Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
Surface leakage currents of A1GaN/GaN high electron mobility transistors are investigated by utilizing a circular double-gate structure to eliminate the influence of mesa leakage current. Different mechanisms are foun...Surface leakage currents of A1GaN/GaN high electron mobility transistors are investigated by utilizing a circular double-gate structure to eliminate the influence of mesa leakage current. Different mechanisms are found under various passivation conditions. The mechanism of the surface leakage current with AI2 03 passivation follows the two-dimensional variable range hopping model, while the mechanism of the surface leakage current with SiN passivation follows the Frenkel-Poole trap assisted emission. Two trap levels are found in the trap-assisted emission. One trap level has a barrier height of 0.22eV for the high electric field, and the other trap level has a barrier height of 0.12eV for the low electric field.展开更多
Solid-solid surface adsorption of Eu2O3 on amorphous Al2O3 have been investigated by Mossbauer spectroscopy, X- ray diffraction analysis and laser Raman spectra (LRS). No X-ray diffraction peak of crystalline Eu2O3 ca...Solid-solid surface adsorption of Eu2O3 on amorphous Al2O3 have been investigated by Mossbauer spectroscopy, X- ray diffraction analysis and laser Raman spectra (LRS). No X-ray diffraction peak of crystalline Eu2O3 can be found for all samples studied. The LRS show that two peaks at 998 and 1051 cm-1 assigned to two-dimensional surface europium-oxygen species appear at Eu2O3 content of 18.7 wt%. The peak at 1068 cm-1 due to the surface species and another peak at 342cm-1 due to crystalline Eu2O3 content start to appear for the sample with an Eu2O3 content of 36.5 wt%. The dispersity of Eu2O3 on the surface of amorphous Al2O3 were compared with that of α-Al2O3,η-Al2O3 and SiO2 gel. The results of these studies indicate that the structure of Eu2O3 dispersed onto the support surface depend on the structure of support and that there is an inductive effect of support on the structure of the Eu2O3.展开更多
A series of alumina samples were prepared using β-cyclodextrin as the non-surfactant template. These samples were characterized by XRD, BET and TEM. The results showed that the alumina samples prepared using β-cyclo...A series of alumina samples were prepared using β-cyclodextrin as the non-surfactant template. These samples were characterized by XRD, BET and TEM. The results showed that the alumina samples prepared using β-cyclodextrin template had the higher surface areas （124-484 m^2/g）, larger pore volumes （0.7-1.27 mL/g） and more thermal stability than samples prepared without using β-cyclodextrin.展开更多
This work concerns with the high temperature deformation of internally oxidized Al2O3/Cu composites. The investigation revealed that dispersive alumina can obstruct dislocation sliding and define the subgrain size the...This work concerns with the high temperature deformation of internally oxidized Al2O3/Cu composites. The investigation revealed that dispersive alumina can obstruct dislocation sliding and define the subgrain size thereby improve significantly the strength of the materials at high temperature. The sliding of dislocations is a main deformation mechanism in the given temperature range. The sliding of grain boundary and diffusive creep play important roles at high temperature and low strain rate. The dispersoids can raise the recrystallization temperature to higher than 1223 K. Dynamic recovery is a main softening way under the experimental conditions. Higher deformation rate and lower deformation temperature imply a higher flow stress.展开更多
An extended-life and ultra-low oxygen sensor has been fabricated by using polycrystalline Caβ″/β/α-Al2O3 as a solid electrolyte. Five reference electrodes CaO+O2, Caβ″/β/α-Al2O3 (powder)+O2,Cr+Cr2O3, Nb+NbO an...An extended-life and ultra-low oxygen sensor has been fabricated by using polycrystalline Caβ″/β/α-Al2O3 as a solid electrolyte. Five reference electrodes CaO+O2, Caβ″/β/α-Al2O3 (powder)+O2,Cr+Cr2O3, Nb+NbO and Mo+MoO2 were tested in order to select a better reference electrode for this sensor. The limit of determining oxygen activity and the extended-life of the sensor were also tested in this study.展开更多
A series of CuO/ZnO/Al_2O_3, CuO/ZnO/ZrO_2/Al_2O_3 and CuO/ZnO/CeO_2/Al_2O_3 catalysts were prepared by coprecipitation and characterized by N_2 adsorption, XRD, TPR, N_2O titration and HRTEM. The catalytic performanc...A series of CuO/ZnO/Al_2O_3, CuO/ZnO/ZrO_2/Al_2O_3 and CuO/ZnO/CeO_2/Al_2O_3 catalysts were prepared by coprecipitation and characterized by N_2 adsorption, XRD, TPR, N_2O titration and HRTEM. The catalytic performances of these catalysts for the steam reforming of methanol were evaluated in a laboratory-scale fixed-bed reactor at 0.1 MPa and temperatures between 473 and 543 K. The results showed that the catalytic activity depended greatly on the catalyst reducibility and the specific surface area of Cu. An approximate linear correlation between the catalytic activity and the Cu surface area was found for all catalysts investigated in this study.Compared to CuO/ZnO/Al_2O_3, the ZrO_2-doped CuO/ZnO/Al_2O_3 exhibited higher activity and selectivity to CO,while the CeO_2-doped catalyst displayed lower activity and selectivity. Finally, an intrinsic kinetic study was carried out over a screened CuO/ZnO/CeO_2/Al_2O_3 catalyst in the absence of internal and external mass transfer effects. A good agreement was observed between the model-derived effluent concentrations of CO(CO_2) and the experimental data. The activation energies for the reactions of methanol-steam reforming, water-gas shift and methanol decomposition over CuO/ZnO/CeO_2/Al_2O_3 were 93.1, 85.1 and 116.5 k J·mol^(-1), respectively.展开更多
Al2O hollow microspheres without noticeable aggregation have been prepared via a facile templating route with urea-mediated precipitation. The precipitation process is different from the surfaceadsorption method which...Al2O hollow microspheres without noticeable aggregation have been prepared via a facile templating route with urea-mediated precipitation. The precipitation process is different from the surfaceadsorption method which is confined to the adsorption capacity of the template surface. TEM and SEM images indicate that most of these Al2O hollow microspheres with shell thickness of tens of nanometers and diameters in a narrow range of 100-200 nm consist of a shell of closely packed nanoparticles. The optimal amount of H2O and EtOH are 40 and 120 mL, respectively. The specific surface area, average pore size and pore volume of the Al2O hollow microspheres (calcinated at 600 °C) are 328.52 m2/g, 17.496 nm and 1.985 cm'/g, respectively. As the calcination temperature increases from 600 to 1 100 °C, the phase composition changes from y-Al2O3 to &-AI2O3 and a-Al2O3, and the surface morphology appears to change from a relatively rough surface formed by nanoparticles to a smooth surface formed by lamellar, which lead to the closure of pore channels and the reduction of specific surface.展开更多
In this paper, study on the effect of preparation conditions of K2CO3/Al2O3 sorbent was done. Box-Behnken design was applied to study the influence of four parameters involve initial solution concentration, impregnati...In this paper, study on the effect of preparation conditions of K2CO3/Al2O3 sorbent was done. Box-Behnken design was applied to study the influence of four parameters involve initial solution concentration, impregnation time and calcination step temperature and time. A quadratic model was used to correlate the sorbent capture capacity. The model was used to calculate the optimum conditions for preparing sorbent. From the analysis of variance (ANOVA), the most influential factor on each experimental design response was identified. The potassium-based sorbents used in this study were prepared by impregnating K2CO3 on Al2O3 support. The CO2 capture capacity was measured in the presence of H2O in a fixed-bed reactor at CO2 capture temperature of 60°C using breakthrough curves. The optimum sorbent prepared by this method showed CO2 capture capacity of 77.21 mg CO2/g sorbent. It was observed that the experimental values obtained were in good agreement with the values predicted by the model, with relatively small errors between the predicted and the actual values. The results obtained in this study can be used as basic data for study on design and operating condition optimization of CO2 capture process using these sorbents.展开更多
The superplasticity of an Al203p/6061Al composite, fabricated by powder metallurgy techniques, has been investigated. Instead of any special thermomechanical processing or hot rolling, simple ...The superplasticity of an Al203p/6061Al composite, fabricated by powder metallurgy techniques, has been investigated. Instead of any special thermomechanical processing or hot rolling, simple hot extrusion has been employed to obtain a fine grained structure before superplastic testing. Superplastic tensile tests were performed at strain rates ranging from 10-2 to 10-4 s-1 and at temperatures from 833 to 893 K. A maximum elongation of 200% was achieved at a temperature of 853 K and an initial strain rate of 1.67×103 s-1. The highest value obtained for the strain rate sensitivity index (in) was 0.32. Differential scanning calorimeter was used to ascertain the possibility of any partial melting in the vicinity of optimum superplastic temperature. These results suggested that no liquid phase existed where maximum elongation was achieved and deformation took place entirely in the solid state.展开更多
Microwave characteristics of MgB2/Al2O3 superconducting thin films were investigated by coplanar resonator technique. The thin films studied have different grain sizes resulting from different growth techniques. The ...Microwave characteristics of MgB2/Al2O3 superconducting thin films were investigated by coplanar resonator technique. The thin films studied have different grain sizes resulting from different growth techniques. The experimental results can be described very well by a grain-size model which combines coplanar resonator theory and Josephson junction network model. It was found that the penetration depth and surface resistance of thin films with smaller grain sizes are larger than those of thin films with larger grain sizes.展开更多
The purpose of this study was to investigate the effect of preadsorbed CO at different temperatures, calcination temperatures, the combined influence of reduction temperature and time, and pretreatment using hydrogen ...The purpose of this study was to investigate the effect of preadsorbed CO at different temperatures, calcination temperatures, the combined influence of reduction temperature and time, and pretreatment using hydrogen or syngas as reduction agents on the F-T synthesis （FTS） activity and selectivity of Co/Al2O3 catalyst. The reactivity of the carbon species at higher preadsorption temperature with H2 in TPSR decreased, whereas the carbon-containing species showed higher reactivity over Co/Al2O3 catalyst with low calcination temperature. This agreed well with the order of catalytic activity for F-T synthesis on this catalyst. The catalytic activity of the catalyst varied with reduction temperature and time remarkably. CODEX optimization gave an optimum reduction temperature of 756 K and reduction time of 6.2 h and estimated C5＋ yield perfectly. The pretreatment of Co/Al2O3 catalyst with different reduction agents （hydrogen or syngas） showed important influences on the catalytic performance. A high CO conversion and C5＋ yield were obtained on the catalyst reduced by hydrogen, whereas methane selectivity on the catalyst reduced by syngas was much higher than that on the catalyst reduced by hydrogen.展开更多
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.
基金Supported by the National High-Technology Research and Development Program of China under Grant No 2014AA032602the National Natural Science Foundation of China under Grant Nos 61474115 and 61501421
文摘Surface leakage currents of A1GaN/GaN high electron mobility transistors are investigated by utilizing a circular double-gate structure to eliminate the influence of mesa leakage current. Different mechanisms are found under various passivation conditions. The mechanism of the surface leakage current with AI2 03 passivation follows the two-dimensional variable range hopping model, while the mechanism of the surface leakage current with SiN passivation follows the Frenkel-Poole trap assisted emission. Two trap levels are found in the trap-assisted emission. One trap level has a barrier height of 0.22eV for the high electric field, and the other trap level has a barrier height of 0.12eV for the low electric field.
文摘Solid-solid surface adsorption of Eu2O3 on amorphous Al2O3 have been investigated by Mossbauer spectroscopy, X- ray diffraction analysis and laser Raman spectra (LRS). No X-ray diffraction peak of crystalline Eu2O3 can be found for all samples studied. The LRS show that two peaks at 998 and 1051 cm-1 assigned to two-dimensional surface europium-oxygen species appear at Eu2O3 content of 18.7 wt%. The peak at 1068 cm-1 due to the surface species and another peak at 342cm-1 due to crystalline Eu2O3 content start to appear for the sample with an Eu2O3 content of 36.5 wt%. The dispersity of Eu2O3 on the surface of amorphous Al2O3 were compared with that of α-Al2O3,η-Al2O3 and SiO2 gel. The results of these studies indicate that the structure of Eu2O3 dispersed onto the support surface depend on the structure of support and that there is an inductive effect of support on the structure of the Eu2O3.
文摘A series of alumina samples were prepared using β-cyclodextrin as the non-surfactant template. These samples were characterized by XRD, BET and TEM. The results showed that the alumina samples prepared using β-cyclodextrin template had the higher surface areas （124-484 m^2/g）, larger pore volumes （0.7-1.27 mL/g） and more thermal stability than samples prepared without using β-cyclodextrin.
基金The work was financiaIly supported hy the NaturalScience Foundation of Hebei Province (No.94087) alld Pd-ucation Conlmittee of
文摘This work concerns with the high temperature deformation of internally oxidized Al2O3/Cu composites. The investigation revealed that dispersive alumina can obstruct dislocation sliding and define the subgrain size thereby improve significantly the strength of the materials at high temperature. The sliding of dislocations is a main deformation mechanism in the given temperature range. The sliding of grain boundary and diffusive creep play important roles at high temperature and low strain rate. The dispersoids can raise the recrystallization temperature to higher than 1223 K. Dynamic recovery is a main softening way under the experimental conditions. Higher deformation rate and lower deformation temperature imply a higher flow stress.
文摘An extended-life and ultra-low oxygen sensor has been fabricated by using polycrystalline Caβ″/β/α-Al2O3 as a solid electrolyte. Five reference electrodes CaO+O2, Caβ″/β/α-Al2O3 (powder)+O2,Cr+Cr2O3, Nb+NbO and Mo+MoO2 were tested in order to select a better reference electrode for this sensor. The limit of determining oxygen activity and the extended-life of the sensor were also tested in this study.
基金Supported by the National Natural Science Foundation of China(21276076)the Program for New Century Excellent Talents in University(NCET-13-0801)the"111"Project(B08021)
文摘A series of CuO/ZnO/Al_2O_3, CuO/ZnO/ZrO_2/Al_2O_3 and CuO/ZnO/CeO_2/Al_2O_3 catalysts were prepared by coprecipitation and characterized by N_2 adsorption, XRD, TPR, N_2O titration and HRTEM. The catalytic performances of these catalysts for the steam reforming of methanol were evaluated in a laboratory-scale fixed-bed reactor at 0.1 MPa and temperatures between 473 and 543 K. The results showed that the catalytic activity depended greatly on the catalyst reducibility and the specific surface area of Cu. An approximate linear correlation between the catalytic activity and the Cu surface area was found for all catalysts investigated in this study.Compared to CuO/ZnO/Al_2O_3, the ZrO_2-doped CuO/ZnO/Al_2O_3 exhibited higher activity and selectivity to CO,while the CeO_2-doped catalyst displayed lower activity and selectivity. Finally, an intrinsic kinetic study was carried out over a screened CuO/ZnO/CeO_2/Al_2O_3 catalyst in the absence of internal and external mass transfer effects. A good agreement was observed between the model-derived effluent concentrations of CO(CO_2) and the experimental data. The activation energies for the reactions of methanol-steam reforming, water-gas shift and methanol decomposition over CuO/ZnO/CeO_2/Al_2O_3 were 93.1, 85.1 and 116.5 k J·mol^(-1), respectively.
文摘Al2O hollow microspheres without noticeable aggregation have been prepared via a facile templating route with urea-mediated precipitation. The precipitation process is different from the surfaceadsorption method which is confined to the adsorption capacity of the template surface. TEM and SEM images indicate that most of these Al2O hollow microspheres with shell thickness of tens of nanometers and diameters in a narrow range of 100-200 nm consist of a shell of closely packed nanoparticles. The optimal amount of H2O and EtOH are 40 and 120 mL, respectively. The specific surface area, average pore size and pore volume of the Al2O hollow microspheres (calcinated at 600 °C) are 328.52 m2/g, 17.496 nm and 1.985 cm'/g, respectively. As the calcination temperature increases from 600 to 1 100 °C, the phase composition changes from y-Al2O3 to &-AI2O3 and a-Al2O3, and the surface morphology appears to change from a relatively rough surface formed by nanoparticles to a smooth surface formed by lamellar, which lead to the closure of pore channels and the reduction of specific surface.
文摘In this paper, study on the effect of preparation conditions of K2CO3/Al2O3 sorbent was done. Box-Behnken design was applied to study the influence of four parameters involve initial solution concentration, impregnation time and calcination step temperature and time. A quadratic model was used to correlate the sorbent capture capacity. The model was used to calculate the optimum conditions for preparing sorbent. From the analysis of variance (ANOVA), the most influential factor on each experimental design response was identified. The potassium-based sorbents used in this study were prepared by impregnating K2CO3 on Al2O3 support. The CO2 capture capacity was measured in the presence of H2O in a fixed-bed reactor at CO2 capture temperature of 60°C using breakthrough curves. The optimum sorbent prepared by this method showed CO2 capture capacity of 77.21 mg CO2/g sorbent. It was observed that the experimental values obtained were in good agreement with the values predicted by the model, with relatively small errors between the predicted and the actual values. The results obtained in this study can be used as basic data for study on design and operating condition optimization of CO2 capture process using these sorbents.
基金This work was supported by the National Natural Science Foundation of China,under grant No.59781004.
文摘The superplasticity of an Al203p/6061Al composite, fabricated by powder metallurgy techniques, has been investigated. Instead of any special thermomechanical processing or hot rolling, simple hot extrusion has been employed to obtain a fine grained structure before superplastic testing. Superplastic tensile tests were performed at strain rates ranging from 10-2 to 10-4 s-1 and at temperatures from 833 to 893 K. A maximum elongation of 200% was achieved at a temperature of 853 K and an initial strain rate of 1.67×103 s-1. The highest value obtained for the strain rate sensitivity index (in) was 0.32. Differential scanning calorimeter was used to ascertain the possibility of any partial melting in the vicinity of optimum superplastic temperature. These results suggested that no liquid phase existed where maximum elongation was achieved and deformation took place entirely in the solid state.
基金Project supported by the National Natural Science Foundation of China （Grant No 10174006）.
文摘Microwave characteristics of MgB2/Al2O3 superconducting thin films were investigated by coplanar resonator technique. The thin films studied have different grain sizes resulting from different growth techniques. The experimental results can be described very well by a grain-size model which combines coplanar resonator theory and Josephson junction network model. It was found that the penetration depth and surface resistance of thin films with smaller grain sizes are larger than those of thin films with larger grain sizes.
基金The National Basic Research Program of China (973 Program) (No. 2005CB221402)China National Petroleum Corporation
文摘The purpose of this study was to investigate the effect of preadsorbed CO at different temperatures, calcination temperatures, the combined influence of reduction temperature and time, and pretreatment using hydrogen or syngas as reduction agents on the F-T synthesis （FTS） activity and selectivity of Co/Al2O3 catalyst. The reactivity of the carbon species at higher preadsorption temperature with H2 in TPSR decreased, whereas the carbon-containing species showed higher reactivity over Co/Al2O3 catalyst with low calcination temperature. This agreed well with the order of catalytic activity for F-T synthesis on this catalyst. The catalytic activity of the catalyst varied with reduction temperature and time remarkably. CODEX optimization gave an optimum reduction temperature of 756 K and reduction time of 6.2 h and estimated C5＋ yield perfectly. The pretreatment of Co/Al2O3 catalyst with different reduction agents （hydrogen or syngas） showed important influences on the catalytic performance. A high CO conversion and C5＋ yield were obtained on the catalyst reduced by hydrogen, whereas methane selectivity on the catalyst reduced by syngas was much higher than that on the catalyst reduced by hydrogen.