Development of Steel Slag-Based Solidification/Stabilization Materials for High Moisture Content Soil

To solve the problems of high moisture content,high viscosity,and poor engineering mechanical properties of soil,this paper using with steel slag(SS)and desulfurization ash(DS)as initial raw materials,realizing the coop-erative treatment of solid waste and solidification of silt soil.The synergistic utilization of SS and DS can reduce the production cost of curing agent and promote its own consumption.According to blended cement of various SS contents and inspected compressive strength performances,the most suitable raw materials ratio was selected.The best formula for this curing agent is cement:steel slag=3:7 with 5%DS,and its 28-day compressive strength can reach 30 MPa.The experiment shows that the effect of DS and Na_(2)SO_(4) reagent with the same quality on early compressive strength improvement of cement and SS system is not much different.In this study,the mineral composition and microstructure of different gel system blocks were characterized by XRD,SEM and EDX,and a large number of webbed structures were found in the SEM test,which was not seen in previous studies.Besides,unconfined compressive strength(UCS),water resistance,and toxic characteristic leaching procedure(TCLP)were used to evaluate silt solidified soil properties.The results demonstrated that the solidified silt could meet not only the standard of general subgrade;but also has a partial stabilization effect of heavy metal ions.

Experimental Study of High Moisture Content Gas Flow Across a Cylinder at Moderate Reynolds Numbers

The Nusselt number for cross flow of a mixture of air and vapor over a cylinder was measured at moderate Reynolds numbers (30007000) for temperatures from 300℃ to 700℃ and for vapor mass fractions of 0.180.35. Results are also presented for a set of three cylinders aligned perpendicular to the flow for the same range of conditions. The effect of the vapor concentration and temperature on the convection coefficients was investigated to develop a modified Zhukauskas correlation. The results show that the Nusselt number increases as the moisture content increases and that the increase is more than could be accounted for by typical models for the property variations of mixtures. The exponent of the vapor concentration term in the modified correlation is 0.145 for the entire data set indicating the importance of the property variation due to the moisture content.

Moisture effect on compressive behavior of concrete under dynamic loading

The effect of moisture content upon compressive mechanical behavior of concrete under impact loading was studied. The axial rapid compressive loading tests of over 50 specimens with five different saturations were executed. The technique "split Hopkinson pressure bar"(SHPB) was used. The impact velocity was 10 m/s with corresponding strain rate of 50 s-1. The compressive behavior of materials was measured in terms of stress-strain curves, dynamic compressive strength, dynamic increase factor(DIF) and critical strain at a maximum stress. The data obtained from test indicate that both ascending and descending portions of stress-stain curves are affected by moisture content. However, the effect is noted to be more significant in ascending portion of the stress-strain curves. Dynamic compressive strength is higher at lower moisture content and weaker at higher moisture content.Furthermore, under nearly saturated condition, an increase in compressive strength can be found. The effect of moisture content on the average DIF of concrete is not significant. The critical compressive strain of concrete does not change with moisture content.

An Experimental Study of Composite Columns Filled with Eucalyptus nitens Timber under Axial Compression

Eucalyptus nitens(E.nitens)has been much used for producing paper but also shows promise for structural applications.In this study,static compressive tests were undertaken to examine its suitability to be used in an innovative composite column.The composite column was comprised of a rectangular steel tube with E.nitens timber infill.The nonlinear compressive behaviour of the composite column filled with E.nitens wood for both dry and wet conditions was examined.The same tests on rectangular steel tubes and bare dry and wet E.nitens samples were also undertaken as a comparison.For samples with different conditions,the ultimate capacity was evaluated and the effect of each condition on the compressive behaviour of the composite column was clarified.The steel tubes showed greater ductile behaviour,and more ductility was found in the wet samples.The steel tubes with E.nitens timber infill samples exhibited a greater linear elastic range connected with higher maximum loads,while the bare timber samples could support only lower maximum loads.The results from this research were promising for the use of rectangular steel tubes with E.nitens timber infill in structural applications.