The effects of separation time and magnetic induction intensity on the separation efficiency of alumina particles with diameters varying from 30 to 200 μm in aluminum melt were investigated. The experimental results ...The effects of separation time and magnetic induction intensity on the separation efficiency of alumina particles with diameters varying from 30 to 200 μm in aluminum melt were investigated. The experimental results show that the particle-accumulated layer is formed in the periphery of the solidified specimen when the diameter of the separated molten metal, the magnetic induction intensity and the separation time are 10 mm, 0.04 T and 1 s, respectively. When the separation time is 2 s, the particle-accumulated layer can be observed obviously and the separation efficiency is about 80%. There are few alumina particles in the inner of the solidified specimen when the separation time is 3 s. The separation efficiency higher than 85% can be achieved when the separation time is longer than 3 s. When the magnetic induction intensity is 0.06 T, the visible particle-accumulated layer can be formed in 1 s and the separation efficiency is higher than 95%. The experimental results were compared with the calculated results at last.展开更多
On the basis of reviewing the progress in the high efficient enrichment from secondary resources of low grade precious metals at home and abroad, a process route of the high efficient enrichment precious metals from s...On the basis of reviewing the progress in the high efficient enrichment from secondary resources of low grade precious metals at home and abroad, a process route of the high efficient enrichment precious metals from secondary resources of low-grade metals by adding iron oxide as the trapping agent, reducing agent, additive, mixing uniformly and grinding, pelletizing, reduction, grinding and separation, and selectively acid leaching iron has been put forward in this paper. The experiments of reduction, grinding and separation, and selectively acid leaching iron were carried out mainly. Under the decided experiment parameters and conditions, iron generated during the reduction can trap precious metals during reduction, high active alloy powders were obtained from the reduced products by grinding and separation, the concentration of precious metals was obtained by acid leaching high active alloy powders. The better enrichment effect was obtained by adopting the technical route of processing. Other low grade noble metal materials and enrichment ratio of precious metals from the materials to acid products was high through acid leaching. This process has the advantages of simple process, environmental-friendly, strong adaptability of raw materials, high concentration ratio, which was regarded as a kind of the general efficient enrichment technology of low grade precious metal materials.展开更多
为了使旋风分离器分离出来的颗粒大小适用于高效过滤器容尘性能试验,采用试验设计(Design of Experiment,DOE)法,并借助计算流体力学(Computational Fluid Dynamics,CFD)软件优化旋风分离器的结构尺寸,显著提升了分离性能,使切割粒径从...为了使旋风分离器分离出来的颗粒大小适用于高效过滤器容尘性能试验,采用试验设计(Design of Experiment,DOE)法,并借助计算流体力学(Computational Fluid Dynamics,CFD)软件优化旋风分离器的结构尺寸,显著提升了分离性能,使切割粒径从微米级减小至亚微米级。同时,分析了各结构尺寸对分离效率的显著影响及交互作用。展开更多
基金Projects(50474055, 50274018) supported by the National Natural Science Foundation of ChinaProject (20052176) supported by the Natural Science Foundation of Liaoning Province, China
文摘The effects of separation time and magnetic induction intensity on the separation efficiency of alumina particles with diameters varying from 30 to 200 μm in aluminum melt were investigated. The experimental results show that the particle-accumulated layer is formed in the periphery of the solidified specimen when the diameter of the separated molten metal, the magnetic induction intensity and the separation time are 10 mm, 0.04 T and 1 s, respectively. When the separation time is 2 s, the particle-accumulated layer can be observed obviously and the separation efficiency is about 80%. There are few alumina particles in the inner of the solidified specimen when the separation time is 3 s. The separation efficiency higher than 85% can be achieved when the separation time is longer than 3 s. When the magnetic induction intensity is 0.06 T, the visible particle-accumulated layer can be formed in 1 s and the separation efficiency is higher than 95%. The experimental results were compared with the calculated results at last.
基金The National Basic Research Program( 973 Plan) of China(2012CB724201)
文摘On the basis of reviewing the progress in the high efficient enrichment from secondary resources of low grade precious metals at home and abroad, a process route of the high efficient enrichment precious metals from secondary resources of low-grade metals by adding iron oxide as the trapping agent, reducing agent, additive, mixing uniformly and grinding, pelletizing, reduction, grinding and separation, and selectively acid leaching iron has been put forward in this paper. The experiments of reduction, grinding and separation, and selectively acid leaching iron were carried out mainly. Under the decided experiment parameters and conditions, iron generated during the reduction can trap precious metals during reduction, high active alloy powders were obtained from the reduced products by grinding and separation, the concentration of precious metals was obtained by acid leaching high active alloy powders. The better enrichment effect was obtained by adopting the technical route of processing. Other low grade noble metal materials and enrichment ratio of precious metals from the materials to acid products was high through acid leaching. This process has the advantages of simple process, environmental-friendly, strong adaptability of raw materials, high concentration ratio, which was regarded as a kind of the general efficient enrichment technology of low grade precious metal materials.
文摘为了使旋风分离器分离出来的颗粒大小适用于高效过滤器容尘性能试验,采用试验设计(Design of Experiment,DOE)法,并借助计算流体力学(Computational Fluid Dynamics,CFD)软件优化旋风分离器的结构尺寸,显著提升了分离性能,使切割粒径从微米级减小至亚微米级。同时,分析了各结构尺寸对分离效率的显著影响及交互作用。