Comparative investigations were carried out of the effect of heat treatment regimes Jor steel GC-4(40CrMnSiMoVA)on its crack propagating rates,from corrosion fatigue, (da/dN)_(CF),or stress corrosion cracking,(da/dt)_...Comparative investigations were carried out of the effect of heat treatment regimes Jor steel GC-4(40CrMnSiMoVA)on its crack propagating rates,from corrosion fatigue, (da/dN)_(CF),or stress corrosion cracking,(da/dt)_(SCC),in media with various constituents and pH values.Both(da/dN)_(CF) and(da/dt)_(SCC) accelerate with the increase of yield stress of the steel,yet the former is far less than the later.In comparison with media,the (da/dt)_(SCC) in distilled water is slightly greater than that in 3.5% NaCl solution,and the (da/dN)_(CF) in distilled water is far less than that in 3.5% NaCl solution.With the pH value increasing in 3.5% NaCl solution,the(da/dN)_(CF) lowers down and the(da/dt)_(SCC) speeds up.An explanation was also proposed with concept of the cyclic hardening and softening at crack tip,as well as the crack closure and occluded cell effect.展开更多
The effect of heat treatment on shape memory properties of the ductile CuAlMn alloys was studied. The results show that the heating temperature for the solution treatment should be around 100 ℃ above the transformati...The effect of heat treatment on shape memory properties of the ductile CuAlMn alloys was studied. The results show that the heating temperature for the solution treatment should be around 100 ℃ above the transformation temperature in order to obtain good shape memory properties, heating for 10 min at this temperature doesn’t have much influence on the shape memory properties, faster cooling rate helps to obtain good shape memory properties and the shape recovery rate(SRR) decreases with raising ageing temperatures. For Cu 16Al 10Mn alloy, the heat treatment process to acquire higher recovery rate is heating at 800 ℃ for 15 min, quenching into ice water and ageing below 150 ℃ for 15 min. For Cu 17Al 10Mn alloy, the process is the same except heating at 700 ℃.[展开更多
The dissimilar metals 1Crl8Ni9 and 16MnR are welded by shielded metal arc welding process using electrode A312. The corrosion experiments are carried out on welded joint samples, which is as-welded and post-weld heat ...The dissimilar metals 1Crl8Ni9 and 16MnR are welded by shielded metal arc welding process using electrode A312. The corrosion experiments are carried out on welded joint samples, which is as-welded and post-weld heat treatment at 650 ℃, 750 ℃ and 850 ℃, for 2 h in 70% sodium hydroxide solution. EDS and X-ray diffraction analysis are carried out on the samples after corrosion. Average corrosion rate calculation and microhardness measurement are conducted on both as- welded and post-weld heat treatment samples. The results indicate that average corrosion rate of as-welded joint metal is smaller than that of post-weld heat treatment joint metal. Compared with that of post-weld heat treatment at 750 ℃ and 850 ℃ for 2 h, the average corrosion rate of welded joint after post-weld heat treatment at 650 ℃ for 2 h increases greatly.展开更多
The effect of heat treatment on the electrochemical and mechanical properties of SS400 steel was investigated, and the effects of annealing conditions on notched specimens subjected to the slow strain rate test (SSRT)...The effect of heat treatment on the electrochemical and mechanical properties of SS400 steel was investigated, and the effects of annealing conditions on notched specimens subjected to the slow strain rate test (SSRT) were studied. The results show that no correlations are observed among the maximum tensile strength, yield strength, and stress corrosion cracking. In contrast, the elongation and time-to-fracture are improved with stress-relieving annealing compared with the as-received condition. The elongation, time-to-fracture, and number of dimples increase with annealing heat treatment.展开更多
文摘Comparative investigations were carried out of the effect of heat treatment regimes Jor steel GC-4(40CrMnSiMoVA)on its crack propagating rates,from corrosion fatigue, (da/dN)_(CF),or stress corrosion cracking,(da/dt)_(SCC),in media with various constituents and pH values.Both(da/dN)_(CF) and(da/dt)_(SCC) accelerate with the increase of yield stress of the steel,yet the former is far less than the later.In comparison with media,the (da/dt)_(SCC) in distilled water is slightly greater than that in 3.5% NaCl solution,and the (da/dN)_(CF) in distilled water is far less than that in 3.5% NaCl solution.With the pH value increasing in 3.5% NaCl solution,the(da/dN)_(CF) lowers down and the(da/dt)_(SCC) speeds up.An explanation was also proposed with concept of the cyclic hardening and softening at crack tip,as well as the crack closure and occluded cell effect.
文摘The effect of heat treatment on shape memory properties of the ductile CuAlMn alloys was studied. The results show that the heating temperature for the solution treatment should be around 100 ℃ above the transformation temperature in order to obtain good shape memory properties, heating for 10 min at this temperature doesn’t have much influence on the shape memory properties, faster cooling rate helps to obtain good shape memory properties and the shape recovery rate(SRR) decreases with raising ageing temperatures. For Cu 16Al 10Mn alloy, the heat treatment process to acquire higher recovery rate is heating at 800 ℃ for 15 min, quenching into ice water and ageing below 150 ℃ for 15 min. For Cu 17Al 10Mn alloy, the process is the same except heating at 700 ℃.[
文摘The dissimilar metals 1Crl8Ni9 and 16MnR are welded by shielded metal arc welding process using electrode A312. The corrosion experiments are carried out on welded joint samples, which is as-welded and post-weld heat treatment at 650 ℃, 750 ℃ and 850 ℃, for 2 h in 70% sodium hydroxide solution. EDS and X-ray diffraction analysis are carried out on the samples after corrosion. Average corrosion rate calculation and microhardness measurement are conducted on both as- welded and post-weld heat treatment samples. The results indicate that average corrosion rate of as-welded joint metal is smaller than that of post-weld heat treatment joint metal. Compared with that of post-weld heat treatment at 750 ℃ and 850 ℃ for 2 h, the average corrosion rate of welded joint after post-weld heat treatment at 650 ℃ for 2 h increases greatly.
文摘The effect of heat treatment on the electrochemical and mechanical properties of SS400 steel was investigated, and the effects of annealing conditions on notched specimens subjected to the slow strain rate test (SSRT) were studied. The results show that no correlations are observed among the maximum tensile strength, yield strength, and stress corrosion cracking. In contrast, the elongation and time-to-fracture are improved with stress-relieving annealing compared with the as-received condition. The elongation, time-to-fracture, and number of dimples increase with annealing heat treatment.