Properties of ferroelectric xBiInO3-（1-x）PbTiO3（xBI-（1-x）PT） thin films deposited on（101） SrRuO3/（200）Pt/（200） MgO substrates by rf magnetron sputtering method and effects of deposition conditions are inve...Properties of ferroelectric xBiInO3-（1-x）PbTiO3（xBI-（1-x）PT） thin films deposited on（101） SrRuO3/（200）Pt/（200） MgO substrates by rf magnetron sputtering method and effects of deposition conditions are investigated.The structures of the xBI-（1-x）PT films are characterized by x-ray diffraction and scanning electron microscopy.The results indicate that the thin films are grown with mainly（001） orientation. The chemical compositions of the films are analyzed by scanning electron probe and the results indicate that the loss phenomena of Pb and Bi elements depend on the pressure and temperature during the sputtering process.The sputtering parameters including target composition, substrate temperature, and gas pressure are adjusted to obtain optimum sputtering conditions. To decrease leakage currents,2 mol% La2 O3 is doped in the targets. The P-E hysteresis loops show that the optimized xBI-（1-x）PT（x = 0.24） film has high ferroelectricities with remnant polarization2 Pr = 80μC/cm2 and coercive electric field 2 EC = 300 kV/cm. The Curie temperature is about 640℃. The results show that the films have optimum performance and will have wide applications.展开更多
基金Supported by the National Natural Science Foundation of China under Grant No 11304160the Special Fund for Public Interest of China under Grant No 201510068,and the NUPTFC under Grant No NY215111
文摘Properties of ferroelectric xBiInO3-（1-x）PbTiO3（xBI-（1-x）PT） thin films deposited on（101） SrRuO3/（200）Pt/（200） MgO substrates by rf magnetron sputtering method and effects of deposition conditions are investigated.The structures of the xBI-（1-x）PT films are characterized by x-ray diffraction and scanning electron microscopy.The results indicate that the thin films are grown with mainly（001） orientation. The chemical compositions of the films are analyzed by scanning electron probe and the results indicate that the loss phenomena of Pb and Bi elements depend on the pressure and temperature during the sputtering process.The sputtering parameters including target composition, substrate temperature, and gas pressure are adjusted to obtain optimum sputtering conditions. To decrease leakage currents,2 mol% La2 O3 is doped in the targets. The P-E hysteresis loops show that the optimized xBI-（1-x）PT（x = 0.24） film has high ferroelectricities with remnant polarization2 Pr = 80μC/cm2 and coercive electric field 2 EC = 300 kV/cm. The Curie temperature is about 640℃. The results show that the films have optimum performance and will have wide applications.