To study the dynamic mechanical behavior of C 60 concrete at high temperatures,impact tests under different steady-state temperature fields( 100,200,300,400 and 500 ℃) were conducted under a variety of durations at...To study the dynamic mechanical behavior of C 60 concrete at high temperatures,impact tests under different steady-state temperature fields( 100,200,300,400 and 500 ℃) were conducted under a variety of durations at the corresponding constant high temperature,namely 0,30,60,90 and 120 min,employing split H opkinson pressure bar( SH PB) system. In addition,the impact tests were also conducted on the specimens cooled fromthe high temperature to the roomtemperature and the specimen under roomtemperature. Fromthe analysis,it is found that C 60 concrete has a time-dependent behavior under hightemperature environment. U nder 100,200,300,400 and 500 ℃ steady-state temperature fields respectively,as the duration at the corresponding constant high temperature increases,the dynamic compressive strength and the elastic modulus decrease but the peak strain generally ascends. After cooling to the roomtemperature,the dynamic compressive strength and the elastic modulus descend as well,but the peak strain increases first and then decreases slightly,when the duration increases. For specimens under and cooled fromthe high-temperature,as the temperature increases,the dynamic compressive strength and the peak strain raise first and then reduce gradually,and the dynamic compressive strength of specimen under high temperature is higher than that of the specimen cooled fromthe same high temperature.展开更多
The basic sintering characteristics of Yandi ore from Australia, including assimilation ability, liquid phase fluidity, self-strength of bonding phase, forming ability of silico ferrite of calcium and aluminum (SFCA...The basic sintering characteristics of Yandi ore from Australia, including assimilation ability, liquid phase fluidity, self-strength of bonding phase, forming ability of silico ferrite of calcium and aluminum (SFCA), and so on, were investigated in detail. Besides, the high temperature behavior and function of sintering were obtained. As a result, the techniques for ore-proportioning in sintering were obtained. The results show that Yandi ore possessing higher assimilation ability, better liquid phase fluidity, lower self-strength of bonding phase, and better forming ability of SFCA, should be mixed with iron ores whose properties are opposite to those of Yandi ore. In the optimization of sintering ore-proportioning, Yandi ore, whose price is relatively low, can be mixed as high as 40wt%.展开更多
During high speed machining in the field of manufacture,chip formation is a severe plastic deformation process including large strain,high strain rate and high temperature.And the strain rate in high speed cutting pro...During high speed machining in the field of manufacture,chip formation is a severe plastic deformation process including large strain,high strain rate and high temperature.And the strain rate in high speed cutting process can be achieved to 105 s^(-1).30CrMnSiNi2Asteel is a kind of important high-strength low-alloy structural steel with wide application range.Obtaining the dynamic mechanical properties of30CrMnSiNi2Aunder the conditions of high strain rate and high temperature is necessary to construct the constitutive relation model for high speed machining.The dynamic compressive mechanical properties of30CrMnSiNi2Asteel were studied using split Hopkinson pressure bar(SHPB)tests at 30-700°C and3000-10000s^(-1).The stress-strain curves of 30CrMnSiNi2Asteel at different temperatures and strain rates were investigated,and the strain hardening effect and temperature effect were discussed.Experimental results show that 30CrMnSiNi2Ahas obvious temperature sensitivity at 300°C.Moreover,the flow stress decreased significantly with the increase of temperature.The strain hardening effect of the material at high strain rate is not significant with the increase of strain.The strain rate hardening effect is obvious with increasing the temperature.According to the experimental results,the established Johnson-Cook(J-C)constitutive model of 30CrMnSiNi2Asteel could be used at high strain rate and high temperature.展开更多
Isothermal compression testing of Ti555211 titanium alloys was carried out at deformation temperatures from 750 to 950 °C in 50 °C intervals with a strain rate of0.001-1.000 s^(-1). The high-temperature de...Isothermal compression testing of Ti555211 titanium alloys was carried out at deformation temperatures from 750 to 950 °C in 50 °C intervals with a strain rate of0.001-1.000 s^(-1). The high-temperature deformation behavior of the Ti555211 alloy was characterized by analysis of stress-strain behavior, kinetics and processing maps. A constitutive equation was formulated to describe the flow stress as a function of deformation temperature and strain rate, and the calculated apparent activation energies are found to be 454.50 and 207.52 k J mol^(-1)in the a b-phase and b-phase regions, respectively. A processing map based on the Murty instability criterion was developed at a strain of 0.7. The maps exhibit two domains of peak efficiency from 750 to 950 °C. A *60 % peak efficiency occurs at 800-850 °C/0.001-0.010 s^(-1). The other peak efficiency of *60 % occurs at C950 °C/0.001-0.010 s^(-1), which can be considered to be the optimum condition for high-temperature working of this alloy.However, at strain rates of higher than 1.000 s^(-1)and deformation temperatures of 750 and 950 °C, clear process flow lines and bands of flow localization occur in the hightemperature deformation process, which should be avoided in Ti555211 alloy hot processing. The mechanism in stability domain and instability domain was also discussed.展开更多
文摘To study the dynamic mechanical behavior of C 60 concrete at high temperatures,impact tests under different steady-state temperature fields( 100,200,300,400 and 500 ℃) were conducted under a variety of durations at the corresponding constant high temperature,namely 0,30,60,90 and 120 min,employing split H opkinson pressure bar( SH PB) system. In addition,the impact tests were also conducted on the specimens cooled fromthe high temperature to the roomtemperature and the specimen under roomtemperature. Fromthe analysis,it is found that C 60 concrete has a time-dependent behavior under hightemperature environment. U nder 100,200,300,400 and 500 ℃ steady-state temperature fields respectively,as the duration at the corresponding constant high temperature increases,the dynamic compressive strength and the elastic modulus decrease but the peak strain generally ascends. After cooling to the roomtemperature,the dynamic compressive strength and the elastic modulus descend as well,but the peak strain increases first and then decreases slightly,when the duration increases. For specimens under and cooled fromthe high-temperature,as the temperature increases,the dynamic compressive strength and the peak strain raise first and then reduce gradually,and the dynamic compressive strength of specimen under high temperature is higher than that of the specimen cooled fromthe same high temperature.
文摘The basic sintering characteristics of Yandi ore from Australia, including assimilation ability, liquid phase fluidity, self-strength of bonding phase, forming ability of silico ferrite of calcium and aluminum (SFCA), and so on, were investigated in detail. Besides, the high temperature behavior and function of sintering were obtained. As a result, the techniques for ore-proportioning in sintering were obtained. The results show that Yandi ore possessing higher assimilation ability, better liquid phase fluidity, lower self-strength of bonding phase, and better forming ability of SFCA, should be mixed with iron ores whose properties are opposite to those of Yandi ore. In the optimization of sintering ore-proportioning, Yandi ore, whose price is relatively low, can be mixed as high as 40wt%.
基金supported by the National High Technology Research and Development Program of China(2014AA041504)the National Natural Science Foundation of China(51605161)
文摘During high speed machining in the field of manufacture,chip formation is a severe plastic deformation process including large strain,high strain rate and high temperature.And the strain rate in high speed cutting process can be achieved to 105 s^(-1).30CrMnSiNi2Asteel is a kind of important high-strength low-alloy structural steel with wide application range.Obtaining the dynamic mechanical properties of30CrMnSiNi2Aunder the conditions of high strain rate and high temperature is necessary to construct the constitutive relation model for high speed machining.The dynamic compressive mechanical properties of30CrMnSiNi2Asteel were studied using split Hopkinson pressure bar(SHPB)tests at 30-700°C and3000-10000s^(-1).The stress-strain curves of 30CrMnSiNi2Asteel at different temperatures and strain rates were investigated,and the strain hardening effect and temperature effect were discussed.Experimental results show that 30CrMnSiNi2Ahas obvious temperature sensitivity at 300°C.Moreover,the flow stress decreased significantly with the increase of temperature.The strain hardening effect of the material at high strain rate is not significant with the increase of strain.The strain rate hardening effect is obvious with increasing the temperature.According to the experimental results,the established Johnson-Cook(J-C)constitutive model of 30CrMnSiNi2Asteel could be used at high strain rate and high temperature.
基金financially supported by the Project of Introducing Talents of Discipline to Universities‘‘111’’Project(No.B08040)
文摘Isothermal compression testing of Ti555211 titanium alloys was carried out at deformation temperatures from 750 to 950 °C in 50 °C intervals with a strain rate of0.001-1.000 s^(-1). The high-temperature deformation behavior of the Ti555211 alloy was characterized by analysis of stress-strain behavior, kinetics and processing maps. A constitutive equation was formulated to describe the flow stress as a function of deformation temperature and strain rate, and the calculated apparent activation energies are found to be 454.50 and 207.52 k J mol^(-1)in the a b-phase and b-phase regions, respectively. A processing map based on the Murty instability criterion was developed at a strain of 0.7. The maps exhibit two domains of peak efficiency from 750 to 950 °C. A *60 % peak efficiency occurs at 800-850 °C/0.001-0.010 s^(-1). The other peak efficiency of *60 % occurs at C950 °C/0.001-0.010 s^(-1), which can be considered to be the optimum condition for high-temperature working of this alloy.However, at strain rates of higher than 1.000 s^(-1)and deformation temperatures of 750 and 950 °C, clear process flow lines and bands of flow localization occur in the hightemperature deformation process, which should be avoided in Ti555211 alloy hot processing. The mechanism in stability domain and instability domain was also discussed.