The new technology of continuous casting by heated mold was used to produce directional solidification ZA alloy lines to eliminate the inter defects of these lines and increase their mechanical properties. The results...The new technology of continuous casting by heated mold was used to produce directional solidification ZA alloy lines to eliminate the inter defects of these lines and increase their mechanical properties. The results are as follows: (1) The microstruc-ture of the ZA alloy lines is the parallel directional dendritic columnar crystal. Every dendritic crystal of eutectic alloy ZA5 was composed of many layer eutectic β and η phases. The micro structure of hypereutectic ZA alloys is primary dendritic crystal and interdendritic eutectic structure. The primary phase of ZA8 and ZA12 is β, among them, but the primary phase of ZA22 and ZA27 is a. (2) Through the test to the as-cast ZA alloy lines made in continuous casting by heated mold, it is found that the tensile strength and hardness increase greatly, but the elongation decreases. With the increase of aluminum amount from ZA 5 to ZA 12, ZA22 and ZA27, the tensile strength increases gradually. ZA27 has the best comprehensive mechanical properties in these four kinds of ZA alloys. (3) Heat treatment can decrease the dendritic segregation and improve the elongation of ZA alloy, but make their strength decrease slightly.展开更多
The metallurgical phenomena occurring in the continuous casting mold have a significant influence on the performance and the quality of steel product.The multiphase flow phenomena of molten steel,steel/slag interface ...The metallurgical phenomena occurring in the continuous casting mold have a significant influence on the performance and the quality of steel product.The multiphase flow phenomena of molten steel,steel/slag interface and gas bubbles in the slab continuous casting mold were described by numerical simulation,and the effect of electromagnetic brake（EMBR） and argon gas blowing on the process were investigated.The relationship between wavy fluctuation height near meniscus and the level fluctuation index F,which reflects the situation of mold flux entrapment,was clarified.Moreover,based on a microsegregation model of solute elements in mushy zone with δ/γ transformation and a thermo-mechanical coupling finite element model of shell solidification,the thermal and mechanical behaviors of solidifying shell including the dynamic distribution laws of air gap and mold flux,temperature and stress of shell in slab continuous casting mold were described.展开更多
文摘The new technology of continuous casting by heated mold was used to produce directional solidification ZA alloy lines to eliminate the inter defects of these lines and increase their mechanical properties. The results are as follows: (1) The microstruc-ture of the ZA alloy lines is the parallel directional dendritic columnar crystal. Every dendritic crystal of eutectic alloy ZA5 was composed of many layer eutectic β and η phases. The micro structure of hypereutectic ZA alloys is primary dendritic crystal and interdendritic eutectic structure. The primary phase of ZA8 and ZA12 is β, among them, but the primary phase of ZA22 and ZA27 is a. (2) Through the test to the as-cast ZA alloy lines made in continuous casting by heated mold, it is found that the tensile strength and hardness increase greatly, but the elongation decreases. With the increase of aluminum amount from ZA 5 to ZA 12, ZA22 and ZA27, the tensile strength increases gradually. ZA27 has the best comprehensive mechanical properties in these four kinds of ZA alloys. (3) Heat treatment can decrease the dendritic segregation and improve the elongation of ZA alloy, but make their strength decrease slightly.
基金Item Sponsored by National Outstanding Young Scientist Foundation of China(50925415)Fundamental Research Funds for Central Universities of China(N100102001)
文摘The metallurgical phenomena occurring in the continuous casting mold have a significant influence on the performance and the quality of steel product.The multiphase flow phenomena of molten steel,steel/slag interface and gas bubbles in the slab continuous casting mold were described by numerical simulation,and the effect of electromagnetic brake（EMBR） and argon gas blowing on the process were investigated.The relationship between wavy fluctuation height near meniscus and the level fluctuation index F,which reflects the situation of mold flux entrapment,was clarified.Moreover,based on a microsegregation model of solute elements in mushy zone with δ/γ transformation and a thermo-mechanical coupling finite element model of shell solidification,the thermal and mechanical behaviors of solidifying shell including the dynamic distribution laws of air gap and mold flux,temperature and stress of shell in slab continuous casting mold were described.