Two kinds of silver based medium temperature brazing filler metals(45AgCuZnSn and 60AgCuSn) were selected to braze and seal brass flange pipe and copper pipe by high frequency heating brazing. In this paper, the quali...Two kinds of silver based medium temperature brazing filler metals(45AgCuZnSn and 60AgCuSn) were selected to braze and seal brass flange pipe and copper pipe by high frequency heating brazing. In this paper, the quality of the braze was evaluated by immersion ultrasound, and the microstructure of the brazed joint was observed by SEM and EDS. The experimental results show that the high frequency heating brazing can quickly achieve the device sealing;through the ultrasonic flaw detection image calculation, the brazed bonding rate obtained by 60AgCuSn brazing is 87%, and by 45AgCuZnSn brazing is 71%;the cross-sectional area of the brazed joint obtained by two kinds of silver based medium temperature brazing filler metals is observed, the brazed joint obtained by 45AgCuZnSn brazing has defects visual, and a large amount of Zn element gathered in the defects, there is no obvious porosity in the brazed joint by 60AgCuSn brazing,and the bonding layer is dense and coherent. Through the contrast test, the choice of 60AgCuSn alloy brazing can meet the needs of high frequency brazing of brass flange pipe and copper pipe.展开更多
棒材是国内产量占比较大的钢材品种,为了保证棒材质量,需对其实施无损检测。相控阵超声换能器基于惠更斯原理设计,通过电子激发控制实现超声声束的聚焦和偏转。水浸相控阵超声设备扫查效率快、灵敏度高,能够实现棒材全截面扫查,适用于...棒材是国内产量占比较大的钢材品种,为了保证棒材质量,需对其实施无损检测。相控阵超声换能器基于惠更斯原理设计,通过电子激发控制实现超声声束的聚焦和偏转。水浸相控阵超声设备扫查效率快、灵敏度高,能够实现棒材全截面扫查,适用于棒材产品的无损检测。使用相控阵超声设备前要对所有聚焦法则进行均一性校准,保证各聚焦法则的检测灵敏度差异在既定范围内。通过棒材检测实践,验证了水浸相控阵超声设备能够在500 mm/s进给速度下检测出棒材中大于0.7 mm FBH当量的夹杂物。展开更多
基金supported by the National Key R&D Program of China(Grant No. 2017YFB0305702)。
文摘Two kinds of silver based medium temperature brazing filler metals(45AgCuZnSn and 60AgCuSn) were selected to braze and seal brass flange pipe and copper pipe by high frequency heating brazing. In this paper, the quality of the braze was evaluated by immersion ultrasound, and the microstructure of the brazed joint was observed by SEM and EDS. The experimental results show that the high frequency heating brazing can quickly achieve the device sealing;through the ultrasonic flaw detection image calculation, the brazed bonding rate obtained by 60AgCuSn brazing is 87%, and by 45AgCuZnSn brazing is 71%;the cross-sectional area of the brazed joint obtained by two kinds of silver based medium temperature brazing filler metals is observed, the brazed joint obtained by 45AgCuZnSn brazing has defects visual, and a large amount of Zn element gathered in the defects, there is no obvious porosity in the brazed joint by 60AgCuSn brazing,and the bonding layer is dense and coherent. Through the contrast test, the choice of 60AgCuSn alloy brazing can meet the needs of high frequency brazing of brass flange pipe and copper pipe.
文摘棒材是国内产量占比较大的钢材品种,为了保证棒材质量,需对其实施无损检测。相控阵超声换能器基于惠更斯原理设计,通过电子激发控制实现超声声束的聚焦和偏转。水浸相控阵超声设备扫查效率快、灵敏度高,能够实现棒材全截面扫查,适用于棒材产品的无损检测。使用相控阵超声设备前要对所有聚焦法则进行均一性校准,保证各聚焦法则的检测灵敏度差异在既定范围内。通过棒材检测实践,验证了水浸相控阵超声设备能够在500 mm/s进给速度下检测出棒材中大于0.7 mm FBH当量的夹杂物。