Uniaxial tension tests and hole-expansion tests were carried out to determine the influence of silicon on the microstructures, mechanical properties, and stretch-flangeability of conventional dual-phase steels. Compar...Uniaxial tension tests and hole-expansion tests were carried out to determine the influence of silicon on the microstructures, mechanical properties, and stretch-flangeability of conventional dual-phase steels. Compared to 0.03wt% silicon, the addition of 1.08wt% silicon induced the formation of finer ferrite grains （6.8μm ） and a higher carbon content of martensite （Cm≈ 0.32wt%）. AS the silicon level increased, the initial strain-hardening rate （n value） and the uniform elongation increased, whereas the yield strength, yield ratio, and stretch-flangeability decreased. The microstructures were observed after hole-expansion tests. The results showed that low carbon content martensite （Cm ≈ 0.19wt%） can easily deform in coordination with ferrite. The relationship between the mechanical properties and stretch-flangeability indicated that the steel with large post-uniform elongation has good stretch-flangeability due to a closer plastic incom- patibility of the ferrite and martensite phases, which can effectively delay the production and decohesion of microvoids.展开更多
基金financially supported by the Fundamental Research Funds for the Central Universities of China (No. FRF-TP-12-046A)the Beijing Higher Education Young Elite Teacher Project (No. YETP0355)
文摘Uniaxial tension tests and hole-expansion tests were carried out to determine the influence of silicon on the microstructures, mechanical properties, and stretch-flangeability of conventional dual-phase steels. Compared to 0.03wt% silicon, the addition of 1.08wt% silicon induced the formation of finer ferrite grains （6.8μm ） and a higher carbon content of martensite （Cm≈ 0.32wt%）. AS the silicon level increased, the initial strain-hardening rate （n value） and the uniform elongation increased, whereas the yield strength, yield ratio, and stretch-flangeability decreased. The microstructures were observed after hole-expansion tests. The results showed that low carbon content martensite （Cm ≈ 0.19wt%） can easily deform in coordination with ferrite. The relationship between the mechanical properties and stretch-flangeability indicated that the steel with large post-uniform elongation has good stretch-flangeability due to a closer plastic incom- patibility of the ferrite and martensite phases, which can effectively delay the production and decohesion of microvoids.