The high-temperature friction and wear properties of TiAl alloys and Ti2AlN/TiAl composites (TTC) in contact with nickel-based superalloy were studied. The results showed that, at 800 and 1 000 ℃, the coefficient o...The high-temperature friction and wear properties of TiAl alloys and Ti2AlN/TiAl composites (TTC) in contact with nickel-based superalloy were studied. The results showed that, at 800 and 1 000 ℃, the coefficient of the friction (COF) decreased with the increase of sliding velocity and the wear loss of the TTC decreased with the increase of volume fraction of Ti2AlN. The wear mechanisms of the pairs are adhesive wear and the wear debris mainly comes from the contacting nickel-based superalloy. The intergranular fracture and the cracking of the phase boundary in the lamellar structure are the wear mode of TiAl alloy. The wear mode of TTC is phase boundary fracture and adhesive spalling. The abrasive resistance of TTC is slightly higher than that of TiAl alloy.展开更多
Ni-Cr based alloys were prepared by hot-pressing the mixture of strengthening phases Mo, Al, Ti, and lubricant phase MoS2. The hardness, tribological properties as well as the high temperature oxidation properties wer...Ni-Cr based alloys were prepared by hot-pressing the mixture of strengthening phases Mo, Al, Ti, and lubricant phase MoS2. The hardness, tribological properties as well as the high temperature oxidation properties were evaluated, The results show that the strengthening phases can improve the mechanical properties of Ni-Cr based alloy obviously, and the wear and friction properties of Ni-based alloy with strengthening phase can be improved. Its friction coefficient and wear rate rubbed with Al2O3 ceramic disk are about 0.4 and 10 -14m3/(N·m), respectively, and the oxidation process is mainly affected by Cr2O3.展开更多
In this work,the high temperature friction mechanism of the tetrahedral amorphous carbon(ta-C)film was elucidated.The multilayer ta-C film with alternating hard and soft sub-layers exhibited a low friction coefficient...In this work,the high temperature friction mechanism of the tetrahedral amorphous carbon(ta-C)film was elucidated.The multilayer ta-C film with alternating hard and soft sub-layers exhibited a low friction coefficient of 0.14 at 400℃ before a sudden failure occurred at 4600 cycles.The wear failure was attributed to the gradual consumption of the ta-C film at the contact region.The design of a hard or soft top layer effectively regulated the high temperature friction properties of the multilayer ta-C.The addition of a hard top layer contributed to a low friction coefficient(0.11)and a minor wear rate(4.0×10^(-7)mm^(3)/(N m)),while a soft top layer deteriorated the lubrication effect.It was proposed that the passivation of dangling bonds at the sliding interface dominated the low-friction mechanism of the ta-C film at high temperature,while the friction induced graphitization and the formation of sp^(2)-rich carbonaceous transfer layer triggered C-C inter-film bonding,resulting in serious adhesion force and lubrication failure.Moreover,the multilayer ta-C film with hard top layer obtained excellent friction performance within 500℃,while the high temperature induced oxidation and volatilization of carbon atoms led to the wear failure at 600℃.展开更多
The in-situ formation of oxides on alloy surface induced by high temperature can effectively reduce wear and resist oxidation.In consideration of the solid solution strengthening effect and great oxidation resistance ...The in-situ formation of oxides on alloy surface induced by high temperature can effectively reduce wear and resist oxidation.In consideration of the solid solution strengthening effect and great oxidation resistance of additional elements at elevated temperature,the NiCrWMoCuCBFe coating was prepared by high velocity oxygen flame(HVOF)spraying technology,and its tribological behavior was scrutinized from 25 to 800°C.By means of high temperature Vickers hardness tester and high temperature X-ray diffractometer,the mechanical properties and microstructures of NiCrWMoCuCBFe coating were measured.And the effect of the mechanical properties and microstructures of the coating on tribological performance was discussed in detail.The results showed both its friction coefficient(0.37)and wear rate(5.067×10^(−6)mm^(3)·N^(−1)·m^(−1))at 800℃ were the lowest,which was mainly related to the formation of“glaze”layer on the coating surface at high temperature.The glaze layer consisted of two parts,which were NiCr_(2)O_(4)oxide film with the ability of interlaminar slip formed in the outer layer and nano-grains existed in the inner layer.Worth mentioning,these nano-grains provided bearing capability while the oxide film was vital to reduce wear rate and friction coefficient.As the ambient temperature increased,many hard oxides were produced on the wear scars,including NiO,Cr_(2)O_(3),MoO_(3),and Mo_(2)C.They can improve tribological and mechanical properties of NiCrWMoCuCBFe coating at a wide temperature range.展开更多
文摘The high-temperature friction and wear properties of TiAl alloys and Ti2AlN/TiAl composites (TTC) in contact with nickel-based superalloy were studied. The results showed that, at 800 and 1 000 ℃, the coefficient of the friction (COF) decreased with the increase of sliding velocity and the wear loss of the TTC decreased with the increase of volume fraction of Ti2AlN. The wear mechanisms of the pairs are adhesive wear and the wear debris mainly comes from the contacting nickel-based superalloy. The intergranular fracture and the cracking of the phase boundary in the lamellar structure are the wear mode of TiAl alloy. The wear mode of TTC is phase boundary fracture and adhesive spalling. The abrasive resistance of TTC is slightly higher than that of TiAl alloy.
文摘Ni-Cr based alloys were prepared by hot-pressing the mixture of strengthening phases Mo, Al, Ti, and lubricant phase MoS2. The hardness, tribological properties as well as the high temperature oxidation properties were evaluated, The results show that the strengthening phases can improve the mechanical properties of Ni-Cr based alloy obviously, and the wear and friction properties of Ni-based alloy with strengthening phase can be improved. Its friction coefficient and wear rate rubbed with Al2O3 ceramic disk are about 0.4 and 10 -14m3/(N·m), respectively, and the oxidation process is mainly affected by Cr2O3.
基金funded by The National Science Fund for Distinguished Young Scholars of China(No.52025014)National Science and Technology Major Project(No.2017-VII-0012-0108)+2 种基金K.C.Wong Education Foundation(No.GJTD-2019-13)CAS Interdisciplinary Innovation Team(No.292020000008)Ningbo Science and Technology Innovation Project(No.2018B10012)。
文摘In this work,the high temperature friction mechanism of the tetrahedral amorphous carbon(ta-C)film was elucidated.The multilayer ta-C film with alternating hard and soft sub-layers exhibited a low friction coefficient of 0.14 at 400℃ before a sudden failure occurred at 4600 cycles.The wear failure was attributed to the gradual consumption of the ta-C film at the contact region.The design of a hard or soft top layer effectively regulated the high temperature friction properties of the multilayer ta-C.The addition of a hard top layer contributed to a low friction coefficient(0.11)and a minor wear rate(4.0×10^(-7)mm^(3)/(N m)),while a soft top layer deteriorated the lubrication effect.It was proposed that the passivation of dangling bonds at the sliding interface dominated the low-friction mechanism of the ta-C film at high temperature,while the friction induced graphitization and the formation of sp^(2)-rich carbonaceous transfer layer triggered C-C inter-film bonding,resulting in serious adhesion force and lubrication failure.Moreover,the multilayer ta-C film with hard top layer obtained excellent friction performance within 500℃,while the high temperature induced oxidation and volatilization of carbon atoms led to the wear failure at 600℃.
基金This work was supported by the National Natural Science Foundation of China(No.51771214)the Youth Innovation Promotion Association of Chinese Academy of Sciences(No.2014378).
文摘The in-situ formation of oxides on alloy surface induced by high temperature can effectively reduce wear and resist oxidation.In consideration of the solid solution strengthening effect and great oxidation resistance of additional elements at elevated temperature,the NiCrWMoCuCBFe coating was prepared by high velocity oxygen flame(HVOF)spraying technology,and its tribological behavior was scrutinized from 25 to 800°C.By means of high temperature Vickers hardness tester and high temperature X-ray diffractometer,the mechanical properties and microstructures of NiCrWMoCuCBFe coating were measured.And the effect of the mechanical properties and microstructures of the coating on tribological performance was discussed in detail.The results showed both its friction coefficient(0.37)and wear rate(5.067×10^(−6)mm^(3)·N^(−1)·m^(−1))at 800℃ were the lowest,which was mainly related to the formation of“glaze”layer on the coating surface at high temperature.The glaze layer consisted of two parts,which were NiCr_(2)O_(4)oxide film with the ability of interlaminar slip formed in the outer layer and nano-grains existed in the inner layer.Worth mentioning,these nano-grains provided bearing capability while the oxide film was vital to reduce wear rate and friction coefficient.As the ambient temperature increased,many hard oxides were produced on the wear scars,including NiO,Cr_(2)O_(3),MoO_(3),and Mo_(2)C.They can improve tribological and mechanical properties of NiCrWMoCuCBFe coating at a wide temperature range.