Effect of low temperature aging on microstructure and mechanical properties of super-high strength aluminum alloy

The effects of heat treatment on the microstructure and mechanical properties of two alloys, namely Al-12.2%Zn-2.48%Cu-2.0%Mg-0.15%Zr-0.166%Ag（alloy 1）, and Al-9.99%Zn-1.72%Cu-2.5%Mg- 0.13%Zr （alloy 2） were investigated. The results show that low temperature aging after promotive solution treatment can increase elongation without the loss of strength for the studied alloys. The optimum aging treatment （T6） for alloy 1 and alloy 2 is 100℃/80h and 100℃/48h, respectively. Compared with other heat treatment alloys, alloy 1 and alloy 2 show super-high tensile strength up to 753MPa and 788MPa, remaining 9.3% and 9.7% elongation under T6 condition, respectively. During aging, trace addition of Ag enhances the formations of GP zone and metastable phase, and stabilizes GP zone and metastable phase to a higher temperature. Trace addition of Ag prolongs the aging time of reaching the peak strength and delays over-aging condition of the alloy. However, trace addition of Ag promotes the formation of coarse constituent in the alloy and consumes hardening alloying elements of Zn and Mg. Moreover, the addition of the transition element Zr in 7000 series super-high alloy forms incoherent Al3Zr dispersoid which can serve as nucleation sites for nonuniform precipitation of η phase during aging process. The higher the aging temperature, the greater the tendency for nonuniform precipitation of η phase.

Piezoelectric properties of low loss and high Curie temperature (Bi, La)FeO_3-Pb(Ti, Mn)O_3 ceramics with Mn doping

Piezoelectric ceramics of 0.6(Bi0.9La0.1)FeO3-0.4Pb(Ti1-xMnx)O3 (BLF-PTM) for x=0, 0.01, 0.02, and 0.03 were prepared by sol-gel process combined with a solid-state reaction method. The tan? for BLF-PTM of x=0.01 is just 0.006 at 1 kHz, drastically decreasing by using Mn dopants. The TC increases to 490 ℃ for BLF-PTM of x=0.02. Furthermore, Mn modification effectively enhances the poling state and the piezoelectric properties of BLF-PTM. The kp, Qm, d33, and g33 of 0.34, 403, and 124 pC1·N-1 and 37×10-3 Vm·N-1 are achieved for BLF-PTM of x=0.01. The results indicate that Mn modified BLF-PTM is a competitive high power and high temperature piezoelectric material with excellent piezoelectric properties.

Comparison of mechanical properties in high temperature and thermal treatment granite

Static mechanical experiments were carried out on granite after and under different temperatures using an electro-hydraulic and servo-controlled material testing machine with a heating device. Variations in obvious form, stress-strain curve, peak strength, peak strain and elastic modulus with temperature were analyzed and the essence of rock failure modes was explored. The results indicate that, compared with granite after the high temperature treatment, the brittle-ductile transition critical temperature is lower, the densification stage is longer, the elastic modulus is smaller and the damage is larger under high temperature. In addition, the peak stress is lower and the peak strain is greater, but both of them change more obviously with the increase of temperature compared with that of granite after the high temperature treatment. Furthermore, the failure modes of granite after the high temperature treatment and under high temperature show a remarkable difference. Below 100 ℃, the failure modes of granite under both conditions are the same, presenting splitting failure. However, after 100 ℃, the failure modes of granite after the high temperature treatment and under high temperature present splitting failure and shear failure, respectively.

Effect of temperature on dielectric property and microwave heating behavior of low grade Panzhihua ilmenite ore

The permittivity of low grade Panzhuhua ilmenite ore at 2.45 GHz in the temperatures from 20 ℃ up to 100 ℃ was measured using the technology of open-ended coaxial sensor combined with theoretical computation. The results show that both the real （ε′） and imaginary （ε′） part of complex permittivity （ε′-jε′） of the ilmenite significantly increase with temperature. The loss tangent （tanδ） is a quadratic function of temperature, and the penetration depth of ilmenite decreases with temperature increase from 20 ℃to 100 ℃ The increase of the sample temperature under microwave radiation displays a nonlinear relationship between the temperature （T） and microwave heating time （t）. The positive feedback interaction between complex permittivity and sample temperature amplifies the interaction between ilmenite and the microwave radiation. The optimum dimensions for uniform heat deposition vary from 10 cm to 5 cm （about two power penetration depths） in a sample being irradiated from both sides in a 2.45 GHz microwave field when temperature increases from room temperature to 100 ℃

High temperature mechanical properties of low carbon silicon-bearing steel by twin-roll strip casting

The tensile equipment of the advanced confocal scanning laser microscope （CSLM） was used to research the high temperature mechanical properties of low carbon silicon-bearing steel by twin-roll strip casting. The results show that, at the strain rate of 0. 000 5 s ^-1, the strip clearly shows signs of brittleness at around 600 ℃ and its plasticity falls considerably between 750 ℃ and 600 ℃. This is because during the transformation from austenite to ferrite, the low strength ferrite at the austenite grain boundaries greatly reduces the steel＇ s high temperature plasticity. The subsequent strip coiling process should be controlled at less than the brittle temperature of approximately 600 ℃, so cracks at the coiling stage can be prevented.

Mechanical properties of Mg-6Gd-1Y-0.5Zr alloy processed by low temperature thermo-mechanical treatment

An as-solution treated Mg-6Gd-1Y-0.4Zr alloy was processed by low temperature thermo-mechanical treatments （LT-TMT）, including cold tension with various strains followed by aging at 200 °C to peak hardness. The results show that the precipitation kinetics of the alloy experienced LT-TMT is greatly accelerated and the aging time to peak hardness is greatly decreased with increasing tensile strain. The tensile yield strength, ultimate tensile strength and elongation at room temperature of the alloy after cold tension with strain of 10% and peak aging at 200 °C are 251 MPa, 296 MPa and 8%, respectively, which are superior to the commercial heat-resistant WE54 alloy, although the latter has a higher rare earth element content.

Analysis on the Climatic Characteristics of High and Low Temperature in the East of Hexi Corridor in Recent 50 Years

[Objective] The research aimed to provide the certain theory basis for the accurate forecast and early warning of high and low temperature in the east of Hexi Corridor.[Method] Based on the high(the daily highest temperature ≥35 ℃) and low(the daily lowest temperature ≤-20 ℃) temperature data in five observatories in the east of Hexi Corridor during 1960-2009,the temporal and spatial distribution,intensity,continuity and circulation situation of high and low temperature were analyzed in detail by using the statistical method.[Result] The high temperature weather in the east of Hexi Corridor mainly happened in the edge of northeast desert,and the low temperature mainly happened in the mountain zone where the altitude was higher and the edge of north desert.As the climate became warm,the high temperature days showed the weak increase trend,and the intensity strengthened.The low temperature days showed the obvious decrease trend,and the intensity weakened.The high temperature weather mainly occurred in June,August,and the low temperature mainly occurred in January,February,December.The high and low temperature weather had the durative characteristic.The strong high and low temperature mainly occurred in the durative time of high and low temperature.The high temperature weather appeared in the zone where was controlled and affected by the subtropical high.The low temperature weather appeared in the zone where the strong cold air accumulated and invaded.[Conclusion] The research had the extremely important significance on servicing for the agriculture,preventing and reducing the natural disasters,promoting the local economic development.

Temperature dependence of mechanical properties and damage evolution of hot dry rocks under rapid cooling

Understanding the differences in mechanical properties and damage characteristics of granitoid under high temperatures is crucial for exploring deep geothermal resources.This study analyzes the evolution of the acoustic emission(AE)characteristics and mechanical parameters of granodiorite and granite after heating and water cooling by uniaxial compression and variable-angle shear tests under different temperature gradients.We identify their changes in mesostructure and mineral composition with electron probe microanalysis and scanning electron microscopy.Results show that these two hot dry rocks have similar diagenetic minerals and microstructure,but show significantly different mechanical and acoustic characteristics,and even opposing evolution trends in a certain temperature range.At the temperatures ranging from 100℃to 500℃,the compressive and shear mechanical properties of granodiorite switch repeatedly between weakening and strengthening,and those of granite show a continuous weakening trend.At 600℃,both rocks exhibit a deterioration of mechanical properties.The damage mode of granite is characterized by initiating at low stress,exponential evolutionary activity,and intensified energy release.In contrast,granodiorite exhibits the characteristics of initiating at high stress,volatile evolutionary activity,and intermittent energy release,due to its more stable microstructure and fewer thermal defects compared to granite.As the temperature increases,the initiation and propagation of secondary cracks in granodiorite are suppressed to a certain extent,and the seismicity and brittleness are enhanced.The subtle differences in grain size,microscopic heterogeneity,and mineral composition of the two hot dry rocks determine the different acoustic-mechanical characteristics under heating and cooling,and the evolution trends with temperature.These findings are of great significance for the scientific and efficient construction of rock mass engineering by rationally utilizing different rock strata properties.

Higher Grain-Filling Rate in Inferior Spikelets of Tolerant Rice Genotype Offset Grain Yield Loss under Post-Anthesis High Night Temperatures

Increased nighttime respiratory losses decrease the amount of photoassimilates available for plant growth and yield. We hypothesized that the increased respiratory carbon loss under high night temperatures(HNT) could be compensated for by increased photosynthesis during the day following HNT exposure. Two rice genotypes, Vandana(HNT-sensitive) and Nagina 22(HNT-tolerant), were exposed to HNT(4 ℃ above the control) from flowering to physiological maturity. They were assessed for alterations in the carbon balance of the source(flag leaf) and its subsequent impact on grain filling dynamics and the quality of spatially differentiated sinks(superior and inferior spikelets). Both genotypes exhibited significantly higher night respiration rates. However, only Nagina 22 compensated for the high respiration rates with an increased photosynthetic rate, resulting in a steady production of total dry matter under HNT. Nagina 22 also recorded a higher grain-filling rate, particularly at 5 and 10 d after flowering, with 1.5- and 4.0-fold increases in the translocation of ^(14)C sugars to the superior and inferior spikelets, respectively. The ratio of photosynthetic rate to respiratory rate on a leaf area basis was negatively correlated with spikelet sterility, resulting in a higher filled spikelet number and grain weight per plant, particularly for inferior grains in Nagina 22. Grain quality parameters such as head rice recovery, high-density grains, and gelatinization temperature were maintained in Nagina 22. An increase in the rheological properties of rice flour starch in Nagina 22 under HNT indicated the stability of starch and its ability to reorganize during the cooling process of product formation. Thus, our study showed that sink adjustments between superior and inferior spikelets favored the growth of inferior spikelets, which helped to offset the reduction in grain weight under HNT in the tolerant genotype Nagina 22.

Effects of low temperature on properties of structural steels

The experiments were carried out to measure the mechanical properties ofthree grades of structural steels (Q235A, 16Mn and Q390E steel) at low temperature. It was shownthat the strength of the steels increases while the plasticity and toughness decrease as temperaturedrops. In the transitional area the toughness drops rapidly with temperature. Among the threestructural steels, Q390E steel has the best toughness and the lowest sensitivity.

High Temperature Rheological Performance of Graphene Modified Rubber Asphalt

To elucidate the high temperature rheological capability of graphene modified rubber asphalt,three contents of graphene and crumb rubber were prepared by a combination of mechanical agitation and high speed shearing machine,then used dynamic shear rheological test(DSR)and multiple stress creep recovery(MSCR)tests to evaluate.The hardness and softening point with rotational viscosity of samples raised with the addition of graphene,especially the addition of 0.04%.Dynamic shear rheological test revealedthat the dynamic shear modulus G*,rutting factor G*/Sin δ,and zero shear viscosity(ZSV)of graphene-modified rubber asphalt were greatly influenced along with graphene-increased,on the contrary,phase angle δ which characterize the viscoelastic ratio of asphalt decreased.Multiple stress creep recovery(MSCR)tests showed that the graphene-enhanced rubber asphalt had high-temperature stability through non-recoverable creep compliance(Jnr).Based on these findings,graphene-modified rubber asphalt binders with the addition of 0.04% graphene had good viscoelastic properties as well as high temperature rutting resistance performance.In the meantime,G*/Sin δ,ZSV,and Jnr100,Jnr3200 have good correlation,which can reveal the excellent high-temperature stability performance of asphalt.

Effect of microstructure on the low temperature toughness of high strength pipeline steels

Microstructure observations and drop-weight tear test were performed to study the microstructures and mechanical properties of two kinds of industrial X70 and two kinds of industrial X80 grade pipeline steels. The effective grain size and the fraction of high angle grain boundaries in the pipeline steels were investigated by electron backscatter diffraction analysis. It is found that the low temperature toughness of the pipeline steels depends not only on the effective grain size, but also on other microstructural factors such as martensite-austenite （MA） constituents and precipitates. The morphology and size of MA constituents significantly affect the mechanical properties of the pipeline steels. Nubby MA constituents with large size have significant negative effects on the toughness, while smaller granular MA constituents have less harmful effects. Similarly, larger Ti-rich nitrides with sharp corners have a strongly negative effect on the toughness, while fine, spherical Nb-rich carbides have a less deleterious effect. The low temperature toughness of the steels is independent of the fraction of high angle grain boundaries.

Mechanical properties and fracture toughness of rail steels and thermite welds at low temperature

Brittle fracture occurs frequently in rails and thermite welded joints, which intimidates the security and reliability of railway ser- vice. Railways in cold regions, such as Qinghai-Tibet Railway, make the problem of brittle fi＇acture in rails even worse. A series of tests such as uniaxial tensile tests, Charpy impact tests, and three-point bending tests were carried out at low temperature to investigate the mechanical properties and fracture toughness of U71Mn and U75V rail steels and their thermite welds. Fracture micromechanisms were analyzed by scanning electron microscopy （SEM） on the fracture surfaces of the tested specimens. The ductility indices （percentage elongation aider frac- ture and percentage reduction of area） and the toughness indices （Charpy impact energy Ak and plane-strain fracture toughness Kic） of the two kinds of rail steels and the corresponding thermite welds all decrease as the temperature decreases. The thermite welds are more critical to fracture than the rail steel base metals, as indicated by a higher yield-to-ultimate ratio and a much lower Charpy impact energy. U71Mn rail steel is relatively higher in toughness than U75V, as demonstrated by larger Ak and Klc values. Therefore, U71Mn rail steel and the corresponding thermite weld are recommended in railway construction and maintenance in cold regions.

Microstructure of Surface Layer Formed at Low Temperature and High Carbon Concentration Carburizing with Rare Earth Element

A suitable carburized microstructure with fine granular dispersed carbides in hypereutectoid zone,ultra fine martensite in matrix and recrystallized austenite to be refined to the grain size of 12～14 has been obtained by a new process,which is a high carbon concentration carburizing with rare earth element at low temperature(860～880℃)in a discontinuous gas carburization furnace.There was not much difference for the microstructure in eutectic zone between this and conventional process.Forming mechanism of granular carbides has been also studied in this paper.

Numerical Simulation of High Temperature Air Combustion Flames Properties

High temperature air combustion (HTAC) is an attractive technology of saving energy and controlling environment. The mathematical models of turbulent jet flame under the highly preheated air combustion condition are conducted in the paper. The mixture fraction/probability density function model is employed. The results show that the maximum flame temperature is decreased, the temperature in the HTAC furnace is more uniform than that in the conventional furnace, and the NO x emission is low. The numerical results are partially validated by some experimental measurements.

Rheological properties of oil-based drilling fluids at high temperature and high pressure

The rheological properties of two kinds of oil-based drilling fluids with typically composition were studied at pressures up to 138 MPa and temperatures up to 204 ℃ using the RheoChan 7400 Rheometer.The experimental results show that the apparent viscosity,plastic viscosity and yield point decrease with the increase of temperature,and increase with the increase of pressure.The effect of pressure on the apparent viscosity,plastic viscosity and yield point is considerable at ambient temperature.However,this effect gradually reduces with the increase of temperature.The major factor influencing the rheological properties of oil-based drilling fluids is temperature instead of pressure in the deep sections of oil wells.On the basis of numerous experiments,the model for predict the apparent viscosity,plastic viscosity and yield point of oil-based drilling fluids at high temperature and pressure was established using the method of regressive analysis.It is confirmed that the calculated data are in good agreement with the measured data,and the correlation coefficients are more than 0.98.The model is convenient for use and suitable for the application in drilling operations.

Properties of failure mode and thermal damage for limestone at high temperature

The mechanical properties of limestone such as the stress-strain curve, the variable characteristics of peak strength and the modulus of elasticity of limestone were studied under the action of temperatures ranging from room temperature to 800 °C.Our results show that:1) the temperature has not clear effect on the mechanical properties of limestone from room temperature to 600 °C.However, the mechanical properties of limestone deteriorate rapidly when the temperature is above 600 °C.In this case, the peak stress and modulus of elasticity decrease rapidly.When the temperature reaches 800 °C, the entire process, showing the stress-strain curve is displayed indicating an obvious state of plastic-deformation;2) the failure mode of limestone shows the breakdown of tensile strength from room temperature to 600 °C, as well as the compress shearing damage over 600 °C;3) combining our test results with the concept of thermal damage, a thermal damage equation was derived.

High temperature mechanical behavior of low-pressure sand-cast Mg-Gd-Y-Zr magnesium alloy

The aim of this work is firstly to optimize T6 heat-treatment of low-pressure sand-cast Mg-10Gd-3Y-0.5Zr alloy,and then systematically investigate the mechanical behavior of the T6-treated alloy from room temperature to 300℃.It turned out that the optimum T6 heat-treatments for the tested alloy are 525℃×12 h+225℃×14 h and 525℃×12 h+250℃×12 h which integrated age-hardening and tensile properties into account,respectively.The strength of the T6-treated alloy indicates obvious anomalous temperature dependence from room temperature to 300℃,namely both ultimate tensile strength and yield strength of the tested alloy firstly increase with tensile temperature,and then decrease as temperature increases further.Elongation increased with temperature monotonously.The tensile fracture mode of the tested alloy changes from transgranular fracture to intergranular fracture with the increasing of test temperature.

ISOCHRONOUS STRESS-STRAIN CURVES OF LOW ALLOY STEEL CROSS-WELD-SPECIMEN AT HIGH TEMPERATURE

In this work, a parametric approach is presented and utilized to determine the creep properties of weldments; then the model of creep strain for cross weld specimen is given. On the basis of the experimental results, attempt has been made to establish equations of the isochronous stress-strain for weld joint that can predict the function of loading and service time in use of the creep data of base metal and weld metal.

High-temperature properties and microstructure of Mo microalloyed ultra-high-strength steel

The high-temperature mechanical properties and microstructure of forging billets of C-Si-Mn-Cr and C-Si-Mn-Cr-Mo ultra-high-strength cold-rolled steels（tensile strength≥1000 MPa,elongation≥10%） were studied.Through the comparison of reduction in area and hot deformation resistance at 600-1300°C,the Mo-containing steel was found to possess a higher strength and a better plasticity than the Mo-free one.The equilibrium phase diagram and atom fraction of Mo in different phases at different temperatures were calculated by Thermo-Calc software（TCW）.The results analyzed by using transmission electron microscopy and TCW show that precipitates in the Mo-containing steel are primarily M23C6,which promote pearlite formation.The experimental data also show that a lower ductility point existing in the Mo-free steel at 850°C is eliminated in the Mo-containing one.This is mainly due to the segregation of Mo at grain boundaries investigated by electron probe microanalysis（EPMA）,which improves the strength of grain boundaries.