Advanced manufacturing technologies of large martensitic stainless steel castings with ultra low carbon and high cleanliness

The key manufacturing technologies associated with composition, microstructure, mechanical properties, casting quality and key process control for large martensitic stainless steel castings are involved in this paper. The achievements fully satisfeid the technical requirements of the large 700 MW stainless steel hydraulic turbine runner for the Three Gorges Hydropower Station, and become the major technical support for the design and manufacture of the largest 700 MW hydraulic turbine generator unit in the world developed through our own efforts. The characteristics of a new high yield to tensile strength (R p0.2/R m ) ratio and high obdurability martensitic stainless steel with ultra low carbon and high cleanliness are also described. Over the next ten years, the large martensitic stainless steel castings and advanced manufacturing technologies will see a huge demand in clean energy industry such as nuclear power, hydraulic power at home and abroad. Therefore, the new high yield o tensile strength (R p0.2/R m ) ratio and high obdurability martensitic stainless steel materials, the fast and flexible manufacturing technologies of large size castings, and new environment friendly sustainable process will face new challenges and opportunities.

Layer Structure Analysis of Low-Carbon Steel Containing Rare Earth by High-Temperature Carburizing of Liquid Cast-Iron

The layer structure of low-carbon steel containing RE by high-temperature (T>1200 ℃) carburizing of liquid cast-iron was studied and the diffusion activation energy of carbon was calculated by metallographic microscpe, chemical analysis etc. The result shows that the technology of carburizing in liquid cast-iron can expedite caburization distinctly and changes the carburizing layer structure. The carburizing rate is 60～80 times of that of the traditional technology, and there is about 43% decrease in the activation energy compared with gas-carburization. In outer structure layer, cementite is formed simultaneously both on the crystal boundary reticularly and inside the crystal grains stripedly. In inner carburizing layer, there is undissolved blocky ferrite in reticular cementite. Besides, rare earth element can expedite carburization process.

Solidification Structure of Low Carbon Steel Strips with Different Phosphorus Contents Produced by Strip Casting

In the present paper, low carbon steel strips with different phosphorus contents were produced using a twin roll strip casting process. The solidification structure was studied and its features were analyzed in detail. It was found that the strips possessed a fine microstructure compared with the mould cast steels. With increasing phosphorus content more ferrite has been formed with finer grains.

Microstructure and mechanical properties of a new type of austempered boron alloyed high silicon cast steel

In the present paper, a new type of austempered boron alloyed high silicon cast steel has been developed, and its microstructures and mechanical properties at different temperatures were investigated. The experimental results indicate that the boron alloyed high silicon cast steel comprises a dendritic matrix and interdendritic eutectic borides in as-cast condition. The dendritic matrix is made up of pearlite, ferrite, and the interdendritic eutectic boride is with a chemical formula of M2B （M represents Fe, Cr, Mn or Mo） which is much like that of carbide in high chromium white cast iron. Pure ausferrite structure that consists of bainitic ferrite and retained austenite can be obtained in the matrix by austempering treatment to the cast steel. No carbides precipitate in the ausferrite structure and the morphology of borides remains almost unchanged after austempering treatments. Secondary boride particles precipitate during the course of austenitizing. The hardness and tensile strength of the austempered cast steel decrease with the increase of the austempering temperature, from 250℃ to 400 ℃. The impact toughness is 4-11 J.cm^-2 at room temperature and the impact fracture fractogragh indicates that the fracture is caused by the brittle fracture of the borides.

Effect of casting technology on microstructure and phases of high carbon high speed steel

The as-cast microstructures of high carbon high speed steels （HC-HSS） made by sand casting, centrifugal casting and electromagnetic centrifugal casting, respectively, were studied by using of optical microscopy （OM） and D/max2200pc X-ray diffraction. The results show that the microstructure of as-cast HC- HSS is dominated by alloy carbides （W2C, VC, Cr7C3）, martensite and austenite. The centrifugal casting and electromagnetic centrifugal casting apparently improve the solidification structure of HCoHSS. With the increase of magnetic intensity （B）, the volume fraction of austenite in the HC-HSS solidification structure increases significantly while the eutectic ledeburite decreases. Moreover, the secondary carbides precipitated from the austenite are finer with more homogeneous distribution in the electromagnetic centrifugal castings. It has also been found that the lath of eutectic carbide in ledeburite becomes finer and carbide phase spacing in eutectic ledeburite increases along with the higher magnetic field strength.

Spheroidization and Ostwald Growth of Carbide in Isothermal Process of Hot-Deformed High Carbon Chromium Cast Steel

In isothermal spheroidizing process,the spheroidization and growth of the carbide formed in hot-deformed high-carbon chromium cast steel at high temperature were investigated.The results showed that the spheroidizing growth of carbide proceeds in such a way that the bigger carbide particles swallow the smaller ones,and the short rhabdoid carbides dissolve and are spheroidized by itself.When the samples were held at 720℃ for more than 3 h,the spheroidization is not obvious.The feature of the process is the size increment and the amount decrement of carbide particles.The empirical equation for growth rate of carbides was obtained.The volume fraction of carbides keeps constant.The growth process agrees well with Ostwald Ripening Law.

Microstructure and Property of High Carbonic-Chromium Cast Steel with Different Hot Deformation Ratio

The microstructure and properties of high carbonic-chromium cast steel subjected to different hot deformation ratios were studied.The experimental results show that the microstructure and properties of high carbonic-chromium cast steel are obviously improved after hot deformation,and the best mechanical properties of the cast steel can be obtained under hot deformation ratio of 40 %-50 %,which leads to the morphology change of eutectic carbide and the precipitation of granular carbides.

Effect of High Pressure Heat Treatment on Microstructure and Compressive Properties of Low Carbon Steel

The effect of high pressure heat treatment on microstructure and compressive properties of low carbon steel were investigated by optical microscope,transmission electron microscope,hardness tester and compression test methods.The results show that martensite appears in low carbon steel at 1-5GPa GPa and 950°C for 15 minutes treatment,high pressure heat treatment can improve the hardness and compressive properties of the steel,the yield strength of the steel increases with increasing pressure,and its compressive properties are better than that treated under normal pressure quenching.

Effect of Boron on Delayed Fracture Resistance of Medium-Carbon High Strength Spring Steel

The delayed fracture behavior of medium carbon high strength spring steel containing different amounts of boron （0. 000 5%, 0. 001 6 %） was studied using sustained load delayed fracture test. The results show that delayed fracture resistance of boron containing steels is higher than that of conventional steel 60Si2MnA at the same strength level and it increases with the increase of boron eontent from 0. 000 5% to 0. 001 6%. The delayed fracture mode is mainly intergranular in the boron containing steels tempered at 350℃, which indicates that the addition of boron does not change the fracture character. However, the increase of boron content enlarges the size of the crack initia tion area. Further study of phase analysis indicates that most boron is in solid solution, and only a very small quantity of boron is in the M3 （C, B） phase.

Effect of Fast Cooling Rate on the Microstructure and Mechanical Properties of Low-Carbon High-Strength Steel Annealed in the Intercritical Region

The effect of fast cooling rate on the microstructure and mechanical properties of low-carbon high-strength steel annealed in the intercritical region was investigated using a Gleeble 1500 thermomechanical simulator and a continuous annealing thermomeehanical simulator. The results showed that the microstructure consisted of ferrite and bainite as the main phases with a small amount of retained austenite and martensite islands at cooling rate of 5 and 50 ℃/s, respectively. Fast cooling after continuous annealing affected all constituents of the microstructure. The mechanical properties were improved considerably. Ultimate tensile strength （U-TS） increased and total elongation （TEL） decreased with increasing cooling rate in all specimens. The specimen 1 at a cooling rate of 5 ℃/s exhibited the maximum TEL and UTSxTEL （20% and 27 200 MPa%, respectively） because of the competition between weakening by presence of the retained austenite plus the carbon indigence by carbide precipitation, and strengthening by martensitic islands and precipitation. The maximum UTS and YS （1 450 and 951 MPa, respectively） were obtained for specimen 2 at a cooling rate of 50 ℃/s. This is attributed to the effect of dispersion strengthening of finer martensite islands and the effect of precipitation strengthening of carbide precipitates.

The micro structure of high carbon low alloy steel for easy drawing

For better processing performance of high carbon low alloy steel wire rod,an investigation about the influence of cementite lamellar spacing on wire 'easy drawing' performance is completed.It is pointed out that too thin cementite lamellar spacing(<80 um) reduces the strain hardening level of wire drawing, and reduce the torsion performance of drawn wire at same time.For the wire or wire rod from industrial production,compared with the micro-structure with troostite,the micro-structure with sorbite or sorbite mixed with pearlite is more suitable to the drawing process with high reduction ratio.

Research on Welding Test of Grey Cast Iron and Low-Carbon Steel

Grey cast iron’s welding itself is a complex proble m.So proper welding materials must be selected,complex welding techniques such as preheating before weldingslow cooling after welding etc,should be taken. However the carbon component in low-carbon steel is comparatively low,the carbo n of welded joint will diffuse to the low-carbon steel when it is welded with gr ey cast iron,which will cause the component of carbon greatly increased at the low-carbon steel side in HAZ,high carbon martensite and cracks will occur.If p reheating before weldingslow cooling after welding and other welding procedure are taken,the grey cast iron side can probably be qualified.But the carbon wi ll diffuse to HAZ of the low-carbon steel side more easily.Therefore after stud ying the weldabilities of grey cast iron and low-carbon steel,the author develo ped a new type of cast iron electrode considering the demands of factories’prac tices,and the welding technology test of grey cast iron and low-carbon steel ar e carried out. In this paper,a new type of grey cast iron electrode is developed based on the practices in factories,its ingredients and properties are introduced.The w elding tests of grey cast iron and low-carbon steel are practiced.The joint str ucture of the dissimilar metal and the appearance of weld are observed.The hard ness distribution of the welded joint is tested.The results show that the elect rode can meet the welding requirements of the grey cast iron and low-carbon stee l.There are no cracksgas pores and other defects of metallurgy in welded join t,the appearance of welded joint are good.

Analysis of surface microcracks in low-carbon steel produced via twin-roll strip casting

In this study,morphological and microstructural analyses were conducted on net-shaped microcracks appearing on the surface of low-carbon steel manufactured via twin-roll strip casting. The fractograph and microscale distribution of elements in the cracked region were also analyzed. Results revealed that the cracked surfaces were characterized by slight pits,along with inclusions composed of manganese and silicon oxide distributed along both the sides of the cracks. Fractograph analysis revealed that the crack and smooth dendrite surfaces were oxidized. These phenomena indicate that microcracks on the cast strip surface form at the hightemperature stage of the solidification process during twin-roll casting and rolling. Microcracks were present in each region with pits in the cast strip and extended along the dendrite interface because of the combined effects of phasechange stress,thermal stress,mechanical stress,and fractional crystallization during the solidification process.

Study on Carburizing Kinetics of Low-carbon Steel at High-temperature and Short-term

In this paper, the carburizing kinetics of low-carbon steel at high-temperature and short-term in liquid cast-iron were studied by metallographic microscope, chemical analysis and so on, and the microstructure of carburized layer was also analyzed. The results show that the carburizing rate of low-carbon steel at high-temperature and short-term is so fast, and the microstructure of carburized layer possess higher carbon content, and cementite, pearlite and ferrite exist in carburized layer structure simultaneously. Besides, the kinetic equations of permeating layer forming have been presented, and the carburizing mechanism was preliminary discussed also.

Investigation of longitudinal surface cracks in a continuous casting slab of high-carbon steel

Based on a series of related investigations, a mechanism for the formation of longitudinal surface cracks on a continuous casting slab of high-carbon steel was investigated. High-temperature tensile tests performed on slab samples,metallographic and scanning electron microscopy studies, as well as heat flux and shell thickness in continuous casting predicted on the basis of a mathematical model were conducted. The results showed that high- carbon steel exhibited a much lower liquidus temperature and a wider brittle temperature range immediately after solidification compared with those of low-carbon steel. Concentrations of elements K and Na, which are contained in the mold fluxes, were not observed in the cracks during this study. The calculated results showed that the heat flux and the shell thickness were uneven along the mold width and that the shell was thinner and close to the center line of the slab surface. The longitudinal cracks were observed in situ using confocal laser scanning microscopy, to first occur close to the solidification front,where the ductility was extremely low;in addition ,the shell growth was slower than in other regions, which led to a thinner shell and depressed shrinkage owing to a lack of lubrication by the mold fluxes below the meniscus. Furthermore, the pouring temperature of high-carbon steel is - 100 ~C lower than that of low-carbon steel,so the formation of a stable liquid flux near the meniscus within a short time at the beginning of casting is difficult. The amounts of liquid slag film and crystalline slag film were insufficient to provide adequate lubrication between the shell and the mold, which resulted in greater friction force that induced or aggravated cracks. Therefore, the homogeneity of mold fluxes and initial solidification in the mold should be improved to reduce the concentration of slab surface defects.

Effect of electromagnetic stirring in mold on the macroscopic quality of high carbon steel billet

An industrial plant trial for optimizing the process parameters in a round billet continuous casting mold with electromagnetic stirring （M-EMS） was performed, in which the influences of stirring parameters with M-EMS on the solidification macrostructure of high carbon steel were investigated. The results show that the billet quality is not well controlled under the condition of working current and frequency with EMS, in which the subsurface crack of grade 1.0-2.0 ups to 38.09%, the central pipe of grade 1.0-1.5 reaches to 14.28%, and the central porosity of grade 1.5 is 14.29%. The parameters of current 260 A and frequency 8 Hz as the final optimum scheme has a remarkable effect for improving the macroscopic quality of billet, in which the subsurface crack, central pipe and skin blowhole are all disappeared, and the central porosity and carbon segregation are also well improved.

Influence of carbon content on microstructure and mechanical properties of Mn13Cr2 and Mn18Cr2 cast steels

In this paper, a comparison study was carried out to investigate the influence of carbon content on the microstructure, hardness, and impact toughness of water-quenched Mn13Cr2 and Mn18Cr2 cast steels. The study results indicate that both steels' water-quenched microstructures are composed of austenite and a small amount of carbide. The study also found that, when the carbon contents are the same, there is less carbide in Mn18Cr2 steel than in Mn13Cr2 steel. Therefore, the hardness of Mn18Cr2 steel is lower than that of Mn13Cr2 steel but the impact toughness of Mn18Cr2 steel is higher than that of Mn13Cr2 steel. With increasing the carbon content, the hardness increases and the impact toughness decreases in these two kinds of steels, and the impact toughness of Mn18Cr2 steel substantially exceeds that of Mn13Cr2 steel. Therefore, the water-quenched Mn18Cr2 steel with high carbon content could be applied to relatively high impact abrasive working conditions, while the as-cast Mn18Cr2 steel could be only used under working conditions of relatively low impact abrasive load due to lower impact toughness.

Latest Development and Application of High Strength and Heavy Gauge Pipeline Steel in China

Over the past twenty years, significant advances have been made in the field of microalloying and associated applications, among which one of the most successful application cases is HTP practice for heavy gauge, high strength pipeline steels. Combined the strengthening effects of TMCP and retardation effects of austenite recrystallization with increasing Nb in austenite region, HTP conception with low carbon and high niobium alloy design has been successfully applied to develop X80 coil with a thickness of 18.4 mm used for China＇s Second West-East pipeline. During this process, big efforts were made to further develop and enrich the application of microalloying technology, and at the same time the strengthening effects of Nb have been completely unfolded and fully utilized with improved metallurgical quality and quantitative analysis of microstructure. In this paper, the existing status and strengthening effect of Nb during reheating, rolling and cooling have been analyzed and characterized based on mass production samples and laboratory analysis. As confirmed, grain refinement remains the most basic strengthening measure to reduce the microstructure gradient along the thickness, which in turn enlarges the processing window to improve upon low temperature toughness, and finally make it possible to develop heavy gauge, high strength pipeline steels with more challenging fracture toughness requirements. As stated by a good saying that practice makes perfect. Based on application practice and theoretical analysis, HTP has been extended to develop heavy gauge and high strength pipeline steels with increasing requirements, including X80 SSAW pipe with a thickness of 22.0 mm and above, X80 LSAW pipe combining heavy gauge and large diameter, heavy gauge X80 LSAW pipe with low temperature requirements, as well as X90 steels. In this paper, alloy design, production processing, as well as mechanical properties and microstructure used for these products would be illustrated.