The application of self-compacting recycled concrete can solve the problem of environmental pollution caused by construction waste but its mechanical properties have not been unified and need further study.The strengt...The application of self-compacting recycled concrete can solve the problem of environmental pollution caused by construction waste but its mechanical properties have not been unified and need further study.The strength of recycled concrete is unstable,and its performance still needs further study.The combination of fixed sand and stone volume method and free water cement ratio method is used to determine the mix ratio of self-compacting recycled concrete.24 sets of slump expansion tests and 24 sets of cube axial compression tests were carried out to study the effect of recycled aggregate replacement rate on the flow performance and axial compressive strength of self-compacting recycled concrete,and the performance conversion formula of self-compacting recycled concrete was given.The results show that with the increase of the regenerated coarse aggregate substitution rate,the fluidity and filling property of the self-compacting regenerated concrete mix decreased.The failure of self-compacting recycled concrete is mainly due to the failure of strength between old mortar and new mixture.As the substitution rate increases from 0 to 100%,the axial compressive strength decreases by 15.2%.展开更多
Recycled large aggregate self-compacting concrete (RLA-SCC) within multiple weak areas. These weak areas have poor resistance to chloride ion erosion, which affects the service life of RLA-SCC in the marine environmen...Recycled large aggregate self-compacting concrete (RLA-SCC) within multiple weak areas. These weak areas have poor resistance to chloride ion erosion, which affects the service life of RLA-SCC in the marine environment. A three-dimensional multi-phase mesoscopic numerical model of RLA-SCC was established to simulate the chloride ions transportation in concrete. Experiments of RLA-SCC immersing in chloride solution were carried out to verify the simulation results. The effects of recycled large aggregate (RLA) content and RLA particle size on the service life of concrete were explored. The results indicate that the mesoscopic numerical simulation results are in good agreement with the experimental results. At the same depth, the closer to the surface of the RLA, the greater the chloride ion concentration. The service life of RLA-SCC in marine environment decreases with the increase of RLA content. Compared with the service life of 20% content, the service life of 25% and 30% content decreased by 20% and 42% respectively. Increasing the particle size of RLA can effectively improve the service life of RLA-SCC in chloride environment. Compared with the service life of 50 mm particle size, the service life of 70 mm and 90 mm increased by 61% and 163%, respectively. .展开更多
The aim and scope of the present study were to determine the efficacy of UFFA in evaluating the workability,static and dynamic stabilization properties,retention period,and slump loss of SCC systems in their fresh sta...The aim and scope of the present study were to determine the efficacy of UFFA in evaluating the workability,static and dynamic stabilization properties,retention period,and slump loss of SCC systems in their fresh state,as well as their compressive strength at various ages.Microstructure(SEM and XRD)of blended SCC systems were studied.Also,the thermogravimetry behavior of blended SCC specimens were researched.According to the evaluated results,incorporating up to 20%UFFA into fresh concrete improved its performance due to its engineered fine particle size and spherical geometry,both of which contribute to the enhancement of characteristics.Blends of 25%and 30%of UFFA show effect on the water-binder ratio and chemical enhancer dosage,resulting in a loss of homogeneity in fresh SCC systems.The reduced particle size,increased amorphous content,and increased surface area all contribute to the pozzolanic reactivity of the early and later ages,resulting in denser packing and thus an increase in compressive strength.The experimental results indicate that UFFA enhances the properties of SCC in both its fresh and hardened states,which can be attributed to the particles’fineness and their relative effect on SCC.展开更多
To investigate the assumptions proposed in this paper,the evolution law governing the strength and expansion performance of MgO and nano-MgO micro-expansive concrete in the environment of mineral powder was firstly ob...To investigate the assumptions proposed in this paper,the evolution law governing the strength and expansion performance of MgO and nano-MgO micro-expansive concrete in the environment of mineral powder was firstly observed in this study.Secondly,SEM,XRD,and TG-DSC microscopic tests were conducted to reveal the effects of the active mineral-powder admixture on the hydration degree and expansion performance of MgO and nano-MgO in HPC.Our experimental results successfully verified our hypothesis,which indicated that the expansion performance of macro-MgO and nano-MgO was indeed depressed by the addition of active mineral power admixtures,even though the mechanical property of concrete composites was effectively improved.Furthermore,the hydration test also demonstrated the negative interference on the mineral powders,which was induced by the expansion agents.It is found the amounts of hydrates tend to decrease because the mineral powder ratio reaches and exceeds 40%.Moreover,it is also concluded the effect of expansion agents is governed by the alkalinity cement paste,especially for the nano-MgO.In other words,the expansion performance of nano-MgO will vary more obviously with the hydration process,than MgO.The results of this study provide that effective experimental and theoretical data support the hydration-inhibition mechanism of magnesium expansive agents.展开更多
By the addition of superplasticizer and air entraining agent,manufactured sand selfcompacting concrete(MS SCC)with slump flow varying from 500 to 700 mm and air content varying from 2.0%to 9.0%were prepared and the pu...By the addition of superplasticizer and air entraining agent,manufactured sand selfcompacting concrete(MS SCC)with slump flow varying from 500 to 700 mm and air content varying from 2.0%to 9.0%were prepared and the pumpability of MS SCC was studied by a sliding pipe rheometer(Sliper).According to the Kaplan’s model,the initial pump pressure and the pump resistance of MS SCC were obtained.Meanwhile,rheological properties including the yield stress and the plastic viscosity of MS SCC were measured by a rheometer.The experimental results show that the increase of slump flow contributes to a higher pumpability and a proper air content,i e,6%is beneficial for the pumpability of MS SCC.Due to the existence of stone powder and stronger angularity of MS,the initial pump pressure of MS SCC is only about 60%-88%that of river sand(RS)SCC with the same slump flow and air content,indicating that MS SCC possesses a higher pumpability than RS SCC.展开更多
This study focuses on the workability and compressive strength of ceramsite self-compacting concrete with fine aggregate partially substituted by steel slag sand(CSLSCC)to prevent the pollution of steel slag in the en...This study focuses on the workability and compressive strength of ceramsite self-compacting concrete with fine aggregate partially substituted by steel slag sand(CSLSCC)to prevent the pollution of steel slag in the environment.The SF,J-ring,visual stability index,and sieve analysis tests are primarily employed in this research to investigate the workability of freshly mixed self-compacting concrete containing steel slag at various steel slag sand replacement rates.The experiment results indicate that CSLSCC with the 20%volume percentage of steel slag(VPS)performs better workability,higher strength,and higher specific strength.The 7-day compressive strength of CSLSCC with the 0.4 of the water-binder ratio(W/B),decreases with the increase of steel slag content,while the 28-day compressive strength increases significantly.The ceramsite self-compacting concrete with good comprehensive performance can be obtained when the substitution rate of steel slag sand for fine aggregate is less than 20%(volume percentage).展开更多
Different rubber aggregates lead to changes in the effect of stress conditions on the mechanical behavior of concrete,and studies on the triaxial properties of self-compacting rubber concrete(SCRC)are rare.In this stu...Different rubber aggregates lead to changes in the effect of stress conditions on the mechanical behavior of concrete,and studies on the triaxial properties of self-compacting rubber concrete(SCRC)are rare.In this study,35 cylindrical specimens taking lateral stress and rubber type as variables were prepared to study the fresh properties and mechanical behaviors of SCRC under triaxial compression,where the rubber contains two types,i.e.,380μm rubber powder and 1–4 mm rubber particles,and four contents,i.e.,10%,20%and 30%.The test results demonstrated that SCRC exhibited a typical oblique shear failure mode under triaxial compression and had a more moderate descending branch compared with self-compacting concrete(SCC).The presence of lateral stress can significantly improve the compression properties,including initial elastic modulus,peak stress and peak strain,with an improvement range of 3%–73%for peak stress.While rubber aggregates mainly targeted the deformation abilities and toughness for improvement,and the peak strain improvement ranges were 0.1–3.1 times and 0.1–1.0 times for SCRC containing rubber powder and SCRC containing rubber particles,respectively,relative to SCC.At a high lateral stress of at least 12 MPa,the loss of strength due to the addition of rubber can be controlled within 10%,in which case the content of rubber powder and rubber particles was recommended to be at most 20%and 30%,respectively.Based on the Mohr-Coulomb theory,the failure criteria of SCRC with different rubber types were established.For analysis and design purposes,an empirical model was proposed to predict the stressstrain behavior under triaxial compression,considering the influence of different rubber content and lateral stress.The results obtained in this study can provide a valuable reference for the design and application of self-compacting rubberized concrete in practical projects,especially those involving three-way compression states and requiring high-quality deformation and energy dissipation.展开更多
This research was carried out to evaluate the relationship between the incorporation of calcite precipitation bacteria,sporosarcina pasteurii using calcium lactate as nutrient source and the properties of calcined cla...This research was carried out to evaluate the relationship between the incorporation of calcite precipitation bacteria,sporosarcina pasteurii using calcium lactate as nutrient source and the properties of calcined clay and limestone powder blended self-compacting concrete.Ten mixes were designed and designated S0 to S9 with S0 the control(without bacteria and nutrient)and S1 to S9 at varying bacteria and calcium lactate concentrations and the effect of the bacteria cell density and calcium lactate concentration on the compressive strength,sorptivity and tensile strength with age were evaluated using experimental program and statistical packages(ANOVA and post hoc tests).The result of both the experimental program and statistical evaluation shows that the incorporation of sporosarcina pasteurii and calcium lactate as nutrients had a positive impact on the properties of the ternary blended self-compacting concrete.展开更多
A high strength self-compacting pervious concrete(SCPC) with top-bottom interconnected pores was prepared in this paper. The frost-resisting durability of such SCPC in different deicing salt concentrations(0%, 3%, 5%,...A high strength self-compacting pervious concrete(SCPC) with top-bottom interconnected pores was prepared in this paper. The frost-resisting durability of such SCPC in different deicing salt concentrations(0%, 3%, 5%, 10%, and 20%) was investigated. The mass-loss rate, relative dynamic modulus of elasticity, compressive strength, flexural strength and hydraulic conductivity of SCPC after 300 freeze-thaw cycles were measured to evaluate the frost-resisting durability. In addition, the microstructures of SCPC near the top-bottom interconnected pores after 300 freeze-thaw cycles were observed by SEM. The results show that the high strength SCPC possesses much better frost-resisting durability than traditional pervious concrete(TPC) after 300 freeze-thaw cycles, which can be used in heavy loading roads. The most serious freeze-thaw damage emerges in the SCPC immersed in the 3% of Na Cl solution, while there is no obvious damage in 20% of Na Cl solution. Furthermore, it can be deduced that the high strength SCPC can be used for 100 years in a cold environment.展开更多
In recent decades,the utilization of waste tires,plastic and artificial shale ceramsite as alternative fine aggregate to make self-compacting concrete(SCC)has been recognized as an eco-friendly and sustainable method ...In recent decades,the utilization of waste tires,plastic and artificial shale ceramsite as alternative fine aggregate to make self-compacting concrete(SCC)has been recognized as an eco-friendly and sustainable method to manufacture renewable construction materials.In this study,three kinds of recycled aggregates:recycled tire rubber particles,wood-plastic particles,artificial shale ceramsite were used to replace the sand by different volume(5%,10%,20%and 30%),and their effects on the fresh and hardened properties of SCC were investigated.The slump flow and V-funnel tests were conducted to evaluate the fresh properties of modified-SCC mixtures.The hardened properties include 3,7 and 28-day compressive strengths,axial compressive strength,static elastic modulus,and compressive stress-strain behavior at 28 days.The test results showed that the incorporation of these three kinds of alternative aggregates had a negative impact on the fresh properties of SCC.Besides,the 28-day compressive strength and axial compressive strength decreased with the increase of rubber and wood-plastic particles content.In this experiment,all the three kinds of recycled aggregates can improve the ductility and deformability of SCC,and the most excellent performance comes from SCC with recycled rubber particles.展开更多
High-performance concrete (HPC) has specific performance advantages over conventional concrete in strength and durability. HPC mixtures are usually produced with water/binder mass ratios (mW/mB) in the range of 0....High-performance concrete (HPC) has specific performance advantages over conventional concrete in strength and durability. HPC mixtures are usually produced with water/binder mass ratios (mW/mB) in the range of 0.2-0.4, so volume changes of concrete as a result of drying, chemical reactions, and temperature change cannot be avoided. For these reasons, shrinkage and cracking are frequent phenomena. It is necessary to add some types of admixture for reduction of shrinkage and cracking of HPC. This study used a shrinkage-reducing admixture (SRA) for that purpose. Concrete was prepared with two different mW/mB (0.22 and 0.40) and four different mass fractions of SRA to binder (w(SRA) = 0%, 1%, 2%, and 4%). The mineral admixtures used for concrete mixes were: 25% fly ash (FA) and 25% slag by mass of binder for the mixture with mW/mB = 0.40, and 15% silica fume (SF) and 25% FA for the mixture with mW/mB = 0.22. Tests were conducted on 24 prismatic specimens, and shrinkage strains were measured through 120 days of drying. Compressive strength, splitting strength, and static modulus of elasticity were also determined. The results show that the SRA effectively reduces some mechanical properties of HPC. The reductions in compressive strength, splitting tensile strength, and elastic modulus of the concrete were 7%-24%, 9%-19%, and 5%-12%, respectively, after 90 days, compared to concrete mixtures without SRA. SRA can also help reduce drying shrinkage of concrete. The shrinkage strains of HPC with SRA were only as high as 41% of the average free shrinkage of concrete without SRA after 120 days of drying.展开更多
The improvements of the mechanical properties, including bulk density of fresh mixtures, elastic modulus, and compressive strengths of four high-performance concrete mixtures, made with the addition of fly ash, refine...The improvements of the mechanical properties, including bulk density of fresh mixtures, elastic modulus, and compressive strengths of four high-performance concrete mixtures, made with the addition of fly ash, refined ground blast - furnace microslag (microslag) and silica fume are studied. The concrete mixtures were determined based on the dispersion testing results. The study indicates that the elastic modulus at 28 and 91 days, and compressive strengths of the concretes are improved a lot when fly ash and microslag by 25 percent by weight of cement are added into the mixtures individually. The improvement is especially evident when silica fume by 5 percent and fly ash by 25 percent by weight of cement are added together into the mixture, while the fresh concrete mixture keeps a good workability. Through the analysis of chemically combined water ratios of the four mixtures at various hydration ages, it is found that the addition of all these mineral mixtures are beneficial to the hydration process, especially, at later stages, which might be one of the reasons for the improvement of mechanical properties. (Author abstract) 4 Refs.展开更多
Spalling and mechanical properties of FRHPC subjected to fire were tested on notched beams. The results confirm that the internal vapor pressure is the leading reason for spalling of high-performance concrete (HPC)....Spalling and mechanical properties of FRHPC subjected to fire were tested on notched beams. The results confirm that the internal vapor pressure is the leading reason for spalling of high-performance concrete (HPC). At the same time, the temperature-increasing velocity and constrained conditions of concrete element also play significant roles in spalling. Steel fibers cannot reduce the risk of spalling, although they have obvious beneficial effects on the mechanical properties of concrete before and after exposure to fire. Polypropylene (PP) fibers are very useful in preventing HPC from spalling, however, they have negative effects on the strengths. By using hybrid fibers (steel fibers+PP fibers), both good anti-spalling performance and improved mechanical properties come true, which may provide necessary safe guarantee for the rescue work and structure repair after fire disaster.展开更多
Self-compacting concrete (SCC) was used for the filling layer of CRTSⅢ plate ballastless track, which needs excellent workability. The rheological properties of SCC cement paste containing chemical admixtures (CA...Self-compacting concrete (SCC) was used for the filling layer of CRTSⅢ plate ballastless track, which needs excellent workability. The rheological properties of SCC cement paste containing chemical admixtures (CA) such as polycarboxylate-based superplasticizer (PCE), air-entraining agent (AE) and defoamer (DF) were investigated using a Brookfield R/S SST2000 soft solid tester with a vane geometry spindle. The cementitious materials were designed as one, two and, three components systems by addition of ordinary portland cement (OPC) with these chemical admixtures. The rheological properties of one-component system (PCE paste) were improved with increasing the content of PCE. For two components systems of PCE-AE and PCE-DF, yield stress and plastic viscosity reduced firstly and increased afterward with the increasing of AE content. And the plastic viscosity reached the optimum when the content of AE is 0.004wt%. In general, the trend of yield stress and plastic viscosity decreased with the increasing of the DF content. For three components systems, PCE-AE-DF systems, the rheological properties were improved compared with the sample with AE or DF, which attributed to mixes of the active components mentioned above (CA) which could have a synergetic effect.展开更多
High-performance concrete (HPC) is stronger and more durable than conventional concrete. However, shrinkage and shrinkage cracking are common phenomena in HPC, especially early-age cracking. This study assessed earl...High-performance concrete (HPC) is stronger and more durable than conventional concrete. However, shrinkage and shrinkage cracking are common phenomena in HPC, especially early-age cracking. This study assessed early-age cracking of HPC for two mixtures using restrained ring tests. The two mixtures were produced with water/binder mass ratio (mw/mB) of 0.22 and 0.40, respectively. The results show that, with greater steel thickness, the higher degree of restraint resulted in a higher interface pressure and earlier cracking. With steel thickness of 6 mm, 19 mm, and 30 mm, the age of cracking were, respectively, 12 days, 8 days, and 5.4 days with the mw/mB = 0.22 mixture; and 22.5 days, 12.6 days, and 7.1 days with the mw/mB= 0.40 mixture. Cases of the same steel thickness show that the ring specimens with a thicker concrete wall crack later. With the mw/mB = 0.22 mixture, concrete walls with thicknesses of 37.5 mm, 75 mm, and 112.5 mm cracked at 3.4 days, 8.0 days, and 9.8 days, respectively; with the mw/mB = 0.40 mixture, the ages of cracking were 7.1 days, 12.6 days, and 16.0 days, respectively.展开更多
The impermeability mechanism of water-proof self-compacting concrete (WPSCC )w as studied. The mechanism and influential factors, such as water-cement ratio(w /c), dosage of powder, superplasticizer, sand content, agg...The impermeability mechanism of water-proof self-compacting concrete (WPSCC )w as studied. The mechanism and influential factors, such as water-cement ratio(w /c), dosage of powder, superplasticizer, sand content, aggregate conte nt, fly ash, UEA, PP fiber, on compactibility and crack resistance of WPSCC were analyzed. A type of WPSCC successfully applied in tunnel liner with its validit ies, conveniences and economies by mockup test was developed and optimized. Expe rimental results show that the WPSCC has good workability, mechanical properties and impermeability when reasonable requirements are fulfilled.展开更多
Factors that have effect on concrete creep include mixture composition,curing conditions,ambient exposure conditions,and element geometry.Considering concrete mixtures influence and in order to improve the prediction ...Factors that have effect on concrete creep include mixture composition,curing conditions,ambient exposure conditions,and element geometry.Considering concrete mixtures influence and in order to improve the prediction of prestress loss in important structures,an experimental test under laboratory conditions was carried out to investigate compression creep of two high performance concrete mixtures used for prestressed members in one bridge.Based on the experimental results,a power exponent function of creep degree for structural numerical analysis was used to model the creep degree of two HPCs,and two series of parameters of this function for two HPCs were calculated with evolution program optimum method.The experimental data was compared with CEB-FIP 90 and ACI 209(92) models,and the two code models both overestimated creep degrees of the two HPCs.So it is recommended that the power exponent function should be used in this bridge structure analysis.展开更多
An orthotropic constitutive relationship with temperature parameters for plain highstrength high-performance concrete (HSHPC) under biaxial compression is developed. It is based on the experiments performed for char...An orthotropic constitutive relationship with temperature parameters for plain highstrength high-performance concrete (HSHPC) under biaxial compression is developed. It is based on the experiments performed for characterizing the strength and deformation behavior at two strength levels of HSHPC at 7 different stress ratios including a=σs : σ3=0.00:-1,-0.20:-1,-0.30 : -1,-0.40:-1,-0.50:-1,-0.75:-1,-1.00:-1, after the exposure to normal and high temperatures of 20, 200, 300, 400, 500 and 600℃, and using a large static-dynamic true triaxial machine. The biaxial tests were performed on 100 mm×100 mm×100 mm cubic specimens, and friction-reducing pads were used consisting of three layers of plastic membrane with glycerine in-between for the compressive loading plane. Based on the experimental results, failure modes of HSHPC specimens were described. The principal static compressive strengths, strains at the peak stress and stress-strain curves were measured; and the influence of the temperature and stress ratios on them was also analyzed. The experimental results showed that the uniaxial compressive strength of plain HSHPC after exposure to high temperatures does not decrease dramatically with the increase of temperature. The ratio of the biaxial to its uniaxial compressive strength depends on the stress ratios and brittleness-stiffness of HSHPC after exposure to different temperature levels. Comparison of the stress-strain results obtained from the theoretical model and the experimental data indicates good agreement.展开更多
To meet the requirements of construction of concretes filled in the steel tube arches,a C60 grade micro-expansive self-compacting concrete (SCC) was prepared from manufactured sand (MS).The utilization of MS with ...To meet the requirements of construction of concretes filled in the steel tube arches,a C60 grade micro-expansive self-compacting concrete (SCC) was prepared from manufactured sand (MS).The utilization of MS with a high content of quarry limestone fines was dealed for SCC applications.The workability,compressive and splitting strength,modulus of elasticity,restrained expansion and chloride ion permeability as well as freeze-thaw resistance of three MS-SCC mixes with fines content of 3%,7% and 10% were tested and compared with those of the natural sand (NS)-SCC mix.The experimental results indicate that the performances of the C60 MS-SCC with fines content of 7% are excellent and compared favorably with those of C60 NS-SCC.展开更多
It has become a research hotspot to explore raw material substitutes of concrete.It is important to research the mechanical properties of self-compacting concrete(SCC)with slag powder(SP)and rubber particle(RP)replaci...It has become a research hotspot to explore raw material substitutes of concrete.It is important to research the mechanical properties of self-compacting concrete(SCC)with slag powder(SP)and rubber particle(RP)replacing cement and coarse aggregate,respectively.12 kinds of composite modified self-compacting concrete(CMSCC)specimens were prepared by using 10%,20%and 30%SP and 30%,40%,50%and 60%RP.The rheological properties,mechanical properties and microstructure of the CMSCC were investigated.Results indicate that the workability,compressive strength,splitting tensile strength and flexural strength of CMSCC prepared by 20%SP and less than 40%RP are improved.In order to maximize the utilization of waste materials,20%SP and 40%RP can be used as the optimal ratio of the combined modifier.The microstructure shows that the addition of proper amount of SP is conducive to the formation of increasingly more uniform C-S-H gel.C-SH gel can fill the internal pores of the sample and enhance the adhesion between the aggregate,thus improving the mechanical properties of CMSCC.RP has a rougher surface and lower density and stiffness,which inhibits the workability and mechanical properties of CMSCC.The above research results have important theoretical and practical significance for the selection of raw materials of self-compacting concrete and the rational use of industrial wastes.展开更多
文摘The application of self-compacting recycled concrete can solve the problem of environmental pollution caused by construction waste but its mechanical properties have not been unified and need further study.The strength of recycled concrete is unstable,and its performance still needs further study.The combination of fixed sand and stone volume method and free water cement ratio method is used to determine the mix ratio of self-compacting recycled concrete.24 sets of slump expansion tests and 24 sets of cube axial compression tests were carried out to study the effect of recycled aggregate replacement rate on the flow performance and axial compressive strength of self-compacting recycled concrete,and the performance conversion formula of self-compacting recycled concrete was given.The results show that with the increase of the regenerated coarse aggregate substitution rate,the fluidity and filling property of the self-compacting regenerated concrete mix decreased.The failure of self-compacting recycled concrete is mainly due to the failure of strength between old mortar and new mixture.As the substitution rate increases from 0 to 100%,the axial compressive strength decreases by 15.2%.
文摘Recycled large aggregate self-compacting concrete (RLA-SCC) within multiple weak areas. These weak areas have poor resistance to chloride ion erosion, which affects the service life of RLA-SCC in the marine environment. A three-dimensional multi-phase mesoscopic numerical model of RLA-SCC was established to simulate the chloride ions transportation in concrete. Experiments of RLA-SCC immersing in chloride solution were carried out to verify the simulation results. The effects of recycled large aggregate (RLA) content and RLA particle size on the service life of concrete were explored. The results indicate that the mesoscopic numerical simulation results are in good agreement with the experimental results. At the same depth, the closer to the surface of the RLA, the greater the chloride ion concentration. The service life of RLA-SCC in marine environment decreases with the increase of RLA content. Compared with the service life of 20% content, the service life of 25% and 30% content decreased by 20% and 42% respectively. Increasing the particle size of RLA can effectively improve the service life of RLA-SCC in chloride environment. Compared with the service life of 50 mm particle size, the service life of 70 mm and 90 mm increased by 61% and 163%, respectively. .
文摘The aim and scope of the present study were to determine the efficacy of UFFA in evaluating the workability,static and dynamic stabilization properties,retention period,and slump loss of SCC systems in their fresh state,as well as their compressive strength at various ages.Microstructure(SEM and XRD)of blended SCC systems were studied.Also,the thermogravimetry behavior of blended SCC specimens were researched.According to the evaluated results,incorporating up to 20%UFFA into fresh concrete improved its performance due to its engineered fine particle size and spherical geometry,both of which contribute to the enhancement of characteristics.Blends of 25%and 30%of UFFA show effect on the water-binder ratio and chemical enhancer dosage,resulting in a loss of homogeneity in fresh SCC systems.The reduced particle size,increased amorphous content,and increased surface area all contribute to the pozzolanic reactivity of the early and later ages,resulting in denser packing and thus an increase in compressive strength.The experimental results indicate that UFFA enhances the properties of SCC in both its fresh and hardened states,which can be attributed to the particles’fineness and their relative effect on SCC.
基金Funded by the National Natural Science Foundation of China(No.51578325)。
文摘To investigate the assumptions proposed in this paper,the evolution law governing the strength and expansion performance of MgO and nano-MgO micro-expansive concrete in the environment of mineral powder was firstly observed in this study.Secondly,SEM,XRD,and TG-DSC microscopic tests were conducted to reveal the effects of the active mineral-powder admixture on the hydration degree and expansion performance of MgO and nano-MgO in HPC.Our experimental results successfully verified our hypothesis,which indicated that the expansion performance of macro-MgO and nano-MgO was indeed depressed by the addition of active mineral power admixtures,even though the mechanical property of concrete composites was effectively improved.Furthermore,the hydration test also demonstrated the negative interference on the mineral powders,which was induced by the expansion agents.It is found the amounts of hydrates tend to decrease because the mineral powder ratio reaches and exceeds 40%.Moreover,it is also concluded the effect of expansion agents is governed by the alkalinity cement paste,especially for the nano-MgO.In other words,the expansion performance of nano-MgO will vary more obviously with the hydration process,than MgO.The results of this study provide that effective experimental and theoretical data support the hydration-inhibition mechanism of magnesium expansive agents.
基金Funded by the National Natural Science Foundation of China(Nos.U1934206 and 52108260)the Foundation of China Academy of Railway Science Corporation Limited(No.2020YJ049)。
文摘By the addition of superplasticizer and air entraining agent,manufactured sand selfcompacting concrete(MS SCC)with slump flow varying from 500 to 700 mm and air content varying from 2.0%to 9.0%were prepared and the pumpability of MS SCC was studied by a sliding pipe rheometer(Sliper).According to the Kaplan’s model,the initial pump pressure and the pump resistance of MS SCC were obtained.Meanwhile,rheological properties including the yield stress and the plastic viscosity of MS SCC were measured by a rheometer.The experimental results show that the increase of slump flow contributes to a higher pumpability and a proper air content,i e,6%is beneficial for the pumpability of MS SCC.Due to the existence of stone powder and stronger angularity of MS,the initial pump pressure of MS SCC is only about 60%-88%that of river sand(RS)SCC with the same slump flow and air content,indicating that MS SCC possesses a higher pumpability than RS SCC.
基金supported by the National Key Research and Development Program of China(No.2021YFB3802005)the National Natural Science Foundation of China(Grant No.51978002)+1 种基金the Natural Science Foundation for the Higher Education Institutions in Anhui Province of China(Grant No.KJ2020A0845)the Housing and Urban-Rural Construction Science and Technology Plan in Anhui Province of China(Grant No.2021-YF69).
文摘This study focuses on the workability and compressive strength of ceramsite self-compacting concrete with fine aggregate partially substituted by steel slag sand(CSLSCC)to prevent the pollution of steel slag in the environment.The SF,J-ring,visual stability index,and sieve analysis tests are primarily employed in this research to investigate the workability of freshly mixed self-compacting concrete containing steel slag at various steel slag sand replacement rates.The experiment results indicate that CSLSCC with the 20%volume percentage of steel slag(VPS)performs better workability,higher strength,and higher specific strength.The 7-day compressive strength of CSLSCC with the 0.4 of the water-binder ratio(W/B),decreases with the increase of steel slag content,while the 28-day compressive strength increases significantly.The ceramsite self-compacting concrete with good comprehensive performance can be obtained when the substitution rate of steel slag sand for fine aggregate is less than 20%(volume percentage).
基金supported by National Natural Science Foundation of China(Project No.51468003)Natural Science Foundation of Guangxi Province(Project No.2018GXNSFAA050007).
文摘Different rubber aggregates lead to changes in the effect of stress conditions on the mechanical behavior of concrete,and studies on the triaxial properties of self-compacting rubber concrete(SCRC)are rare.In this study,35 cylindrical specimens taking lateral stress and rubber type as variables were prepared to study the fresh properties and mechanical behaviors of SCRC under triaxial compression,where the rubber contains two types,i.e.,380μm rubber powder and 1–4 mm rubber particles,and four contents,i.e.,10%,20%and 30%.The test results demonstrated that SCRC exhibited a typical oblique shear failure mode under triaxial compression and had a more moderate descending branch compared with self-compacting concrete(SCC).The presence of lateral stress can significantly improve the compression properties,including initial elastic modulus,peak stress and peak strain,with an improvement range of 3%–73%for peak stress.While rubber aggregates mainly targeted the deformation abilities and toughness for improvement,and the peak strain improvement ranges were 0.1–3.1 times and 0.1–1.0 times for SCRC containing rubber powder and SCRC containing rubber particles,respectively,relative to SCC.At a high lateral stress of at least 12 MPa,the loss of strength due to the addition of rubber can be controlled within 10%,in which case the content of rubber powder and rubber particles was recommended to be at most 20%and 30%,respectively.Based on the Mohr-Coulomb theory,the failure criteria of SCRC with different rubber types were established.For analysis and design purposes,an empirical model was proposed to predict the stressstrain behavior under triaxial compression,considering the influence of different rubber content and lateral stress.The results obtained in this study can provide a valuable reference for the design and application of self-compacting rubberized concrete in practical projects,especially those involving three-way compression states and requiring high-quality deformation and energy dissipation.
文摘This research was carried out to evaluate the relationship between the incorporation of calcite precipitation bacteria,sporosarcina pasteurii using calcium lactate as nutrient source and the properties of calcined clay and limestone powder blended self-compacting concrete.Ten mixes were designed and designated S0 to S9 with S0 the control(without bacteria and nutrient)and S1 to S9 at varying bacteria and calcium lactate concentrations and the effect of the bacteria cell density and calcium lactate concentration on the compressive strength,sorptivity and tensile strength with age were evaluated using experimental program and statistical packages(ANOVA and post hoc tests).The result of both the experimental program and statistical evaluation shows that the incorporation of sporosarcina pasteurii and calcium lactate as nutrients had a positive impact on the properties of the ternary blended self-compacting concrete.
基金Funded by the National Natural Science Foundation of China(No.51878081).
文摘A high strength self-compacting pervious concrete(SCPC) with top-bottom interconnected pores was prepared in this paper. The frost-resisting durability of such SCPC in different deicing salt concentrations(0%, 3%, 5%, 10%, and 20%) was investigated. The mass-loss rate, relative dynamic modulus of elasticity, compressive strength, flexural strength and hydraulic conductivity of SCPC after 300 freeze-thaw cycles were measured to evaluate the frost-resisting durability. In addition, the microstructures of SCPC near the top-bottom interconnected pores after 300 freeze-thaw cycles were observed by SEM. The results show that the high strength SCPC possesses much better frost-resisting durability than traditional pervious concrete(TPC) after 300 freeze-thaw cycles, which can be used in heavy loading roads. The most serious freeze-thaw damage emerges in the SCPC immersed in the 3% of Na Cl solution, while there is no obvious damage in 20% of Na Cl solution. Furthermore, it can be deduced that the high strength SCPC can be used for 100 years in a cold environment.
基金the financial support from the National Natural Science Foundation of China,grant number 11772351Double Shield TBM Material Optimization and Supporting Technology Research-TBM Segment Rapid Support Scientific Research Project[contract NO:PM2017/D02]the National Key R&D Program of China(No.2018YFC0406604).
文摘In recent decades,the utilization of waste tires,plastic and artificial shale ceramsite as alternative fine aggregate to make self-compacting concrete(SCC)has been recognized as an eco-friendly and sustainable method to manufacture renewable construction materials.In this study,three kinds of recycled aggregates:recycled tire rubber particles,wood-plastic particles,artificial shale ceramsite were used to replace the sand by different volume(5%,10%,20%and 30%),and their effects on the fresh and hardened properties of SCC were investigated.The slump flow and V-funnel tests were conducted to evaluate the fresh properties of modified-SCC mixtures.The hardened properties include 3,7 and 28-day compressive strengths,axial compressive strength,static elastic modulus,and compressive stress-strain behavior at 28 days.The test results showed that the incorporation of these three kinds of alternative aggregates had a negative impact on the fresh properties of SCC.Besides,the 28-day compressive strength and axial compressive strength decreased with the increase of rubber and wood-plastic particles content.In this experiment,all the three kinds of recycled aggregates can improve the ductility and deformability of SCC,and the most excellent performance comes from SCC with recycled rubber particles.
文摘High-performance concrete (HPC) has specific performance advantages over conventional concrete in strength and durability. HPC mixtures are usually produced with water/binder mass ratios (mW/mB) in the range of 0.2-0.4, so volume changes of concrete as a result of drying, chemical reactions, and temperature change cannot be avoided. For these reasons, shrinkage and cracking are frequent phenomena. It is necessary to add some types of admixture for reduction of shrinkage and cracking of HPC. This study used a shrinkage-reducing admixture (SRA) for that purpose. Concrete was prepared with two different mW/mB (0.22 and 0.40) and four different mass fractions of SRA to binder (w(SRA) = 0%, 1%, 2%, and 4%). The mineral admixtures used for concrete mixes were: 25% fly ash (FA) and 25% slag by mass of binder for the mixture with mW/mB = 0.40, and 15% silica fume (SF) and 25% FA for the mixture with mW/mB = 0.22. Tests were conducted on 24 prismatic specimens, and shrinkage strains were measured through 120 days of drying. Compressive strength, splitting strength, and static modulus of elasticity were also determined. The results show that the SRA effectively reduces some mechanical properties of HPC. The reductions in compressive strength, splitting tensile strength, and elastic modulus of the concrete were 7%-24%, 9%-19%, and 5%-12%, respectively, after 90 days, compared to concrete mixtures without SRA. SRA can also help reduce drying shrinkage of concrete. The shrinkage strains of HPC with SRA were only as high as 41% of the average free shrinkage of concrete without SRA after 120 days of drying.
基金Funded by the Reasearch Grant Council to Hongkong University of Science and Technology (Grant No. R1G94195. EG07).
文摘The improvements of the mechanical properties, including bulk density of fresh mixtures, elastic modulus, and compressive strengths of four high-performance concrete mixtures, made with the addition of fly ash, refined ground blast - furnace microslag (microslag) and silica fume are studied. The concrete mixtures were determined based on the dispersion testing results. The study indicates that the elastic modulus at 28 and 91 days, and compressive strengths of the concretes are improved a lot when fly ash and microslag by 25 percent by weight of cement are added into the mixtures individually. The improvement is especially evident when silica fume by 5 percent and fly ash by 25 percent by weight of cement are added together into the mixture, while the fresh concrete mixture keeps a good workability. Through the analysis of chemically combined water ratios of the four mixtures at various hydration ages, it is found that the addition of all these mineral mixtures are beneficial to the hydration process, especially, at later stages, which might be one of the reasons for the improvement of mechanical properties. (Author abstract) 4 Refs.
基金the National Natural Science Foundation of China (No. 50278013)
文摘Spalling and mechanical properties of FRHPC subjected to fire were tested on notched beams. The results confirm that the internal vapor pressure is the leading reason for spalling of high-performance concrete (HPC). At the same time, the temperature-increasing velocity and constrained conditions of concrete element also play significant roles in spalling. Steel fibers cannot reduce the risk of spalling, although they have obvious beneficial effects on the mechanical properties of concrete before and after exposure to fire. Polypropylene (PP) fibers are very useful in preventing HPC from spalling, however, they have negative effects on the strengths. By using hybrid fibers (steel fibers+PP fibers), both good anti-spalling performance and improved mechanical properties come true, which may provide necessary safe guarantee for the rescue work and structure repair after fire disaster.
基金Funded by the National Natural Science Foundation of China(No.51178363)
文摘Self-compacting concrete (SCC) was used for the filling layer of CRTSⅢ plate ballastless track, which needs excellent workability. The rheological properties of SCC cement paste containing chemical admixtures (CA) such as polycarboxylate-based superplasticizer (PCE), air-entraining agent (AE) and defoamer (DF) were investigated using a Brookfield R/S SST2000 soft solid tester with a vane geometry spindle. The cementitious materials were designed as one, two and, three components systems by addition of ordinary portland cement (OPC) with these chemical admixtures. The rheological properties of one-component system (PCE paste) were improved with increasing the content of PCE. For two components systems of PCE-AE and PCE-DF, yield stress and plastic viscosity reduced firstly and increased afterward with the increasing of AE content. And the plastic viscosity reached the optimum when the content of AE is 0.004wt%. In general, the trend of yield stress and plastic viscosity decreased with the increasing of the DF content. For three components systems, PCE-AE-DF systems, the rheological properties were improved compared with the sample with AE or DF, which attributed to mixes of the active components mentioned above (CA) which could have a synergetic effect.
文摘High-performance concrete (HPC) is stronger and more durable than conventional concrete. However, shrinkage and shrinkage cracking are common phenomena in HPC, especially early-age cracking. This study assessed early-age cracking of HPC for two mixtures using restrained ring tests. The two mixtures were produced with water/binder mass ratio (mw/mB) of 0.22 and 0.40, respectively. The results show that, with greater steel thickness, the higher degree of restraint resulted in a higher interface pressure and earlier cracking. With steel thickness of 6 mm, 19 mm, and 30 mm, the age of cracking were, respectively, 12 days, 8 days, and 5.4 days with the mw/mB = 0.22 mixture; and 22.5 days, 12.6 days, and 7.1 days with the mw/mB= 0.40 mixture. Cases of the same steel thickness show that the ring specimens with a thicker concrete wall crack later. With the mw/mB = 0.22 mixture, concrete walls with thicknesses of 37.5 mm, 75 mm, and 112.5 mm cracked at 3.4 days, 8.0 days, and 9.8 days, respectively; with the mw/mB = 0.40 mixture, the ages of cracking were 7.1 days, 12.6 days, and 16.0 days, respectively.
基金Funded By the Wuhan Natural Science Foundation for Distin guished Young Scholars(No.20035002016 13)
文摘The impermeability mechanism of water-proof self-compacting concrete (WPSCC )w as studied. The mechanism and influential factors, such as water-cement ratio(w /c), dosage of powder, superplasticizer, sand content, aggregate conte nt, fly ash, UEA, PP fiber, on compactibility and crack resistance of WPSCC were analyzed. A type of WPSCC successfully applied in tunnel liner with its validit ies, conveniences and economies by mockup test was developed and optimized. Expe rimental results show that the WPSCC has good workability, mechanical properties and impermeability when reasonable requirements are fulfilled.
文摘Factors that have effect on concrete creep include mixture composition,curing conditions,ambient exposure conditions,and element geometry.Considering concrete mixtures influence and in order to improve the prediction of prestress loss in important structures,an experimental test under laboratory conditions was carried out to investigate compression creep of two high performance concrete mixtures used for prestressed members in one bridge.Based on the experimental results,a power exponent function of creep degree for structural numerical analysis was used to model the creep degree of two HPCs,and two series of parameters of this function for two HPCs were calculated with evolution program optimum method.The experimental data was compared with CEB-FIP 90 and ACI 209(92) models,and the two code models both overestimated creep degrees of the two HPCs.So it is recommended that the power exponent function should be used in this bridge structure analysis.
文摘An orthotropic constitutive relationship with temperature parameters for plain highstrength high-performance concrete (HSHPC) under biaxial compression is developed. It is based on the experiments performed for characterizing the strength and deformation behavior at two strength levels of HSHPC at 7 different stress ratios including a=σs : σ3=0.00:-1,-0.20:-1,-0.30 : -1,-0.40:-1,-0.50:-1,-0.75:-1,-1.00:-1, after the exposure to normal and high temperatures of 20, 200, 300, 400, 500 and 600℃, and using a large static-dynamic true triaxial machine. The biaxial tests were performed on 100 mm×100 mm×100 mm cubic specimens, and friction-reducing pads were used consisting of three layers of plastic membrane with glycerine in-between for the compressive loading plane. Based on the experimental results, failure modes of HSHPC specimens were described. The principal static compressive strengths, strains at the peak stress and stress-strain curves were measured; and the influence of the temperature and stress ratios on them was also analyzed. The experimental results showed that the uniaxial compressive strength of plain HSHPC after exposure to high temperatures does not decrease dramatically with the increase of temperature. The ratio of the biaxial to its uniaxial compressive strength depends on the stress ratios and brittleness-stiffness of HSHPC after exposure to different temperature levels. Comparison of the stress-strain results obtained from the theoretical model and the experimental data indicates good agreement.
基金Funded by the Science and Technology Item of Communication Construction for West China (No.2009318811082)
文摘To meet the requirements of construction of concretes filled in the steel tube arches,a C60 grade micro-expansive self-compacting concrete (SCC) was prepared from manufactured sand (MS).The utilization of MS with a high content of quarry limestone fines was dealed for SCC applications.The workability,compressive and splitting strength,modulus of elasticity,restrained expansion and chloride ion permeability as well as freeze-thaw resistance of three MS-SCC mixes with fines content of 3%,7% and 10% were tested and compared with those of the natural sand (NS)-SCC mix.The experimental results indicate that the performances of the C60 MS-SCC with fines content of 7% are excellent and compared favorably with those of C60 NS-SCC.
基金This research was supported by the Key Science and Technology Projects in Transportation Industry(2018-MS2-051).
文摘It has become a research hotspot to explore raw material substitutes of concrete.It is important to research the mechanical properties of self-compacting concrete(SCC)with slag powder(SP)and rubber particle(RP)replacing cement and coarse aggregate,respectively.12 kinds of composite modified self-compacting concrete(CMSCC)specimens were prepared by using 10%,20%and 30%SP and 30%,40%,50%and 60%RP.The rheological properties,mechanical properties and microstructure of the CMSCC were investigated.Results indicate that the workability,compressive strength,splitting tensile strength and flexural strength of CMSCC prepared by 20%SP and less than 40%RP are improved.In order to maximize the utilization of waste materials,20%SP and 40%RP can be used as the optimal ratio of the combined modifier.The microstructure shows that the addition of proper amount of SP is conducive to the formation of increasingly more uniform C-S-H gel.C-SH gel can fill the internal pores of the sample and enhance the adhesion between the aggregate,thus improving the mechanical properties of CMSCC.RP has a rougher surface and lower density and stiffness,which inhibits the workability and mechanical properties of CMSCC.The above research results have important theoretical and practical significance for the selection of raw materials of self-compacting concrete and the rational use of industrial wastes.