Optimization of Extrusion Process Parameters of Recycled High-Density Polyethylene-Thermoplastic Starch Composite for Fused Filament Fabrication

High-density poly-ethylene (HDPE) is a nonbiodegradable recyclable plastic which is widely utilized in single use packaging applications. Consequently, it constitutes a significant amount of plastic waste found in landfills. From literature, it has been shown that parts produced using composites of HDPE with carbohydrate-based polymers, such as thermoplastic starch (TPS), experience mechanical degradation through hydrolytic degradation process. The possible utilization of recycled-HDPE (rHDPE) and TPS composite in nonconventional manufacturing processes such as Fused filament fabrication (FFF) has however not been explored. This study explores the potential application of rHDPE and TPS composites in FFF and optimizes the extrusion process parameters used in rHDPE-TPS filament production process. Taguchi method was utilized to analyze the extrusion process. The extrusion process parameters studied were the spooling speed, extrusion speed and the extrusion temperatures. The response variable studied was the filament diameter. In this research, the maximum TPS content achieved during filament production was 40 wt%. This filament was however challenging to use in FFF printers due to frequent nozzle clogging. Printing was therefore done with filaments that contained 0 - 30 wt% TPS. The experimental results showed that the most significant parameter in extrusion process was the spooling speed, followed by extrusion speed. Extrusion temperature had the least significant influence on the filament diameter. It was observed that increase in TPS content resulted in reduced warping and increased rate of hydrolytic degradation. Mechanical properties of printed parts were investigated and the results showed that increasing TPS content resulted in reduction in tensile strength, reduction in compression strength and increase in stiffness. The findings of this research provide valuable insights to plastic recycling industries and researchers regarding the utilization of recycled HDPE and TPS composites as substitute materials in FFF.

Mechanical, Thermal and Crystallization Properties of Polypropylene (PP) Reinforced Composites with High Density Polyethylene (HDPE) as Matrix

Our work aims to evaluate a complete outlook of virgin high density polyethylene (HDPE) and polypropylene (PP) polyblends. Virgin PP of 20, 30 and 50 weight% is compounded with virgin HDPE. The properties like tensile strength, flexural strength, Izod impact strength are examined. Scanning electron microscopy (SEM) and polarised light microscopy (PLM) are used to observe the surface and crystal morphology. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) tests verify the non compatibility of both polymers. Differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) techniques are used to study the thermal behaviour of composites. The results manifest co-occurring spherulites for polyblends;indicating the composite to be a physical blend of continuous and dispersed phases, but on the other hand PP improves the tensile and flexural properties of HDPE.

MAPPING THE DAMAGED ZONE AROUND THE CRACK TIP IN HIGH DENSITY POLYETHYLENE WITH SYNCHROTRON MICROFOCUS SMALL ANGLE X-RAY SCATTERING TECHNIQUE

The structural changes around a crack tip in a high density polyethylene were investigated by means of scanning synchrotron microfocus small-angle X-ray scattering technique. The scattering data confirm the process of craze structure development near a crack tip based on the evolution of voids. In addition, it was found that the main stress in the plastic zone near a crack tip exhibited a gradient distribution with respect to its strength and direction. The whole damaged area showed a strain distribution indicating a flow behavior toward the crack tip.

PREPARATION OF HIGH DENSITY POLYETHYLENE/POLYETHYLENE-BLOCK-POLY(ETHYLENE GLYCOL)COPOLYMER BLEND POROUS MEMBRANES VIA THERMALLY INDUCED PHASE SEPARATION PROCESS AND THEIR PROPERTIES

High density polyethylene （HDPE）/polyethylene-block-poly（ethylene glycol） （PE-b-PEG） blend porous membranes were prepared via thermally induced phase separation （TIPS） process using diphenyl ether （DPE） as diluent. The phase diagrams of HDPE/PE-b-PEG/DPE systems were determined by optical microscopy and differential scanning calorimetry （DSC）. By varying the content of PE-b-PEG, the effects of PE-b-PEG copolymer on morphology and crystalline structure of membranes were studied by scanning electron microscopy （SEM） and wide angle X-ray diffraction （WAXD）. The chemical compositions of whole membranes and surface layers were characterized by elementary analysis, Fourier transform infrared spectroscopy-attenuated total reflection （FTIR-ATR） and X-ray photoelectron spectroscopy （XPS）. Water contact angle, static protein adsorption and water flux experiments were used to evaluate the hydrophilicity, antifouling and water permeation properties of the membranes. It was found that the addition of PE-b-PEG increased the pore size of the obtained blend membranes. In the investigated range of PE-b-PEG content, the PEG blocks could not aggregate into obviously separated domains in membrane matrix. More importantly, PE-b-PEG could not only be retained stably in the membrane matrix during membrane formation, but also enrich at the membrane surface layer. Such stability and surface enrichment of PE-b-PEG endowed the blend membranes with improved hydrophilicity, protein absorption resistance and water permeation properties, which would be substantially beneficial to HDPE membranes for water treatment application.

Study on the Basic Mechanical Behaviors of High Density Polyethylene Electrofusion Welded Joints at Different Temperature

The basic mechanical behaviors of high density polyethylene electrofusion welded joint at different temperatures were studied by using differently designed specimens in this paper. The results show that the strength of weld bonding plane is higher than that of the pipe and socket materials at room temperature. In order to get the shear strength of electrofusion welded joint, the effective bond lengths were reduced by cutting artificial groove through the socket. The effective bonding length of welded joint to get the shear strength is decreased with decreasing testing temperature. The shear strength and the sensibility to sharp notch of HDPE material increased with decreasing temperature.

High density porous polyethylene material (Medpor) as an unwrapped orbital implant

Objective: To introduce the clinical effect among patients who received an unwrapped orbital implant with high density porous polyethylene material (Medpor) after enucleation or evisceration. Methods: Retrospective analysis of a series of 302 patients with anophthalmia who underwent placement of an unwrapped high density porous polyethylene orbital implant. We compared the patients (n=180) who accepted primary implant placement with those (n=122) who accepted secondary implant placement. Parameters evaluated included: age at time of surgery, date of surgery, sex, implant type and size, surgery type, the surgical procedure and technique performed, and complications. Results: The time of follow-up ranged from 2.0 to 58.0 months (mean 32.5 months). A total of 5 of 302 (1.66%) cases had documented postoperative complications. The following problems were noted after surgery: implant exposure, 3 patients (0.99%); implant removed due to orbital infection, 1 patient (0.34%); ptosis, 1 patient (0.34%). There were no significant complications observed in other 297 cases and all implants showed good orbital mo- tility. The clinical effect of primary implant placement is better than that of secondary placement. Conclusion: High density porous polyethylene material can be used successfully as an unwrapped orbital implant in anopthalmic socket surgery with minimal complications. The material is well tolerated, nonantigenic and has low rate of infection and migration.

EFFECT OF PAN-MILLING STRESS ON CRYSTAL STRUCTURES OF HIGH DENSITY POLYETHYLENE

A detailed study was performed on the crystal structures of pan-milled high-density polyethylene (HDPE) using differential scanning calorimetry (DSC) and X-ray diffraction. The crystallinity of HDPE first decreased slightly, followed by a gradual increase with increasing milling times. Monoclinic crystals appeared after 4 cycles of milling. With increasing times of milling, the proportion of monoclinic crystals increased significantly while the proportion of orthorhombic crystals decreased gradually. With increasing times of milling, the crystallite size of orthorhombic form decreased greatly, while the size of monoclinic crystallites kept almost constant during milling.

One step graft copolymerization of acrylic acid and sodium styrene sulfonate onto high-density polyethylene film by preirradiation method

High-density polyethylene (HDPE) films were irradiated by 60Co gamma ray with a dose of 100 kGy in air and then immersed in aqueous solution of acrylic acid (AA) and sodium styrene sulfonate (SSS) at different temperature. The effects of grafting conditions such as temperature, reaction time, Mohr’s salt concentration, and total concentration of monomer on grafting yield were studied. Both grafting yield of AA and SSS onto HDPE respectively increases with total concentration of monomers. The highest grafting yield was observed at 3 mol/L monomers where the grafted PE swelled to the largest extent in the monomers mixture. The grafting yield increases with reaction time and then levels off. At higher temperature, the grafting yield decreases with Mohr’s salt concentration, but increases at low temperature when Mohr’s salt concentration is 0.083%. Which can be interpreted that in the presence of Fe2+ diperoxides and hydroperoxides may decompose at low temperature to form radical which can initiate the grafting. The physical and chemical properties of grafting films were also investigated.

EFFECT OF PAN-MILLING ON RHEOLOGICAL PROPERTIES OF HIGH DENSITY POLYETHYLENE

The effect of pan-milling on the rheological properties of high density polyethylene (HDPE) was studied. An innovative milling apparatus, viz. an inlaid pan-mill, was used. Melt indexer, capillary rheometer, Haake Rheocord 90 single-screw extruder and Brabender rheometer were used to evaluate the rheological properties of HDPE. HDPE with higher initial molecular weight and larger particle size was easier to degrade under pan-milling stress, as indicated by the melt index. Pressure oscillation in capillary flow occurred at significantly higher shear stress and shear rate for milled HDPE than for unmilled HDPE. The apparent shear viscosity of HDPE decreased with increasing times of milling. After milling, the flow activation energy decreased and thus the sensitivity of viscosity to temperature was reduced. Die pressure and torque during single screw extrusion were reduced significantly after milling. Plasticizing time as measured in a Brabander mixer decreased markedly with increasing milling times.

Characterization and Comparison of Rheological Properties of Agro Fiber Filled High-Density Polyethylene Bio-Composites

The rheological behavior of composites made with high-density polyethylene (HDPE) and different agro fiber by-products such as corncob (CCF), Rice hull (RHF), Flax shives (FSF) and Walnut shell (WSF) flour of 60 - 100 mesh were studied. The experimental results were obtained from samples containing 65 vol.% agro fiber and 3 wt.% lubricant. Particle sizes distribution of the agro fibers was in the range of 0.295 mm to ?0.125 mm. SEM showed evidence of complete matrix/fiber impregnation or wetting. The melt rheological data in terms of complex viscosity (η*), storage modulus (G'), loss modulus (G"), and loss tangent (tanδ) were evaluated and compared for different samples. Due to higher probability of agglomeration formation in the samples containing 65 vol.% of agro fillers, the storage modulus, loss modulus and complex viscosity of these samples were high. The unique change in all the samples is due to the particle size distribution of the agro fibers. The storage and loss modulus increased with increasing shear rates for all the composites, except for Walnut shell composite which exhibited unusual decrease in storage modulus with increasing shear rate. Damping factor (tanδ) decreased with increasing shear rate for all the composites at 65 vol.% filler load although there were differences among the composites. Maximum torque tended to increase at the 65 vol.% agro fiber load for all composites. Corncob and Walnut shell composites gave higher torque and steady state torque values in comparison with Flax shives and Rice hull composites due to differences in particle sizes distribution of the agro fibers.

Study on fracture characteristic of welded high-density polyethylene pipe

Crack opening displacement(COD) was applied to characterize the fracture initiation of the tough high density polyethylene. Normal single side notched three point bend specimens and silica rubber replica techniques were used to study the characteristic COD of high density polyethylene pipe and its butt fusion joints including the weld fusion zone and heat affected zone at different temperature from -78 ℃ to 20 ℃ . Testing results show that the characteristic COD appears to depend on the structural features that are determined by welding process and the testing temperature. As the temperature is lowered, the characteristic COD of all zones studied decreases. Because the welding process significantly changes some structural feature of the material, characteristic COD of the weld fusion zone is the smallest one among those of the three zones. The results can be used for the engineering design and failure analysis of HDPE pipe.

Improving the Dielectric Properties of High Density Polyethylene by Incorporating Clay-Nanofiller

Polymer nanocomposites have been used for various important industrial applications. The preparation of high density polyethylene composed with Na-montmorillonite nanofiller using melt compounding method for different concentrations of clay-nanofiller of 0%, 2%, 6%, 10%, and 15% has been successfully done. The morphology of the obtained samples was optimized and characterized by scanning electron microscope showing the formation of the polymer nanocomposites. The thermal stability and dielectric properties were measured for the prepared samples. Thermal gravimetric analysis results show that thermal stability in polymer nanocomposites is more than that in the base polymer. It has been shown that the polymer nanocomposites exhibit some very different dielectric characteristics when compared to the base polymer. The dielectric breakdown strength is enhanced by the addition of clay-nanofiller. The dielectric constant (εr) and dissipation factor (Tan δ) have been studied in the frequency range 200 Hz to 2 MHz at room temperature indicating that enhancements have been occurred in εr and Tan δ by the addition of clay-nanofiller in the polymer material when compared with the pure material.

Characterization and Lifetime Estimation of High Density Polyethylene Containing a Prodegradant Agent

High density polyethylene (HDPE) samples, containing different concentrations of prodegradant additive d2w?, were prepared. The properties of the samples were evaluated through differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FTIR), rheometry, and scanning electron microscopy (SEM). The work contributes to decreasing the products made of non-biodegradable polymeric materials derived from fossil sources which are have become a problem due to their increasingly inappropriate disposal and long degradation time in the environment. The obtained results indicated that there was no degradation of the samples due to processing. No significant changes in melting temperature, crystallinity, viscoelastic behavior, molecular weight and chemical composition were observed. Images from SEM analysis showed particles on HDPE surface, attributed to prodegradant additive d2w?. Oxidation Onset Temperature (OOT) results showed that the additive d2w? accelerated the degradation of HDPE. The activation energy (Ea) was determined by Ozawa-Wall-Flynn method. The obtained values were used for lifetime estimation of the samples. At 25°C, HDPE with d2w? showed a lifetime 50% higher than that of HDPE without this additive. This fact is attributed to the presence of stabilizers in masterbatch d2w? and the absence of oxygen in thermogravimetric analysis.

Effect of substrates on crystallization of high density polyethylene

The experimental observations about remarkable influence of the substrates on the isothermal crystallization rate of a high density polyethylene(HDPE) were presented.Two methods were used to characterize the crystallization rate:the change of turbidity of the HDPE specimen and the changes of the complex viscosity and storage modulus measured by a rotational rheometer,which gave consistent results showing that the isothermal crystallization rate decreased in sequence as the specimen contacted with aluminum,brass and stainless steel plates,respectively.As to the dominant influence factor,the chemical composition of the substrates can be excluded via insulating the plate by an aluminum foil.Instead,we propose the plate's ability of removing the latent heat of crystallization from the specimen.Rheological measurement is sensitive to the crystallization process.The colloid like model proposed by BOUTAHAR et al for the crystallization of HDPE gives reasonable predictions of the crystallized fraction from the measured storage modulus.

OLEOPHOBIC AND HYDROPHOBIC FEATURE EXPERIMENTS OF FLUORINATED HIGH DENSITY POLYETHYLENE

The surface performances of directly fluorinated high density polyethylene(HDPE)are studied with Fourier transform infrared(FT-IR)spectra,scanning electron microscopy(SEM)and contact angle(CA)system. The SEM images show that there is a three-layer structure called the reaction,virgin and boundary layer structure. The depth of fluorinated layer is 5.75μm with 1h fluorination time and 7.86μm with 2h.The depths are 5.46μm and 5.07μm when fluorine density is 2% and 1%,respectively.CA indicates that the HDPE surface property becomes more hydrophobic with the increasing water contact angle from 78.5° to 104.5°.Oleophobic and hydrophobic features of HDPE are identified by comparison of mass change experiments.It is shown that the increment rate of fluorinated HDPE is much lower than that of un-fluorinated HDPE filled in neither distilled water nor jet fuel.

Selection of Thickness of High Density Polyethylene Film for Mulching in Paddy Rice

In water deficit area, judicious use of water is essential for increasing area under crop production with limited water supply. Film Mulching has been advocated as an effective means for conserving soil moisture in rice production. The effects of high density polyethylene (HDPE) film on increasing rice production, controlling weeds and residue amount of plastic were studied under five treatments, including 5, 10, 15 and 20 μm thickness as well as bare cultivation (CK). The results indicated that the HDPE film mulching mode had significant effects on weed control, soil temperature, soil moisture, photosynthetic rate, seedling biomass, yield and residues of plastic film. Combined with economic effect, it showed that the HDPE film of 10 μm is the best option for rice production.

Studies on the Effects of Bentonite (Nanoclay) on the Mechanical Properties of High-Density Polyethylene

In this work, the effect of Bentonite (Nanoclay) on the mechanical and mor-phology properties of HDPE/Nanoclay composite pipe material was investi-gated. This led to the development of a composite material with improved me-chanical properties. The HDPE/nanoclay composites were produced using an injection moulding machine at 200?C and rotor speed of 50 rpm. The compati-bilizer used in this study was Polyethylene-graft-Maleic Anhydride. Different compositions of nanoclay reinforcements were prepared and added to HDPE resin. A particle size of 425 μm was used in proportions of 0%, 5%, 10%, 15%, and 20% on weight fraction basis. All the composites samples were characterized by Zwick Roell tensile testing machine and Scanning Election Microscopy (SEM). Experimental results obtained showed improvements in the tensile strength, and modulus at the expense of elongation. The maximum tensile strength and modulus was obtained at 10% filler composition. These enhanced properties are due to the homogenous dispersion of nanoclay in HDPE matrix, which is evident from the structure that was evaluated using SEM.

Physical and Thermo-Oxidative Characterization of Asphalt Modified with High Density Polyethylene and Recycled Engine Oil

Modification of asphalt using polymers, oils and other additives has been an option to improve asphalt pavement performance and extend its lifespan. The present work aims to evaluate the influence of the addition of engine oil on the consistency and thermal properties of HDPE-modified asphalt. For this study, compositions containing asphalt, engine oil and high-density polyethylene (HDPE) were prepared, varying the concentration of engine oil by 2.5 wt%, 5 wt%, 7.5 wt% and 10 wt% and keeping the concentration of HDPE at 5 wt%. The samples were characterized by conventional tests of penetration, softening point and viscosity, aging in a Rotational Thin Film Oven (RTFO), Thermogravimetric Analysis (TGA). According to the results, the addition of HDPE to virgin asphalt causes an increase in the consistency of the virgin asphalt, which then decreases linearly as the engine oil is added into the matrix. Conventional tests showed improvements in the applicability of the asphalt in terms of resistance to cracks and permanent deformation. TGA showed a slight increase in stability for the modified asphalt samples at elevated temperatures. The RTFO showed mass gain and loss for samples with and without engine oil, respectively.

High-Density Polyethylene Based on Exfoliated Graphite Nanoplatelets/Nano-Magnesium Oxide: An Investigation of Thermal Properties and Morphology

In this study, high-density polyethylene (HDPE)/exfoliated graphite nanoplatelet (xGnP) composites reinforced with a 2 wt.% concentration of nano-magnesia (n-MgO) were fabricated using an injection moulding machine. The thermal properties and morphological structures of the composites were investigated. The XRD results showed the peaks of xGnP and n-MgO, where the intensity of the xGnP peaks became stronger with adding increasing amounts of xGnP into the polymermatrix. In terms of morphology, some agglomeration of particles was observed within the matrix, and the agglomeration decreased the thermal properties of the composites. The nanocomposites showed less thermal stability than the pristine polymer. The reduction in the onset temperature compared to that of neat HDPE was attributed to less adhesion between the fillers and the matrix. In addition, the crystallinity was reduced by the addition of fillers.

HDPE/改性蛭石复合材料的制备与气体阻隔性能研究

利用改性后的蛭石作为填充材料,通过熔融共混法制备了高密度聚乙烯(HDPE)/改性蛭石复合材料。研究了改性蛭石的添加量对复合材料热稳定性能、结晶性能、力学性能和氧气阻隔性能的影响。结果表明,相比纯HDPE,HDPE/改性蛭石复合材料仍能保持较好的拉伸强度,当含量为1%时拉伸强度为24.1 MPa,断裂伸长率先提高后下降,当含量为0.5%时断裂伸长率达到最高为535%;改性蛭石的加入提升了材料的韧性,当改性蛭石含量为1%时材料缺口冲击强度达到最高为45.8 kJ/m^(2);HDPE/改性蛭石复合材料的氧气阻隔性能明显提升,当改性蛭石含量为1%时材料的氧气阻隔性能达到最优,氧气渗透系数为6.9×10^(-15)cm^(3)·cm/(cm^(2)·s·Pa)。