Ultrahigh strength and improved electrical conductivity in an aging strengthened copper alloy processed by combination of equal channel angular pressing and thermomechanical treatment

In this paper,equal channel angular pressing and thermomechanical treatment was employed to improve the strength and electrical conductivity of an aging strengthened Cu-Ti-Cr-Mg alloy,and the microstructure and properties of the alloy were investigated in detail.The results showed that the samples deformed by the combination of cryogenic equal channel angular pressing(ECAP)and rolling had good comprehensive properties after aging at 400℃.The tensile strength of the peak-aged and over-aged samples was 1120 MPa and 940 MPa,with their corresponding electrical conductivity of 14.7%IACS and 22.1%IACS,respectively.ECAP and cryogenic rolling introduced high density dislocations,leading to the inhibition of the softening effects and refinement of the grains.After a long time aging at 400℃,the alloy exhibited ultra-high strength with obvious increasing electrical conductivity.The high strength was attributed to the synergistic effect of work hardening,grain refinement strengthening and precipitation strengthening.The precipitation of a large amount of Ti atoms from the matrix led to the high electrical conductivity of the over-aged sample.

Design of a low-alloy high-strength and high-toughness martensitic steel

To develop a high strength low alloy （HSLA） steel with high strength and high toughness, a series of martensitic steels were studied through alloying with various elements and thermodynamic simulation. The microstructure and mechanical properties of the designed steel were investigated by optical microscopy, scanning electron microscopy, tensile testing and Charpy impact test. The results show that cementite exists between 500℃ and 700℃, M7C3 exits below 720℃, and they are much lower than the austenitizing temperature of the designed steel. Furthermore, the Ti（C,N） precipitate exists until 1280℃, which refines the microstructure and increases the strength and toughness. The optimal alloying components are 0.19% C, 1.19% Si, 2.83% Mn, 1.24% Ni, and 0.049% Ti; the tensile strength and the V notch impact toughness of the designed steel are more than 1500 MPa and 100 J, respectively.

Product Development of High Strength and Toughness Spring Flat Steel

With the continuous development of mechanical industry,higher requirements are put forward for the comprehensive properties of spring steel.The chemical composition and production process of spring flat steel are designed to meet the requirements of high strength and high toughness of spring flat steel,through the test,the product surface quality and internal quality all meet the national standards,the performance indicators to meet user requirements.

Application of Lanthanum in High Strength and High Conductivity Copper Alloys

China is quite poor in argent resource. Roughly 80% of this industrial argent is imported every year. In order to improve the situation, we took advantage of rare earth (RE) mineral resource and successfully developed the non-argent Lanthanum-tellurium-copper alloy as a substitute for industry argent-copper. In our research, we were able to successfully apply rare earth lanthanum to copper alloy. The defects as porosity, inclusion, etc. originating from nonvacuum melting processing were controlled. Fine grain was obtained. Meanwhile, the comprehensive properties of the copper alloy, such as strength, conductivity and thermal conductivity were improved. The research results in increasing conductivity and thermal conductivity by 5% and 15%, respectively, while the tensile strength is increased by 6% higher than Ag-Cu alloy. The anti-electric corrosion property is good, and there is no argent-cadmium steam population originating from the electric arc effect. The addition of lanthanum further reduces the content of oxygen and hydrogen. The optimum quantity of the addition of RE lanthanum in the copper alloy is 0.010% - 0.020% .

Designing new low alloyed Mg-RE alloys with high strength and ductility via high-speed extrusion

Two new low-alloyed Mg-2RE-0.8Mn-0.6Ca-0.5Zn(wt%,RE=Sm or Y)alloys are developed,which can be produced on an in-dustrial scale via relatively high-speed extrusion.These two alloys are not only comparable to commercial AZ31 alloy in extrudability,but also have superior mechanical properties,especially in terms of yield strength(YS).The excellent extrudability is related to less coarse second-phase particles and high initial melting point of the two as-cast alloys.The high strength-ductility mainly comes from the formation of fine grains,nano-spaced submicron/nano precipitates,and weak texture.Moreover,it is worth noting that the YS of the two alloys can maintain above 160 MPa at elevated temperature of 250°C,significantly higher than that of AZ31 alloy(YS:45 MPa).The Zn/Ca solute segregation at grain boundaries,the improved heat resistance of matrix due to addition of RE,and the high melting points of strengthening particles(Mn,MgZn_(2),and Mg-Zn-RE/Mg-Zn-RE-Ca)are mainly responsible for the excellent high-temperature strength.

Microstructure and mechanical properties of high-strength low alloy steel by wire and arc additive manufacturing

A high-building multi-directional pipe joint(HBMDPJ)was fabricated by wire and arc additive manufacturing using high-strength low-alloy(HSLA)steel.The microstructure characteristics and transformation were observed and analyzed.The results show that the forming part includes four regions.The solidification zone solidifies as typical columnar crystals from a molten pool.The complete austenitizing zone forms from the solidification zone heated to a temperature greater than 1100℃,and the typical columnar crystals in this zone are difficult to observe.The partial austenitizing zone forms from the completely austenite zone heated between Ac1(austenite transition temperature)and1100℃,which is mainly equiaxed grains.After several thermal cycles,the partial austenitizing zone transforms to the tempering zone,which consistes of fully equiaxed grains.From the solidification zone to the tempering zone,the average grain size decreases from 75 to20μm.The mechanical properties of HBMDPJ satisfies the requirement for the intended application.

GRAIN BOUNDARY SEGREGATION AND INTERGRANULAR BRITTLENESS IN HIGH STRENGTH ALUMINIUM ALLOY

ＧＲＡＩＮＢＯＵＮＤＡＲＹＳＥＧＲＥＧＡＴＩＯＮＡＮＤＩＮＴＥＲＧＲＡＮＵＬＡＲＢＲＩＴＴＬＥＮＥＳＳＩＮＨＩＧＨＳＴＲＥＮＧＴＨＡＬＵＭＩＮＩＵＭＡＬＬＯＹ￥Ｓｏｎｇ，Ｒｅｎｇｕｏ；Ｚｈｅｎｇ，Ｍｅｉｇｕａｎｇ（ＤｅｐａｒｒｍｅｎｔｏｆＭａｔｅｒｉ...

Research progress on microstructure evolution and hot processing maps of high strength β titanium alloys during hot deformation

High strength β titanium alloys are widely used in large load bearing components in the aerospace field. At present, large parts are generally formed by die forging. Different initial microstructures and deformation process parameters will significantly affect the flow behavior. To precisely control the microstructures, researchers have conducted many studies to analyze the microstructure evolution law and deformation mechanism during hot compression. This review focuses on the microstructure evolution of high strength β titanium alloys during hot deformation, including dynamic recrystallization and dynamic recovery in the single-phase region and the dynamic evolution of the α phase in the two-phase region. Furthermore, the optimal hot processing regions, instability regions,and the relationship between the efficiency of power dissipation and the deformation mechanism in the hot processing map are summarized. Finally, the problems and development direction of using hot processing maps to optimize process parameters are also emphasized.

Numerical simulation of residual stress and deformation for submerged arc welding of Q690D high strength low alloy steel thick plate

The finite element simulation software SYSWELD is used to numerically simulate the temperature field,residual stress field,and welding deformation of Q690D thick plate multi-layer and multi-pass welding under different welding heat input and groove angles.The simulation results show that as the welding heat input increases,the peak temperature during the welding process is higher,and the residual stress increases,they are all between 330–340 MPa,and the residual stress is concentrated in the area near the weld.The hole-drilling method is used to measure the actual welding residual stress,and the measured data is in good agreement with the simulated value.The type of post-welding deformation is angular deformation,and as the welding heat input increases,the maximum deformation also increases.It shows smaller residual stress and deformation when the groove angle is 40°under the same heat input.In engineering applications,under the premise of guaranteeing welding quality,smaller heat input and 40°groove angle should be used.

Effect of welding processes on mechanical and microstructural characteristics of high strength low alloy naval grade steel joints

Naval grade high strength low alloy(HSLA) steels can be easily welded by all types of fusion welding processes. However, fusion welding of these steels leads to the problems such as cold cracking, residual stress, distortion and fatigue damage. These problems can be eliminated by solid state welding process such as friction stir welding(FSW). In this investigation, a comparative evaluation of mechanical(tensile, impact,hardness) properties and microstructural features of shielded metal arc(SMA), gas metal arc(GMA) and friction stir welded(FSW) naval grade HSLA steel joints was carried out. It was found that the use of FSW process eliminated the problems related to fusion welding processes and also resulted in the superior mechanical properties compared to GMA and SMA welded joints.

Microstructures and mechanical properties of high strength Mg-Zn-Mn alloy

The microstructures and mechanical properties of a new Mg-6%Zn-1%Mn(mass fraction) wrought magnesium alloy were studied,which could be extruded smoothly at 310-330℃with a complete dynamic recrystallization.After solution treatment one and two-step aging techniques were used.All as-aged microstructures contained two types of dispersed phases:β' phases and pureα-Mn particles.The two-step aging had a better strengthening effect than the traditional one-step aging,and the strength value achieved by the two-step aging could reach that of the ZK60 wrought magnesium alloy.The outstanding precipitation strengthening effect of the alloy should be attribute to the GP zones,diffusive solute-rich zones and some metastable phases formed during the first step aging that provide more effective nuclei for Mg-Zn strengthening phases during the second step aging.

Process of friction-stir welding high-strength aluminum alloy and mechanical properties of joint

The process of friction-stir welding 2A12CZ alloy has been studied. And strength and elongation tests have been performed, which demonstrated that the opportunity existed to manipulate friction-stir welding parameters in order to improve a range of material properties. The results showed that the joint strength and elongation arrived at their maximums (331 MPa and 4%) at 37.5 mm/min and 300 rpm. As welding parameters changing, joint tensile strength and elongation had similar development. Hardness measurement indicated that the weld was softened. However, there was considerable difference in softening degree for different joint zone. The weld top had lower hardness and wider softening zone than other zone of the weld. And softening zone at advancing side was wider than that at retreating side.

Effect of Plastic Deformation and H_2S on Dynamic Fracture Toughness of High Strength Casing Steel

The effects of plastic deformation and H2 S on fracture toughness of high strength casing steel（C110 steel） were investigated. The studied casing specimens are as follows： original casing, plastic deformation（PD） casing and PD casing after being immersed in NACE A solution saturated with H2S（PD＋H2S）. Instrumented impact method was employed to evaluate the impact behaviors of the specimens, meanwhile, dynamic fracture toughness（JId） was calculated by using Rice model and Schindler model. The experimental results show that dynamic fracture toughness of the casing decreases after plastic deformation. Compared with that of the original casing and PD casing, the dynamic fracture toughness decreases further when the PD casing immersed in H2 S, moreover, there are ridge-shaped feature and many secondary cracks present on the fracture surface of the specimens. Impact fracture mechanism of the casing is proposed as follows： the plastic deformation results in the increase of defect density of materials where the atomic hydrogen can accumulate in reversible or irreversible traps and even recombine to form molecular hydrogen, subsequently, the casing material toughness decreases greatly.

High strength magnesium alloy with α-Mg and W-phase processed by hot extrusion

Fine-grained Mg-6Zn-4Y alloy was prepared by an ingot metallurgy process with hot extrusion at 300 ℃.The microstructure was studied by XRD,OM,SEM and TEM,and the tensile properties were tested at room temperature.The results show that the alloy is composed of α-Mg and W-phase.The microstructure of the as-extruded alloy has a bimodal grain size distribution.The fine grains with the mean size of 1.2 μm are formed by dynamic recrystallization.The coarse grains（about 23% in area fraction） are unrecrystallized regions which are elongated along extrusion direction.The engineering stress—strain curve shows a pronounced yield point.The ultimate tensile strength,yield strength,and elongation are（371±10） MPa,（350±5） MPa and（7±2）%,respectively.The high strengths are attributed to the fine-grained matrix structure enhanced by W-phase particles,nano-scaled precipitates,and strong basal plane texture.

Thermal Activation Analyses of Dynamic FractureToughness of High Strength Low Alloy Steels

A formula is derived for determining the influence of temperature and loading rate on dynamic fracture toughness of a high strength low alloy steel (HQ785C) from thermal activation analysis of the experimental results of three-point bend specimens as well as introducing an Arrhenius formula. It is shown that the results obtained by the given formula are in good agreement with the experimental ones in the thermal activation region. The present method is also valuable to describe the relationship between dynamic fracture toughness and temperature and loading rate of other high strength low alloy steels.

Towards designing high mechanical performance low-alloyed wrought magnesium alloys via grain boundary segregation strategy:A review

Low-alloyed magnesium(Mg)alloys have emerged as one of the most promising candidates for lightweight materials.However,their further application potential has been hampered by limitations such as low strength,poor plasticity at room temperature,and unsatisfactory formability.To address these challenges,grain refinement and grain structure control have been identified as crucial factors to achieving high performance in low-alloyed Mg alloys.An effective way for regulating grain structure is through grain boundary(GB)segregation.This review presents a comprehensive summary of the distribution criteria of segregated atoms and the effects of solute segregation on grain size and growth in Mg alloys.The analysis encompasses both single element segregation and multi-element co-segregation behavior,considering coherent interfaces and incoherent interfaces.Furthermore,we introduce the high mechanical performance low-alloyed wrought Mg alloys that utilize GB segregation and analyze the potential impact mechanisms through which GB segregation influences materials properties.Drawing upon these studies,we propose strategies for the design of high mechanical performance Mg alloys with desirable properties,including high strength,excellent ductility,and good formability,achieved through the implementation of GB segregation.The findings of this review contribute to advancing the understanding of grain boundary engineering in Mg alloys and provide valuable insights for future alloy design and optimization.

Effect of Heat Treatment on Microstructure and Mechanical properties of high strength low alloy(HSLA)steel

In this paper,a Fe-based Mn-Ni–Cr–Mo high strength low alloy(HSLA)steel was prepared by using Vacuum melting,following by hot rolling with 78%deformation and various heat treatment processes.Microstructure were characterized by optical microscope(OM),scanning electron microscope(SEM)equipped with energy dispersive spectrometer.Tensile tests were performed.After direct quenching(Q)from 860℃,the samples were subjected to secondary quenching(L)at different intercritical temperatures within the two-phase region and various tempering temperatures(T).Results show that QLT treatment increases elongation and decreases yield ratio compared with conventional quenching and tempering process(QT).The optimum QLT heat treatment parameter in terms of temperature are determined as Q:860℃,L:700℃,and T:600℃,resulting in the better combined properties with yield strength of 756MPa,tensile strength of 820MPa,tensile elongation of 16.76%and yield ratio of 0.923.

Recent developments in high-strength Mg-RE-based alloys:Focusing on Mg-Gd and Mg-Y systems

Higher strength is always the goal pursued by researchers for the structural materials,especially for the lightweight magnesium(Mg)alloys which generally have relatively low strength at present.From this aspect,the present paper reviews the recent reports of a kind of Mg alloys,i.e.Mg-RE(RE:rare earths,mainly Gd or Y)casting and wrought alloys,which have been able to achieve high strength compared with common or commercial Mg alloys,from the viewpoint and content of the alloy system,alloying constitution,preparation process,tensile strength and each of the main strengthening mechanisms.This review of recent research and developments in high-strength Mg-RE alloys is beneficial for the further design of Mg alloys with higher strength as well as excellent comprehensive performance.

Tensile properties of high strength cast Mg alloys at room temperature:A review

As most Mg alloy products are now produced by a casting process,the development of high strength cast Mg alloys can promote their further applications and has already become one of the hot research areas of Mg alloys.The present paper reviews the strengthening mechanisms,tensile properties and modification results of commercial high strength cast Mg alloys;as well as the development of Mg-Gd,Mg-Nd and Mg-Sn based alloys.It concludes that precipitation strengthening is the most important strengthening mechanism in high strength cast Mg alloys,which contributes more than 60%of yield strength in solution&peak-aged(T6)cast Mg alloys.For the yield strength,the alloys follow the sequence of Mg-Gd(Y)-Ag>Mg-Gd(Y)-Zn>Mg-Gd-Y/Sm/Nd>Mg-Y-Nd(WE series)>ZK61>Mg-Nd>AZ91>Mg-Sn.Mg-Gd(Y)-Ag based alloys are the strongest cast Mg alloys at present,followed by Mg-Gd(Y)-Zn based alloys.The high yield strengths of Mg-Gd(Y)-Ag and Mg-Gd(Y)-Zn cast alloys are due to the co-precipitation of basal and prismatic meta-stable phases.

Microstructure investigation of a new type super high strength aluminum alloy at different heat-treated conditions

As a structural material with low density and high strength, super-highstrength aluminum alloys have a future for wide application. However, its poor stress corrosionresistance (SCC) restricts further development. In present, retrogression and re-ageing (RRA)treatment, which can improve both strength and SCCR of 7XXX series alloy, is a best method to solvethis problem. The effect of RRA treatment on the microstructure evolution of a new type lowfrequency electric-magnetic casting Al-9.OZn-2.45Mg-2.2Cu-0.15Zr alloy was investigated using DSCand TEM technologies. The results show that the typical microstructure of the alloy at T6 conditionis characterized by both fine eta' and GP zone homogeneously distributed in the matrix andcontinuous r) particles occurred on the grain-boundary. After RRA treatment, the matrixprecipitations are mainly fine and dispersed eta' and eta phases, being coarser and more stable thanthat from T6 temper. While, the grain-boundary microstructure is very close to that resulting fromT73 temper. High retrogression temperature and long retrogression time leads to a more stablemicrostructure after re-ageing.