Microstructure,mechanical properties and phase transformation of a heat-resistant rare-earth(RE)Mg-16.1Gd-3.5Nd-0.38Zn-0.26Zr-0.15Y(wt.%)alloy were investigated.The as-cast alloy is composed of equiaxedα-Mg matrix,ne...Microstructure,mechanical properties and phase transformation of a heat-resistant rare-earth(RE)Mg-16.1Gd-3.5Nd-0.38Zn-0.26Zr-0.15Y(wt.%)alloy were investigated.The as-cast alloy is composed of equiaxedα-Mg matrix,net-shaped Mg5RE and Zr-rich phases.According to aging hardening curves and tensile properties variation,the optimized condition of solution treatment at 520℃for 8 h and subsequent aging at 204℃for 12 h was selected.The continuous secondary Mg5RE phase predominantly formed at grain boundaries during solidification transforms to residual discontinuousβ-Mg5RE phase and fine cuboid REH2particles after heat treatment.The annealed alloy exhibits good comprehensive tensile property at 350℃,with ultimate tensile strength of 153 MPa and elongation to fracture of 6.9%.Segregation of RE elements and eventually RE-rich precipitation at grain boundaries are responsible for the high strength at elevated temperature.展开更多
The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron mi...The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron microscopy(SEM)and laboratory computed tomography(CT).Results showed that the newly developed AlSi9MnMoV alloy exhibited improved mechanical properties when compared to the AlSi10MnMg alloy.The AlSi9MnMoV alloy,which was designed with trace multicomponent additions,displays a notable grain refining effect in comparison to the AlSi10MnMg alloy.Refining elements Ti,Zr,V,Nb,B promote heterogeneous nucleation and reduce the grain size of primaryα-Al.At a lower slow shot speed,the large ESCs are easier to form and gather,developing into the dendrite net and net-shrinkage.With an increase in slow shot speed,the size and number of ESCs and porosities significantly reduce.In addition,the distribution of ESCs is more dispersed and the net-shrinkage disappears.The tensile property is greatly improved by adopting a higher slow shot speed.The ultimate tensile strength is enhanced from 260.31 MPa to 290.31 MPa(increased by 11.52%),and the elongation is enhanced from 3.72%to 6.34%(increased by 70.52%).展开更多
Heat-resistant alloys with excellent mechanical properties are widely used in various fields,and further improvement in their properties is essential to meet the requirements in new-generation advanced supercritical b...Heat-resistant alloys with excellent mechanical properties are widely used in various fields,and further improvement in their properties is essential to meet the requirements in new-generation advanced supercritical boilers,nuclear reactors,superheaters,and other new materials applications.To effectively enhance the comprehensive performance of heat-resistant alloys,second-phase particle strengthening has been widely studied,and in the face of different service envi-ronments of advanced heat-resistant steels,the selection of suitable second-phase particles is essential to maximize the performance of these alloys.To this end,three major types of reinforcing phases in heat-resistant alloys such as carbides,rare earth oxides,and intermetallic compounds are summarized.A comparative analysis of the precipitation behavior of the reinforcing phases with different types as well as the risks and means of controlling their use in service,is presented.Key parameters for the application of various types of second-phase particles in heat-resistant alloys are provided to support the design and preparation of new ultrahigh-performance heat-resistant alloys.展开更多
An Al-Si-P master alloy has been developed by an in-situ reaction and the electron probe microanalyzer (EPMA) results show that there are many pre-formed AlP particles contained in the master alloy. Silicon introduc...An Al-Si-P master alloy has been developed by an in-situ reaction and the electron probe microanalyzer (EPMA) results show that there are many pre-formed AlP particles contained in the master alloy. Silicon introduced into the system plays an important role in remarkably improving the distribution and content of AlP particles due to their similar crystal structure and lattice parameters. ZL109 alloys have shown fast modification response to the addition of 0.5% Al-15Si-3.5P master alloy at 720℃, with a mass of primary Si precipitating in size of about 15 μm. Also, coarse primary Si grains in AI-30Si alloy can be refined dramatically from 150 μm to 37 μm after the addition of 2.0% Al-15Si-3.5P master alloy at 850℃. The P recovery of the Al-15Si-3.5P master alloy is much higher than that of a Cu-8.5P master alloy due to the pre-formed AlP particles.展开更多
Being used more and more widely in engineering,AlSi alloys comprise about 80%of all kinds of aluminum alloys,which are the most widely utilized nonferrous alloys.Although most Al-Si alloys consist of multiple componen...Being used more and more widely in engineering,AlSi alloys comprise about 80%of all kinds of aluminum alloys,which are the most widely utilized nonferrous alloys.Although most Al-Si alloys consist of multiple components,the eutectics in the structure accounts for 50%-90%of the sum volume of such alloys.Therefore,understanding the modification mechanism and function rules of the AlSi eutectic solidification is the technical key in controlling the structures and properties of such casting alloys.The present paper chiefly reviews recent investigation developments and important conclusions along the lines of the functions of modification elements and their modification mechanism in the eutectic solidification of Al-Si alloys.展开更多
Large and segregated primary Si particles may drastically decrease the mechanical properties of Al-Si alloys. To solve this problem, a P-Cr complex modif ier was added into the alloy, and the effects of P-Cr complex m...Large and segregated primary Si particles may drastically decrease the mechanical properties of Al-Si alloys. To solve this problem, a P-Cr complex modif ier was added into the alloy, and the effects of P-Cr complex modification and solidification conditions on the microstructure of hypereutectic Al-Si alloys casting produced in wedge-shaped copper mould were studied. The thermal analysis technique was applied to calculate the cooling rate during solidification. The microstructures were observed by means of optical and scanning electron microscopies. Results showed that the primary Si segregates in the as-cast hypereutectic Al-Si alloys. The segregation of primary Si can be inhibited by adding a P+Cr complex modif ier and increasing the cooling rate during solidif ication. The ref inement of primary Si particles by P+Cr complex modif ication is due to the formation of CrS i2 and AlP particles which act as the heterogeneous nuclei for the primary Si phase. The segregation of Si was also inhibited through the adherence of heavier CrS i2 particles to the primary Si particles.展开更多
Most evaluations of modification level are done according to a specific scale based on an American Foundry Society (AFS) standard wall chart as qualitative analysis in Al-Si casting production currently. This method i...Most evaluations of modification level are done according to a specific scale based on an American Foundry Society (AFS) standard wall chart as qualitative analysis in Al-Si casting production currently. This method is quite dependent on human experience when making comparisons of the microstructure with the standard chart. And the structures depicted in the AFS chart do not always resemble those seen in actual Al-Si castings. Therefore, this qualitative analysis procedure is subjective and can introduce human-caused errors into comparative metallographic analyses. A quantization parameter of the modification level was introduced by setting up the relationship between mean area weighted shape factor of eutectic silicon phase and the modification level using image analysis technology. In order to evaluate the modification level, a new method called "intelligent evaluating of melt quality by pattern recognition of thermal analysis cooling curves" has also been introduced. The results show that silicon modification level can be precisely assessed by comparison of the cooling curve of the melt to be evaluated with the one most similar to it in a database.展开更多
The components of the equipment for processing the Al melts into the molded parts can be markedly corroded by the molten Al. In this study, a 4 μm CrN coating or CrN/TiN multilayer coating for providing the physical ...The components of the equipment for processing the Al melts into the molded parts can be markedly corroded by the molten Al. In this study, a 4 μm CrN coating or CrN/TiN multilayer coating for providing the physical and chemical barriers between the molten reactive Al and the steel substrate were deposited by Cathodic Arc Evaporation onto 10 mm-thick heat-resistant steel plates. The dipping tests were conducted in a 700℃ A356 melt for 1 to 21 h at intervals of 3 h. The damage of the coated steel was eva...展开更多
Microstructure and mechanical properties of hyper-eutectic Al-Si alloy fabricated by spray casting were in- vestigated and then these results were compared with those by squeeze cast.The spray-cast specimen was found ...Microstructure and mechanical properties of hyper-eutectic Al-Si alloy fabricated by spray casting were in- vestigated and then these results were compared with those by squeeze cast.The spray-cast specimen was found to have finer Si particles (~5μm) compared to the squeeze-cast specimen (10-25μm).The tensile strength and elongation of the spray-cast specimen are also higher than those of the squeeze cast one.It was considered that the increased mechanical properties of the spray-cast specimen were mainly due to finer size of the Si particles distributed in Al matrix.展开更多
The electrical resistivity and viscosity of liquid hypoeutectic Al 7%Si and hypereutectic Al 18%Si alloys, and the influences of trace strontium and phosphorus on them were investigated. The trace additions of the t...The electrical resistivity and viscosity of liquid hypoeutectic Al 7%Si and hypereutectic Al 18%Si alloys, and the influences of trace strontium and phosphorus on them were investigated. The trace additions of the two elements increase the electrical resistivity. At the precipitation temperatures of primary phase, the electrical resistivity exhibits a discontinuity for all experimental Al Si alloys. In the discontinuity the electrical resistivity, respectively, decreases and increases abruptly for Al 7%Si alloys and Al 18%Si alloys. Phosphorus and strontium both have some effects on the discontinuity temperature and the jump value of electrical resistivity of Al 18%Si alloys, but strontium hardly has effect on them in Al 7%Si alloys. The trace additions of strontium and phosphorus increase the viscosity of the experimental alloy.展开更多
This work aims to present a perspective for porosity formation in three different alloys:A356,A413 and A380.1 by taking into account the addition of Al-B grain refiners:AlTi5B1 and Al3B.The directional solidification ...This work aims to present a perspective for porosity formation in three different alloys:A356,A413 and A380.1 by taking into account the addition of Al-B grain refiners:AlTi5B1 and Al3B.The directional solidification method was used,and microstructural changes of the alloys and its correlation with porosity formation were investigated.Pore size,number of pores,average pore length and distribution of pores were statistically analyzed.Also,external shrinkage was examined,and the volume of external shrinkage was calculated.It was found that there was a relationship between external shrinkage and the size and number of pores.As the size and number of pores internally decrease,external shrinkage increases.Additionally,porosity is decreased in all the three Al-Si alloys when Al-B grain refiners are used.The distribution of pore diameters is low when AlTi5B1 is used.Grain refiners have a different effect on porosity formation of Al-Si alloys with regard to their solidification morphology.展开更多
Several concepts of the grain refinement mechanism of B on hypoeutectic Al-Si alloys have been adopted: the refining effect of B on the a-AI and eutectic Si with the different additions of Al-B master alloys made at ...Several concepts of the grain refinement mechanism of B on hypoeutectic Al-Si alloys have been adopted: the refining effect of B on the a-AI and eutectic Si with the different additions of Al-B master alloys made at 850℃ was investigated; and the Al-B master alloys formed under different temperature conditions have been studied to explore the morphologies of AIB2 particles; slowly cooled sample with addition of Al-B was made to explore the refinement mechanism. AI-B master alloy can refine not only a-AI, but eutectic Si. Theoretical analysis indicates that, although AIB2 does not take part directly in the nucleation process in pure Al in the presence of Si, it provides a substrate for precipitation of a small content of Si from which a-At will grow without any undercooling. When the temperature decreases to eutectic line, AIB2 subsequently nucleates eutectic Si; AIB2 particles appear in two different morphologies, namely, hexagonal platelet and tetradehedron morphology which depend on the processing temperature conditions.展开更多
To obtain the finer primary silicon crystals, the proprietary Al-P masteralloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process wasmade in the experiments. The SEM (Scanning E...To obtain the finer primary silicon crystals, the proprietary Al-P masteralloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process wasmade in the experiments. The SEM (Scanning Electron Microscope) and DSC (Differential ScanningCalorimeter) analysis indicate that the Al-P modifier has more advantages over Cu-P and Fe-Pmodifier in easily addition, no elemental alteration and less undercooling of primary silicon'ssolidification, which suggests the Al-P master alloy is an effective modifier of eutectic Al-Sialloys.展开更多
Electropulse modification (EPM) process, a new physical field method for improving the solidification structure of metals was introduced.Different from other research, EPM is only acting pulse current on melt under li...Electropulse modification (EPM) process, a new physical field method for improving the solidification structure of metals was introduced.Different from other research, EPM is only acting pulse current on melt under liquid state.The solidification structure of Al-Si alloys, A1-Cu alloys,cast iron and steel can be modified obviously with this method: the solidification structure of ZL101 alloy presented the Na and Sr modification and the mechanical properties were enhanced; a large number of primary silicon appeared in the microstructure of ZL109 alloy; the equiaxed grain zone was expanded and the grains were fined in Al-5.0wt% Cu alloy; the graphitization took place in solidification process of molten cast iron; the grain sizes of solidification structure of T8 steel were reduced significantly and the shape of steel pearlites also changed; the equiaxed grain zone increased to 88% from original untreated 19%, the equiaxed grains were fined and the intercrystalline crack was avoided in concasting billet by continuously treating liquid electrical sheet steel in tundish.Effects of rare earths on casting Al-Si alloys were also summarized.The method of modifying the solidification structure of rare earth Al-Si alloys with EPM in producing the alloys was proposed.展开更多
In the light of DSC, electronic microprobe and X-ray diffration analyses of the melt-spinning ribbons and the structures of liquid hypoeutectic Al-7%Si, euteclic Al-12.7%Si and hypereutectic A1-18%Si alloys have been ...In the light of DSC, electronic microprobe and X-ray diffration analyses of the melt-spinning ribbons and the structures of liquid hypoeutectic Al-7%Si, euteclic Al-12.7%Si and hypereutectic A1-18%Si alloys have been investigated. The results show that the Al-Si clusters in liquid hypoeutectic Al-Si alloy, the Si-Si clusters in liquid eutectic and hypereutectic Al-Si alloys exist at low temperatures, however, the size of clusters decreases gradurally with increasing temperature. This process in which inhomogeneous liquid turns into homogeneous one happens in a range of temperatures.展开更多
To obtain the finer primary silicon crystals, the proprietary Al-P master alloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process was made in the experiments. The SEM (Scanning...To obtain the finer primary silicon crystals, the proprietary Al-P master alloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process was made in the experiments. The SEM (Scanning Electron Microscope) and DSC (Differential Scanning Calorimeter) analysis indicate that the Al-P modifier has more advantages over Cu-P and Fe-P modifier in easily addition, no elemental alteration and less undercooling of primary silicon’s solidification, which suggests the Al-P master alloy is an effective modifier of eutectic Al-Si alloys.展开更多
An addition of Ti as alloying element to Al-Si binary alloy will reduce the undercooling-abili- ty on rapid solidification of the melt-spun ribbon.The microstructure will be encoarsened even at initiation of its solid...An addition of Ti as alloying element to Al-Si binary alloy will reduce the undercooling-abili- ty on rapid solidification of the melt-spun ribbon.The microstructure will be encoarsened even at initiation of its solidification,so as to aggravate the eellular segregation of Si in the alloy ribbon.展开更多
By inserting the single crystal silicon seeds into Sr modified Al-22wt-% Si alloy melts,the fact that nucleation and growth of Si-phase are affected by Sr addition has been confirmed.It is suggested that this effect i...By inserting the single crystal silicon seeds into Sr modified Al-22wt-% Si alloy melts,the fact that nucleation and growth of Si-phase are affected by Sr addition has been confirmed.It is suggested that this effect is caused by the adsorption of Sr on{111}_(si),and the modification of eutectic structure results from the variation of leading phase in the eutectic from Si to α-Al.展开更多
The influence of rare earth Y on the microstructure and mechanical properties of Al-Zr alloy produced by dynamic ECAE was studied by OLYMPUS-BX51M optical microscope(OM),S4800 energy disperse spectroscopy(EDS)and SANS...The influence of rare earth Y on the microstructure and mechanical properties of Al-Zr alloy produced by dynamic ECAE was studied by OLYMPUS-BX51M optical microscope(OM),S4800 energy disperse spectroscopy(EDS)and SANS CMT5105 electronic universal material testing machine,and the corresponding equivalent conductivity was also investigated by using QJ48 DC electric bridge.The results show that the tensile strength of Al-Zr conductor first increases and then decreases with the increase of the aging time and temperature,and the highest tensile value can be obtained under the aging temperature of 160°C for 4 h.The ductility and the resistivity of the Al-Zr alloy have inverse proportion to the aging time.The rare earth Y has significantly improved the electrical and mechanical properties of Al-0.3%Zr heat-resistant alloy.In this study,the tensile strength and the elongation of the Al-0.3%Zr-0.2%Y alloy,after aging treatment at 220°C for 14 h,are about 278.49 MPa and 6.7%,respectively,and the equivalent conductivity is about 59.6 IACS.Hence the synthetical properties of the Y-containing alloy are significantly improved compared with traditional Al-0.3%Zr alloy.展开更多
Aluminum high pressure die casting(HPDC)technology has evolved in the past decades,enabling stronger and larger one-piece casting with significant part consolidation.It also offers a higher design freedom for more mas...Aluminum high pressure die casting(HPDC)technology has evolved in the past decades,enabling stronger and larger one-piece casting with significant part consolidation.It also offers a higher design freedom for more mass-efficient thin-walled body structures.For body structures that require excellent ductility and fracture toughness to be joined with steel sheet via self-piercing riveting(for instance,shock towers and hinge pillars,etc.),a costly T7 heat treatment comprising a solution heat treatment at elevated temperatures(450℃-500℃)followed by an over-ageing heat treatment is needed to optimize microstructure for meeting product requirement.To enable cost-efficient mass production of HPDC body structures,it is important to eliminate the expensive T7 heat treatment without sacrificing mechanical properties.Optimizing die cast alloy chemistry is a potential solution to improve fracture toughness and ductility of the HPDC components.The present study intends to tailor the Mg and Cu additions for a new Al-Si-Cr type die casting alloy(registered as A379 with The Aluminum Association,USA)to achieve the desired tensile properties without using T7 heat treatment.It was found that Cu addition should be avoided,as it is not effective in enhancing strength while degrades tensile ductility.Mg addition is very effective in improving strength and has minor impact on tensile ductility.The investigated Al-Si-Cr alloy with a nominal composition of Al-8.5wt.%Si-0.3wt.%Cr-0.2wt.%Fe shows comparable tensile properties with the T7 treated AlSi10MnMg alloy which is currently used for manufacturing shock towers and hinge pillars.展开更多
基金support of the National Natural Science Foundation of China(Grant number 52071088)。
文摘Microstructure,mechanical properties and phase transformation of a heat-resistant rare-earth(RE)Mg-16.1Gd-3.5Nd-0.38Zn-0.26Zr-0.15Y(wt.%)alloy were investigated.The as-cast alloy is composed of equiaxedα-Mg matrix,net-shaped Mg5RE and Zr-rich phases.According to aging hardening curves and tensile properties variation,the optimized condition of solution treatment at 520℃for 8 h and subsequent aging at 204℃for 12 h was selected.The continuous secondary Mg5RE phase predominantly formed at grain boundaries during solidification transforms to residual discontinuousβ-Mg5RE phase and fine cuboid REH2particles after heat treatment.The annealed alloy exhibits good comprehensive tensile property at 350℃,with ultimate tensile strength of 153 MPa and elongation to fracture of 6.9%.Segregation of RE elements and eventually RE-rich precipitation at grain boundaries are responsible for the high strength at elevated temperature.
基金financially supported by the National Key Research and Development Program of China(2022YFB3404201)the Major Science and Technology Project of Changchun City,Jilin Province(Grant No.20210301024GX)。
文摘The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron microscopy(SEM)and laboratory computed tomography(CT).Results showed that the newly developed AlSi9MnMoV alloy exhibited improved mechanical properties when compared to the AlSi10MnMg alloy.The AlSi9MnMoV alloy,which was designed with trace multicomponent additions,displays a notable grain refining effect in comparison to the AlSi10MnMg alloy.Refining elements Ti,Zr,V,Nb,B promote heterogeneous nucleation and reduce the grain size of primaryα-Al.At a lower slow shot speed,the large ESCs are easier to form and gather,developing into the dendrite net and net-shrinkage.With an increase in slow shot speed,the size and number of ESCs and porosities significantly reduce.In addition,the distribution of ESCs is more dispersed and the net-shrinkage disappears.The tensile property is greatly improved by adopting a higher slow shot speed.The ultimate tensile strength is enhanced from 260.31 MPa to 290.31 MPa(increased by 11.52%),and the elongation is enhanced from 3.72%to 6.34%(increased by 70.52%).
基金The authors express their gratitude to the National Science Foundation for Young Scientists of China(51704021)Key Research and Development Projects of Shandong Province(2021CXGC010)+1 种基金Key Research and Development Projects of Sichuan Province(021YFG0114)Fundamental Research Funds for the Central Universities(FRF-IDRY-20-015,FRF-TP-20-004A3,FRF-TP-19-030A2,and FRF-TP-16-079A1)for their kind financial support.
文摘Heat-resistant alloys with excellent mechanical properties are widely used in various fields,and further improvement in their properties is essential to meet the requirements in new-generation advanced supercritical boilers,nuclear reactors,superheaters,and other new materials applications.To effectively enhance the comprehensive performance of heat-resistant alloys,second-phase particle strengthening has been widely studied,and in the face of different service envi-ronments of advanced heat-resistant steels,the selection of suitable second-phase particles is essential to maximize the performance of these alloys.To this end,three major types of reinforcing phases in heat-resistant alloys such as carbides,rare earth oxides,and intermetallic compounds are summarized.A comparative analysis of the precipitation behavior of the reinforcing phases with different types as well as the risks and means of controlling their use in service,is presented.Key parameters for the application of various types of second-phase particles in heat-resistant alloys are provided to support the design and preparation of new ultrahigh-performance heat-resistant alloys.
基金supported by the National Science Fund for Distinguished Young Scholars (No. 50625101)the Key Project of Science and Technology Research of the Ministry of Education of China (No. 106103)
文摘An Al-Si-P master alloy has been developed by an in-situ reaction and the electron probe microanalyzer (EPMA) results show that there are many pre-formed AlP particles contained in the master alloy. Silicon introduced into the system plays an important role in remarkably improving the distribution and content of AlP particles due to their similar crystal structure and lattice parameters. ZL109 alloys have shown fast modification response to the addition of 0.5% Al-15Si-3.5P master alloy at 720℃, with a mass of primary Si precipitating in size of about 15 μm. Also, coarse primary Si grains in AI-30Si alloy can be refined dramatically from 150 μm to 37 μm after the addition of 2.0% Al-15Si-3.5P master alloy at 850℃. The P recovery of the Al-15Si-3.5P master alloy is much higher than that of a Cu-8.5P master alloy due to the pre-formed AlP particles.
文摘Being used more and more widely in engineering,AlSi alloys comprise about 80%of all kinds of aluminum alloys,which are the most widely utilized nonferrous alloys.Although most Al-Si alloys consist of multiple components,the eutectics in the structure accounts for 50%-90%of the sum volume of such alloys.Therefore,understanding the modification mechanism and function rules of the AlSi eutectic solidification is the technical key in controlling the structures and properties of such casting alloys.The present paper chiefly reviews recent investigation developments and important conclusions along the lines of the functions of modification elements and their modification mechanism in the eutectic solidification of Al-Si alloys.
基金financially supported by the National Basic Research Program of China(Grant No.:2012CB723307-03)the Fundamental Research Funds for the Central Universities(Grant No.:N130409003)the National Natural Science Foundation of China(Grant No.:51204046)of China
文摘Large and segregated primary Si particles may drastically decrease the mechanical properties of Al-Si alloys. To solve this problem, a P-Cr complex modif ier was added into the alloy, and the effects of P-Cr complex modification and solidification conditions on the microstructure of hypereutectic Al-Si alloys casting produced in wedge-shaped copper mould were studied. The thermal analysis technique was applied to calculate the cooling rate during solidification. The microstructures were observed by means of optical and scanning electron microscopies. Results showed that the primary Si segregates in the as-cast hypereutectic Al-Si alloys. The segregation of primary Si can be inhibited by adding a P+Cr complex modif ier and increasing the cooling rate during solidif ication. The ref inement of primary Si particles by P+Cr complex modif ication is due to the formation of CrS i2 and AlP particles which act as the heterogeneous nuclei for the primary Si phase. The segregation of Si was also inhibited through the adherence of heavier CrS i2 particles to the primary Si particles.
基金The paper is support by Foundation Key Project of Yunnan:The Study on inoculated theory and reliability of low carbonductile iron, NO. 1999E0004Z
文摘Most evaluations of modification level are done according to a specific scale based on an American Foundry Society (AFS) standard wall chart as qualitative analysis in Al-Si casting production currently. This method is quite dependent on human experience when making comparisons of the microstructure with the standard chart. And the structures depicted in the AFS chart do not always resemble those seen in actual Al-Si castings. Therefore, this qualitative analysis procedure is subjective and can introduce human-caused errors into comparative metallographic analyses. A quantization parameter of the modification level was introduced by setting up the relationship between mean area weighted shape factor of eutectic silicon phase and the modification level using image analysis technology. In order to evaluate the modification level, a new method called "intelligent evaluating of melt quality by pattern recognition of thermal analysis cooling curves" has also been introduced. The results show that silicon modification level can be precisely assessed by comparison of the cooling curve of the melt to be evaluated with the one most similar to it in a database.
文摘The components of the equipment for processing the Al melts into the molded parts can be markedly corroded by the molten Al. In this study, a 4 μm CrN coating or CrN/TiN multilayer coating for providing the physical and chemical barriers between the molten reactive Al and the steel substrate were deposited by Cathodic Arc Evaporation onto 10 mm-thick heat-resistant steel plates. The dipping tests were conducted in a 700℃ A356 melt for 1 to 21 h at intervals of 3 h. The damage of the coated steel was eva...
文摘Microstructure and mechanical properties of hyper-eutectic Al-Si alloy fabricated by spray casting were in- vestigated and then these results were compared with those by squeeze cast.The spray-cast specimen was found to have finer Si particles (~5μm) compared to the squeeze-cast specimen (10-25μm).The tensile strength and elongation of the spray-cast specimen are also higher than those of the squeeze cast one.It was considered that the increased mechanical properties of the spray-cast specimen were mainly due to finer size of the Si particles distributed in Al matrix.
文摘The electrical resistivity and viscosity of liquid hypoeutectic Al 7%Si and hypereutectic Al 18%Si alloys, and the influences of trace strontium and phosphorus on them were investigated. The trace additions of the two elements increase the electrical resistivity. At the precipitation temperatures of primary phase, the electrical resistivity exhibits a discontinuity for all experimental Al Si alloys. In the discontinuity the electrical resistivity, respectively, decreases and increases abruptly for Al 7%Si alloys and Al 18%Si alloys. Phosphorus and strontium both have some effects on the discontinuity temperature and the jump value of electrical resistivity of Al 18%Si alloys, but strontium hardly has effect on them in Al 7%Si alloys. The trace additions of strontium and phosphorus increase the viscosity of the experimental alloy.
文摘This work aims to present a perspective for porosity formation in three different alloys:A356,A413 and A380.1 by taking into account the addition of Al-B grain refiners:AlTi5B1 and Al3B.The directional solidification method was used,and microstructural changes of the alloys and its correlation with porosity formation were investigated.Pore size,number of pores,average pore length and distribution of pores were statistically analyzed.Also,external shrinkage was examined,and the volume of external shrinkage was calculated.It was found that there was a relationship between external shrinkage and the size and number of pores.As the size and number of pores internally decrease,external shrinkage increases.Additionally,porosity is decreased in all the three Al-Si alloys when Al-B grain refiners are used.The distribution of pore diameters is low when AlTi5B1 is used.Grain refiners have a different effect on porosity formation of Al-Si alloys with regard to their solidification morphology.
基金Shandong Natural Foundation !(Grant No:Z99F01)the Natiotal Natals Science Foundation of China !(Grant NO.59671046).
文摘Several concepts of the grain refinement mechanism of B on hypoeutectic Al-Si alloys have been adopted: the refining effect of B on the a-AI and eutectic Si with the different additions of Al-B master alloys made at 850℃ was investigated; and the Al-B master alloys formed under different temperature conditions have been studied to explore the morphologies of AIB2 particles; slowly cooled sample with addition of Al-B was made to explore the refinement mechanism. AI-B master alloy can refine not only a-AI, but eutectic Si. Theoretical analysis indicates that, although AIB2 does not take part directly in the nucleation process in pure Al in the presence of Si, it provides a substrate for precipitation of a small content of Si from which a-At will grow without any undercooling. When the temperature decreases to eutectic line, AIB2 subsequently nucleates eutectic Si; AIB2 particles appear in two different morphologies, namely, hexagonal platelet and tetradehedron morphology which depend on the processing temperature conditions.
基金The work was financially supported by National Natural Science Foundation of China (No.50071028) Nature Science Foundation of Shandong Province of China (No.L2000F01).
文摘To obtain the finer primary silicon crystals, the proprietary Al-P masteralloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process wasmade in the experiments. The SEM (Scanning Electron Microscope) and DSC (Differential ScanningCalorimeter) analysis indicate that the Al-P modifier has more advantages over Cu-P and Fe-Pmodifier in easily addition, no elemental alteration and less undercooling of primary silicon'ssolidification, which suggests the Al-P master alloy is an effective modifier of eutectic Al-Sialloys.
基金Project supported by the National Natural Science Foundation of China (50344030)
文摘Electropulse modification (EPM) process, a new physical field method for improving the solidification structure of metals was introduced.Different from other research, EPM is only acting pulse current on melt under liquid state.The solidification structure of Al-Si alloys, A1-Cu alloys,cast iron and steel can be modified obviously with this method: the solidification structure of ZL101 alloy presented the Na and Sr modification and the mechanical properties were enhanced; a large number of primary silicon appeared in the microstructure of ZL109 alloy; the equiaxed grain zone was expanded and the grains were fined in Al-5.0wt% Cu alloy; the graphitization took place in solidification process of molten cast iron; the grain sizes of solidification structure of T8 steel were reduced significantly and the shape of steel pearlites also changed; the equiaxed grain zone increased to 88% from original untreated 19%, the equiaxed grains were fined and the intercrystalline crack was avoided in concasting billet by continuously treating liquid electrical sheet steel in tundish.Effects of rare earths on casting Al-Si alloys were also summarized.The method of modifying the solidification structure of rare earth Al-Si alloys with EPM in producing the alloys was proposed.
文摘In the light of DSC, electronic microprobe and X-ray diffration analyses of the melt-spinning ribbons and the structures of liquid hypoeutectic Al-7%Si, euteclic Al-12.7%Si and hypereutectic A1-18%Si alloys have been investigated. The results show that the Al-Si clusters in liquid hypoeutectic Al-Si alloy, the Si-Si clusters in liquid eutectic and hypereutectic Al-Si alloys exist at low temperatures, however, the size of clusters decreases gradurally with increasing temperature. This process in which inhomogeneous liquid turns into homogeneous one happens in a range of temperatures.
文摘To obtain the finer primary silicon crystals, the proprietary Al-P master alloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process was made in the experiments. The SEM (Scanning Electron Microscope) and DSC (Differential Scanning Calorimeter) analysis indicate that the Al-P modifier has more advantages over Cu-P and Fe-P modifier in easily addition, no elemental alteration and less undercooling of primary silicon’s solidification, which suggests the Al-P master alloy is an effective modifier of eutectic Al-Si alloys.
文摘An addition of Ti as alloying element to Al-Si binary alloy will reduce the undercooling-abili- ty on rapid solidification of the melt-spun ribbon.The microstructure will be encoarsened even at initiation of its solidification,so as to aggravate the eellular segregation of Si in the alloy ribbon.
文摘By inserting the single crystal silicon seeds into Sr modified Al-22wt-% Si alloy melts,the fact that nucleation and growth of Si-phase are affected by Sr addition has been confirmed.It is suggested that this effect is caused by the adsorption of Sr on{111}_(si),and the modification of eutectic structure results from the variation of leading phase in the eutectic from Si to α-Al.
基金Funded by the Science and Research Program of Chongqing Municipal Education Commission(No.KJZD-M201801401)Talent Start Fund of Yangtze Normal University(No.2018KYQD006)
文摘The influence of rare earth Y on the microstructure and mechanical properties of Al-Zr alloy produced by dynamic ECAE was studied by OLYMPUS-BX51M optical microscope(OM),S4800 energy disperse spectroscopy(EDS)and SANS CMT5105 electronic universal material testing machine,and the corresponding equivalent conductivity was also investigated by using QJ48 DC electric bridge.The results show that the tensile strength of Al-Zr conductor first increases and then decreases with the increase of the aging time and temperature,and the highest tensile value can be obtained under the aging temperature of 160°C for 4 h.The ductility and the resistivity of the Al-Zr alloy have inverse proportion to the aging time.The rare earth Y has significantly improved the electrical and mechanical properties of Al-0.3%Zr heat-resistant alloy.In this study,the tensile strength and the elongation of the Al-0.3%Zr-0.2%Y alloy,after aging treatment at 220°C for 14 h,are about 278.49 MPa and 6.7%,respectively,and the equivalent conductivity is about 59.6 IACS.Hence the synthetical properties of the Y-containing alloy are significantly improved compared with traditional Al-0.3%Zr alloy.
文摘Aluminum high pressure die casting(HPDC)technology has evolved in the past decades,enabling stronger and larger one-piece casting with significant part consolidation.It also offers a higher design freedom for more mass-efficient thin-walled body structures.For body structures that require excellent ductility and fracture toughness to be joined with steel sheet via self-piercing riveting(for instance,shock towers and hinge pillars,etc.),a costly T7 heat treatment comprising a solution heat treatment at elevated temperatures(450℃-500℃)followed by an over-ageing heat treatment is needed to optimize microstructure for meeting product requirement.To enable cost-efficient mass production of HPDC body structures,it is important to eliminate the expensive T7 heat treatment without sacrificing mechanical properties.Optimizing die cast alloy chemistry is a potential solution to improve fracture toughness and ductility of the HPDC components.The present study intends to tailor the Mg and Cu additions for a new Al-Si-Cr type die casting alloy(registered as A379 with The Aluminum Association,USA)to achieve the desired tensile properties without using T7 heat treatment.It was found that Cu addition should be avoided,as it is not effective in enhancing strength while degrades tensile ductility.Mg addition is very effective in improving strength and has minor impact on tensile ductility.The investigated Al-Si-Cr alloy with a nominal composition of Al-8.5wt.%Si-0.3wt.%Cr-0.2wt.%Fe shows comparable tensile properties with the T7 treated AlSi10MnMg alloy which is currently used for manufacturing shock towers and hinge pillars.