Improving corrosion resistance of additively manufactured WE43 magnesium alloy by high temperature oxidation for biodegradable applications

Laser powder bed fusion(L-PBF)has been employed to additively manufacture WE43 magnesium(Mg)alloy biodegradable implants,but WE43 L-PBF samples exhibit excessively rapid corrosion.In this work,dense WE43 L-PBF samples were built with the relativity density reaching 99.9%.High temperature oxidation was performed on the L-PBF samples in circulating air via various heating temperatures and holding durations.The oxidation and diffusion at the elevated temperature generated a gradient structure composed of an oxide layer at the surface,a transition layer in the middle and the matrix.The oxide layer consisted of rare earth(RE)oxides,and became dense and thick with increasing the holding duration.The matrix was composed ofα-Mg,RE oxides and Mg_(24)RE_(5) precipitates.The precipitates almost disappeared in the transition layer.Enhanced passivation effect was observed in the samples treated by a suitable high temperature oxidation.The original L-PBF samples lost 40%weight after 3-day immersion in Hank’s solution,and broke into fragments after 7-day immersion.The casted and solution treated samples lost roughly half of the weight after 28-day immersion.The high temperature oxidation samples,which were heated at 525℃ for 8 h,kept the structural integrity,and lost only 6.88%weight after 28-day immersion.The substantially improved corrosion resistance was contributed to the gradient structure at the surface.On one hand,the outmost dense layer of RE oxides isolated the corrosive medium;on the other hand,the transition layer considerably inhibited the corrosion owing to the lack of precipitates.Overall,high temperature oxidation provides an efficient,economic and safe approach to inhibit the corrosion of WE43 L-PBF samples,and has promising prospects for future clinical applications.

Effect of Rare Earth Doping on the Tensile Properties of High Temperature Oxidation Coating

The failure process was characterized by complex diffusion of elements in the bonding layer,TGO growth and growth stress inside the coating.We studied the aluminum migration phenomenon of NiCoCrAlY and NiCoCrAlYHf coatings under high temperature oxidation,TGO growth characteristics,the microstructure and composition of the bonding layer,and integrates them into the description of the surface strain under coating tension.The experimental results show that the TGO growth rate of NiCoCrAIYHf coating is lower than that of NiCoCrAIY coating,and the formed TGO is thinner.After high temperature oxidation,the cracking time of NiCoCrAIY coating is advanced,while the cracking time of rare earth doped coating is delayed.The addition of rare earth elements can effectively inhibit the generation of spinel phase,improve the fracture toughness of TGO,refine the grains in the bonding layer,and increase the grain boundary strengthening by 29.1 MPa which is consistent with the experimental value.Therefore,the yield strength of the doped coating is improved and the crack time of the coating is delayed.

Fretting wear and friction oxidation behavior of 0Cr20Ni32AlTi alloy at high temperature

The fretting wear behavior of 0Cr20Ni32AlTi alloy was investigated with crossed cylinder contact under 80 N at 300 and 400 °C.Wear scar and debris were analyzed systematically by scanning electron microscopy and X-ray photoelectron spectroscopy.The results show that the friction logs are mixed fretting regime and gross slip regime with the magnitudes of displacement of 10 and 20 μm,respectively.Severe wear and friction oxidation occur on the material surface.A large number of granular debris produced in the fretting process can be easily congregated and adhered at the contact zone after repeated crushes.The resultant of friction oxidation is mainly composed of Fe3O4,Fe2O3,Cr2O3 and NiO.Temperature and friction are the major factors affecting the oxidation reaction rate.The fretting friction effect can enhance the oxidation reaction activity of surface atoms of 0Cr20Ni32AlTi alloy and reduce the oxidation activation energy.As result,the oxidation reaction rate is accelerated.

High temperature oxidation resistance and microstructure change of aluminized coating on copper substrate

The outermost coating with single phase Ni2Al3 was obtained on copper surface by electrodepositing nickel followed by slurry pack aluminizing at 800 °C for 12 h. The oxidation resistance and microstructure of the coating oxidized in ambient air at 1000 °C for 25-250 h were investigated using SEM, X-ray diffraction and optical microscope methods. The results show that the copper with single phase Ni2Al3 coating possesses the best high temperature oxidation resistance, and the mass gain of the coating is 1/15 that of pure copper and 1/2 that of nickel coating, respectively. The specimen surface after being oxidized for 25 h still comprises Ni2Al3 phase. However, when the time of oxidizing treatment increases to 50 h, the Ni Al phase is formed. It is also found that the Ni2Al3 phase completely turns into Ni Al phase after oxidizing treatment for 100 h and above. The Ni Al coating shows excellent high temperature oxidation resistance when oxidation time is 250 h.

Microstructure and high temperature oxidation resistance of Si-Y co-deposition coatings prepared on TiAl alloy by pack cementation process

In order to improve the high temperature oxidation resistance of TiAl alloy, Y modified silicide coatings were prepared by pack cementation process at 1030, 1080 and 1130 °C, respectively, for 5 h. The microstructures, phase constitutions and oxidation behavior of these coatings were studied. The results show that the coating prepared by co-depositing Si?Y at 1080 °C for 5 h has a multiple layer structure: a superficial zone consisting of Al-rich (Ti,Nb)5Si4 and (Ti,Nb)5Si3, an out layer consisting of (Ti,Nb)Si2, a middle layer consisting of (Ti,Nb)5Si4 and (Ti,Nb)5Si3, and aγ-TiAl inner layer. Co-deposition temperature imposes strong influences on the coating structure. The coating prepared by Si?Y co-depositing at 1080 °C for 5 h shows relatively good oxidation resistance at 1000 °C in air, and the oxidation rate constant of the coating is about two orders of magnitude lower than that of the bare TiAl alloy.

High temperature oxidation behavior of Ti(Al,Si)_3 diffusion coating on γ-TiAl by cold spray

A Ti(Al,Si)3 diffusion coating was prepared on γ-TiAl alloy by cold sprayed Al?20Si alloy coating, followed by a heat-treatment. The isothermal and cyclic oxidation tests were conducted at 900 °C for 1000 h and 120 cycles to check the oxidation resistance of the coating. The microstructure and phase transformation of the coating before and after the oxidation were studied by SEM, XRD and EPMA. The results indicate that the diffusion coating shows good oxidation resistance. The mass gain of the diffusion coating is only a quarter of that of bare alloy. After oxidation, the diffusion coating is degraded into three layers: an inner TiAl2 layer, a two-phase intermediate layer composed of a Ti(Al,Si)3 matrix and Si-rich precipitates, and a porous layer because of the inter-diffusion between the coating and substrate.

High temperature oxidation behavior of directionally solidified NiAl-31Cr-2.9Mo-0.1Hf-0.05Ho eutectic alloy

The isothermal oxidation behavior of NiAl-31Cr-2.9Mo-0.1Hf-0.05Ho directional eutectic alloy was investigated with the help of scanning electron microscopy and X-ray diffraction.The results revealed that a continuous Al2O3 scale was formed and owned excellent oxidation resistance in the temperature range of 900-1100°C.When the temperature was up to 1150°C,the continuous Al2O3 oxide film ruptured.Trace rare earth element Ho distributed uniformly in the alloy and relatively high level of Al in Cr（Mo）phase are beneficial to the formation of continuous and compact Al2O3 scale.During the oxidation,a phase transformation fromθ-Al2O3 toα-Al2O3 existed on the surface of oxidation film.It resulted in the abnormal oxidation mass gain happening when the alloy was oxidized at 1000°C or 1050°C.

Effects of Al and Mo on high temperature oxidation behavior of refractory high entropy alloys

Refractory high entropy alloys have superior mechanical properties at high temperatures, and the oxidation behavior of these alloys is very important. The present work investigated the high temperature oxidation behavior of three alloys with compositions of TiNbTa0.5Zr, TiNbTa0.5ZrAl and TiNbTa0.5ZrAlMo0.5, and the effects of alloying elements were discussed. Results indicated that the oxidation rates of the TiNbTa0.5Zr and TiNbTa0.5ZrAl alloys are controlled by diffusion, and obey the exponential rule. However, the oxidation rate of the TiNbTa0.5ZrAlMo0.5 alloy is controlled by interface reaction, and obeys the linear rule. The addition of Al leads to a better oxidation resistance by forming a protective oxide scale. However, the protection of Al-rich scale is weakened by the addition of Mo. Extensive pores and cracks occur in the oxide scale of the TiNbTa0.5ZrAlMo0.5 alloy, resulting in a significant decrease in oxidation resistance.

Comparative Studies on Low Noise Greases Operating under High Temperature Oxidation Conditions

Oxidation induction time(OIT) testing by differential scanning calorimetry(DSC) was used to evaluate the oxidation resistance of lubricating greases. Under the high temperature condition, bearing noise was detected when grease passed the initial stable stage of oxidation. The chemical and physical structure of grease samples before and after high temperature oxidation were also analyzed by FT-IR spectrometry and scanning electron microscopy(SEM), then the effects of oxidation at high temperature on bearing noise were investigated. It is found out that for lithium greases, oxidation of base oil and thickener is the main reason responsible for the increasing bearing noise. As regards the polyurea greases, the change of fiber microstructure at high temperature is the main reason for the increasing bearing noise.

Effect of Yttrium on High Temperature Oxidation Resistance ofa Directionally Solidified Superalloy

The effect of rare earth element yttrium on the high temperature oxidation resistance of a directionally solidified Ni-base superalloy was studied with scanning electron microscopy(SEM), energy dispersive spectrum(EDS)and X-ray diffraction(XRD)techniques. The results show that the oxidation resistance of the alloy is substantially improved by adding proper amount of yttrium.

HIGH-TEMPERATURE OXIDATION OF FGH96 P/M SUPERALLOY

High temperature oxidation behaviors of FGH96 P/M superaUoy have been studied in air at temperatures ranging from 600 to 1000℃. By means of isothermal oxidation testing, X-ray diffraction, SEM （scanning electron microscopy）, and EDS （energy dispersive X-ray spectroscopy） analyses, the oxidation kinetics as well as the composition and morphology of scales were investigated. Thermodynamic calculations were used to explain the oxidation mechanism. The results showed that as the oxidation temperature increased, the oxidation rate, the scale thickness, and scale spallation increased. FGH96 P/M superalloy exhibits good oxidation resistance at temperature below 800℃. The oxidation kinetics follows an approximately parabolic rate law, and the oxide layer was mainly composed of Cr2O3 TiO2 and a little amount of NiCr2O4. The oxidation is controlled by the transmission of chromium. titanium, and oxygen through the oxide scale.

Oxidation behaviors of wrought nickel-based superalloys in various high temperature environments

Oxidation characteristics of Alloy 617 and Haynes 230 at 900 oC in simulated helium environment,hot steam environment containing H2 as well as in air and pure helium conditions were investigated.Compared to air condition,the oxidation rate of Alloy 617 was not significantly affected in helium and hot steam environments,while Haynes 230 showed lower oxidation rate in helium environment.On the other hand,the oxide morphology and structure of Alloy 617 were strongly affected by the environments,but those of Haynes 230 were less dependent on the environments.For Haynes 230,a Cr2O3 inner layer and a protective MnCr2O4 outer layer were formed in all environments,which contributed to the better oxidation resistance.As the mechanical properties,such as creep and tensile properties,were significantly affected by the oxidation behaviors,surface treatment methods to enhance oxidation resistance of these alloys should be developed.

Protective Effect of the Sputtered TiAlCrAg Coating on the High-Temperature Oxidation and Hot Corrosion Resistance of Ti-Al-Nb Alloy

The effect of a sputtered Ti-48AI-8Cr-2Ag (at. pct) coating on the oxidation resistance of the cast Ti-46.5AI-5Nb (at. pct) alloy was investigated in air at 1000-1100℃. Hot corrosion in molten 75 wt pct Na2SO4+25 wt pct K2SO4 was investigated at 900℃. The scale on the cast TiAINb tends to spall in air, while the scale on coating is very adherent. The sputtered Ti-48AI-8Cr-2Ag coating remarkably improved high temperature oxidation resistance of the cast Ti-46.5AI-5Nb alloy because of the formation of an adherent Al2O3 scale. Due to the inward diffusion of Cr, Kirkendall voids were found at the coating/substrate interface. TiAICrAg coating provided excellent hot corrosion resistance for TiAINb alloy in molten 75 wt pct Na2SO4+25 wt pct K2S04 at 900℃ due to the formation of a continuous Al_2O_3 scale.

High Temperature Oxidation Behavior of NiCrAlY Coating by Arc Ion Plating

A NiCrAlY coating was prepared on the cast Ni-base superalloy K17 using arc ion plating. The coating was uniform, dense and well adhesive to the substrate. The oxidation kinetic curves of the alloy K17 and the coating were obtained. The results indicated that the oxidation resistance of the alloy K17 was evidently improved with NiCrAlY coatings at 900∼1100°C. As oxidation temperature rising, the interdiffusion between the coatings and substrates was enhanced. Ti atoms diffused from the substrate to the surface of coating to form the oxide, which was one of the reasons for the decrement of oxidation resistance. The oxidation resistance of NiCrAlY coating was decreased due to the spalling of pieces of oxide.

Interfacial Behavior of Sulfur and Yttrium in Yttrium Modified Ni _3Al Based Alloy IC6 during High Temperature Oxidation Process

The interfacial behavior of sulfur and yttrium in the yttrium modified Ni 3Al based alloy IC6 during oxidation at 1100 ℃ was analyzed by X ray line scan of electron probe microstructural analysis(EPMA). The results show that the migration and segregation of sulfur to the interface between oxide scale and the substrate at high temperature is retarded owing to the presence of yttrium. This is attributed to the desulfurization by yttrium in the melt and the trapping of sulfur by yttrium rich phases during oxidation, which leads to improving the coherence between oxide scale and substrate. Another reason of increasing the high temperature oxidation resistance of alloy IC6 by the addition of yttrium is that yttrium migrates to the grain boundaries of oxides during oxidation and hence improve their strength. This results in the transformation of the oxide scale spallation cracks from intergranular cracks for alloy without yttrium to transgranular ones for yttrium modified alloy.

Tribological property and high temperature oxidation behavior of Ni-based alloy

Ni-Cr based alloys were prepared by hot-pressing the mixture of strengthening phases Mo, Al, Ti, and lubricant phase MoS2. The hardness, tribological properties as well as the high temperature oxidation properties were evaluated, The results show that the strengthening phases can improve the mechanical properties of Ni-Cr based alloy obviously, and the wear and friction properties of Ni-based alloy with strengthening phase can be improved. Its friction coefficient and wear rate rubbed with Al2O3 ceramic disk are about 0.4 and 10 -14m3/（N·m）, respectively, and the oxidation process is mainly affected by Cr2O3.

Oxidation Behavior of Pd-Modified Aluminide Coating at High Temperature

(Ni,Pd)AI coating, prepared by low pressure pack cementation on the Ni-base superalloy M38 where Pd-20 wt pct Ni alloy was predeposited, consists of a single β-(Ni,Pd)AI phase. The initial isothermal oxidation behavior of (Ni,Pd)AI coating was investigated by TGA, XRD, SEM/EDS at 800-1100℃. Results show that oxidation kinetics accord preferably with parabolic law at 800, 900 and 1100℃, but not at 1000℃. θ-AI203 was observed at 800-1100℃. It is found that Pd plays an important role in accelerating the diffusion of Ti from the substrate to the coating surface in the aluminide coating.

Evaluation of Oxidation of Ti-Al and Ti-Al-Cr Coatings Arc-ion Plated on Ti-60 High-temperature Titanium Alloy

High-temperature titanium alloy for aeroengine compressor applications suffers from high-temperature oxidation and environmental corrosion, which prohibits long-term service of this kind alloy at temperatures above 600℃. In an attempt to tackle this problem, Ti-48Al （at. pct） and Ti-48Al-12Cr （at. pct） protective coatings were plated on the substrate of alloy Ti-60 by arc ion plating （ALP） method. Isothermal and cyclic oxidation tests were performed in static air at elevated temperatures. Phase composition, morphology of the coatings and distribution of elements were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and energy dispersive X-ray analysis （EDX）. The results showed that the Ti-48Al coating exhibited good isothermal oxidation resistance during exposure at 800℃, but poorer resistance against oxidation at 900℃. By contrast Ti-48Al-12Cr coating demonstrated excellent isothermal oxidation resistance at both temperatures. Cyclic oxidation tests performed at 800℃ indicated that resistance and no spallation of coatings was observed. But both coatings demonstrated good cyclic oxidation at 900℃ only Ti-48Al-12Cr coating demonstrated excellent cyclic oxidation resistance.

High temperature oxidation behavior of high speed steel for hot rolls material

The oxidation characteristics of high speed steel (HSS) were studied at 500 to 800°C. The non-isothermal oxidation and isothermal oxidation (500, 575, 650, 725, 800°C) of HSS were investigated by thermo-gravimetric analysis (TGA). The microstruc- ture, morphology and oxide scale thickness of the isothermal oxidation samples were analyzed by optical microscope (OM), electron probe micro analyzer (EPMA), X-ray diffraction spectrum (XRD) and scanning electron microscope (SEM). The results indicate that the oxidation rate of HSS is very slow at 500 to 650°C, increasing gradually at 650 to 750°C, and drastically at 750 to 800°C, be- cause the phase transformation happens at about 750°C.

High-temperature oxidation behavior of CeO_2-SiO_2/Ni-W-P composites

Ni-W-P matrix composites containing CeO2 and SiO2 nano-particles were prepared on common carbon steel surface by means of pulse electrodeposition,and the high-temperature oxidation behavior was investigated.The results show that when the oxidation time is controlled in 1 h,oxidation kinetics curve between oxidation mass gain rate and oxidation temperature of CeO2-SiO2/Ni-W-P composites accords with the index increasing law.When the oxidation temperature is controlled at 300℃,the kinetics curve between oxidation mass gain rate and oxidation time accords with the linear increasing law.The composites as-deposited are in the amorphous state and turn into the crystal state at 400℃.The microstructures of oxidation film on the composites will change from the compact state to the loose state with increasing oxidation temperature to 800℃.They are still continuous and compact,and there are no crackle,strip and falling-out.CeO2 and SiO2 nano-particles co-deposited into Ni-W-P alloy can improve the high-temperature oxidation resistance.