Effects of Ti addition on the microstructures and mechanical properties of AICrFeNiMo0.5 Tix （x = 0, 0.25, 0.4, 0.5, 0.6, 0.75） high entropy alloys （HEAs） are investigated. All these HEAs of various Ti contents po...Effects of Ti addition on the microstructures and mechanical properties of AICrFeNiMo0.5 Tix （x = 0, 0.25, 0.4, 0.5, 0.6, 0.75） high entropy alloys （HEAs） are investigated. All these HEAs of various Ti contents possess dual BCC structures, indicating that Ti addition does not induce the formation of any new phase in these alloys. As Ti addition x varies from 0 to 0.75, the Vickers hardness （HV） of the alloy system increases from 623.7HV to 766.2HV, whereas the compressive yield stress firstly increases and then decreases with increasing x above 0.5. Meanwhile, the compressive ductility of the alloy system decreases with Ti addition. The AlCrFeNiMo0.5 Ti0.6 and AlCrFeNiMo0.5Ti0.75 HEAs become brittle and fracture with very limited plasticity. In the AlCrFeNiMo0.5Tix HEAs, the AlCrFeNiMoo.5 HEA possesses the highest compressive fracture strength of 4027 MPa and the largest compressive plastic strain of 27.9%, while the AlCrFeNiMo0.5 Ti0.5 HEA has the highest compressive yield strength of 2229 MPa and a compressive plastic strain of 10.1%. The combination of high strength and large plasticity of the AICrFeNiMoo.sTix （x = 0, 0.25, 0.4, 0.5） HEAs demonstrates that this alloy system is very promising for engineering applications.展开更多
The NiAl-28Cr-5.85Mo-0.15Hf alloy was prepared by high-pressure die casting (HPDC) and subsequent hot isostatic pressing(HIP), and tested for compressible strength and fracture behavior at 300-1 373 K. The results sho...The NiAl-28Cr-5.85Mo-0.15Hf alloy was prepared by high-pressure die casting (HPDC) and subsequent hot isostatic pressing(HIP), and tested for compressible strength and fracture behavior at 300-1 373 K. The results show that the elevated temperature 0.2% compressible yield strength as well as the room-temperature compressible fracture strain of as-HIP alloy are larger than those of the same alloy prepared by directional solidification (DS). It suggests that the fine structures with a homogeneous distribution of fine Cr (Mo) and Hf-rich phase created by high-pressure die casting lead to these improvements.展开更多
Thermal stability,crystallization behavior,Vickers hardness and magnetic properties of the Fe41Co7-xNixCr15Mo14C15B6Y2（x=0,1,3,5） bulk metallic glasses were investigated.The Fe41Co7-xNixCr15Mo14C15B6Y2（x=0,1,3,5） ...Thermal stability,crystallization behavior,Vickers hardness and magnetic properties of the Fe41Co7-xNixCr15Mo14C15B6Y2（x=0,1,3,5） bulk metallic glasses were investigated.The Fe41Co7-xNixCr15Mo14C15B6Y2（x=0,1,3,5） metallic glasses were fabricated by copper mold casting method.The thermal stability and crystallization behavior of the metallic glass rods were investigated by differential scanning calorimetry and isothermal experiments.Hardness measurements for samples annealed at different temperatures for different time were carried out at room temperature by the Vickers hardness tester,and magnetic measurements were performed at different temperatures by the vibrating sample magnetometer.It is shown that the addition of Ni does not play a positive role for enlarging ΔTx and GFA from parameter γ（=Tx/（Tg＋Tl））,and it can,however,increase the activation energy in the initial stage of crystallization by changing the initial crystallization behavior.The minor addition of Ni can refine the crystal grain obtained from the full crystallization experiment.The primary crystallization causes the decrease of hardness in these alloys,and as the crystallization continues,the hardness in all samples increases instead due to the precipitation of carbide and boride.The annealing temperature has an obvious effect on magnetic properties of these alloys,and the minor addition of Ni can effectively prevent the alloy annealed at high temperature to transform from paramagnetic to ferromagnetic state.展开更多
The viscoplastic friction and nanostructure formation mechanism of laser-clad Co-based coating were studied by rotary friction between laser-clad Co-Cr-Ni-Mo coating and WC-Co rod.The friction coefficient,friction int...The viscoplastic friction and nanostructure formation mechanism of laser-clad Co-based coating were studied by rotary friction between laser-clad Co-Cr-Ni-Mo coating and WC-Co rod.The friction coefficient,friction interface temperature and axial displacement—time curves during rotary friction process were measured.The results showed that all the curves firstly experienced rising stage and then steady stage.The rising stage corresponded to sliding friction while the steady stage corresponded to viscoplastic friction.After viscoplastic friction processing,three typical zones of viscoplastic deformation zone,thermo-mechanically affected zone,and original laser-clad zone can be observed successively from the friction surface to the interior.The viscoplastic deformation significantly crushed the network M23C7 phase in original laser-clad zone and made it dispersively distributed with equiaxial shape and in nano-scale.The viscoplastic zone,in width of 37-131 μm,is mainly characterized by refined M23C7 and α-Co phase with grain size bellow 50 nm,and even a small quantity of amorphous.Thus,the hardness of viscoplastic zone about HV997 was improved compared with the hardness of original laser-clad zone about HV600.展开更多
基金Supported by the National Natural Science Foundation of China under Grant No 51571127
文摘Effects of Ti addition on the microstructures and mechanical properties of AICrFeNiMo0.5 Tix （x = 0, 0.25, 0.4, 0.5, 0.6, 0.75） high entropy alloys （HEAs） are investigated. All these HEAs of various Ti contents possess dual BCC structures, indicating that Ti addition does not induce the formation of any new phase in these alloys. As Ti addition x varies from 0 to 0.75, the Vickers hardness （HV） of the alloy system increases from 623.7HV to 766.2HV, whereas the compressive yield stress firstly increases and then decreases with increasing x above 0.5. Meanwhile, the compressive ductility of the alloy system decreases with Ti addition. The AlCrFeNiMo0.5 Ti0.6 and AlCrFeNiMo0.5Ti0.75 HEAs become brittle and fracture with very limited plasticity. In the AlCrFeNiMo0.5Tix HEAs, the AlCrFeNiMoo.5 HEA possesses the highest compressive fracture strength of 4027 MPa and the largest compressive plastic strain of 27.9%, while the AlCrFeNiMo0.5 Ti0.5 HEA has the highest compressive yield strength of 2229 MPa and a compressive plastic strain of 10.1%. The combination of high strength and large plasticity of the AICrFeNiMoo.sTix （x = 0, 0.25, 0.4, 0.5） HEAs demonstrates that this alloy system is very promising for engineering applications.
基金Project (05YB31) supported by the Scientific Research Initial Foundation for Doctor of Shenyang Institute of Aeronautical Engineering,China
文摘The NiAl-28Cr-5.85Mo-0.15Hf alloy was prepared by high-pressure die casting (HPDC) and subsequent hot isostatic pressing(HIP), and tested for compressible strength and fracture behavior at 300-1 373 K. The results show that the elevated temperature 0.2% compressible yield strength as well as the room-temperature compressible fracture strain of as-HIP alloy are larger than those of the same alloy prepared by directional solidification (DS). It suggests that the fine structures with a homogeneous distribution of fine Cr (Mo) and Hf-rich phase created by high-pressure die casting lead to these improvements.
基金Project(2012CB825700) supported by the National Basic Research Program of China
文摘Thermal stability,crystallization behavior,Vickers hardness and magnetic properties of the Fe41Co7-xNixCr15Mo14C15B6Y2（x=0,1,3,5） bulk metallic glasses were investigated.The Fe41Co7-xNixCr15Mo14C15B6Y2（x=0,1,3,5） metallic glasses were fabricated by copper mold casting method.The thermal stability and crystallization behavior of the metallic glass rods were investigated by differential scanning calorimetry and isothermal experiments.Hardness measurements for samples annealed at different temperatures for different time were carried out at room temperature by the Vickers hardness tester,and magnetic measurements were performed at different temperatures by the vibrating sample magnetometer.It is shown that the addition of Ni does not play a positive role for enlarging ΔTx and GFA from parameter γ（=Tx/（Tg＋Tl））,and it can,however,increase the activation energy in the initial stage of crystallization by changing the initial crystallization behavior.The minor addition of Ni can refine the crystal grain obtained from the full crystallization experiment.The primary crystallization causes the decrease of hardness in these alloys,and as the crystallization continues,the hardness in all samples increases instead due to the precipitation of carbide and boride.The annealing temperature has an obvious effect on magnetic properties of these alloys,and the minor addition of Ni can effectively prevent the alloy annealed at high temperature to transform from paramagnetic to ferromagnetic state.
基金Project(51101126) supported by the National Natural Science Foundation of ChinaProjects(20110491684,2012T50817) supported by the China Postdoctoral Science FoundationProject(20110942K) supported by the Open Fund of State Key Laboratory of Powder Metallurgy,China
文摘The viscoplastic friction and nanostructure formation mechanism of laser-clad Co-based coating were studied by rotary friction between laser-clad Co-Cr-Ni-Mo coating and WC-Co rod.The friction coefficient,friction interface temperature and axial displacement—time curves during rotary friction process were measured.The results showed that all the curves firstly experienced rising stage and then steady stage.The rising stage corresponded to sliding friction while the steady stage corresponded to viscoplastic friction.After viscoplastic friction processing,three typical zones of viscoplastic deformation zone,thermo-mechanically affected zone,and original laser-clad zone can be observed successively from the friction surface to the interior.The viscoplastic deformation significantly crushed the network M23C7 phase in original laser-clad zone and made it dispersively distributed with equiaxial shape and in nano-scale.The viscoplastic zone,in width of 37-131 μm,is mainly characterized by refined M23C7 and α-Co phase with grain size bellow 50 nm,and even a small quantity of amorphous.Thus,the hardness of viscoplastic zone about HV997 was improved compared with the hardness of original laser-clad zone about HV600.