Anti-cracking Property of EVA-modified Polypropylene Fiber-reinforced Concrete Under Thermal-cooling Cycling Curing

In order to investigate the synergistic effect of re-dispersible powder-ethylene-vinyl acetate copolymer(EVA) and polypropylene fiber on the crack resistance of concrete under thermal fatigue loading, the compressive strength, ultimate tensile strength, ultimate tensile strain and tensile modulus of elasticity were tested. In addition, ultrasonic method and scanning electron microscope analysis were used to explain the microstructure mechanism. The results show that polypropylene fiberreinforced concrete presents a better performance on crack resistance than ordinary concrete, and the synergism of EVA and polypropylene fiber can improve the anti-cracking ability of concrete further.

STUDY ON OPTIMIZATION OF HIGH PERFORMANCE CONCRETE ADMIXTURES

Influences of admixtures on the workability and strength of high performance concrete （HPC） are in- vestigated. The types of investigated admixtures include naphthalene series high range water reducing agent, polycarboxlic series high range water reduce agent and sodium sulfate hardening accelerating agent. Two kinds of curing condition, namely steam curing condition and standard curing condition, are adopted. The result shows that HPC, added with polycarboxlic series of high performance water reducer, has high workability and strength, while sodium sulfate accelerating agent causes poor workability and low strength. Thus for vapor-cured HPC and its formulations, naphthalene series high range water reducing agent with less sodium sulfate should be given pri- ority. Therefore, the differences of curing conditions should be considered when selecting HPC admixtures.

Fatigue reliability quantitative analysis of cement concrete for highway pavement under high stress ratio

In order to obtain the change law of the fatigue reliability of cement concrete for highway pavement under high stress ratios, first, the probability densities of monotonic random variables including concrete fatigue life are deduced. And then, the fatigue damage probability densities of the Miner and Chaboche-Zhao models are deduced. By virtue of laboratory fatigue test results, the fatigue damage probability density functions of the two models can be obtained, considering different stress ratios. Finally, substituting load cycles into them, the change law of cement concrete fatigue reliability about load cycles can be acquired. The results show that under the same stress ratio, with the increase in the load cycle, the fatigue reliability declines from almost 100% to 0% gradually. No matter under what stress ratio, during the initial stage of the load action, there is always a relatively stable phase for fatigue reliability. With the increase in the stress ratio, the stable phase gradually shortens and the load cycle corresponding to the reliability of 0% also decreases. In the descent phase of reliability, the higher the stress ratio is, the lower the concrete reliability is for the same load cycle. Besides, compared with the Chaboche-Zhao fatigue damage model, the Miner fatigue damage model is safer.

Study on High Strength Concrete Confined by Continuous Carbon Fiber Sheet

Eight high strength concrete (HSC) prisms strengthened with continuous carbon fiber sheet(CFS)were tested.As a result of the confinement provided by CFS,the concrete would fail at a greater strain than the unconfined and then a significant increase in ductility can be achieved.The lateral pressure exerted by CFS would increase the compressive strength of the concrete,resulting in higher load bearing capacity.This paper proposes the stress strain curve of this kind of hybrid specimen,which agrees well with the test results.Based on the stress strain relationship and the assumptions proposed in this paper,a computer program was developed to analyze HSC columns,confined by CFS,which were subjected to axial compression and biaxial bending.The results shown in this paper indicate that the ductility of HSC column is significantly improved and the strength is also increased by some degree.

INFLUENCE OF AIRCRAFT DEICER ON FREEZE-THAW DURABILITY OF HIGH PERFORMANCE CONCRETE

The influence of glycol,the main composition of the most frequently used aircraft dicer,on the freeze-thaw durability of high performance concrete（HPC）is investigated.Freeze-thaw durability of HPC is tested by accelerated freeze-thaw test.Four kinds of the solution,i.e.,tap water,3.5% NaCl solution,glycol solutions,and a LBR-A type commercial aircraft deicer are employed.Results show that freeze-thaw durability of HPC exposed to glycol solutions is closely related to the solution concentrations.The failure of HPC exposed to 3.5% glycol solution is similar to that of those exposed to 3.5% NaCl solution,i.e.,serious surface scaling.While the damage of HPC exposed to 12.5%—25% glycol solutions is postponed.Compared with glycol solution,the commercial aircraft deicer has much more negative effects on HPC freeze-thaw durability compared with 3.5% NaCl solution.In the presence of commercial aircraft deicer for HPC subjected to freeze-thaw cycles,the deterioration is mainly due to scaling and spalling.

RESEARCH ON T SHAPED HIGH STRENGTH CONCRETE MEMBERS SUBJECTED TO AXIAL COMPRESSION AND BIAXIAL BENDING

Based on experiments, a computer program is developed. The calculated results agree well with the experimental results. The flexural behavior of T shaped high strength concrete members subjected to axial compression and biaxial bending is studied. The main factors affecting the flexural behavior of T shaped high strength concrete members are loading angle, axial compression ratio and reinforcement ratio.

The Frost-resisting Durability of High Strength Self-Compacting Pervious Concrete in Deicing Salt Environment

A high strength self-compacting pervious concrete(SCPC) with top-bottom interconnected pores was prepared in this paper. The frost-resisting durability of such SCPC in different deicing salt concentrations(0%, 3%, 5%, 10%, and 20%) was investigated. The mass-loss rate, relative dynamic modulus of elasticity, compressive strength, flexural strength and hydraulic conductivity of SCPC after 300 freeze-thaw cycles were measured to evaluate the frost-resisting durability. In addition, the microstructures of SCPC near the top-bottom interconnected pores after 300 freeze-thaw cycles were observed by SEM. The results show that the high strength SCPC possesses much better frost-resisting durability than traditional pervious concrete(TPC) after 300 freeze-thaw cycles, which can be used in heavy loading roads. The most serious freeze-thaw damage emerges in the SCPC immersed in the 3% of Na Cl solution, while there is no obvious damage in 20% of Na Cl solution. Furthermore, it can be deduced that the high strength SCPC can be used for 100 years in a cold environment.

Influence of MB-value of Manufactured Sand on the Shrinkage and Cracking of High Strength Concrete

The relation between methylene blue （MB） value of MS and its limestone dust content and clay content was investigated. The effects of MB value ranging from 0.35 to 2.5 on the workability of fresh concrete and crack propagation characteristics at the age of 24 hours, and effects on the mechanical properties, dry shrinkage of the harden concrete were tested. The experimental results show that the MB value is not related with the limestone dust content of MS, but in direct proportion to clay content. With the increase of MB value, the concrete workability decreases, and the flexural strength and 7 d compressive strength reduce markedly, whearas the 28 d compressive strength is not affected. When the MB-value is less than or equal to 1.35, the change of the MB-value has a little influence on early plastic cracking and dry shrinkage property of concrete, but when the MB-value is more than 1.35, the tendency of plastic cracking and dry shrinkage is remarkable.

Study of damage to a high concrete dam subjected to underwater shock waves

To study the effect of a strong underwater shock wave on a concrete dam, this research aims to improve hammer impact methods in model tests. Six 1:200 scale models were designed and tested under distributed impact loads. A device was deployed for a direct measurement of the impact force at the upstream face of the dams. The model dam bases were anchored to prevent displacement. The experimental results indicate that the top part of the concrete dam is a weak zone, and the impact failure initiates with a fracture on the top of the dam. The peak value of impact stress increases when the second crack appears in the concrete dam from the upstream face to the downstream face. And, the level of the second crack in the dam body is lower as the peak value of impact stress increases. In this study, dynamic analysis was conducted by calculating the results to verify the effectiveness of a device to directly measure the impact force. This method may be used to approximately forecast the damage of concrete dam and may also be useful in other engineering applications.

Effect of SAP on Properties of High Performance Concrete under Marine Wetting and Drying Cycles

The internal curing effect of superabsorbent polymer(SAP) on the properties of high performance concrete(HPC) under marine wetting and drying cycles(WD cycles) was investigated. Compressive strength, hydration and chloride migration were experimentally investigated and the results were evaluated by compasison with those under fresh water curing(FW). Water absorption and porosity were also evaluated only under WD cycles. The results showed the important influence of wetting and drying cycles on the properties of SAP modified HPC properties. Carefully designed, SAP minimized the long-term compressive strength of HPC under marine WD cycles. The hydration rate was faster in the initial curing, but became lower as compared with that cured in FW. In addition, SAP improved the long-term water absorption resistance and chloride migration resistance of HPC under marine WD cycles. The examination of the porosity showed a lower increase of the volume of capillary pores in SAP modified HPC under long term WD cycles compared with that without SAP. Therefore, internal curing by SAP could improve the durability properties of HPC under marine WD cycles.

Internal Curing Using Water-releasing Material for High Strength Micro-expansive Concrete

Due to its low water content, it is difficult for expansive agent to have an effective expansive effect on high strength concrete to compensate its extensive shrinkage and form a certain expansion. To solve this problem, water-releasing material with water storage and releasing characteristics was incorporated into high strength micro-expansive concrete to provide internal curing, and expansive effect of expansive agent was improved. Migration of water from initially saturated water-releasing material to the surrounding hydrating cement paste was investigated. Based on a given efficient diffusion distance of water stored in water-releasing material, the mass and real water-cement ratio of cured cement paste were estimated. At the same time, the effect of internal curing of water-releasing material on the volume deformation of high strength micro-expansive concrete was investigated.

Combined effect of steel fibres and steel rebars on impact resistance of high performance concrete

The impact properties of normal concrete (NC) and reinforced concrete (RC) specimens,steel fibre reinforced concrete (SFRC) specimens and RC+SFRC specimens with different steel fibre dosages were investigated with the drop-weight impact test recommended by ACI Committee 544.The results indicate that the number of blows to final failure is greatly increased by addition of steel fibres.Moreover,the combination of steel fibres and steel rebars demonstrates a significant positive composite effect on the impact resistance,which results in the improvement in impact toughness of concrete specimens.In the view of variation of impact test results,the two-parameter Weibull distribution was adopted to analyze the experimental data.It is proved that the probabilistic distributions of the blows to first crack and to final failure of six types of samples approximately follow two-parameter Weibull distribution.

Carbonation Resistance of Sulphoaluminate Cement-based High Performance Concrete

The influences of water/cement ratio and admixtures on carbonation resistance of sulphoaluminate cement-based high performance concrete （HPC） were investigated. The experimental results show that with the decreasing water/cement ratio, the carbonation depth of sulphoaluminate cement-based HPC is decreased remarkably, and the carbonation resistance capability is also improved with the adding admixtures. The morphologies and structure characteristics of sulphoaluminate cement hydration products before and after carbonation were analyzed using SEM and XRD. The analysis results reveal that the main hydration product of sulphoaluminate cement, that is ettringite （AFt）, decomposes after carbonation.

Pore Size Distribution of High Performance Metakaolin Concrete

The Compressive strength, porosity and pore size distribution of high performance metakaolin (MK) concrete were investigated. Concretes containing 0,5% , 10% and 20% metakaolin were prepared at a water / cementitious material ratio ( W/C) of 0. 30. In parallel, concrete mixtures with the replacement of cement by 20% fly ash or 5 and 10% silica fume were prepared for comparison. The specimens were cured in water at 27℃ for 3 to 90 days. The results show that at the early age of curing (3 days and 7 days), metakaolin replacements increase the compressive strength, but silica fume replacement slightly reduces the compressive strength. At the age of and after 28 days , the compressive strength of the concrete with metakaolin and silica fume replacement increases. A strong reduction in the total porosity and average pore diameter were observed in the concrete with MK 20% and 10% in the first 7 days.

Anti-Crack Performance of Low-Heat Portland Cement Concrete

The properties of low-heat Portland cement concrete（LHC） were studied in detail. The experimental results show that the LHC concrete has characteristics of a higher physical mechanical behavior, deformation and durability. Compared with moderate-heat Portland cement（MHC）, the average hydration heat of LHC concrete is reduced by about 17.5%. Under same mixing proportion, the adiabatic temperature rise of LHC concrete was reduced by 2 ℃-3 ℃,and the limits tension of LHC concrete was increased by 10× 10^-6-15×10^-6 than that of MHC. Moreover, it is indicated that LHC concrete has a better anti-crack behavior than MHC concrete.

Dynamic and Seismic Property Experiments of High Damping Concrete and Its Frame Models

The loss tangent and storage modulus of cement mortar containing treated silica fume and styrene-acrylic are measured. Shaking table tests on three groups of 1/4 models of high damping concrete frames are conducted to compare the effects of reducing vibration. A relationship between the viscosity coefficient of high damping concrete and the damping coefficient of structure is established by analyzing dynamic parameters like damping ratio and frequency, and comparing responses of relative displacement and absolute acceleration. Surface treatment of silica fume and styrene-acrylic emulsion prior to incorporation in a cement mortar increases the loss tangent of the resulting composite by 40-400% as compared to the cement mortar without any admixtures, and the damping ratio of the reinforced concrete is raised by 7%-9%. In addition, a theoretical method of determining the viscosity coefficient of the material on the basis of shaking table test results is put forward.

Seismic performance of steel reinforced ultra high-strength concrete composite frame joints

To investigate the seismic performance of a composite frame comprised of steel reinforced ultra high-strength concrete （SRUHSC） columns and steel reinforced concrete （SRC） beams, six interior frame joint specimens were designed and tested under low cyclically lateral load. The effects of the axial load ratio and volumetric stirrup ratio were studied on the characteristics of the frame joint performance including crack pattern, failure mode, ductility, energy dissipation capacity, strength degradation and rigidity degradation. It was found that all joint specimens behaved in a ductile manner with flexural-shear failure in the joint core region while plastic hinges appeared at the beam ends. The ductility and energy absorption capacity of joints increased as the axial load ratio decreased and the volumetric stirIup ratio increased. The displacement ductility coefficient and equivalent damping coefficient of the joints fell between the corresponding coefficients of the steel reinforced concrete （SRC） frame joint and RC frame joint. The axial load ratio and volumetric stirrup ratio have less influence on the strength degradation and more influence on the stiffness degradation. The stiffness of the joint degrades more significantly for a low volumetric stirrup ratio and high axial load ratio. The characteristics obtained from the SRUHSC composite frame joint specimens with better seismic performance may be a useful reference in future engineering applications.

Behavior of concrete and concrete-filled circular steel tubular stub columns at constant high temperatures

Based on reanalyzing test results of uniaxial compressive behavior of concrete at constant high temperatures in China, with the compressive cube strength of concrete from 20 to 80 MPa, unified formulas for uniaxial compressive strength, elastic modulus, strain at peak uniaxial compression and mathematical expression for unaxial compressive stress-strain relations for the concrete at constant high temperatures were studied. Furthermore, the axial stress-axial strain relations between laterally confined concrete under axial compression and multiaxial stress-strain relations for steel at constant high temperatures were studied. Finally, based on continuum mechanics, the mechanics model for concentric cylinders of circular steel tube with concrete core of entire section loaded at constant high temperatures was established. Applying elasto-plastic analysis method, a FORTRAN program was developed, and the concrete-filled circular steel tubular （CFST） stub colunms at constant high temperatures were analyzed. The analysis results are in agreement with the experiment ones from references.

Residual Mechanical Properties and Explosive Spalling Behavior of Ultra-High-Strength Concrete Exposed to High Temperature

In order to explore the characteristics of ultra-high-strength concrete exposed to high temperature,residual mechanical properties and explosive spalling behavior of ultra-high-strength concrete( UHSC) and high strength concrete( HSC) exposed to high temperatures ranging from 20 ℃ to 800 ℃ were determined. The microstructure of the specimens after exposure to elevated temperature was analyzed by means of scanning electron microscope( SEM) and mercury intrusion porosimetry( MIP). The residual compressive strengths of UHSC and HSC were first increased and then decreased as temperature increased. After exposure to 800 ℃,the compressive strengths of UHSC and HSC were 24. 2 % and 22. 3 % of their original strengths at 20 ℃,respectively. The residual splitting tensile strengths of both UHSC and HSC were consistently decreased with the temperature increasing and were approximately 20% of their original strengths after 800 ℃. However,the residual fracture energies of both concretes tended to ascend even at 600 ℃. The explosive spalling of UHSC was more serious than that of HSC. Moisture content of the specimens governs the explosive spalling of both concretes with a positive correlations,and it is more pronounced in UHSC. These results suggest that UHSC suffers a substantial loss in load-bearing capacity and is highly prone to explosive spalling due to high temperature. The changes in compressive strength are due to the changes in the density and the pore structure of concrete. The probability and severity of explosive spalling of UHSC are much higher than those of HSC due to the higher pore volume in HSC.

High Performance Concrete and Its Typical Mixes

With the modern development of chemical and mineral admixtures, it is now possible to produce much higher performance concrete than before. Higher performance does not only mean higher strength, but also better durability, lower risk of thermal cracking and higher dimensional stability etc. The three most effective admixtures for producing high performance concrete are superplastieizer, pulverized fuel ash and condensed silica fume. This paper outlines the properties of these materials and presents some practical guidelines for their usage.