The dynamic mechanical analyzer(DMA)was applied to investigate the damping properties of Mg-Cu based alloys.The results show that the as-cast hypoeutectic Mg-Cu binary alloys exhibit ultra-high damping capacities,whil...The dynamic mechanical analyzer(DMA)was applied to investigate the damping properties of Mg-Cu based alloys.The results show that the as-cast hypoeutectic Mg-Cu binary alloys exhibit ultra-high damping capacities,while the eutectic Mg-Cu alloy exhibits low damping capacity.The strain amplitude dependent damping performance reveals that the dislocation damping mainly dominates in Mg-Cu alloys.Furthermore,the influence of eutectic phase on damping mechanisms of Mg-Cu binary alloys was discussed in detail and the effect of Si addition on the damping of Mg-1%Cu based alloy was also reported.Two damping peaks are observed on the temperature dependent spectrum of Mg-Cu based alloys.One is located at room temperature,which is dislocation related peak;and the other is located at moderate temperature,which is caused by the grain boundary sliding.展开更多
TiAlNb based intermetallic alloys,a potential competitor for next-generation super alloys,are susceptible to high-temperature embrittlement due to nucleation of a metastable single B2 phase in the fusion zone(FZ)durin...TiAlNb based intermetallic alloys,a potential competitor for next-generation super alloys,are susceptible to high-temperature embrittlement due to nucleation of a metastable single B2 phase in the fusion zone(FZ)during laser beam welding(LBW).In this study,a high entropy alloy(HEA),Ti-Hf-Zr-Cu-Ni,was self-developed and introduced as an interlayer into laser beam welded joint(LBWJ)of Ti-22 Al-27 Nb to analyze its impact on the evolution of microstructure in the weld zone(WZ)and subsequently on joint performance.Microstructural examination was carried out through electron probe micro analysis(EPMA),electron backscattered diffraction(EBSD)analysis,high-resolution scanning transmission electron microscopy(HRSTEM)comprising bright field(BF),selective area electron diffraction(SAED)and high angle annular dark-field(HAADF)imaging.Addition of the HEA into FZ of LBWJ triggered heterogenous nucleation during solidification,resultantly,fine-grained B2 with a greater proportion of high angle grain boundaries(HAGBs)was developed.FZ of Ti-22 Al-27 Nb LBWJ,prepared with an interlayer of HEA,was composed of planar,cellular,columnar and equiaxed dendritic grains;a solidification mode which was different from that observed in LBWJ prepared without adulteration of the HEA.The impact of heterogenous nucleation during epitaxial solidification on mechanical properties was established through micro vickers hardness mapping and tensile test,conducted at room temperature.The average hardness,343.5 HV,in the FZ of LBWJ prepared with an interlayer of HEA,was compatible with that of base material(BM),345 HV.The ultimate tensile strength(UTS),1062 MPa,and percentage elongation,11.2%,of the HEA tempered LBWJ were found in close approximation with that of BM,1060 MPa and 13.4%,respectively.A ductile mode of failure was observed during tensile test of the Ti-Hf-Zr-Cu-Ni supplemented LBWJ of Ti-22 Al-27 Nb,while quasi-cleavage mode of fracture was apparent in the joint of Ti-22 Al-27 Nb welded without addition of the HEA.展开更多
基金Project(50671083)supported by the National Natural Science Foundation of China
文摘The dynamic mechanical analyzer(DMA)was applied to investigate the damping properties of Mg-Cu based alloys.The results show that the as-cast hypoeutectic Mg-Cu binary alloys exhibit ultra-high damping capacities,while the eutectic Mg-Cu alloy exhibits low damping capacity.The strain amplitude dependent damping performance reveals that the dislocation damping mainly dominates in Mg-Cu alloys.Furthermore,the influence of eutectic phase on damping mechanisms of Mg-Cu binary alloys was discussed in detail and the effect of Si addition on the damping of Mg-1%Cu based alloy was also reported.Two damping peaks are observed on the temperature dependent spectrum of Mg-Cu based alloys.One is located at room temperature,which is dislocation related peak;and the other is located at moderate temperature,which is caused by the grain boundary sliding.
基金funded by the National Natural Science Foundations of China(Nos.52075449,51975480 and U1737205)the Aeronautical Science Foundation of China(No.20185470007)。
文摘TiAlNb based intermetallic alloys,a potential competitor for next-generation super alloys,are susceptible to high-temperature embrittlement due to nucleation of a metastable single B2 phase in the fusion zone(FZ)during laser beam welding(LBW).In this study,a high entropy alloy(HEA),Ti-Hf-Zr-Cu-Ni,was self-developed and introduced as an interlayer into laser beam welded joint(LBWJ)of Ti-22 Al-27 Nb to analyze its impact on the evolution of microstructure in the weld zone(WZ)and subsequently on joint performance.Microstructural examination was carried out through electron probe micro analysis(EPMA),electron backscattered diffraction(EBSD)analysis,high-resolution scanning transmission electron microscopy(HRSTEM)comprising bright field(BF),selective area electron diffraction(SAED)and high angle annular dark-field(HAADF)imaging.Addition of the HEA into FZ of LBWJ triggered heterogenous nucleation during solidification,resultantly,fine-grained B2 with a greater proportion of high angle grain boundaries(HAGBs)was developed.FZ of Ti-22 Al-27 Nb LBWJ,prepared with an interlayer of HEA,was composed of planar,cellular,columnar and equiaxed dendritic grains;a solidification mode which was different from that observed in LBWJ prepared without adulteration of the HEA.The impact of heterogenous nucleation during epitaxial solidification on mechanical properties was established through micro vickers hardness mapping and tensile test,conducted at room temperature.The average hardness,343.5 HV,in the FZ of LBWJ prepared with an interlayer of HEA,was compatible with that of base material(BM),345 HV.The ultimate tensile strength(UTS),1062 MPa,and percentage elongation,11.2%,of the HEA tempered LBWJ were found in close approximation with that of BM,1060 MPa and 13.4%,respectively.A ductile mode of failure was observed during tensile test of the Ti-Hf-Zr-Cu-Ni supplemented LBWJ of Ti-22 Al-27 Nb,while quasi-cleavage mode of fracture was apparent in the joint of Ti-22 Al-27 Nb welded without addition of the HEA.