Effects of iron oxide on crystallization behavior and spatial distribution of spinel in stainless steel slag

Chromium plays a vital role in stainless steel due to its ability to improve the corrosion resistance of the latter.However,the re-lease of chromium from stainless steel slag(SSS)during SSS stockpiling causes detrimental environmental issues.To prevent chromium pollution,the effects of iron oxide on crystallization behavior and spatial distribution of spinel were investigated in this work.The results revealed that FeO was more conducive to the growth of spinels compared with Fe2O3 and Fe3O4.Spinels were found to be mainly distrib-uted at the top and bottom of slag.The amount of spinel phase at the bottom decreased with the increasing FeO content,while that at the top increased.The average particle size of spinel in the slag with 18wt%FeO content was 12.8μm.Meanwhile,no notable structural changes were observed with a further increase in FeO content.In other words,the spatial distribution of spinel changed when the content of iron oxide varied in the range of 8wt%to 18wt%.Finally,less spinel was found at the bottom of slag with a FeO content of 23wt%.

Microstructure and mechanical properties of a cast TRIP-assisted multiphase stainless steel

Stainless steels are used in a wide range of complex environments due to their excellent corrosion resistance.Multiphase stainless steels can offer an excellent combination of strength,toughness and corrosion resistance due to the coexistence of different microstructures.The microstructure and mechanical properties of a novel cast multiphase stainless steel,composed of martensite,ferrite,and austenite,were investigated following appropriate heat treatment processes:solution treatment at 1,050℃ for 0.5 h followed by water quenching to room temperature,and aging treatment at 500℃ for 4 h followed by water quenching to room temperature.Results show reversed austenite is formed by diffusion of Ni element during aging process,and the enrichment of Ni atoms directly determines the mechanical stability of austenite.The austenite with a lower Ni content undergoes a martensitic transformation during plastic deformation.The tensile strength of the specimen exceeds 1,100 MPa and the elongation exceeds 24%after solid solution,and further increases to 1,247 MPa and 25%after aging treatment.This enhancement is due to the TRIP effect of austenite and the precipitation of the nanoscale G-phase pinning dislocations in ferrite and martensite.

Experimental Study on Corrosion of Stainless Steel in Low Temperature Multi effect Seawater Desalination

Starting from the corrosion mechanism,this paper analyzes the characteristics of various types of stainless steel and selects the best performance composite plate composite plate stainless steel.Analyze and select the most suitable corrosion detection method based on specific practical multi working conditions,discuss the interference factors that affect metal corrosion during experimental simulation,and the advantages of newly developed sheet metal.The new development of composite board panels,with the substrate and composite materials applying their respective capabilities for MED,will bring breakthrough progress to the scientific research and engineering applica-tion of composite boards.

Achieving a high-strength dissimilar joint of T91 heat-resistant steel to 316L stainless steel via friction stir welding

The reliable welding of T91 heat-resistant steel to 316L stainless steel is a considerable issue for ensuring the safety in service of ultrasupercritical power generation unit and nuclear fusion reactor,but the high-quality dissimilar joint of these two steels was difficult to be obtained by traditional fusion welding methods.Here we improved the structure-property synergy in a dissimilar joint of T91 steel to 316L steel via friction stir welding.A defect-free joint with a large bonding interface was produced using a small-sized tool under a relatively high welding speed.The bonding interface was involved in a mixing zone with both mechanical mixing and metallurgical bonding.No obvious material softening was detected in the joint except a negligible hardness decline of only HV~10 in the heat-affected zone of the T91 steel side due to the formation of ferrite phase.The welded joint exhibited an excellent ultimate tensile strength as high as that of the 316L parent metal and a greatly enhanced yield strength on account of the dependable bonding and material renovation in the weld zone.This work recommends a promising technique for producing high-strength weldments of dissimilar nuclear steels.

Effect of surface damage induced by cavitation erosion on pitting and passive behaviors of 304L stainless steel

The corrosion behavior of 304L stainless steel(SS)in 3.5wt%NaCl solution after different cavitation erosion(CE)times was mainly evaluated using electrochemical noise and potentiostatic polarization techniques.It was found that the antagonism effect resulting in the passivation and depassivation of 304L SS had significant distinctions at different CE periods.The passive behavior was predominant during the incubation period of CE where the metastable pitting initiated at the surface of 304L SS.Over the rising period of CE,the 304L SS experienced a transition from passivation to depassivation,leading to the massive growth of metastable pitting and stable pitting.The depassivation of304L SS was found to be dominant at the stable period of CE where serious localized corrosion occurred.

Sputtered Stainless Steel on Silicon Photoanode for Stable Seawater Splitting in Photoelectrochemical Flow Cell

Photoelectrochemical(PEC)seawater splitting is a promising method for the direct utilization of solar energy and abundant seawater resources for hydrogen production.Photoelectrodes are susceptible to various ions in seawater and complicated competitive reactions,resulting in the failure of photoelectrodes.This paper proposes the design and fabrication of diff erent sputtered stainless steel(SS)fi lms deposited on silicon photoanodes,completely isolating the electrolytes and semiconductor substrate.Upon coupling with the PEC flow cell,the back-illuminated photoanode coated with 316 SS cocatalyst achieves stable operation for 70 h in natural seawater with a highly alkaline KOH(30 wt.%,7.64 mol/L)electrolyte due to the remarkable protection eff ect of the substrate from stainless steel,while the PEC seawater splitting system achieves a record hydrogen production rate of 600μmol/(h·cm^(2)).An appropriate Ni/Fe ratio in the SS ensures remarkable oxygen evolution activity,while chromic oxide ensures the effective anticorrosion effect by adjusting the microenvironment of the photoanodes.Moreover,fabricating PEC flow cells with photoanodes coated with SS cocatalysts are a viable strategy for PEC seawater splitting.

Study on the corrosion behavior of 316H stainless steel in molten NaCl–KCl–MgCl_(2) salts with and without purification

The corrosion behavior of 316H stainless steel(SS)in the impure and purified Na Cl–KCl–Mg Cl_(2) salt was investigated at700°C.Results indicate that the main deleterious impurity induced corrosion in the impure salt was the absorbed moisture,present in the form of Mg Cl_(2)·6H_(2)O.316H SS occurred severe intergranular corrosion with a corrosion depth of 130μm for1000 h in the impure Na Cl–KCl–Mg Cl_(2) salt.In contrast,the purification treatment of molten chloride salt by the dissolved Mg metal can remove the absorbed moisture,and the corresponding reactions were also discussed.As a result,the corrosiveness of Na Cl–KCl–Mg Cl_(2) salt is reduced significantly.316H SS occurred slight uniform corrosion with a depth of less than 5μm for 3000 h in the purified Na Cl–KCl–Mg Cl_(2) salt.

Effect of Chromium-enhanced Diffusivity on Reverted Transformation in Metastable Austenitic Stainless Steels:Theoretical Calculation and Experiment

Effects of nucleation sites and diffusivity enhancement of chromium on reverted transformation of AISI 304 stainless steel during annealing process were investigated.Dynamics calculation revealed that the reverted transformation of strain-inducedα’-martensite→γaustenite could were closely associated with active nucleation sites and diffusivity enhancement of chromium in nanocrystallineα’-martensite.The experimental data and the results were in accordance with 2-grain austenite/α’-martensite junctions calculated theoretically,which could result from high chromium diffusion rate in nanocrystallineα’-martensite.In addition,low temperature is not conducive to reversed transformation,while high temperature and long annealing time will lead to inhomogeneous grain size distribution.

Processing map and dynamic recrystallization behaviours of 316LN-Mn austenitic stainless steel

The hot deformation behaviours of 316LN-Mn austenitic stainless steel were investigated by uniaxial isothermal compression tests at different temperatures and strain rates.The microstructural evolutions were also studied using electron backscatter diffraction.The flow stress decreases with the increasing temperature and decreasing strain rate.A constitutive equation was established to characterize the relationship among the deformation parameters,and the deformation activation energy was calculated to be 497.92 k J/mol.Processing maps were constructed to describe the appropriate processing window,and the optimum processing parameters were determined at a temperature of 1107-1160℃ and a strain rate of 0.005-0.026 s^(-1).Experimental results showed that the main nucleation mechanism is discontinuous dynamic recrystallization(DDRX),followed by continuous dynamic recrystallization(CDRX).In addition,the formation of twin boundaries facilitated the nucleation of dynamic recrystallization.

High throughput screening of localised and general corrosion in type 2205 duplex stainless steel at ambient temperature

Bipolar electrochemistry is used to produce a linear potential gradient across a bipolar electrode(BPE),providing direct access to the anodic and cathodic reactions under a wide range of applied potentials.The occurrence of pitting corrosion,crevice corrosion,and general corrosion on type 2205 duplex stainless steel(DSS 2205)BPE has been observed at room temperature.The critical pit depth of 10-20μm with a55%-75% probability of pits developing into stable pits at potential from+0.9 to+1.2 V vs.OCP(open circuit potential)are measured.All pit nucleation sites are either within ferritic grains or at the interface between austenite and ferrite.The critical conditions for pitting and crevice corrosion are discussed with Epit(critical pitting potential)and Ecre(critical crevice potential)decreasing from 0.87 and 0.80 V vs.OCP after150 s of exposure to 0.84 and 0.76 V vs.OCP after 900 s of exposure,respectively.Pit growth kinetics under different applied bipolar potentials and exposure times have been obtained.The ferrite is shown to be more susceptible to general dissolution.

Deformation Mechanism of Bimodal Structured 2205 Duplex Stainless Steel in Two Yield Stages

A kind of micro/nanostructured 2205 duplex stainless steel(DSS)with uniform distribution of nanocrystals was prepared via aluminothermic reaction method.The analysis of stress-strain curve showed that the fracture strength and elongation of the specimen were 946 MPa and 24.7%,respectively.At present,the research on microstructure of bimodal 2205 DSS at room temperature(RT)mainly depended on scanning electron microscope(SEM)observation after loading experiments.The test result indicates that there are two different yield stages in stress-strain curve of specimen during tensile process.The microstructure of duplex bimodal structured stainless steel consists of two pairs of soft hard regions and phases.By studying deformation mechanism of bimodal structured stainless steel,the interaction between soft phase and hard phase are discussed.The principle of composition design and microstructure control of typical duplex stainless steel is obtained,which provides an important research basis for designing of advanced duplex stainless steel.

Investigation on influence of alloying on phase transitions of duplex stainless steel based on thermochemical calculation

This paper investigated on influence of different alloying elements added into duplex stainless steel (DSS) on phase transitions using thermochemical methods in comparison with experiment.The results showed that the most possible species in the ferrite phase,austenite phase,σphase,Hcp phase,χphase,and carbide were Cr:Va-type,Fe:Va-type,Ni:Cr:Mo-type,Cr_(2)N-type,Fe_(24)Mo_(10)Cr_(24)-type,and Cr:Mo:C-type,respectively.Furthermore,the Ni,N,Cr,and Mo alloying had significant influences on the transition of each DSS phase.The Ni and N additions obviously raised the temperature at ferrite-1/austenite-1 balance while the Cr and Mo decreased the dual-phase balance temperature.In addition,the Ni addition can promote the precipitating ofσphase at relatively high temperature while the precipitating of Hcp phase at relatively low temperature.The Hcp phase andχphase can be obviously increased by the N addition.The introduction of Cr and Mo notably enhances the precipitation ofσphase.However,the promotion ofχphase precipitation is facilitated by the presence of Mo,while the Cr element acts as an inhibitor forχphase precipitation.Furthermore,the ferrite/austenite ratio tested by experiment was higher than that calculated by thermochemical methods,thus pre-designed solution temperature should be lower about 30-100℃than that calculated by thermochemical methods.

Laser Additive Manufacturing of 316L Stainless Steel Thin-wall Ring Parts

The process parameters of laser additive manufacturing have an important influence on the forming quality of the produced items or parts.In the present work,a finite element model for simulating transient heat transfer in such processes has been implemented using the ANSYS software,and the temperature and stress distributions related to 316L stainless steel thin-walled ring parts have been simulated and analyzed.The effect of the laser power,scanning speed,and scanning mode on temperature distribution,molten pool structure,deformation,and stress field has been studied.The simulation results show that the peak temperature,weld pool size,deformation,and residual stress increase with an increase in laser power and a decrease in the scanning speed.The scanning mode has no obvious effect on temperature distribution,deformation,and residual stress.In addition,a forming experiment was carried out.The experimental results show that the samples prepared by laser power P=800 W,V=6 mm/s,and the normal scanning method display good quality,whereas the samples prepared under other parameters have obvious defects.The experimental findings are consistent with the simulation results.

Experimental and Numerical Studies on Sea Sand Concrete Filled Stainless Steel Tube with Inner FRP Tube Subjected to Axial Compression

Since fibre-reinforced polymer(FRP) and stainless steel(SS) offer advantages of corrosion resistance and hybrid confinement, this study proposed a new type of composite column: sea sand concrete(SSC)-filled SS tubular columns with an inner FRP tube(CFSTFs) to help exploit abundant ocean resources in marine engineering. To study compressive behaviours of these novel members, eight CFSTFs and two SSC-filled SS tubular columns(CFSTs)were tested under axial compression. Their axial load-displacement curves, axial load-strain curves in SS or FRP tubes were obtained, and influences of key test parameters(the existence of glass FRP(GFRP) tubes, steel tube shapes, and GFRP tube thicknesses and diameters) were discussed. Further, specimen failure mechanism was analyzed employing the finite element method using ABAQUS software. Test results confirmed the excellent ductility and load-bearing capacity of CFSTFs. The existence of GFRP tubes inside can postpone SS tube buckling, and the content of inner FRP tubes, particularly increasing diameters, was found to improve compressive behaviours. GFRP contents helped develop the second elastic-plastic stage of the load-displacement curves. Furthermore, the bearing capacity of CFSTFs with a circular cross-section was approximately 26% higher than that with a square cross-section, and this difference narrowed with the increase in GFRP ratios.

Penile and scrotal strangulation by stainless steel rings in an human immunodeficiency virus positive man: A case report

BACKGROUND Penoscrotal constriction devices are either used as autoerotic stimuli or to increase sexual pleasure or performance by maintaining an erection for a longer period,and a variety of metallic and non-metallic objects are used.On the other hand,penile strangulation is a rare urologic emergency that requires prompt evaluation and intervention to prevent long-term complications.The goal of treating penile incarceration is to remove the foreign object as soon as possible.On the other hand,removal can be very challenging,and often requires resourcefulness and a multidisciplinary approach.CASE SUMMARY A 47-year-old man who has sex with men was transferred to our hospital for persistent phallodynia and scrotal pain,accompanying swelling due to strangulation by stainless steel rings.His medical history included acquired immunodeficiency syndrome.One day prior,he had put three stainless steel rings on his penis and scrotum before sexual intercourse.After sexual intercourse,he was unable to remove them,due to swelling of his penis and scrotum.The swelling persisted,and he felt pain in the affected area the next day,then he was transferred to our hospital by ambulance.The emergency department found that his penis and scrotum were markedly engorged and swollen.We established a diagnosis of penile and scrotal strangulation by stainless steel rings.We unsuccessfully attempted to cut the rings using a cutter,then requested a rescue team via emergency medical service.They cut through each ring in two places,using an electric-powered angle grinder,and successfully removed all of the pieces.Finally,he was discharged and went home.CONCLUSION We report the first case of penile and scrotal strangulation by stainless steel rings in an human immunodeficiency virus positive person.

Simulation of the Behaviour Laws in the Thermal Affected Zones of the 13Cr-4Ni Martensitic Stainless Steel

During the welding, many phenomena occur. The materials deform under the action of residual stresses. This tendency is due to the high gradients of temperature during the process. These deformations are really difficult for many professionals operating in the area. In the goal to predict these variations, one has established the behaviour laws which will be applied to evaluate residual stresses and strains. This research is focused on the study of the Thermal Affected Zone (TAZ) during the welding of the 13Cr-4Ni martensitic stainless steel. The TAZ does not know any change of state (solid/liquid). It only knows the metallurgical phase change (austenite/martensite). There are three types of behaviour laws in this study: thermal, mechanical and metallurgical behaviour laws. The thermal behaviour law serves to evaluate the temperature field which induces the mechanical strains. The mechanical behaviour law serves to evaluate spherical stress (pressure) and deviatoric stress which compose the residual stress. It also helps to measure the total strain. The metallurgical behaviour law serves for the evaluation of the metallurgical phase proportions. To validate the modelling developed in this study, one has made the simulations to compare the results obtained with the analytical and experimental data.

Literature Review of Phase Transformations and Cavitation Erosion of Duplex Stainless Steels

Phase transformation is one of the factors that would significantly influence the ability to resist cavitation erosion of stainless steels. Due to the specific properties of duplex stainless steel, the heat treatment would bring about significant phase transformations. In this paper, we have examined the previous studies on the phase transition of stainless steel, including the literature on the classification of stainless steel, spinodal decomposition, sigma phase transformation, and cavitation erosion of double stainless steel. Through these literature investigations, the destruction of cavitation erosion on duplex stainless steel can be clearly known, and the causes of failure of duplex stainless steel in seawater can be clarified, thus providing a theoretical basis for subsequent scientific research. And the review is about to help assess the possibility of using bulk heat treatment to improve the cavitation erosion (CE) behaviour of the duplex stainless steel 7MoPLUS.

Development of heat-resistant ferritic stainless steels for exhaust lines at Nisshin Steel

Exhaust emission regulations of the automotive are enforced in each country to prevent air pollution and global warming,and the restriction standard tends to become severer.Various techniques such as the combustion improvement of gasoline,upgrades of the catalyst,and the thermal capacity decreases in the exhaust lines are adopted to suit the regulations,and these lead to an increase of the maximum temperature of the exhaust gas. Recently,ferritic stainless steels are mainly used to parts of exhaust lines,as their thermal expansion coefficient is small,and the cyclic oxidation resistance and the thermal fatigue property are better than austenitic stainless steels. This paper presents newly developed heat-resistant stainless steels from Nisshin Steel for exhaust lines usage,and describes the currents of the steel development that could be envisaged in the future.With regard to improving the high-temperature strength of ferritic stainless steels,the addition of Nb,Mo and Cu is effective in solution hardening and precipitation hardening at 700℃,while the addition of Nb,Mo and W is effective in mainly solution hardening at 900℃.The addition of Cr,Si and Mn suppress the breakaway oxidation in air at 950℃up to 200 h of ferritic stainless steels containing 14%Cr.Especially,the addition of 0.8%or higher Mn would effectively improve the adherence of oxide scale.It is confirmed that ferritic stainless steels,NSSHR-1(14Cr-lMn-0.9Si-Nb) and NSSHR-2(10Cr-0.9Si-Nb-Ti ),is having a superior heat resistance,formability and cost performance compared to conventional Type441 and Type439 respectively.

The Formation of Colored Film on Stainless Steel and the Study for Surface Structure

本文介绍不锈钢化学着色膜的形成和制备，测定了膜层主要理化性能；利用ＳＥＭ、ＡＥＳ、ＡＦＭ、ＳＴＭ等方法研究着色膜的化学成分、表面形貌、结构特征。

Antibacterial Mechanism of Copper-bearing Antibacterial Stainless Steel against E.Coli

A preliminary study was made on the antibacterial mechanism of copper-bearing antibacterial stainless steels against E.coli through experiments of microbiology such as EDTA （ethylenediaminetetraacetic acid） complexing, DNA smearing and AFM （atomic force microscope） observation. It was measured that the antibacterial stainless steels showed excellent antibacterial functions with antibacterial rate to E.coli over 99.99%. The antibacterial rate was weak if the bacteria solution was complexed by EDTA, indicating that the copper ions play a dominant role in the antibacterial effect of the antibacterial stainless steels. The electrophoresis experiment did not show the phenomenon of DNA smearing for E.coli after contacting antibacterial stainless steels, which meant that DNA of E.coli was not obviously damaged. It was observed by AFM that the morphology of E.coli changed a lot after contacting antibacterial stainless steels, such as cell walls being seriously changed and lots of contents in the cells being leaked.