Improving mechanical properties and high-temperature oxidation of press hardened steel by adding Cr and Si

This work investigated the effect of Cr and Si on the mechanical properties and oxidation resistance of press hardened steel.Results indicated that the microstructure of the Cr-Si micro-alloyed press hardened steel consisted of lath martensite,M_(23)C_(6)carbides,and retained austenite.The retained austenite and carbides are responsible for the increase in elongation of the micro-alloyed steel.In addition,after oxidation at 930℃for 5 min,the thickness of the oxide scales on the Cr-Si micro-alloyed press hardened steel is less than 5μm,much thinner than 45.50μm-thick oxide scales on 22MnB5.The oxide scales of the Cr-Si micro-alloyed steel are composed of Fe_(2)O_(3),Fe_(3)O_(4),mixed spinel oxide(FeCr_(2)O_(4)and Fe_(2)SiO_(4)),and amorphous SiO_(2).Adding Cr and Si significantly reduces the thickness of the oxide scales and prevents the generation of the FeO phase.Due to the increase of spinel FeCr_(2)O_(4)and Fe_(2)SiO_(4)phase in the inner oxide scale and the amorphous SiO_(2)close to the substrate,the oxidation resistance of the Cr-Si micro-alloyed press hardened steel is improved.

Effects of deformation temperatures on microstructures,aging behaviors and mechanical properties of Mg-Gd-Er-Zr alloys fabricated by hard-plate rolling

In this investigation,a high-strength Mg-12Gd-1.0Er-0.5Zr(wt.%)alloy sheet was produced by hot extrusion(HE)and subsequent hard-plate rolling(HPR)at different temperatures.The results indicate that the microstructures of these final-rolled sheets are inhomogeneous,mainly including coarse deformed grains and dynamic recrystallized(DRXed)grains,and the volume fraction of these coarse deformed grains increases as the rolling temperature increases.Thus,more DRXed grains can be found in R-385℃sheet,resulting in a smaller average grain size and weaker basal texture,while the biggest grains and the highest strong basal texture are present in R-450℃sheet.Amounts of dynamic precipitation ofβphases which are mainly determined by the rolling temperature are present in these sheets,and its precipitation can consume the content of Gd solutes in the matrix.As a result,the lowest number density ofβphase in R-450℃sheet is beneficial to modify the age hardening response.Thus,the R-450℃sheet displays the best age hardening response because of a severe traditional precipitation ofβ’(more)andβH/βM(less)precipitates,resulting in a sharp improvement in strength,i.e.ultimate tensile strength(UTS)of∼518±17 MPa and yield strength(YS)of∼438±18 MPa.However,the elongation(EL)of this sheet reduces greatly,and its value is∼2.7±0.3%.By contrasting,the EL of the peak-aging R-385℃sheet keeps better,changing from∼4.9±1.2%to∼4.8±1.4%due to a novel dislocation-induced chain-like precipitate which is helpful to keep good balance between strength and ductility.

Multiple Node Upset in SEU Hardened Storage Cells

We study the problem of multiple node upset （MNU） using three-dimensional device simulation. The results show the transient floating node and charge lateral diffusion are the key reasons for MNU. We compare the MNU with multiple bit upset （MBU）,and find that their characteristics are different. Methods to avoid MNU are also discussed.

Flow characteristics and hot workability of a typical low-alloy high-strength steel during multi-pass deformation

Heavy components of low-alloy high-strength(LAHS) steels are generally formed by multi-pass forging. It is necessary to explore the flow characteristics and hot workability of LAHS steels during the multi-pass forging process, which is beneficial to the formulation of actual processing parameters. In the study, the multi-pass hot compression experiments of a typical LAHS steel are carried out at a wide range of deformation temperatures and strain rates. It is found that the work hardening rate of the experimental material depends on deformation parameters and deformation passes, which is ascribed to the impacts of static and dynamic softening behaviors. A new model is established to describe the flow characteristics at various deformation passes. Compared to the classical Arrhenius model and modified Zerilli and Armstrong model, the newly proposed model shows higher prediction accuracy with a confidence level of 0.98565. Furthermore, the connection between power dissipation efficiency(PDE) and deformation parameters is revealed by analyzing the microstructures. The PDE cannot be utilized to reflect the efficiency of energy dissipation for microstructure evolution during the entire deformation process, but only to assess the efficiency of energy dissipation for microstructure evolution in a specific deformation parameter state.As a result, an integrated processing map is proposed to better study the hot workability of the LAHS steel, which considers the effects of instability factor(IF), PDE, and distribution and size of grains. The optimized processing parameters for the multi-pass deformation process are the deformation parameters of 1223–1318 K and 0.01–0.08 s^(-1). Complete dynamic recrystallization occurs within the optimized processing parameters with an average grain size of 18.36–42.3 μm. This study will guide the optimization of the forging process of heavy components.

A Radiation Hardened Power Device——VDMNOSFET

A radiation hardened N channel Si power device——VDMNOSFET (Vertical Double Diffused Metal Nitride Oxide Semiconductor Field Effect Transistor) is fabricated by using a double layer (Si 3N 4 SiO 2) gate dielectric and a self aligned heavily doped shallow P + region.The effects of ionizing radiation and transient high dose rate radiation of the power VDMNOSFET are also presented.Good radiation hardening performance is obtained,compared with the conventional power VDMOSFET.For the specified 200V VDMNOSFET,the threshold voltage shifts is only -0 5V at a Gamma dose of 1Mrad(Si) with +10V gate bias;the transconductance is degraded by 10% at a Gamma dose of 1Mrad(Si);and no burnout failures occur at the transient high dose rate of 1×10 12 rad(Si)/s.It is demonstrated that the ionizing radiation tolerance and burnout susceptibilities of the power MOSFET are improved significantly by using a double layer (Si 3N 4 SiO 2) gate dielectric and a self aligned heavily doped shallow P + region.

A refined deviatoric hardening plastic model for sand

The classical deviatoric hardening models are capable of characterizing the mechanical response of granular materials for a broad range of degrees of compaction.This work finds that it has limitations in accurately predicting the volumetric deformation characteristics under a wide range of confining/consolidation pressures.The issue stems from the pressure independent hardening law in the classical deviatoric hardening model.To overcome this problem,we propose a refined deviatoric hardening model in which a pressure-dependent hardening law is developed based on experimental observations.Comparisons between numerical results and laboratory triaxial tests indicate that the improved model succeeds in capturing the volumetric deformation behavior under various confining/consolidation pressure conditions for both dense and loose sands.Furthermore,to examine the importance of the improved deviatoric hardening model,it is combined with the bounding surface plasticity theory to investigate the mechanical response of loose sand under complex cyclic loadings and different initial consolidation pressures.It is proved that the proposed pressure-dependent deviatoric hardening law is capable of predicting the volumetric deformation characteristics to a satisfactory degree and plays an important role in the simulation of complex deformations for granular geomaterials.

Hardening mechanism and thermal-solid coupling model of laminar plasma surface hardening of 65 Mn steel

In the present work,the laminar plasma surface hardening method is employed to enhance the service life of metal components fabricated from 65 Mn steel.The mechanical and wear behaviors of the laminar plasma surface hardened 65 Mn steel were analyzed.The martensite transition transformation of the temperature of the laminar plasma-hardened 65 ferrite Mn steel was determined by a thermal-solid coupling model.Based on the orthogonal experimental results,the optimal hardening parameters were confirmed.The scanning velocity,quenching distance and arc current are 130 mm/min,50 mm and 120 A,respectively.The pearlites and ferrites are transformed into martensites in the hardened zone,while the ratio of martensite in the heataffected zone decreases with the increase in the hardening depth.Compared to the untreated 65Mn steel,the average hardness increases from 220 HV_(0.2)to 920 HV_(0.2)in the hardened zone and the corresponding absorbed power increases from 118.7 J to 175.5 J.At the same time,the average coefficient of friction(COF)decreases from 0.763 to 0.546,and the wear rate decreases from 5.39×10^(-6)mm^(3)/(N·m)to 2.95×10^(-6)mm^(3)/(N·m),indicating that the wear resistance of 65Mn steel could be significantly improved by using laminar surface hardening.With the same hardening parameters,the depth and width of the hardened zone predicted by the thermal-solid coupling model are 1.85 mm and 11.20 mm,respectively,which are in accordance with the experimental results;depth is 1.83 mm and width is 11.15 mm.In addition,the predicted hardness distributions of the simulation model are in accordance with the experimental results.These results indicate that the simulation model could effectively predict the microstructure characteristics of 65 Mn steel.

Achieving High Strength and Tensile Ductility in Pure Nickel by Cryorolling with Subsequent Low-Temperature Short-Time Annealing

Ultra fine-grained pure metals and their alloys have high strength and low ductility.In this study,cryorolling under different strains followed by low-temperature short-time annealing was used to fabricate pure nickel sheets combining high strength with good ductility.The results show that,for different cryorolling strains,the uniform elongation was greatly increased without sacrificing the strength after annealing.A yield strength of 607 MPa and a uniform elongation of 11.7%were obtained after annealing at a small cryorolling strain(ε=0.22),while annealing at a large cryorolling strain(ε=1.6)resulted in a yield strength of 990 MPa and a uniform elongation of 6.4%.X-ray diffraction(XRD),transmission electron microscopy(TEM),scanning electron microscopy(SEM),and electron backscattered diffraction(EBSD)were used to characterize the microstructure of the specimens and showed that the high strength could be attributed to strain hardening during cryorolling,with an additional contribution from grain refinement and the formation of dislocation walls.The high ductility could be attributed to annealing twins and micro-shear bands during stretching,which improved the strain hardening capacity.The results show that the synergistic effect of strength and ductility can be regulated through low-temperature short-time annealing with different cryorolling strains,which provides a new reference for the design of future thermo-mechanical processes.

EXPERIMENT ON SURFACE INTEGRITY OF MILLING TOOL FOR HARDENED STEEL SKD11

To evaluate the new designed cutting tools for high-efficiency milling of the hardened die steel SKD11,surface integrities of millers with different geometric structures are analyzed, considering the surface roughness, micrograph of chips, surface microhardness, residual stress and metallurgical texture of the surface layer. The in fluences of geometric characteristics of different cutting tools and their wear characteristics on the surface integrity are studied. Results show that the milling tool with rake angle; 5 of the hardened diesteel. The generation of saw-tooth chips is depressed when a reasonable positive rake angle is selected. And the compressive residual stress is induced on the machined surface in milling the hardened die steel. The occurrence of surface softening is postponed by increasing the clearance angle and reducing the tool flank wear.

Effect of Pre-strain on Microstructure and Stamping Performance of High-strength Low-alloy Steel

In this study,pre-strain ranging from 0 to 0.12 was applied through uniaxial tension on high-strength low-alloy(HSLA)specimens with four kinds of grain size.Effect of pre-strain and grain size on me-chanical property was investigated through tensile tests.Microstructures of the pre-strained and tensile tested samples were analyzed,respectively.The 30.8°v-bending and following flattening,as well as Erichson cupping tests,were performed on the pre-strained samples.Results show the elongation ratio of grain and dislocation density increases with pre-strain.Yielding platform is removed when pre-strain is larger than 0.06 while yielding plateau period decreases with pre-strain less than 0.06 due to reduction of pinning effect.The 30.8°v-bending and the following flattening tests are successfully accomplished on all the pre-strained samples with different grain size.Decrease in grain size,along with increase in pre-strain,causes increase in strength and decrease in elongation rate as well as cupping value.Pre-strain causes very slight effect on bending ability,much less than that on mechanical property and cupping test value.Reciprocal impact of the pre-strain and grain size on HSLA steel deformability is inconspicuous.

Quickly obtaining densely dispersed coherent particles in steel matrix and its related mechanical property

Densely distributed coherent nanoparticles(DCN)in steel matrix can enhance the work-hardening ability and ductility of steel simultaneously.All the routes to this end can be generally classified into the liquid-solid route and the solid-solid route.However,the formation of DCN structures in steel requires long processes and complex steps.So far,obtaining steel with coherent particle enhancement in a short time remains a bottleneck,and some necessary steps remain unavoidable.Here,we show a high-efficiency liquid-phase refining process reinforced by a dynamic magnetic field.Ti-Y-Mn-O particles had an average size of around(3.53±1.21)nm and can be obtained in just around 180 s.These small nanoparticles were coherent with the matrix,implying no accumulated dislocations between the particles and the steel matrix.Our findings have a potential application for improving material machining capacity,creep resistance,and radiation resistance.

A Correlation-Based Stochastic Model for Massive MIMO Channel

In this paper,the channel impulse response matrix(CIRM)can be expressed as a sum of couplings between the steering vectors at the base station(BS)and the eigenbases at the mobile station(MS).Nakagami distribution was used to describe the fading of the coupling between the steering vectors and the eigenbases.Extensive measurements were carried out to evaluate the performance of this proposed model.Furthermore,the physical implications of this model were illustrated and the capacities are analyzed.In addition,the azimuthal power spectrum(APS)of several models was analyzed.Finally,the channel hardening effect was simulated and discussed.Results showed that the proposed model provides a better fit to the measured results than the other CBSM,i.e.,Weichselberger model.Moreover,the proposed model can provide better tradeoff between accuracy and complexity in channel synthesis.This CIRM model can be used for massive MIMO design in the future communication system design.

In situ TEM investigation of electron irradiation and aging-induced high-density nanoprecipitates in an Mg-10Gd-3Y-1Zn-0.5Zr alloy

In-situ electron irradiation and aging are applied to introduce high-density precipitates in an Mg-10Gd-3Y-1Zn-0.5Zr(GWZ1031K,wt.%)alloy to improve the hardness.The results show that the hardness of the Mg alloy after irradiation for 10 h and aging for 9 h at 250℃ is 1.64 GPa,which is approximately 64% higher than that of the samples before being treated.It is mainly attributed to γ'precipitates on the basal plane after irradiation and the high-density nanoscale β'precipitates on the prismatic plane after aging,which should be closely related to the irradiation-induced homogenous clusters.The latter plays a key role in precipitation hardening.This result paves a way to improve the mechanical properties of metallic materials by tailoring the precipitation through irradiation and aging.

Deformation behavior of Mg-Y-Ni alloys containing different volume fraction of LPSO phase during tension and compression through in-situ synchrotron diffraction

The deformation behavior of the as-extruded Mg-Y-Ni alloys with different volume fraction of long period stacking ordered(LPSO)phase during tension and compression was investigated by in-situ synchrotron diffraction.The micro-yielding,macro-yielding,tension-compression asymmetry and strain hardening behavior of the alloys were explored by combining with deformation mechanisms.The micro-yielding is dominated by basal slip of dynamic recrystallized(DRXed)grains in tension,while it is dominated by extension twinning of non-dynamic recrystallized(non-DRXed)grains in compression.At macro-yielding,the non-DRXed grains are still elastic deformed in tension and the basal slip of DRXed grains in compression are activated.Meanwhile,the LPSO phase still retains elastic deformation,but can bear more load,so the higher the volume fraction of hard LPSO phase,the higher the tensile/compressive macro-yield strength of the alloys.Benefiting from the low volume fraction of the non-DRXed grains and the delay effect of LPSO andγphases on extension twinning,the as-extruded alloys exhibit excellent tension-compression symmetry.When the volume fraction of LPSO phase reaches∼50%,tension-compression asymmetry is reversed,which is due to the fact that the LPSO phase is stronger in compression than in tension.The tensile strain hardening behavior is dominated by dislocation slip,while the dominate mechanism for compressive strain hardening changes from twinning in theα-Mg grains to kinking of the LPSO phase with increasing volume fraction of LPSO phase.The activation of kinking leads to the constant compressive strain hardening rate of∼2500 MPa,which is significantly higher than the tensile strain hardening rate.

Mechanical behavior of nanorubber reinforced epoxy over a wide strain rate loading

Nanorubber/epoxy composites containing 0,2,6 and 10 wt%nanorubber are subjected to uniaxial compression over a wide range of strain rate from 8×10^(-4) s^(-1) to~2×10^(4) s^(-1).Unexpectedly,their strain rate sensitivity and strain hardening index increase with increasing nanorubber content.Potential mechanisms are proposed based on numerical simulations using a unit cell model.An increase in the strain rate sensitivity with increasing nanorubber content results from the fact that the nanorubber becomes less incompressible at high strain,generating a higher hydro-static pressure.Adiabatic shear localization starts to occur in the epoxy under a strain rate of 22,000 s^(-1) when the strain exceeds 0.35.The presence of nanorubber in the epoxy reduces adiabatic shear localization by preventing it from propagating.

An Elastoplastic Fracture Model Based on Bond-Based Peridynamics

Fracture in ductile materials often occurs in conjunction with plastic deformation.However,in the bond-based peridynamic(BB-PD)theory,the classic mechanical stress is not defined inherently.This makes it difficult to describe plasticity directly using the classical plastic theory.To address the above issue,a unified bond-based peridynamics model was proposed as an effective tool to solve elastoplastic fracture problems.Compared to the existing models,the proposed model directly describes the elastoplastic theory at the bond level without the need for additional calculation means.The results obtained in the context of this model are shown to be consistent with FEM results in regard to force-displacement curves,displacement fields,stress fields,and plastic deformation regions.The model exhibits good capability of capturing crack propagation in ductile material failure problems.

Low-cycle fatigue behavior of solutionized and aged WE43 magnesium alloys at room temperature

The low-cycle fatigue behavior of solutionized(T4)and aged(T6)WE43 magnesium alloys was studied at room temperature.The total strain amplitudes(△ε_(t)/2)were 0.4%,0.5%,0.6%,0.7%and 1.0%.Detailed microstructure evolution was characterized by scanning electron microscope(SEM),electron backscattered diffraction(EBSD)and transmission electron microscopy(TEM).The results showed that plastic strain amplitude decreased with the increasing cycle number in T4 alloy,which is due to the dense persistent slip bands(PSBs)and dynamic precipitates hinderingdislocation slip.In contrast,the plastic strain amplitude increases gradually in T6 alloy,which is attributed to the enhanced activation of pyramidal slip.The low-cycle fatigue life of T6 alloy with larger fatigue ductility coefficient is longer than that of T4 alloy.The Coffin-Manson model can accurately predict the fatigue life of T4 and T6 alloys compared to Jahed-Varvani(JV)energy model.For T4 alloy,the fatigue damage mechanism was dominated by basal slip.For T6 alloy,the enhanced pyramidal slip plays an important role to accommodate plastic deformation.

EXPERIMENT OF OPTIMUM GEOMETRY STRUC-TURE OF MILLING TOOLS FOR HARDENED STEEL SKD11

To select high performance milling tools with optimum geometry structure suitable for machining hardened steel SKD11, geometry structures of tools are optimized. Four kinds of TiAlN coated cemented carbide tools are developed. The milling performance in high-speed milling hardened steel SKD11 by using these four kinds of tools is evaluated through the aspects of cutting force, cutting vibration, chip deformation, tool life, and tool wear mechanism, thus determining the optimum milling tool. The tool life of the optimum tool is 3 times of that of other tool, and the cutting force and vibration decrease by 70% compared with that of other tools. It has the most stable cutting performance.

In-situ study of the microstructure evolution during tension of a Mg-Y-Zn-Al alloy processed by rapidly solidified ribbon consolidation technique

Mg-Y-Zn-Al alloys processed by rapidly solidified ribbon consolidation(RSRC)technique exhibit an exceptional mechanical performance indicating promising application potential.This material has a bimodal microstructure consisting of fine recrystallized and coarse non-recrystallized grains with solute-rich stacking faults forming cluster arranged layers(CALs)and nanoplates(CANaPs),or complete long period stacking ordered(LPSO)phase.In order to reveal the deformation mechanisms,in-situ synchrotron X-ray diffraction line profile analysis was employed for a detailed study of the dislocation arrangement created during tension in Mg-0.9%Zn-2.05%Y-0.15%Al(at%)alloy.For uncovering the effect of the initial microstructure on the mechanical performance,additional samples were obtained by annealing of the as-consolidated specimen at 300 and 400℃ for 2 h.The heat treatment at 300℃ had no significant effect on the initial microstructure,its evolution during tension and,thus,the overall deformation behavior under tensile loading.On the other hand,annealing at 400℃ resulted in a significant increase of the recrystallized grains fraction and a decrease of the dislocation density,leading to only minor degradation of the mechanical strength.The maximum dislocation density at the failure of the samples corresponding to the plastic strain of 10-25% was estimated to be about 16-20×10^(14)m^(-2).The diffraction profile analysis indicated that most dislocations formed during tension were of non-basal and pyramidal types,what was also in agreement with the Schmid factor values revealed independently from orientation maps.It was also shown that the dislocation-induced Taylor hardening was much lower below the plastic strain of 3% than above this value,which was explained by a model of the interaction between prismatic dislocations and CANaPs/LPSO plates.

Experimental Procedure and Hardening Model to Consider Forming and Baking Effects in Simulation

This paper investigated an experimental method for bake hardening properties, a technique for deriving the true stress-strain curves after reaching the maximum load, and a constitutive equation considering both work hardening and bake hardening in order to apply the work hardening occurring in the forming process of parts and the bake hardening induced in the baking process to an automotive crash simulation. A general bake hardening test is that a pre-tensioned specimen is baked and then the same specimen is tensioned again without any further treatment. For a bake hardening test of automotive steel with a tensile strength of 1.2 GPa or more, fractures often occur in curvature section outside, an extensometer due to the difference in the material strength caused by non-uniform bake hardening. This causes a problem in that the bake hardening properties cannot be obtained. In this paper, to prevent curvature fracture, tensile specimens were re-machined in the uniformly deformed region of large specimens subjected to pre-strain, and the re-machined specimens with uniform strength in all regions were re-tensioned. In the bake hardening test of ultra-high strength steels with a tensile strength of 1 GPa or more, shear band fractures occur when the pre-strain is large. This makes it impossible to obtain a true stress-strain curve because there is no uniformly deformed region under a tensile test. To overcome this problem, a new method to calculate the true stress-strain curve by comparing experimental results and the load calculated by the local strain obtained from digital images was developed. This method can be applied not only where shear band deformation occurs, but also in necking deformation, and true stress-strain curves for strains up to 2 - 3 times the uniform elongation can be obtained. A new constitutive equation was developed since an appropriate hardening model is required to simultaneously apply the work hardening and the bake hardening to the simulation. For the newly developed model, the user material subroutine of LS-Dyna was configured, and the simulation was performed on the single hat specimens with pre-strain. When both work hardening and bake hardening were considered, there was a significant increase in absorbed energy compared to when only work hardening was considered. This means that both work hardening and bake hardening should be considered in the car crash simulations to enhance the accuracy of the simulation.