A pulsed Nd：YAG （yttrium aluminum garnet） laser-based technique was employed to clad low silicon steel with preplaced Si and Fe mixed powders for high Si content. The surface morphology, microstructural evolution, ...A pulsed Nd：YAG （yttrium aluminum garnet） laser-based technique was employed to clad low silicon steel with preplaced Si and Fe mixed powders for high Si content. The surface morphology, microstructural evolution, phase composition, and Si distribution, within the obtained cladding coatings, were characterized by optical microscopy （OM）, field emission scanning electron microscopy （FE-SEM）, with associated energy dispersive spectroscopy （EDS）, transmission electron microscopy （TEM）, and X-ray diffraction （XRD）. The microhardness was also measured along the depth direction of the specimens, A crack- and pore-free cladding coating through excellent metallurgical bonding with the substrate was successfully prepared on low silicon steel by means of optimized single-track and multi-track laser cladding. The phases of the coating are a-Fe, T-Fe, and FeSi. The high microhardness of the lasercladding zone is considered as an increase in Si content and as the refined microstructure produced by the laser treatment. The Si contents of the cladding coatings were about 5.8wt% in the single-track cladding and 6.5wt% in the multi-track cladding, respectively.展开更多
Mesoporous silicon oxynitrides MCM-41 were synthesized successfully. The resulting materials not only have high nitrogen contents and good structural characteristics of MCM-41 (high surface area, narrow pore size dist...Mesoporous silicon oxynitrides MCM-41 were synthesized successfully. The resulting materials not only have high nitrogen contents and good structural characteristics of MCM-41 (high surface area, narrow pore size distribution and good order), but also are amorphous. The composition and structure of the materials were investigated by CNH element analysis, XPS, Si MAS NMR, XRD, HRTEM and N-2 sorption, respectively. Mesoporous silicon oxynitrides MCM-41 with a high nitrogen content are still non-crystal (amorphous).展开更多
Ten studied steels including different carbon content, silicon content, and manganese content were deformed in compression over a temperature range of 600 ?C to 1 000 ?C at the strain rate of 1 s-1. The curves of the ...Ten studied steels including different carbon content, silicon content, and manganese content were deformed in compression over a temperature range of 600 ?C to 1 000 ?C at the strain rate of 1 s-1. The curves of the mean flow stressdeformation temperature were drawn up. The mean flow stresses of higher carbon content steels decreased continuously as the applied deformation temperature increased in the whole temperature range, while the mean flow stress of lowest carbon steel displayed an abrupt drop near the two phases region. The reason for the abrupt drop phenomena was explained as the result of phase transformation. The mean flow stresses of steels with high silicon content and low manganese content also have this phenomena.展开更多
基金the National Natural Science Foundation of China (No.50474084).
文摘A pulsed Nd：YAG （yttrium aluminum garnet） laser-based technique was employed to clad low silicon steel with preplaced Si and Fe mixed powders for high Si content. The surface morphology, microstructural evolution, phase composition, and Si distribution, within the obtained cladding coatings, were characterized by optical microscopy （OM）, field emission scanning electron microscopy （FE-SEM）, with associated energy dispersive spectroscopy （EDS）, transmission electron microscopy （TEM）, and X-ray diffraction （XRD）. The microhardness was also measured along the depth direction of the specimens, A crack- and pore-free cladding coating through excellent metallurgical bonding with the substrate was successfully prepared on low silicon steel by means of optimized single-track and multi-track laser cladding. The phases of the coating are a-Fe, T-Fe, and FeSi. The high microhardness of the lasercladding zone is considered as an increase in Si content and as the refined microstructure produced by the laser treatment. The Si contents of the cladding coatings were about 5.8wt% in the single-track cladding and 6.5wt% in the multi-track cladding, respectively.
文摘Mesoporous silicon oxynitrides MCM-41 were synthesized successfully. The resulting materials not only have high nitrogen contents and good structural characteristics of MCM-41 (high surface area, narrow pore size distribution and good order), but also are amorphous. The composition and structure of the materials were investigated by CNH element analysis, XPS, Si MAS NMR, XRD, HRTEM and N-2 sorption, respectively. Mesoporous silicon oxynitrides MCM-41 with a high nitrogen content are still non-crystal (amorphous).
基金Funded by Shanghai Pujiang Program(No.16PJ1430200)
文摘Ten studied steels including different carbon content, silicon content, and manganese content were deformed in compression over a temperature range of 600 ?C to 1 000 ?C at the strain rate of 1 s-1. The curves of the mean flow stressdeformation temperature were drawn up. The mean flow stresses of higher carbon content steels decreased continuously as the applied deformation temperature increased in the whole temperature range, while the mean flow stress of lowest carbon steel displayed an abrupt drop near the two phases region. The reason for the abrupt drop phenomena was explained as the result of phase transformation. The mean flow stresses of steels with high silicon content and low manganese content also have this phenomena.
