In isothermal spheroidizing process,the spheroidization and growth of the carbide formed in hot-deformed high-carbon chromium cast steel at high temperature were investigated.The results showed that the spheroidizing ...In isothermal spheroidizing process,the spheroidization and growth of the carbide formed in hot-deformed high-carbon chromium cast steel at high temperature were investigated.The results showed that the spheroidizing growth of carbide proceeds in such a way that the bigger carbide particles swallow the smaller ones,and the short rhabdoid carbides dissolve and are spheroidized by itself.When the samples were held at 720℃ for more than 3 h,the spheroidization is not obvious.The feature of the process is the size increment and the amount decrement of carbide particles.The empirical equation for growth rate of carbides was obtained.The volume fraction of carbides keeps constant.The growth process agrees well with Ostwald Ripening Law.展开更多
The microstructure and properties of high carbonic-chromium cast steel subjected to different hot deformation ratios were studied.The experimental results show that the microstructure and properties of high carbonic-c...The microstructure and properties of high carbonic-chromium cast steel subjected to different hot deformation ratios were studied.The experimental results show that the microstructure and properties of high carbonic-chromium cast steel are obviously improved after hot deformation,and the best mechanical properties of the cast steel can be obtained under hot deformation ratio of 40 %-50 %,which leads to the morphology change of eutectic carbide and the precipitation of granular carbides.展开更多
基金Item Sponsored by Guiding Programme of Science and Technology Research of Hebei of China(94122123)
文摘In isothermal spheroidizing process,the spheroidization and growth of the carbide formed in hot-deformed high-carbon chromium cast steel at high temperature were investigated.The results showed that the spheroidizing growth of carbide proceeds in such a way that the bigger carbide particles swallow the smaller ones,and the short rhabdoid carbides dissolve and are spheroidized by itself.When the samples were held at 720℃ for more than 3 h,the spheroidization is not obvious.The feature of the process is the size increment and the amount decrement of carbide particles.The empirical equation for growth rate of carbides was obtained.The volume fraction of carbides keeps constant.The growth process agrees well with Ostwald Ripening Law.
基金Item Sponsored by Guiding Program of Science and Technology Research of Hebei Province of China(94122123)
文摘The microstructure and properties of high carbonic-chromium cast steel subjected to different hot deformation ratios were studied.The experimental results show that the microstructure and properties of high carbonic-chromium cast steel are obviously improved after hot deformation,and the best mechanical properties of the cast steel can be obtained under hot deformation ratio of 40 %-50 %,which leads to the morphology change of eutectic carbide and the precipitation of granular carbides.