In this paper, a high calcium high sulfate ash as the main material, adding fly ash, lime, cement, gypsum and some modifiers to prepare autoclaved aerated concrete. The products complies with the technical requirement...In this paper, a high calcium high sulfate ash as the main material, adding fly ash, lime, cement, gypsum and some modifiers to prepare autoclaved aerated concrete. The products complies with the technical requirements of GB/T11968-2006. This paper also studies the influence of the physical methods and water ratio on autoclaved aerated concrete by high calcium high sulfate ash aerated concrete. The best ratio of water and Grinding time were found in practice study.展开更多
为深入了解神东30 t/h煤粉工业锅炉对应的高倍率灰钙循环脱硫除尘一体化技术(NGD,no gap desulphurization)脱硫过程及机理,研究不同影响因素对脱硫效率的影响。笔者在反应器上沿程打孔取样,检测不同位置脱硫剂硫含量和水分变化,结果发...为深入了解神东30 t/h煤粉工业锅炉对应的高倍率灰钙循环脱硫除尘一体化技术(NGD,no gap desulphurization)脱硫过程及机理,研究不同影响因素对脱硫效率的影响。笔者在反应器上沿程打孔取样,检测不同位置脱硫剂硫含量和水分变化,结果发现,随着脱硫反应的进行,脱硫剂中水分和硫含量分别呈降低和增加的趋势,说明水分对脱硫反应至关重要,在有水存在的条件下,脱硫反应从气固两相反应变为离子间的液相反应,脱硫反应速率显著增加。随着脱硫反应的进行,脱硫剂中反应产物增加导致硫含量增加。检测反应器沿程烟气中成分及含量变化,根据反应器上单位距离脱硫效率的变化率,将脱硫过程分为3个阶段:常速段、降速段、拟平衡段,前2个阶段脱硫反应速率快,为脱硫反应的关键段,所脱除的SO2占SO2总量的90%,因此强化前2个脱硫阶段是提高脱硫效率的有效手段。最后,在NGD脱硫装置上进行工程试验,研究增湿水量、SO2初始浓度、掺混比对脱硫效率的影响规律,结果表明,增湿水量增加,SO2初始浓度降低,熟石灰占比增加,相当于脱硫反应物初始浓度增加,促进脱硫反应向右进行,初始阶段脱硫反应速率增加,因此最终脱硫效率呈现增加的趋势。但由于脱硫剂孔隙结构及活性物质含量的限制,脱硫反应存在最佳的工艺条件使脱硫剂中有效物质被充分利用,根据脱硫效率的变化量最终确定增湿水量、SO2初始浓度、掺混比最佳范围,分别为0.14~0.27 t/h、350~550μL/L、3∶1~2∶1,此时脱硫效率的变化量分别为28.81%、25.87%、10.55%。展开更多
文摘In this paper, a high calcium high sulfate ash as the main material, adding fly ash, lime, cement, gypsum and some modifiers to prepare autoclaved aerated concrete. The products complies with the technical requirements of GB/T11968-2006. This paper also studies the influence of the physical methods and water ratio on autoclaved aerated concrete by high calcium high sulfate ash aerated concrete. The best ratio of water and Grinding time were found in practice study.
文摘为深入了解神东30 t/h煤粉工业锅炉对应的高倍率灰钙循环脱硫除尘一体化技术(NGD,no gap desulphurization)脱硫过程及机理,研究不同影响因素对脱硫效率的影响。笔者在反应器上沿程打孔取样,检测不同位置脱硫剂硫含量和水分变化,结果发现,随着脱硫反应的进行,脱硫剂中水分和硫含量分别呈降低和增加的趋势,说明水分对脱硫反应至关重要,在有水存在的条件下,脱硫反应从气固两相反应变为离子间的液相反应,脱硫反应速率显著增加。随着脱硫反应的进行,脱硫剂中反应产物增加导致硫含量增加。检测反应器沿程烟气中成分及含量变化,根据反应器上单位距离脱硫效率的变化率,将脱硫过程分为3个阶段:常速段、降速段、拟平衡段,前2个阶段脱硫反应速率快,为脱硫反应的关键段,所脱除的SO2占SO2总量的90%,因此强化前2个脱硫阶段是提高脱硫效率的有效手段。最后,在NGD脱硫装置上进行工程试验,研究增湿水量、SO2初始浓度、掺混比对脱硫效率的影响规律,结果表明,增湿水量增加,SO2初始浓度降低,熟石灰占比增加,相当于脱硫反应物初始浓度增加,促进脱硫反应向右进行,初始阶段脱硫反应速率增加,因此最终脱硫效率呈现增加的趋势。但由于脱硫剂孔隙结构及活性物质含量的限制,脱硫反应存在最佳的工艺条件使脱硫剂中有效物质被充分利用,根据脱硫效率的变化量最终确定增湿水量、SO2初始浓度、掺混比最佳范围,分别为0.14~0.27 t/h、350~550μL/L、3∶1~2∶1,此时脱硫效率的变化量分别为28.81%、25.87%、10.55%。