In this paper the heat withstanding mechanism of heat-resisting aluminum alloy conductor is discussed, the types and performance of the conductor and its application on transmission lines are analyzed and introduced, ...In this paper the heat withstanding mechanism of heat-resisting aluminum alloy conductor is discussed, the types and performance of the conductor and its application on transmission lines are analyzed and introduced, and suggestions on accelerating exploitation and application of the conductor are put forward.展开更多
The components of the equipment for processing the Al melts into the molded parts can be markedly corroded by the molten Al. In this study, a 4 μm CrN coating or CrN/TiN multilayer coating for providing the physical ...The components of the equipment for processing the Al melts into the molded parts can be markedly corroded by the molten Al. In this study, a 4 μm CrN coating or CrN/TiN multilayer coating for providing the physical and chemical barriers between the molten reactive Al and the steel substrate were deposited by Cathodic Arc Evaporation onto 10 mm-thick heat-resistant steel plates. The dipping tests were conducted in a 700℃ A356 melt for 1 to 21 h at intervals of 3 h. The damage of the coated steel was eva...展开更多
Edge-to-edge matching(E2EM)model was used to predict the potency of LaB_(6) as the heterogeneous nucleation substrate for primary Al_(13)Mn_(4)Si_(8) phase formed during the solidification of Al−Si−Cu−Mn heat-resistan...Edge-to-edge matching(E2EM)model was used to predict the potency of LaB_(6) as the heterogeneous nucleation substrate for primary Al_(13)Mn_(4)Si_(8) phase formed during the solidification of Al−Si−Cu−Mn heat-resistant alloy.There are five pairs of orientation relationships(ORs)between LaB_(6) and Al_(13)Mn_(4)Si_(8) phases which meet the criteria of E2EM model.One pair of plane ORs((110)LaB_(6)//(110)Al_(13)Mn_(4)Si_(8))are demonstrated by TEM observation.This strongly indicates that the LaB_(6) phase can act as the heterogeneous nucleation substrate for the primary Al_(13)Mn_(4)Si_(8) phase.1.0 wt.%of Al−2La−1B master alloy was also added into Al−12Si−4Cu−2Mn alloy to evaluate the refining effect by microstructure observation and tensile test.Experimental results show that addition of Al−2La−1B master alloy can significantly refine the primary Al_(13)Mn_(4)Si_(8) phase,supporting the prediction accuracy of E2EM model.However,such refinement of primary Al_(13)Mn_(4)Si_(8) phase does not lead to an improvement in strength.This is due to the larger difference in elastic modulus between the finally formed Al_(13)Mn_(4)Si_(8) phase and aluminum matrix than that of Al_(15)Mn_(3)Si_(2) phase.展开更多
文摘In this paper the heat withstanding mechanism of heat-resisting aluminum alloy conductor is discussed, the types and performance of the conductor and its application on transmission lines are analyzed and introduced, and suggestions on accelerating exploitation and application of the conductor are put forward.
文摘The components of the equipment for processing the Al melts into the molded parts can be markedly corroded by the molten Al. In this study, a 4 μm CrN coating or CrN/TiN multilayer coating for providing the physical and chemical barriers between the molten reactive Al and the steel substrate were deposited by Cathodic Arc Evaporation onto 10 mm-thick heat-resistant steel plates. The dipping tests were conducted in a 700℃ A356 melt for 1 to 21 h at intervals of 3 h. The damage of the coated steel was eva...
基金supported by Jiangsu Key Laboratory Metallic Materials, China (No. BM2007204)the Fundamental Research Funds for the Central Universities, China (No. 2242016k40011)。
文摘Edge-to-edge matching(E2EM)model was used to predict the potency of LaB_(6) as the heterogeneous nucleation substrate for primary Al_(13)Mn_(4)Si_(8) phase formed during the solidification of Al−Si−Cu−Mn heat-resistant alloy.There are five pairs of orientation relationships(ORs)between LaB_(6) and Al_(13)Mn_(4)Si_(8) phases which meet the criteria of E2EM model.One pair of plane ORs((110)LaB_(6)//(110)Al_(13)Mn_(4)Si_(8))are demonstrated by TEM observation.This strongly indicates that the LaB_(6) phase can act as the heterogeneous nucleation substrate for the primary Al_(13)Mn_(4)Si_(8) phase.1.0 wt.%of Al−2La−1B master alloy was also added into Al−12Si−4Cu−2Mn alloy to evaluate the refining effect by microstructure observation and tensile test.Experimental results show that addition of Al−2La−1B master alloy can significantly refine the primary Al_(13)Mn_(4)Si_(8) phase,supporting the prediction accuracy of E2EM model.However,such refinement of primary Al_(13)Mn_(4)Si_(8) phase does not lead to an improvement in strength.This is due to the larger difference in elastic modulus between the finally formed Al_(13)Mn_(4)Si_(8) phase and aluminum matrix than that of Al_(15)Mn_(3)Si_(2) phase.