）steels containing different tantalum contents（0wt.%,0.027wt.%,0.073wt.%）were designed and cast.Differential scanning calorimetry and optical microscopy were employe...The RAFM（reduced activation ferritic/martensitic）steels containing different tantalum contents（0wt.%,0.027wt.%,0.073wt.%）were designed and cast.Differential scanning calorimetry and optical microscopy were employed to explore the influence of tantalum content on the austenitic transformation of RAFM steels.The austenitic transformation kinetics was described by aphase-transformation model.The model,involving site saturation nucleation,diffusion-controlled growth and impingement correction,was established based on the classical Johnson-Mehl-Avrami-Kolmogorov model.The phase-transformation kinetics parameters,including D_0（pre-exponential factor for diffusion）and Q_d（activation energy for diffusion）,were calculated by fitting the experimental data and the kinetic model.The results indicated that the average grain size is decreased with the increase of tantalum.The values of A_（c1） and A_（c3） （onset and finish temperature of austenitic transformation,respectively）are increased by increasing the tantalum content.The increase of tantalum caused the decrease of D_0.However,Q_d is increased with the increase of tantalum.In addition,as a carbides forming element,tantalum would reduce the carbon diffusion coefficient and slow down the austenitic transformation rate.展开更多
基金financially sponsored by the China National Funds for Distinguished Young Scientists (Granted No.51325401)the National Natural Science Foundation of China(Granted No.51501126)the National Magnetic Confinement Fusion Energy Research Program(Granted No.2015GB119001)
文摘The RAFM（reduced activation ferritic/martensitic）steels containing different tantalum contents（0wt.%,0.027wt.%,0.073wt.%）were designed and cast.Differential scanning calorimetry and optical microscopy were employed to explore the influence of tantalum content on the austenitic transformation of RAFM steels.The austenitic transformation kinetics was described by aphase-transformation model.The model,involving site saturation nucleation,diffusion-controlled growth and impingement correction,was established based on the classical Johnson-Mehl-Avrami-Kolmogorov model.The phase-transformation kinetics parameters,including D_0（pre-exponential factor for diffusion）and Q_d（activation energy for diffusion）,were calculated by fitting the experimental data and the kinetic model.The results indicated that the average grain size is decreased with the increase of tantalum.The values of A_（c1） and A_（c3） （onset and finish temperature of austenitic transformation,respectively）are increased by increasing the tantalum content.The increase of tantalum caused the decrease of D_0.However,Q_d is increased with the increase of tantalum.In addition,as a carbides forming element,tantalum would reduce the carbon diffusion coefficient and slow down the austenitic transformation rate.