Ultra-high nickel layered oxide cathode material with high energy density is the most promising material to improve the electrochemical performance of lithium-ion batteries(LIBs).However,the poor structural stability ...Ultra-high nickel layered oxide cathode material with high energy density is the most promising material to improve the electrochemical performance of lithium-ion batteries(LIBs).However,the poor structural stability and severe surface/interface side reactions of the material lead to poor rate performance and cyclic stability,which limits its application in practice.In this paper,the dual-modification strategy of Co doping and La_(2)O_(3) coating is used to meet the above challenges.Co doping can effectively widen layer spacing and reduce Li^(+)/Ni^(2+) mixing,and La_(2)O_(3) coating can effectively eliminate the residual alkali on the surface of active material,inhibit the thickening of cathode electrolyte interphase(CEI)film and reduce surface/interface side reactions.Therefore,the modified material(NM90-CL)with excellent electrochemical properties is achieved through the synergistic enhancement of Co doping and La_(2)O_(3) coating.Its capacity retention rate can reach 77.9%after 200 cycles at 1.0℃ and 75.7%after 200 cycles at 5.0℃.Its reversible capacity can up to 153.5 mAh·g^(–1) at 10.0℃.This dual-modification strategy will provide theoretical guidance and technical support for the synthesis of other high-performance electrode materials.展开更多
基金This work was financially supported by the National Science Foundation of China(Nos.22169007 and 22362011)the Science and Technology Major Project of Guangxi(No.AA19046001)+3 种基金the Open Research Fund of Guangxi Key Laboratory of Electrochemical and Magnetochemical Functional Materials(Nos.EMFM20201105 and EMFM20181119)the Characteristic Innovation Projects of Universities in Guangdong Province(No.2022KTSCX324)the Science and Technology Innovation Commission of Shenzhen(No.JCYJ20190808173815205)the University Teachers'Characteristic Innovation Research Project(No.2021XJZZ11).
文摘Ultra-high nickel layered oxide cathode material with high energy density is the most promising material to improve the electrochemical performance of lithium-ion batteries(LIBs).However,the poor structural stability and severe surface/interface side reactions of the material lead to poor rate performance and cyclic stability,which limits its application in practice.In this paper,the dual-modification strategy of Co doping and La_(2)O_(3) coating is used to meet the above challenges.Co doping can effectively widen layer spacing and reduce Li^(+)/Ni^(2+) mixing,and La_(2)O_(3) coating can effectively eliminate the residual alkali on the surface of active material,inhibit the thickening of cathode electrolyte interphase(CEI)film and reduce surface/interface side reactions.Therefore,the modified material(NM90-CL)with excellent electrochemical properties is achieved through the synergistic enhancement of Co doping and La_(2)O_(3) coating.Its capacity retention rate can reach 77.9%after 200 cycles at 1.0℃ and 75.7%after 200 cycles at 5.0℃.Its reversible capacity can up to 153.5 mAh·g^(–1) at 10.0℃.This dual-modification strategy will provide theoretical guidance and technical support for the synthesis of other high-performance electrode materials.
