Development and performance evaluation of high temperature resistant strong adsorption rigid blocking agent

As drilling wells continue to move into deep ultra-deep layers,the requirements for temperature resistance of drilling fluid treatments are getting higher and higher.Among them,blocking agent,as one of the key treatment agents,has also become a hot spot of research.In this study,a high temperature resistant strong adsorption rigid blocking agent(QW-1)was prepared using KH570 modified silica,acrylamide(AM)and allyltrimethylammonium chloride(TMAAC).QW-1 has good thermal stability,average particle size of 1.46μm,water contact angle of 10.5.,has a strong hydrophilicity,can be well dispersed in water.The experimental results showed that when 2 wt%QW-1 was added to recipe A(4 wt%bentonite slurry+0.5 wt%DSP-1(filtration loss depressant)),the API filtration loss decreased from 7.8to 6.4 m L.After aging at 240.C,the API loss of filtration was reduced from 21 to 14 m L,which has certain performance of high temperature loss of filtration.At the same time,it is effective in sealing 80-100mesh and 100-120 mesh sand beds as well as 3 and 5μm ceramic sand discs.Under the same conditions,the blocking performance was superior to silica(5μm)and calcium carbonate(2.6μm).In addition,the mechanism of action of QW-1 was further investigated.The results show that QW-1 with amide and quaternary ammonium groups on the molecular chain can be adsorbed onto the surface of clay particles through hydrogen bonding and electrostatic interaction to form a dense blocking layer,thus preventing further intrusion of drilling fluid into the formation.

Preparation and performance evaluation of the slickwater using novel polymeric drag reducing agent with high temperature and shear resistance ability

Slickwater fracturing fluids are widely used in the development of unconventional oil and gas resources due to the advantages of low cost,low formation damage and high drag reduction performance.However,their performance is severely affected at high temperatures.Drag reducing agent is the key to determine the drag reducing performance of slickwater.In this work,in order to further improve the temperature resistance of slickwater,a temperature-resistant polymeric drag reducing agent(PDRA)was synthesized and used as the basis for preparing the temperature-resistant slickwater.The slickwater system was prepared with the compositions of 0.2 wt%PDRA,0.05 wt%drainage aid nonylphenol polyoxyethylene ether phosphate(NPEP)and 0.5 wt%anti-expansion agent polyepichlorohydrindimethylamine(PDM).The drag reduction ability,rheology properties,temperature and shear resistance ability,and core damage property of slickwater were systematically studied and evaluated.In contrast to on-site drag reducing agent(DRA)and HPAM,the temperature-resistant slickwater demonstrates enhanced drag reduction efficacy at 90℃,exhibiting superior temperature and shear resistance ability.Notably,the drag reduction retention rate for the slickwater achieved an impressive 90.52%after a 30-min shearing period.Additionally,the core damage is only 5.53%.We expect that this study can broaden the application of slickwater in high-temperature reservoirs and provide a theoretical basis for field applications.

Improving corrosion resistance of additively manufactured WE43 magnesium alloy by high temperature oxidation for biodegradable applications

Laser powder bed fusion(L-PBF)has been employed to additively manufacture WE43 magnesium(Mg)alloy biodegradable implants,but WE43 L-PBF samples exhibit excessively rapid corrosion.In this work,dense WE43 L-PBF samples were built with the relativity density reaching 99.9%.High temperature oxidation was performed on the L-PBF samples in circulating air via various heating temperatures and holding durations.The oxidation and diffusion at the elevated temperature generated a gradient structure composed of an oxide layer at the surface,a transition layer in the middle and the matrix.The oxide layer consisted of rare earth(RE)oxides,and became dense and thick with increasing the holding duration.The matrix was composed ofα-Mg,RE oxides and Mg_(24)RE_(5) precipitates.The precipitates almost disappeared in the transition layer.Enhanced passivation effect was observed in the samples treated by a suitable high temperature oxidation.The original L-PBF samples lost 40%weight after 3-day immersion in Hank’s solution,and broke into fragments after 7-day immersion.The casted and solution treated samples lost roughly half of the weight after 28-day immersion.The high temperature oxidation samples,which were heated at 525℃ for 8 h,kept the structural integrity,and lost only 6.88%weight after 28-day immersion.The substantially improved corrosion resistance was contributed to the gradient structure at the surface.On one hand,the outmost dense layer of RE oxides isolated the corrosive medium;on the other hand,the transition layer considerably inhibited the corrosion owing to the lack of precipitates.Overall,high temperature oxidation provides an efficient,economic and safe approach to inhibit the corrosion of WE43 L-PBF samples,and has promising prospects for future clinical applications.

The Application of High-density Resistivity Method to the Evaluation on the Stability of Gongchangling Open Pit＇s Slope

High-density resistivity method is a new, efficient electrical prospecting method, which can complete a two-dimensional （vertical and horizontal） prospecting process, possesses certain imaging functions for the geo-electric structure, and integrates electric profiling method with electric sounding method together. In this paper, the basic principle, data processing, and result explanation and inference of high- density resistivity method are introduced by taking the application of high-density resistivity method to the prospecting project in the slope of Gongchangling Open Pit, Liaoyang. The result of the prospecting result map analysis showed that the prospecting result was basically in line with the actual situation and proved the great significance of high-density resistivity method to the evaluation on the slope stability of Gongchangling open pit.

Nitrogen management improves lodging resistance and production in maize(Zea mays L.)at a high plant density

Lodging in maize leads to yield losses worldwide.In this study,we determined the effects of traditional and optimized nitrogen management strategies on culm morphological characteristics,culm mechanical strength,lignin content,root growth,lodging percentage and production in maize at a high plant density.We compared a traditional nitrogen(N)application rate of 300 kg ha–1(R)and an optimized N application rate of 225 kg ha^(–1)(O)under four N application modes:50%of N applied at sowing and 50%at the 10th-leaf stage(N1);100%of N applied at sowing(N2);40%of N applied at sowing,40%at the 10th-leaf stage and 20%at tasseling stage(N3);and 30%of N applied at sowing,30%at the 10th-leaf stage,20%at the tasseling stage,and 20%at the silking stage(N4).The optimized N rate(225 kg ha^(–1))significantly reduced internode lengths,plant height,ear height,center of gravity height and lodging percentage.The optimized N rate significantly increased internode diameters,filling degrees,culm mechanical strength,root growth and lignin content.The application of N in four split doses(N4)significantly improved culm morphological characteristics,culm mechanical strength,lignin content,and root growth,while it reduced internode lengths,plant height,ear height,center of gravity height and lodging percentage.Internode diameters,filling degrees,culm mechanical strength,lignin content,number and diameter of brace roots,root volume,root dry weight,bleeding safe and grain yield were significantly negatively correlated with plant height,ear height,center of gravity height,internode lengths and lodging percentage.In conclusion,treatment ON4 significantly reduced the lodging percentage by improving the culm morphological characteristics,culm mechanical strength,lignin content,and root growth,so it improved the production of the maize crop at a high plant density.

Mapping coalmine goaf using transient electromagnetic method and high density resistivity method in Ordos City, China

The research about subsurface characteristics by using transient electromagnetic method（TEM） and high density resistivity method（HDRM） were already conducted in Ordos. The objective of this research is to detect coalmine goaf areas based on rock resistivity. The data processing using wavelet transform, three point smoothing, RES2 DINV and Maxwell processing software to obtain 2D resistivity structure. The results showed that the layers with maximum resistivity values（30e33 U m on Line 1, 30e31 U m on Line 2, 32e40 U m on Line3） are founded at station 1e7, and 14e20 on Line 1,13e18 on Line 2, and 8e13 and 16e20 on Line 3 which is predicted as goaf layer, and the minimum resistivity values（20e26 U m of TEM, 45e75 U m of HDRM） at the other layers. This resistivity difference was caused by the geology and characteristics of the study area which is located close by the cleugh with rich coal, so the goaf area distinguishable with aquifer layer and coal seam. The results were also significant accidents and serious destruction of ecological environment.

Testing with high density resistivity method in prevention and cure for mine water disaster and its applied effect

The detecting examples using the high density resistivity method, about the evaluation of containing water characteristic from the floor rock and the height of overburden failure, were given. It expresses that the high density resistivity method has good effect with strong maneuverability and continuous observing section during the prevention and cure for mine water disaster. At the same time, the article pointed out that the study of space data inversion and dynamic watching technology about the high density resistivity method must be enhanced in the future because of special condition of data collecting in mine.

Growth and physical characterization of high resistivityFe:β-Ga2O3 crystals

High quality 0.02 mol%,0.05 mol%,and 0.08 mol%Fe:β-Ga2O3 single crystals were grown by the floating zone method.The crystal structure,optical,electrical,and thermal properties were measured and discussed.Fe:β-Ga2O3 single crystals showed transmittance of higher than 80%in the near infrared region.With the increase of the Fe doping concentration,the optical bandgaps reduced and room temperature resistivity increased.The resistivity of 0.08 mol%Fe:β-Ga2O3 crystal reached to 3.63×1011Ω·cm.The high resistivity Fe:β-Ga2O3 single crystals could be applied as the substrate for the high-power field effect transistors(FETs).

High Water Resistance and Enhanced Mechanical Properties of Bio-Based Waterborne Polyurethane Enabled by in-situ Construction of Interpenetrating Polymer Network

In this study,acrylic acid was used as a neutralizer to prepare bio-based WPU with an interpenetrating polymer network structure by thermally induced free radical emulsion polymerization.The effects of the content of acrylic acid on the properties of the resulting waterborne polyurethane-poly(acrylic acid)(WPU-PAA)dispersion and the films were systematically investigated.The results showed that the cross-linking density of the interpenetrating network polymers was increased and the interlocking structure of the soft and hard phase dislocations in the molecular segments of the double networks was tailored with increasing the content of acrylic acid,leading to enhancement of the mechanical properties and water resistance of WPU-PAA films.Notably,with the increase in content of acrylic acid,the tensile strength,Young’s modulus,and toughness of the WPU-PAA-110 film increased by 3 times,and 8 times,and 2.4 times compared with WPU-PAA-80,respectively.The WPU-PAA-100 film showed the best water resistance,and the water absorption rate at 96 h was only 3.27%.This work provided a new design scheme for constructing bio-based WPU materials with excellent properties.

Wire arc additive manufacturing of a heat-resistant Al-Cu-Ag-Sc alloy:microstructures and high-temperature mechanical properties

With a high energy efficiency,low geometric limitation,and low cracking susceptivity to cracks,wire arc additive manufacturing(WAAM)has become an ideal substitute for casting in the manufacturing of load-bearing high strength aluminum components in aerospace industry.Recently,in scientific researches,the room temperature mechanical performance of additive manufactured high strength aluminum alloys has been continuously broken through,and proves these alloys can achieve comparable or even higher properties than the forged counterpart.Since the aluminum components for aerospace usage experience high-low temperature cycling due to the absence of atmosphere protection,the high temperature performances of additive manufactured high strength aluminum alloys are also important.However,few research focuses on that.A special 2319Ag Sc with 0.4 wt.%Ag and 0.2 wt.%Sc addition designed for high temperature application is deposited successfully via cold metal transfer(CMT)based on WAAM.The microstructures and high temperature tensile properties are investigated.The results show that the as-deposited 2319Ag Sc alloy presents an alternate distribution of columnar grains and equiaxed grains with no significant textures.Main second phases are Al_(2)Cu and Al3Sc,while co-growth of Al_(2)Cu and bulk Al_(3)Sc is found on the grain boundary.During manufacturing,nanoscale Al_(2)Cu can precipitate out from the matrix.Ag and Mg form nano-scaleΩphase on the Al_(2)Cu precipitates.At 260℃,average yield strengths in the horizontal direction and vertical direction are 87 MPa±2 MPa,87 MPa±4 MPa,while average ultimate tensile strengths are 140 MPa±7 MPa,141 MPa±11 MPa,and average elongations are 11.0%±2.5%,13.5%±3.0%.Anisotropy in different directions is weak.

Molecular Mechanism of Rice Necrotic Lesion for Optimized Yield and Disease Resistance

How to balance rice resistance and yield is an important issue in rice breeding.Plants with mutated necrotic lesion genes often have persistent broad-spectrum resistance,but this broad-spectrum resistance usually comes at the expense of yield.Currently,many necrotic lesion mutants in rice have been identified,and these genes are involved in disease resistance pathways.This review provides a detailed introduction to the characteristics,classification,and molecular mechanisms of necrotic lesion formation.Additionally,we review the molecular regulatory pathways of genes involved in rice disease resistance.Concurrently,we summarize the relationship between resistance and yield in rice using newly developed gene editing methods.We discuss a rational and precise breeding strategy to better utilize molecular design technology for breeding disease-resistant and high-yield rice varieties.

Wear property of high-resistivity carbon brushes made with and without MoS_2 in variable humidity

Four kinds of high-resistivity carbon brushes with MoS2 contents of 0%,2%,4%and 6%(mass fraction)were prepared, respectively.Wear tests of brushes were conducted on an alternate current(AC)motor.Scanning electron microscopy(SEM)and energy dispersive X-ray analysis(EDS)were used to analyze the worn surface of brushes,and a thermocouple was used to measure the bulk temperature of the brush.The results show that wear rate of brush made without MoS2 in 10%relative humidity(RH)is two times larger than that in 50%RH,whereas the wear rates change little for the brushes made with MoS2.The wear of brushes has much to do with the surface film.In low humidity,the surface film can not be formed for the former brush while a sulfur layer can be formed for the latter brushes,which can reduce sparks,frictional heat and wear rate,and play a role like the water film in high humidity.

Current progress of research on heat -resistant Mg alloys: A review

With the increasing attention received by lightweight metals,numerous essential fields have increased requirements for mag-nesium(Mg)alloys with good room-temperature and high-temperature mechanical properties.However,the high-temperature mechanic-al properties of commonly used commercial Mg alloys,such as AZ91D,deteriorate considerably with increasing temperatures.Over the past several decades,extensive efforts have been devoted to developing heat-resistant Mg alloys.These approaches either inhibit the gen-eration of thermally unstable phases or promote the formation of thermally stable precipitates/phases in matrices through solid solution or precipitation strengthening.In this review,numerous studies are systematically introduced and discussed.Different alloy systems,includ-ing those based on Mg–Al,Mg–Zn,and Mg–rare earth,are carefully classified and compared to reveal their mechanical properties and strengthening mechanisms.The emphasis,limitations,and future prospects of these heat-resistant Mg alloys are also pointed out and dis-cussed to develop heat-resistant Mg alloys and broaden their potential application areas in the future.

Palmitoleic acid on top of HFD ameliorates insulin resistance independent of diacylglycerols and alters gut microbiota in C57BL/6J mice

With the prevalence of obesity and obesity-related metabolic syndrome,such as insulin resistance in recent years,it is urgent to explore effective interventions to prevent the progression of obesity-related metabolic syndrome.Palmitoleic acid is a monounsaturated fatty acid that is available from dietary sources,mainly derived from marine products.P almitoleic acid plays a positive role in maintaining glucose homeostasis and reducing inflammation.However,it is still unknow the mechanism of palmitoleic acid in ameliorating insulin resistance.Here,we investigated the effects of palmitoleic acid on chow diet(CD)-fed and high-fat diet(HFD)-fed mice,which were fed CD or HFD for 12 weeks before administration.We administrated mice with BSA(control),oleic acid,or palmitoleic acid for 6 weeks on top of CD or HFD feeding.We found that palmitoleic acid only improved glucose homeostasis in HFD-fed obese mice by increasing glucose clearance and reducing HOMA-IR.Further study explored that palmitoleic acid changed the composition of gut microbiota by decreasing Firmicutes population and increasing Bacteroidetes population.In colon,palmitoleic acid increased intestinal tight junction integrity and reduced inflammation.Moreover,palmitoleic acid decreased macrophage infiltration in liver and adipose tissue and increase glucose uptake in adipose tissue.Diacylglycerol(DAG)in tissue(for example,liver)is found to positively correlated with HOMA-IR.HFD enhanced the levels of DAGs in liver but not in adipose tissue in this study.Palmitoleic acid did not reverse the high DAG levels induced by HFD in liver.Therefore,in HFD-fed mice,palmitoleic acid reduced insulin resistance by an independent-manner of DAGs.It might be associated with the beneficial effects of palmitoleic acid on altering the gut microbiota composition,improving of intestinal barrier function,and downregulating the inflammation in colon,liver,and adipose tissue.

Properties of high cis-1,4 content hydroxyl-terminated polybutadiene and its application in composite solid propellants

In this paper,high cis-1,4 content hydroxyl-terminated polybutadiene(cis-HTPB)with different molecular weights was prepared through the oxidative cracking process using cis-butadiene rubber as raw material.Firstly,this article comprehensively compared the differences between cis-HTPB and conventional I-HTPB in terms of molecular weight distribution,functionality,viscosity,molecular polarity,and other physicochemical properties,which provided effective data support for its subsequent application.In addition,the reaction kinetics study showed that cis-HTPB with isocyanate curing agent has high reactivity,allowing it to be rapidly cured at low temperatures,and the cured elastomers had excellent mechanical properties,with tensile strength and elongation up to 1.89 MPa and 1100%,respectively.It was also found that cis-HTPB has extremely excellent low-temperature resistance,and the glass transition temperature(T_(g))of its cured elastomer is as low as-101℃.Based on the above studies,cis-HTPB is applied as a binder in composite solid propellants for the first time to investigate its practical performance,and the results indicated that cis-HTPB-based propellants have excellent process and mechanical properties.

A Provable Positivity-Preserving Local Discontinuous Galerkin Method for the Viscous and Resistive MHD Equations

In this paper,we construct a high-order discontinuous Galerkin(DG)method which can preserve the positivity of the density and the pressure for the viscous and resistive magnetohydrodynamics(VRMHD).To control the divergence error in the magnetic field,both the local divergence-free basis and the Godunov source term would be employed for the multi-dimensional VRMHD.Rigorous theoretical analyses are presented for one-dimensional and multi-dimensional DG schemes,respectively,showing that the scheme can maintain the positivity-preserving(PP)property under some CFL conditions when combined with the strong-stability-preserving time discretization.Then,general frameworks are established to construct the PP limiter for arbitrary order of accuracy DG schemes.Numerical tests demonstrate the effectiveness of the proposed schemes.

Effect of Zr Addition on Resistance to High Temperature Softening and Resistivity of 6082 Al-Mg-Si Alloys

The influence of zirconium on the resistance to high temperature softening of 6082 Al-Mg-Si alloys has been researched. The softening process of 6082 alloys with Zr and without Zr, isothermally conditioned at 250°C, has been investigated. The results show the inclusion of Zr inhibits the decrease of HB in hardness(HB) compared with the alloys without Zr. This is due to the Zr and Al forming coherent dispersoid-A!3Zr, and Al3Zr particles within an Al matrix, which effectively restricts grain boundary movement. A study is also carried out to investigate the changes in resistivity, which occurs during the ageing of alloys containing Zr, compared to those without Zr. It is found that in both cases there is an initial rapid rise in resistivity followed by a slower rise in resistivity as ageing proceeds. The value of resistivity is lower for 6082 alloys with Zr compared with 6082 alloys without Zr; this is explained in terms of the role of Zr in the 6082 alloys.

Ultrahigh frequency properties of discontinuous CoFeB/SiO_2 multilayer films with high resistivity

A series of multilayers of Co36Fe46B18/SiO2 were fabricated by DC/RF magnetron sputtering,and further post-annealed in vacuum magnetic field at 200℃ for 2 h. The results show that the microstructures and electromagnetic properties of Co36Fe46B18/SiO2 multilayer films can be altered by varying the thickness of CoFeB and the process of annealing. High permeability along with high magnetic loss in the GHz frequency range is achieved in the optimized discontinuous multilayer films. Both real and imaginary parts of the complex permeability are larger than 260 at 1.6 GHz for this film,and the resistivity is as high as 1.4 mΩ·cm. The discontinuous Co36Fe46B18/SiO2 multilayers are supposed to serve as the microwave absorbers and EMI shielding materials in GHz range.

Application of high density resistivity method in accuracy of goaf detection

Based on the relationship between the diameter and buried depth of goal, the authors establish the forward modeling by Res2dmod and inverse the model by Res2dinv. Thus, three kinds of models are obtained ： the model of single resistivity anomalous body, model of double different distance resistivity anomalous body, and model of layered resistivity anomalous body. Using forward and inversion, the image of detection is simulated, and the reliability is proved by comparing with the engineering examples.

Simulation of monolithic active pixel sensor with high resistivity epitaxial layer

The time and efficiency of charge collection are the key factors of monolithic active pixel sensor devices for minimum ionizing particles tracking detection.In this paper,3D models of pixels with different resistivity epitaxial layers(epi-layers) are built and simulated using Synopsys-Sentaurus.The basic characteristics of detectors are evaluated,including electric potential,electric field,and depleted region.Results indicate that the high resistivity (HR) epi-layer is a better choice.Further,simulation results show that the key collection performance is significantly improved owing to a wider and stronger electric field in the N type HR epi-layer.